• 한국재료학회지
• /
• 제14권2호
• /
• pp.126-132
• /
• 2004

The high strength steel sheets has been widely used as the automobile parts to reduce the weight of a vehicle. The aim of this research is to develop the TRIP aided high strength low carbon steels using reverse transformation process. The 0.15C-4Mn and 0.15C-6.5Mn steel sheets were reversely transformed by slow heating to intercritical temperature region and air cooling to room temperature. The stability of retained austenite depends on the enrichment of carbon and manganese by diffusion during the reverse transformation. The amount of retained austenite formed after reversely transformed at $645^{\circ}C$ for 12 hrs. was about 46vol.% in hot rolled 0.lC-6.5Mn steel. The change in volume fraction of retained austenite with a holding temperature was consistent with the changes in elongation and the strength-ductility combination. The tendency of tensile strength to increase with increasing the holding temperature was due to the decrease of retained austenite after cooling from the higher temperature of $670 ^{\circ}C$. The maximum strength-ductility combination was about 4,250 kg/$\textrm{mm}^2$ㆍ% when the hot rolled 0.lC-6.5Mn steel was reversely transformed at $645^{\circ}C$ for 12 hrs.

• 자원리싸이클링
• /
• 제23권4호
• /
• pp.21-29
• /
• 2014

폐리튬이온전지 NCM($Li(Ni_xCo_yMn_z)O_2$)양극활물질 내에는 코발트(15 ~ 20%), 니켈(25 ~ 30%), Mn(10 ~ 15%) 및 리튬(5 ~ 10%) 등의 유가금속이 존재한다. 본 연구에서는 폐리튬이온전지 NCM 양극활물질로부터 친환경 유기산인 말릭산을 이용한 유가금속 침출 공정을 연구하였다. 주요공정인자는 말릭산 농도, 과산화수소 농도, 고액비, 반응온도 등이었으며, 침출액 내 금속농도는 ICP-OES(Inductively Coupled Plasma Optic Emission Spectrometer)를 통해 분석하였다. 환원제($H_2O_2$) 첨가로 인해 유가금속의 침출율이 상승하는 효과를 얻었으며, 최적공정인자는 말릭산 2 M, 과산화수소 5 vol.%, 고액비(solid/liquid ratio) 5 wt.%, 반응온도 $80^{\circ}C$이었으며, 침출율은 코발트 99.10%, 니켈 99.80%, 리튬 99.75%이었다.

• 한국재료학회지
• /
• 제11권4호
• /
• pp.283-289
• /
• 2001

50/50 vol% LSM-YSZ (La$_{1-x}$Sr$_{x}$MnO$_3$-yttria stabilized zirconia)의 복합공기극이 콜로이드 증착법에 의해 연마된 YSZ 전해질상에 증착되었다. 그 전극 특성은 주사전자현미경, X선회절과 임피던스 분석기에 의해 연구되어졌다. 90$0^{\circ}C$에서 공기/LSM -YSZ/YSZ/Pt/공기 셀에 대해 측정된 전형적인 임피던스 스펙트럼들은 2개의 불완전한 호(depressed arc)로 구성되었다. LSM 전극에 대한 YSZ의 첨가는 전극내의 삼상계(TPB) 영역을 증가시켰으며, 이것이 LSM-YSZ 복합공기극의 비저항을 감소시켰다. 또한 전해질 표면의 불순물 제거와 TPB 길이의 증가를 위한 전해질 표면연마는 공기극의 비저항을 훨씬 더 감소시켰다. LSM-YSZ 공기극의 비저항은 작동온도, 공기극의 조성과 입자크기, 인가전류 및 전해질의 표면거칠기에 의해 큰 영향을 받았다.

