• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.3
• /
• pp.461-470
• /
• 2002

The present paper investigates the effect of hot isostatic pressing (HIPing) on mechanical properties, e.g., tensile strength, ductility and impact absorption energy of sand and die casted aluminum alloys. After HIPing at various temperatures and pressure conditions, uniaxial tensile test and Izod impact test of the samples were carried out. The experimental results showed improvements in uniaxial tensile strength, elongation and Izod impact toughness of sand casted aluminum alloy, while deterioration of a tensile strength fur die casted aluminum alloy. The effect of HIPing for microstructure of the cast aluminum alloy was also investigated.

• The Korean Journal of Ceramics
• /
• v.3 no.3
• /
• pp.195-198
• /
• 1997

Post-firing process of electronic ceramic, such as electroding and encapsultion with resin, often causes damage by thermal shock. The thermal shock behavior of $BaTiO_3$ ceramics was investigated by the down-quench test, where the relative strength retained is determined after the sample is quenched from an elevated temperature into a fixed temperature bath. The critical temperature drop, $\DeltaTc$, was evaluated for three kinds of sintered $BaTiO_3$ ceramics, which were formed by extrustioin, uniaxial pressing using granules, and uniaxial pressing using powders. A drastic loss in strength caused by microcracking was observed for the specimens quenched with $\DeltaT\geq150^{\circ}C$. This concentp can be adopted as a method of the quality control by monitoring the sudden drop of the strength of capacitor products after each exposure to heat.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.20 no.3
• /
• pp.816-824
• /
• 1996

The densification behaviors of copper powder under high temperature processing were investigated. Experimental data were obtained for copper powder under hot isostatic pressing, hot pressing and uniaxial compression. Finite element calculations from the constitutive models by McMeeking and co-workers were compared with the experimental data, The agreements between experimental data and theoretical calculations are reasonably good when hydrostatic stress is dominant, but not as good then deviatoric stress increases.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.2 s.173
• /
• pp.394-402
• /
• 2000

Densification behavior of titanium alloy powder was investigated under hot isostatic pressing at various pressures and temperatures. Uniaxial creep responses of a dense specimen were also obtained at high temperatures. The densification model of Abouaf and co-workers was implemented into a Finite element program (ABAQUS) to compare with experimental data for titanium alloy powder. The agreements between finite element calculations and experimental data for deformation and densification of titanium alloy powder were good during hot isostatic pressing.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.9
• /
• pp.1831-1841
• /
• 2002

The effect of a rubber mould on densification and deformation of aluminum alloy powder was investigated during warm isostatic pressing. The hyperelastic constitutive equations based on various strain energy potentials were employed to analyze deformation of rubber. The parameters in the strain energy potentials were obtained from experimental data for uniaxial and volumetric compression of Viton rubber at two warm temperatures. For elastoplastic response, the yield function of Shima and Oyane was implemented into a finite element program (ABAQUS) to predict compaction responses of metal powder during warm isostatic pressing. Finite element results were compared with experimental data for densification and deformation of aluminum alloy powder with/without a rubber mould under warm die pressing.

• Progress in Superconductivity and Cryogenics
• /
• v.21 no.2
• /
• pp.40-44
• /
• 2019

In this study, the effects of the compaction method for (Mg+2B) powders on the apparent density and superconducting properties of $MgB_2$ bulk superconductor were investigated. The raw powders used in this study were nano-sized boron (B) and spherical magnesium (Mg). A batch of a powder mixture of (Mg+2B) was put in a steel mold and uniaxially pressed at 1 ton or 3 tons into pellets. Another batch of the powder mixture was uniaxially pressed at 1 ton and then pressed isostatically at $1800kg/cm^2$ in the water chamber. All pellets were heat-treated at $650^{\circ}C$ for 1 h in flowing argon gas for the formation of $MgB_2$. The apparent density of powder compacts pressed at 3 ton was higher than that at 1 ton. The cold isostatic pressing (CIP) in a water chamber allowed further increase of the apparent density of powder compacts, which influenced the pellet density of the final products ($MgB_2$). The compaction methods (uniaxial pressing and CIP) did not affect the formation of $MgB_2$ and superconducting critical temperature ($T_c$) of $MgB_2$, but affected the critical current density ($J_c$) of $MgB_2$ significantly. The sample with the high apparent density showed high $J_c$ at 5 K and 20 K at applied magnetic fields (0-5 T).

