• Journal of the Korean Wood Science and Technology
• /
• 제40권6호
• /
• pp.418-423
• /
• 2012

원통형 단판적층재(LVL)의 구조재 이외의 공예재 등의 용도개발을 위하여 원통형 단판적층재의 내수접착성과 도장처리에 따른 내마모성 및 표면경도를 측정하였다. 레조시놀 수지와 경화제(paraformaldehyde)를 100 : 5의 혼합비로 하여 접착 경화한 원통형 단판적층재의 전체적인 접착층에 대한 삶음박리 접착력은 양호한 편이었다. 내마모성은 횡단면이 접선단면보다 상대적으로 우수하였으며, 접선단면에 자외선 차단 오일을 도장 처리한 경우 내마모성이 향상되었다. 표면경도는 횡단면의 경우, 낙엽송 중심재가 라디에타소나무 단판적층 부위보다 높았고, 접선단면의 경우에는 접착층 부위가 단판부위보다 높게 나타났다.

• 펄프종이기술
• /
• 제33권4호
• /
• pp.15-20
• /
• 2001

The function of the moisture-proof paper is to prevent moisture from adsorbing into the packed goods. Water-vapor transmission rate of the moisture-proof paper should be less than 100g/$m^2$.24hr and the optimum rate would be less than 50g/$m^2$.24hr. In general the moisture-proof paper has been made by laminating polyethylene or polypropylene on top of the base paper. However this kind of moisture-proof paper has a problem in recycling so that it brings about environmental pollution. In general the moisture-proof paper has been made by laminating polyethylene or polypropylene on top of the base paper. However this kind of moisture-proof paper has a problem in recycling so that it brings about environmental pollution. The purpose of this paper was to make moisture-proof paper using the mixture of SB latex and wax emulsion which was recyclable and environmentally friendly. Water vapor transmission rate showed less than 50g/$m^2$.24hr in mixture ratio of 85:15, 87:13, 90:10. Especially the mixture ratio of 87:13 showed the most favorable water-vapor transmission rate. However, the moisture-proof layer was destroyed slightly by folding in packing. It has been observed that there was no close relationship between water-vapor transmission rate of the moisture-proof paper and grammage of the base paper, but the density of base paper had influenced on water vapor transmission rate. It was also observed that the moisture-proof paper could be recycled. The moisture-proof paper was similar to base paper in degree of the pulping, and there was no significant difference in dispersion between moisture-proof paper and base paper. Most of wax particles which caused the spots during drying process could be removed by flotation process. Tensile strength and tear strength of both moisture-proof paper and base paper after pulping were measured to examine the fiber bonding, and no significant difference in physical properties was observed.

• Journal of the Korean Wood Science and Technology
• /
• 제17권2호
• /
• pp.20-25
• /
• 1989

This study was carried out in order to investigate the treatment effect of PEG soln which is a common dimensional stabilizer to green log. sawing panel etc, on bonding product including plywood widely-used in secondary processing unit. The 30% concentration of aqueous PEG soln. with molecular weight of 400, 1.000 and 4,000 were prepared respectively, and also dipping the veneer in the PEG soln. spreading the PEG soln. on veneer and mixing the PEG soln. in the adhesive were allowed. Then the ratio of PEG impregnation on veneer, the adhesive strength of plywood were epitomized as follows: The ratio of impregnation by PEG 4,000 at dipping condition was highest. while that by PEG 400 at same condition was lowest. However, the effect of PEG molecular weight on the ratio of impregnation at spreading condition did not occur. 2. The adhesive strength was great in the order of 4,000>400>1,000 in molecular weight of PEG at dipping and spreading conditions. In case of mixing the PEG soln. in the adhesive, the adhesive strength was great in the order of 400>1,000>4,000 in molecular weight of PEG. Throughout three treatment conditions, PEG 400 was relatively favourable with about 10kg/$cm^2$ dry strength. 3. The adhesive strength was great 10 the order of spreading >dipping >mixing condition. 4. Although adhesive strength with the 30% concentration of aqueous PEG soln. was decreased by 35% and over, compared to control (non-treatment) adhesive strength, all types of PEG treatment except mixing the PEG soln. in the adhesive exceeded the standard dry strength for common use panel. 7.5kg/$cm^2$. 5. In warm water-proof test, the adhesive strengths by all PEG treatment conditions were less than the standard wet strength, 7.5kg cot, and also delamination of glue line occured mostly in mixing in the PEG soln. in the adhesive condition.

• 한국도로학회논문집
• /
• 제11권3호
• /
• pp.1-11
• /
• 2009

본 연구에서는 MMA 계열의 폴리머 콘크리트를 콘크리트 교량 상판의 박층 교면포장용으로 적용 가능성에 대한 검토를 수행하였다. 아크릴수지와 경화재, 충진재(탄산칼슘 및 규사)로 구성되어진 아크릴 콘크리트의 성분 종류 및 배합비율 등이 아크릴 콘크리트의 물리적 특성에 미치는 영향을 파악하기 위하여 점도시험, 압축강도시험, 휨시험 등을 수행하였으며, 시험을 통해 최적 배합비율을 결정하였다. 최적 배합비율로 생산된 아크릴 콘크리트에 대해 투수저항성, 염소이온 침투 저항성, 경화수축량, 열팽창계수, 부착강도 시험 등의 물리적 특성 시험을 실시하였다. 시험결과 폴리머 콘크리트가 기존의 일반 시멘트 콘크리트에 비해 방수성능이 우수하고 염소이온 침투 저항성도 우수한 것으로 나타났다. 또한 기존 바닥 콘크리트와의 부착성도 우수하고 균열 저항성도 우수한 것으로 나타났다. 기존의 아크릴 수지는 경화시 수축량이 크고, 열팽창계수 또한 일반 시멘트 콘크리트에 비해 큰 단점이 있으나 본 연구에서 새롭게 개발한 아크릴 수지를 적용한 결과 대폭 증가된 연성으로 인해 균열발생 가능성을 낮출 수 있을 것으로 확인되었다.