• 한국세라믹학회지
• /
• 제38권9호
• /
• pp.860-865
• /
• 2001

본 논문은 출발물로서 2mol% CdO가 치환된 $0.05Pb(Mn_{1/3}Sb_{2/3})O_3-0.95Pb(Zr_{0.52}Ti_{0.48})O_3$ 분말을 제조 후, 닥터 블레이드 방법으로 green sheet를 제조하기 위한 slurry의 최적 공정첨가제 조성에 관한 연구를 수행하였다. 또한, 제조된 green sheet에 대하여 소결 특성과 두께 변환에 따른 유전 및 압전 특성을 관찰하였다. 공정첨가제의 첨가에 따른 점도거동을 통하여 slurry를 최적화하였고, TGA 분석으로 소결조건을 정하였으며, sheet의 특성에 미세구조와 XRD 등으로 측정하였다. 최적의 slurry는 고형분량 30vol%에 대해 분산제 3.0wt%에서 가장 안정화되었고, 이후 바인더/가소제(0.75/0.25) 3.0wt% 첨가시 점도는 7.55Pa${\cdot}$s이었다. Green sheet의 유전 및 압전 특성들은 각각 900$^{\circ}$C, 950$^{\circ}$C, 1000$^{\circ}$C로 소결온도를 증가함에 따라 다소 증가하였지만, 두께에 따른 특성들은 큰 변화가 관찰되지 않음을 확인하였다.

• 한국재료학회지
• /
• 제22권9호
• /
• pp.470-475
• /
• 2012

$La_{1-x}Sr_xMnO_3$(LSM,$0{\leq}x{\leq}0.5$) powders as the air electrode for solid oxide fuel cell were synthesized by a glycine-nitrate combustion process. The powders were then examined by X-ray diffraction(XRD) and scanning electron microscopy (SEM). The as-formed powders were composed of very fine ash particles linked together in chains. X-ray maps of the LSM powders milled for 1.5 h showed that the metallic elements are homogeneously distributed inside each grain and in the different grains. The powder XRD patterns of the LSM with x < 0.3 showed a rhombohedral phase; the phase changes to the cubic phase at higher compositions($x{\geq}0.3$) calcined in air at $1200^{\circ}C$ for 4 h. Also, the SEM micrographs showed that the average grain size decreases as Sr content increases. Composite air electrodes made of 50/50 vol% of the resulting LSM powders and yttria stabilized zirconia(YSZ) powders were prepared by colloidal deposition technique. The electrodes were studied by ac impedance spectroscopy in order to improve the performance of a solid oxide fuel cell(SOFC). Reproducible impedance spectra were confirmed using the improved cell, which consisted of LSM-YSZ/YSZ. The composite electrode of LSM and YSZ was found to yield a lower cathodic resistivity than that of the non-composite one. Also, the addition of YSZ to the $La_{1-x}Sr_xMnO_3$ ($0.1{\leq}x{\leq}0.2$) electrode led to a pronounced, large decrease in the cathodic resistivity of the LSM-YSZ composite electrodes.

• Environmental Analysis Health and Toxicology
• /
• 제17권4호
• /
• pp.333-339
• /
• 2002

Yellow sand (YS) storms were observed about ten times in the Korean peninsula during March and April in 2002. Twenty four hour fine particle (PM$\_$2.5/) samples were collected onto the 47 mm Teflon - coated quartz filters over 9 days during and after the events using the MiniVol Portable Air Sampler at a flow rate of 5 liters per minute. The highest PM$\_$2.5/ concentration measured during the YS period was 289 $\mu\textrm{g}$/㎥, which is 13 times higher than the lowest of the values for the samples collected during the non-yellow sand period. The filter samples were analyzed for inorganic ions using the IC, AAS and Autoanalyzer, and for metals using the ICP-MS. The results showed that the concentrations of some inorganic ions (e.g., Ca$\^$2+/ and SO$_4$$\^$2-/) and metals (e.g., Fe, Mn) of soil origin were elevated during the yellow sand events.