• Journal of the Korean Ceramic Society
• /
• v.46 no.3
• /
• pp.306-312
• /
• 2009

The size of various alumina ceramics used in semiconductor and display industry is also required to increase with increase in wafer and panel size. In this research, large alumina ceramics was fabricated by filter pressing of alumina slurry using commercial powder and thereafter sintering at $1600^{\circ}C$ in gas furnace. The characteristics of large alumina ceramics thereby were compared to those of small alumina ceramics prepared by pressure forming such as uniaxial pressing and CIP. Careful control of properties of alumina slurry and filter pressing made the fabrication of large alumina ceramics possible, and its characteristics were equivalent to those of small alumina ceramics. The large alumina ceramics, prepared by sintering the green body of 63% relative density at $1600^{\circ}C$, exhibited both dense microstructure corresponding to 98.5% of relative density and 99.8% of high purity as in starting powder.

• Journal of the Korean Ceramic Society
• /
• v.49 no.4
• /
• pp.347-351
• /
• 2012

Vermiculite-silica composites with a layered structure were fabricated by adding cellulose fibers as a pore former and by a simple uniaxial pressing and subsequent sintering process. Three different combinations of additives were used and their effects on the compressive strength and thermal conductivity of the composites were investigated. Both compressive strengths (42-128 MPa) and thermal conductivities (0.75-1.48 $W/m{\cdot}K$) in the direction perpendicular to the pressing direction (T) were higher than those (19-81 MPa and 0.32-1.04 $W/m{\cdot}K$) in the direction parallel to the pressing direction (S) in all samples. The anisotropy in both properties was attributed to the microstructural anisotropy, which was caused by the layered structure developed in the composites.

• Journal of the Korean Ceramic Society
• /
• v.29 no.11
• /
• pp.855-862
• /
• 1992

Thermoelectric power, electrical conductivity and Hall effect were measured, as functions of temperature in the range of 100 to 600 K, on polycrystalline Bi4/3Sb2/3Te3 which had been prepared via uniaxial hot-pressing at different temperatures in the range of 373 K to 773 K, aiming at searching a profitable processing route to a polycrystalline thermoelectric material, a promising, viable alternative to a single crystalline one. It was found that, with increasing temperature of pressing under a fixed pressure, the material, normally a p-type prior to being hot-pressed, underwent a transition to n-type. This transition was confirmed to be due to plastic deformation during hot-pressing and interpreted as being attributed to the change of the major ionic defect BiTe' into TeBi˙at temperature high enough for structure elements mobility. Thermoelectric figure-of-merit of the hot-pressed material was discussed in connection with the p-n transition in addition to microstructure.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.26 no.1
• /
• pp.27-32
• /
• 2013

According to the composition of LTCC material, though it was thought that bulk defect which was made in forming process effects on the densification during the sintering, it was not reported systemically. In this study, we evaluated crystal structure, 3 point bending strength, hardness and microstructure of the samples by uniaxial pressing and tape casting using the commercial powders of the crystallizing glass and the glass/ceramic composite. In the case of glass/ceramic composite, Viox-001 powder with residual glass in the sintering, 3 point bending strength was similar regardless of forming process due to fill the bulk defect by residual glass. In the case of crystallizing glass, MLS-22, because glass phase was small in the sintering, glass did not fill the pore in the sample by uniaxial pressing process, therefore, the 3 point bending strength of it was 167 MPa. However, the 3 point bending strength of the sample by tape casting was 352 MPa and much higher. Meanwhile, crystal structure and hardness were similar regardless of forming process.