• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.05a
• /
• pp.180-182
• /
• 2002

Copper thin films are prepared by a chemical vapor deposition technology for multi-level metallzations in ULSI fabrication. The copper films were deposited on TiN/Si substrates in helium atmosphere with the substrate temperature between $120^{\circ}C$ and $300^{\circ}C$. In order to get more reliable metallizations, effects on the post-annealing treatment to the electrical properties of the copper films have been investigated. The Cu films were annealed at the $5\times$10^{-6}$ Torr vacuum condition, and the electrical resistivity and the nano-structures were measured for the Cu films. The electrical resistivity of Cu films shown to be reduced by the post-annealing. The electrical resistivity of 2.2 $\mu$$\Omega$.cm was obtained for the sample deposited at the substrate temperature of $180^{\circ}C$ after vacuum annealed at $300^{\circ}C$. The resistivity variations of the films was not exactly matched with the size of the nato-structures of the copper grains, but more depended on the deposition temperature of the copper films.

• Journal of the Korean Vacuum Society
• /
• v.4 no.S2
• /
• pp.163-169
• /
• 1995

Ion beam assisted deposition(IBAD) technique was used to synthesize hard coatings including diamond-like carbon(DLC), carbon nitride(CN) and metal-ceramic multilayered films. It was found that DLC films formed at low energy ion bombardment possess more $Sp^3$ bonds and much higher hardness. The films exhibited an excellent wear resistance. Nanometer multialyered Fe/TiC films was deposited by ion beam sputtering. The structure and properties were strongly dependent on the thickness of the individual layers and modulation wave length. It was disclosed that both hardness and toughness of the films could be enhanced by adjusting the deposition parameters. The CN films synthesized by IBAD method consisted of tiny crystallites dispersed in amorphous matrix, which were identified by electron diffraction pattern to be $\beta -C_3N_4$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.130-130
• /
• 2010

Thin Si films were grown by a plasma-enhanced chemical vapor deposition (PECVD, SNTEK, Korea) system. Two different deposition condition were applied and formed a fully amorphous Si (a-Si) film and a micromorph mixing of microcrystalline Si (mc-Si) and a-Si film. Under one sun illumination, the micromorph device provided the enhanced open circuit voltage and fill factor values. It presents the fabrication of the micromorph Si film and the a-Si film by modulating a deposition condition. The performances of the Si thin film Schottky solar cells are discussed.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.87-87
• /
• 2010

We report a new patterning technique of inorganic materials by using thin-film transfer printing (TFTP) with atomic layer deposition. This method consists of the atomic layer deposition (ALD) of inorganic thin film and a nanotransfer printing (nTP) that is based on a water-mediated transfer process. In the TFTP method, the Al2O3 ALD growth occurs on FTS-coated PDMS stamp without specific chemical species, such as hydroxyl group. The CF3-terminated alkylsiloxane monolayer, which is coated on PDMS stamp, provides a weak adhesion between the deposited Al2O3 and stamp, and promotes the easy and complete release of Al2O3 film from the stamp. And also, the water layer serves as an adhesion layer to provide good conformal contact and form strong covalent bonding between the Al2O3 layer and Si substrate. Thus, the TFTP technique is potentially useful for making nanochannels of various inorganic materials.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.178-178
• /
• 2010

We have deposited aluminum-doped ZnO thin films on borosilicate glass by atomic layer deposition. Diethylzinc (DEZ) and dimethylaluminum isopropoxide (DMAIP) were used as the metal precursor and the Al-dopant, respectively. Water was used as an oxygen source. DMAIP was successfully used as an aluminum precursor for chemical vapor deposition and ALD. All deposited films showed n-type conduction. The resistivity decreased to a minimum and then increased with increasing the aluminum content. The carrier concentration increased and the carrier mobility decreased with increasing the DMAIP to DEZ pulse ratio. The average optical transmittance was nearly 80 % in the visible part of the spectrum. The absorption edge moved to the shorter wavelength region with increasing the DMAIP to DEZ pulse ratio. Our results indicate that DMAIP is suitable for Al doping of ZnO films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.461-461
• /
• 2010

