• Journal of Dental Rehabilitation and Applied Science
• /
• v.24 no.3
• /
• pp.231-242
• /
• 2008

Purpose: The purpose of this study was to investigate the bond strength of the core-veneer interface in all ceramic systems. Material and Methods: The all ceramic systems tested with their respective veneer were IPS Empress 2 with IPS Eris, IPS e.max Press with IPS e.max Ceram and IPS-e.max ZirCAD with IPS e.max Ceram. Cores (N=36, N=12/group, diameter: 10mm, thickness: 3mm) were fabricated according to the manufacturer's instruction and cleaned with ultrasonic cleaner. The veneer(diameter: 3mm, thickness: 2mm) were condensed in stainless steel mold and fired on to the core materials. After firing, they were again ultrasonically cleaned and embedded in acrylic resin. The specimens were stored in distilled water at $37^{\circ}C$ for 1 week. The specimens were placed in a mounting jig and subjected to shear force in a universal testing machine(Z020, Zwick, Germany). Load was applied at close to the core-veneer interface as possible with crosshead speed of 1.00mm/min until failure. Average shear bond strengths(MPa) were analyzed with a one-way analysis of variance and the Tukey test(${\alpha}=.05$). The failed specimens were examinated by scanning electron microscopy(JSM-6360, JEOL, Japan). The pattern of failure was classified as cohesive in core, cohesive in veneer, mixed or adhesive. Results: The mean shear bond strength($MPa{\pm}SD$) were IPS e.max Press $32.85{\pm}6.75MPa$, IPS Empress 2 $29.30{\pm}6.51MPa$, IPS e.max ZirCAD $28.10{\pm}4.28MPa$. IPS Empress 2, IPS e.max Press, IPS e.max ZirCAD were not significantly different from each others. Scanning electron microscopy examination revealed that adhesive failure did not occur in any all ceramic systems. IPS Empress 2 and IPS e.max Press exhibited cohesive failure in both the core and the veneer. IPS e.max ZirCAD exhibited cohesive failure in veneer and mixed failure.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.35 no.2
• /
• pp.161-169
• /
• 1999

This paper describes the swimming and escaping behavior of amber fish, Seriola aureovittata released in the first bag net of the setnet and observed with telemetry techniques. The setnet used in experiment is composed of a leader, a fish court with a flying net and two bag nets having ramp net. The behavior of the fish attached an ultrasonic depth pinger of 50 KHz is observed using a prototype LBL fish tracking system. The 3-D underwater position ofthe fish is calculated by hyperbolic method with three channels of receiver and the depth of pinger. The results obtained are as follows: 1. The fish released on the sea surface was escaped down to 15 m depth and rised up to near the sea surface during 5 minutes after release. The average swimming speed of the fish during this time was 0.87 m/sec. 2. The swimming speed of the fish is decreased slowly in relation to the time elapsed and the fish showed some escaping behavior forward to the fish court staying 1 to 7 m depth layer near the ramp net. The average speed of the fish during this time was 0.52 m/sec. 3. During 25 minutes after beginning of hauling net, the fish showed a faster swimming speed than before hauling and an escaping behavior repeatedly from the first ramp net to the second one in horizontal. In vertical, the fish moved up and down between the sea surface and 20 m depth. After this time, the fish showed the escaping behavior forward to fish court after come back to the first ramp net in spite of the hauling was continued. It is found that the fish was escaped from the first ramp net to the fish court while the hauling was carried out. The average speed of the fish after beginning of hauling was 0.72 m/sec which increased 38.5 ％ than right before the hauling and showed 0.44 to 0.82 m/see of speed till escaping the first bag net. The average swimming speed during observation was 0.67 m/sec (2.2 times of body length).

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.33 no.4
• /
• pp.348-355
• /
• 2000

This paper described the relationship between the behavior of the Israeli carp, Cyprinus carpio and the environmental noise level due to the dynamite explosion work. The experiment was conducted in the cage ($L10{\times}W4{\times}D4 m$) of aquaculture located at Chungjoo Lake, Chechon, in 1997. The fish trajectory was obtained by the telemetry system in which a pulsed ultrasonic pinger ($50 kHz, {\phi}16{\times}L70 mm$) attached to the fish was tracked three dimensionally, and the underwater noise levels were measured. The results of the study were as follows: 1. The underwater noise levels in the normal blasting measured at a distance of 400 m from the source of noise increased by $40 dB (re 1 {\mu}Pa)$ compared to the levels before explosion. The dominant frequency and the increased power spectrum level of the underwater noise by the explosion work were $75 to 100 Hz and 22.9 to 35.3 dB$, respectively. 2. The underwater noise levels in the test blasting measured at a distance of 350 m from the source of noise increased by average $49.5 dB (re 1 {\mu}Pa)$compared to the levels before explosion. 3. The swimming area of the fish was reduced with the time after explosion, and after more than one hour the fish represented the similar swimming area and behavior to the status of right before explosion. 4, The swimming depth layer of the fish was most of the case at the sea surface less than 1,0 m except during explosion or right after of it. But the fish swam downward when an external stimulus like the explosion noise was given to the fish. 5. The average swimming speeds of the fish before, during and after the works were about 1.2 times, 1.9 times and 1.0 times of the body length, respectively, and the speed of the fish with explosion was faster 1.6 times than the speed without of that. Consequently, the explosion noise levels measured by this study were sufficiently high to affect the fish, and the heavy shock by the explosion works could produce a considerable unfavorable effects to the fish.