• 한국광물학회지
• /
• 제17권4호
• /
• pp.309-325
• /
• 2004

연구는 호주 퀸즈랜드 주 북서부에 위치하는 은-납-아연 캔닝턴 광상은 호상편마암, 미그마타이트, 규선석-석류석 편암 그리고 각섬암으로 구성된 모암 주변부에서 발달해 있다. 모암에서 산출되는 규선석의 세 가지 다른 결정형태, 규선석을 포획광물로 함유한 아연-첨정석과 석류석 반상변정은 모암의 변성작용과 아연과 관련된 광화작용에 대한 지질학적 지시자로 사용되었다. 변성작용과 아연 광화작용과의 관계는 프로그램 THERMOCALC를 이용하여 KFMASH (K$_2$O-FeO-MgO-A1$_2$O$_3$-SiO$_2$- $H_2O$), KFMASHTO (K$_2$O-FeO-MgO-A1$_2$O$_3$-SiO$_2$-$H_2O$-TiO$_2$-Fe$_2$O$_3$), NCKFMASH ($Na_2$O-CaO-K$_2$O-FeO-MgO-Al$_2$O$_3$-SiO$_2$-$H_2O$) 그리고 MnNCKFMASH (MnO-$Na_2$O-CaO-K$_2$O-FeO-MgO-Al$_2$O$_3$-SiO$_2$-$H_2O$) 화학계에서 이들 세 가지 광물의 공생관계와 규선석-석류석-부분용융의 상평형 관계를 이용하여 결정하였다. MnNCKFMASH와 NCKFMASH계에서 부분 용융은 KFMASH와 KFMASHTO계에서 보다 낮은 온도에서 일어나며, MnNCKFMASH 계에서 용융 온도는 암석 화학 성분의 Na+Ca+K)의 비가 증가함에 따라 감소하는 경향을 보인다. 캔닝턴 광상의 모암은 MnNCKFMASH계의 경우 최고 온도와 압력 환경에서(634$\pm$62$^{\circ}C$, 4.8$\pm$1.3 kbar) 약 15% 용융되지만, KFMASHTO계하에서는 부분 용융이 일어나지 않는다. 규선석의 등변성도선과 모드 비의 변화를 근거로, 주상과 능면형의 규선석과 주상의 규선석을 포획하는 아연-첨정석 반상변정은 부분 용융을 포함하는 온도와 압력의 증가(약 550～$600^{\circ}C$, 2.0～3.0 kbar에서 700～75$0^{\circ}C$, 5.0～7.0 kbar)로 인한 것으로 생각된다. 또한 이와 같은 변성작용 동안의 최대 수축 변형 방향은 남-북 그 다음 동서 방향으로 주로 D$_1$과 D$_2$ 변형작용 동안에 형성되어졌다. 결론적으로 아연-첨정석의 성장과 관련된 아연 광화 작용은 D$_2$ 동안에 일어났고 그 후 부분 용융과 후기 변형/변성작용에 의해 재배치 또는 재농집 되어진 것으로 생각된다.