For a low dielectric constant inter-metal dielectric application, the low-k SiCOH film with a dielectric constant of 2.8-3.2 has been deposited by plasma-enhanced chemical vapor deposition with decamethylcyclopentasiloxane, cyclohexane, and helium which is carrier gas. In this work, we investigated chemical deposition rate, dielectric constant, characterization of plasma polymer films according to temperature(25C-200C) of substrate and change of component concentration. We measured impedance by using V-I prove during process. From experimental result, deposition rate decrease with increasing temperature. Through real time impedance analysis of chamber, we find corelation between film thickness and impedance by assuming equivalent circuit.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.75.1-75.1
• /
• 2013

Atomic layer deposition (ALD) and molecular layer deposition (MLD) are based on sequential, self-limiting surface reactions that produce atomic layer controlled and conformal thin film growth. ALD can deposit inorganic films and MLD can deposit films containing organics. ALD and MLD can be used together to fabricate a wide range of hybrid organic-inorganic alloy films. The relative fraction of inorganic and organic constituents can be defined by controlling the ratio of the ALD and MLD reaction cycles used to grow the film. These hybrid films can be tuned to obtain desirable mechanical, electrical and optical properties. This talk will focus on the growth and properties of metal alkoxide films grown using metal precursors and various organic alcohols that are known as "metalcones". The talk will highlight the tunable mechanical properties of alucone alloys grown using Al2O3 ALD and alucone MLD and the tunable electrical conductivity of zincone alloys grown using ZnO ALD and zincone MLD with DEZ and hydroquinone as the reactants.

• Journal of the Korean Society for Heat Treatment
• /
• v.25 no.2
• /
• pp.85-89
• /
• 2012

Transparent conductive ZnO/Ag/ZnO (ZAZ) multilayer films were deposited by Radio frequency (RF) magnetron sputtering and direct current (DC) magnetron sputtering. The effects of post deposition vacuum annealing temperature on the structural, electrical and optical properties of the ZAZ multilayer films were investigated. The thickness of ZAZ films is kept constant at ZnO 50 nm/Ag 5nm/ZnO 45 nm, while the vacuum annealing temperatures were varied from 200 and $400^{\circ}C$, respectively. As-deposited ZAZ films exhibit a sheet resistance of $6.1{\Omega}/{\Box}$ and optical transmittance of 72.7%. By increasing annealing temperature to $200^{\circ}C$, the resistivity decreased to as low as $5.3{\Omega}/{\Box}$ and optical transmittance also increased to as high as 82.1%. Post-deposition annealing of ZAZ multilayer films lead to considerably lower electrical resistivity and higher optical transparency, simultaneously by increased crystallization of the films.

• Journal of the Korean Vacuum Society
• /
• v.4 no.S1
• /
• pp.130-137
• /
• 1995

Deopsition of thermal quality SiO2 using a high density plasma ECR CVD process has been demonstrated to give void and seam free gap fill of high aspect ratio metallization structures with a simple oxygen-silane chemistry. This is achieved by continuous sputter etching of the film during the deposition process. A two-step process is utilized to deposit a composite layer for higher manufacturing efficiency. The first step, which has a deposition rate of approximately 0.5 $\mu$m/min., is used to provide complete gap fill between the metal lines. The second step, which has a deposition rate of up to 1.5 $\mu$m/min., is used to deposit a total thickness of 2.0$\mu$m for the intermetal dielectric film. The topography of this composite film is very compatible with subsequent chemicl mechanical polishing(CMP) planarization processing.

• Journal of Korean Vacuum Science & Technology
• /
• v.3 no.2
• /
• pp.116-120
• /
• 1999

Possible role of hydrogen atoms on the formation of microcrystalline silicon films was schematically investigated using a plasma enhanced chemical vapor deposition system. A layer-by-layer technique that can alternate deposition of ${\alpha}$-Si thin film and then exposure of H2 plasma was used for this end. The experimental process was extensively carried out under different hydrogen plasma times (t2) at a fixed number of 20 cycles in the deposition. structural properties, such as crystalline volume fractions and grain shapes were analyzed by using a Raman spectroscopy and a scanning electron microscopy. Electrical transports were characterized by the temperature dependence of the dark conductivity that gives rise to the calculation of activation energy (Ea). Optical absorption was measured using an ultra violet spectrophotometer, resulting in the optical energy gap (Eopt). Our experimental results indicate that both of the hydrogen etching and the structural relaxation effects on the film surface seem to be responsible for the growth mechanism of the crystallites in the ${\mu}$c-si films.