• Journal of Korean Society of Environmental Engineers
• /
• v.31 no.2
• /
• pp.79-89
• /
• 2009

Naphthalene is a volatile, hydrophobic, and possibly carcinogenic compound that is known to have a severe detrimental effect to aquatic ecosystem. Our research examined the effects of various operating conditions (temperature, pH, initial concentration, and frequency and type of ultrasound) on the sonochemical degradation of naphthalene and OH radical production. The MDL (Method detection limit) determined by LC/FLD (1200 series, Agilient) using C-18 reversed column is measured up to 0.01 ppm. Naphthalene vapor produced from ultrasound irradiation was detected under 0.05 ppm. Comparison of naphthalene sonodegradion efficiency tested under open and closed reactor cover fell within less than 1% of difference. Increasing the reaction temperature from $15^{\circ}C$ to $40^{\circ}C$ resulted in reduction of naphthalene degradation efficiency ($15^{\circ}C$: 95% ${\rightarrow}$ $40^{\circ}C$: 85%), and altering pH from 12 to 3 increased the effect (pH 12: 84% ${\rightarrow}$pH 3: 95.6%). Pseudo first-order constants ($k_1$) of sonodegradation of naphthalene decreased as initial concentration of naphthalene increased (2.5 ppm: $27.3{\times}10^{-3}\;min^{-3}\;{\rightarrow}$ 10 ppm : $19.3{\times}10^{-3}\;min^{-3}$). Degradation efficiency of 2.5 ppm of naphthalene subjected to 28 kHz of ultrasonic irradiation was found to be 1.46 times as much as when exposed under 132 kHz (132 kHz: 56%, 28 kHz: 82.7%). Additionally, its $k_1$ constant was increased by 2.3 times (132 kHz: $2.4{\times}10^{-3}\;min^{-1}$, 28 kHz: $5.0{\times}10^{-3}\;min^{-1}$). $H_2O_2$ concentration measured 10 minutes after the exposure to 132 kHz of ultrasound, when compared with the measurement under frequency of 28 kHz, was 7.2 times as much. The concentration measured after 90 minutes, however, showed the difference of only 10%. (concentration of $H_2O_2$ under 28 kHz being 1.1 times greater than that under 132 kHz.) The $H_2O_2$ concentration resulting from 2.5 ppm naphthalene after 90 minutes of sonication at 24 kHz and 132 kHz were lower by 0.05 and 0.1 ppm, respectively, than the concentration measured from the irradiated M.Q. water (no naphthalene added.) Degradation efficiency of horn type (24 kHz) and bath type (28 kHz) ultrasound was found to be 87% and 82.7%, respectively, and $k_1$ was calculated into $22.8{\times}10^{-3}\;min^{-1}$ and $18.7{\times}10^{-3}\;min^{-1}$ respectively. Using the multi- frequency and mixed type of ultrasound system (28 kHz bath type + 24 kHz horn type) simultaneously resulted in combined efficiency of 88.1%, while $H_2O_2$ concentration increased 3.5 times (28 kHz + 24 kHz: 2.37 ppm, 24 kHz: 0.7 ppm.) Therefore, the multi-frequency and mixed type of ultrasound system procedure might be most effectively used for removing the substances that are easily oxidized by the OH radical.

• Restorative Dentistry and Endodontics
• /
• v.24 no.1
• /
• pp.166-179
• /
• 1999

Apical sealing is essential for the success of surgical endodontic treatment. Root-end cavity is apt to be contaminated with moisture or blood, and is not always easy to be dried completely. The purpose of this study was to evaluate the influence of dry methods of retrocavity on the apical seal in endodontic surgery. Apical seal was investigated through the evaluation of apical leakage and adaptation of filling material over the cavity wall. To investigate the influence of various dry methods on the apical leakage, 125 palatal roots of extracted human maxillary molar teeth were used. The clinical crown of each tooth was removed at 10 mm from the root apex using a slow-speed diamond saw and water spray. Root canals of the all the specimens were prepared with step-back technique and filled with gutta-percha by lateral condensation method. After removing of the coronal 2 mm of filling material, the access cavities were closed with Cavit$^{(R)}$. Two coats of nail polish were applied to the external surface of each root. Apical three millimeters of each root was resected perpendicular to the long axis of the root with a diamond saw. Class I retrograde cavities were prepared with ultrasonic instruments. Retrocavities were washed with physiologic saline solution and dried with various methods or contaminated with human blood. Retrocavities were filled either with IRM, Super EBA or composite resin. All the specimens were immersed in 2% methylene blue solution for 7 days in an incubator at $37^{\circ}C$. The teeth were dissolved in 14 ml of 35% nitric acid solution and the dye present within the root canal system was returned to solution. The leakage of dye was quantitatively measured via spectrophotometric method. The obtained data were analysed statistically using one-way ANOVA and Duncan's Multiple Range Test. To evaluate the influence of various dry methods on the adaptation of filling material over the cavity wall, 12 palatal roots of extracted human maxillary molar teeth were used. After all the roots were prepared and filled, and retrograde cavities were made and filled as above, roots were sectioned longitudinally. Filling-dentin interface of cut surfaces were examined by scanning electron microscope. The results were as follows: 1. Cavities dried with paper point or compressed air showed less leakage than those dried with cotton pellet in Super EBA filled cavity (p<0.05). However, there was no difference between paper point- and compressed air-dried cavities. 2. When cavities were dried with compressed air, dentin-bonded composite resin-filled cavities showed less apical leakage than IRM- or Super EBA-filled ones (p<0.05). 3. Regardless of the filling material, cavities contaminated with human blood showed significantly more apical leakage than those dried with compressed air after saline irrigation (p<0.05). 4. Outer half of the cavity showed larger dentin-filling interface gap than inner half did when cavities were filled with IRM or Super EBA. 5. In all the filling material groups, cavities contaminated with blood or dried with cotton pellets only showed larger defects at the base of the cavity than ones dried with paper points or compressed air.