• 전기화학회지
• /
• 제17권2호
• /
• pp.103-110
• /
• 2014

본 연구에서는 리튬 이차 전지의 가연성이 높은 액체 전해액의 대체 또는 개선을 위하여 이온성 액체 전해액으로 전극들에서의 거동을 관찰하였다. 이온성 액체인 1-ethyl-1-methyl piperidinium bis(trifluoromethanesulfonyl)imide(PP12 TFSI)는 녹는점이 $85^{\circ}C$이므로 상온에서 고체상이다. PP12 TFSI를 단독으로 전해액에 사용할 수 없으므로 리튬 이온 전지용 용매와 혼합하여 사용한다. PP12 TFSI를 50 wt.% 이상 사용하면 난연성이 아주 좋은 반면에 점도가 높아서 전해액 함침이 어렵다. 이온성 액체의 비율을 44 wt.%(이온성 액체:용매=1:1.25 wt.%)로 맞추고, 혼합한 용매는 EC/DEC(1/1 vol.%)이며, $LiPF_6$의 농도가 1.5 M이 되도록 전해액을 준비하여 연구하였다. 준비한 전해액은 자가소화시간 25초의 준수한 난연성을 가지고 있으며, 여러 종류의 전극에서도 우수한 수명 성능을 보여주었다. 적용된 전극은 $LiNi_{0.5}Mn_{1.5}O_4(LNMO)$, $LiFePO_4(LFP)$, $Li_4Ti_5O_{12}(LTO)$, artificial graphite이며, 특히 음극으로 사용된 artificial graphite에서의 전해액 분해를 방지하기 위한 첨가제의 거동도 관찰하였다. 여전히 전극으로의 함침의 문제가 다소 관찰이 되었으며 이런 문제가 개선될 수 있는 최적화된 혼합 이온성 액체 전해액이 개발된다면 이온성 액체의 난연성 특성은 더욱 활용성이 높아질 것이다.

• 한국재료학회지
• /
• 제9권11호
• /
• pp.1075-1082
• /
• 1999

50/50 vol% LSM-YSZ의 복합공기극(LSM=$\textrm{La}_{1-x}\textrm{Sr}_{x}\textrm{MnO}_{3}$(0$\leq$x$\leq$0.5))이 콜로이드 증착법에 의해 준비으며 주사전자현미경과 임피던스 분석기에 의해 연구되어졌다. 재현성있는 임피던스 스펙트럼들이 LSM-YSZ/YSZ/LSM-YSZ로 구성된 향상된 셀을 사용함으로써 얻어졌다. 이러한 셀들의 임피던스 스펙트럼들은 작동온도에 강하게 영향을 받았으며, 가장 안정된 조건은 $900^{\circ}C$에서 도달되어졌다. $900^{\circ}C$에서 공기//공기 셀에 대해 측정된 전형적인 임피던스 스펙트럼들은 2개의 불완전한 호(depressed arc)로 구성되었다. LSM전극에 대한 YSZ의 첨가는 LSM-YSZ 공기극의 저항 감소를 가져왔으며, 전해질 표면의 불순물의 영향을 제거하기 위한 연마는 공기극 저항을 더욱 감소시켰다. 또한 촉매층(Ni 혹은 Sr)을 가진 LSM-YSZ 전극은 촉매층이 없는 경우에 비해 공기극 저항의 감소를 가져왔다. LSM-YSZ 공기극 저항은 전극조성, 전해질의 형태, 인가 전류에 의해 영향을 받았다.

• 자원리싸이클링
• /
• 제30권5호
• /
• pp.57-66
• /
• 2021

본 연구에서는 습식제련 공정을 이용하여 저품위 동광으로부터 구리를 회수하고자 하였다. 침출시료는 저품위 동광을 파·분쇄하여 0.355 mm 이하로 입도분리하였으며, 1.5%의 구리, 4.7%의 철, 1.0%의 망간 그리고 0.3%의 아연을 함유하고 있다. XRD 분석 결과 구리는 산화물 형태로 관찰이 되었으며3 M 황산, 80℃ 조건에서 97%의 구리를 침출하였다. 침출용액으로부터 LIX9894N를 사용한 용매추출 공정을 통해 구리를 철, 망간, 아연으로부터 회수하였다. 구리와 다른 금속들 사이의 분리 경향은 분배비와 분리계수를 통해 확인하였다. McCabe-Thiele Diagram을 작도하여, 구리를 회수하는 최적 조건으로 5 vol.% LIX984N, O/A 비율 0.5, 향류 2단 추출을 설정하였다. 이 조건에서 99%의 구리를 추출할 수 있었으며, 2 M 황산으로 탈거한 후에 1.6 g/L의 구리를 함유한 황산구리 용액을 얻을 수 있었다.