• Bulletin of the Korean Chemical Society
• /
• 제22권2호
• /
• pp.159-163
• /
• 2001

Si3N4 powder has been analyzed by inductively coupled plasma atomic emission spectrometry (ICP-AES). The sample was dissolved by high-pressure acid digestion with HF, H2SO4 (1+1), and HNO3 mix ture. This technique is well suited for the impurity analysis of Si3N4 because the matrix interference is eliminated. A round-robin samples trace elements, such as Ca, W, Co, Al, Fe, Mg, and Na, were determined. For the direct analysis, slurry nebulization of 0.96 mm Si3N4 powder also has been studied by ICP-AES. Emission intensities of Fe were measured as ICP operational conditions were changed. Significant signal difference between slurry particles and aqueous solution was observed in the present experiment. Analytical results of slurry injection and high-pressure acid digestion were compared. For the use of aqueous standard solution for calibration, k-factor was determined to be 1.71 for further application.

• 한국재료학회지
• /
• 제14권11호
• /
• pp.790-794
• /
• 2004

Ultra-fine Copper particles for a conductive paste in electric-electronic field were prepared using wet-reduction process with hydrazine hydrate ($N_{2}H_4{\cdot}H_{2}O$) as a reductor. The effect of reaction conditions such as the amount of dispersion ($Na_{4}O_{7}P_2{\cdot}10H_{2}O$) and reductor ($N_{2}H_4{\cdot}H_{2}O$) on the particle size and shape for the prepared Cu powders was investigated. The quantity of dispersion and reductor varied from 0 to 0.0025 M and from 5 to 40 ml at a reaction temperature of $70^{\circ}C$, respectively. The particle size, shape, and structure for the obtained Cu particles were characterized by means of XRD, SEM, TEM, EDS and TGA. The aggregation of Cu particles was reduced with relatively increasing of the amount of dispersion at fixed other reaction conditions. The smaller Cu particle with size of approximately 300nm was obtained from 0.032 M $CuSO_4$ with adding of 0.0025 M $Na_{4}O7P_2{\cdot}10H_{2}O$ and 40ml $N_{2}H_4{\cdot}H_{2}O$ at a reaction temperature of $70^{\circ}C$.

• 대한금속재료학회지
• /
• 제46권4호
• /
• pp.223-226
• /
• 2008

The comparison of sintering behavior and mechanical properties of ultra-fine WC-10wt.%Co and WC-10wt.%Fe hard materials produced by high-frequency induction heated sintering (HFIHS) was accomplished using ultra fine powder of WC and binders(Co, Fe). The advantage of this process allows very quick densification to near theoretical density and prohibition of grain growth in nano-structured materials. Highly dense WC-10Co and WC-10Fe with a relative density of up to 99% could be obtained with simultaneous application of 60 MPa pressure and induced current within 1 minute without significant change in grain size. The hardness and fracture toughness of the dense WC-10Co and WC-10Fe composites produced by HFIHS were investigated.

• 한국결정성장학회지
• /
• 제15권6호
• /
• pp.239-243
• /
• 2005

The effect of pH and particle size on the dispersion stability of ultra-fine $BaTiO_3$ suspensions in aqueous medium have been investigated by means of zeta potential, sediment experiments, and powder properties (particle analysis, specific surface area) etc. Zeta potential as a function of pH for two particles of different size increases from -75 to +10 mV with decreasing pH from 8.5 to 1.4. The curve of zeta potential for small particle (150 nm) has slow slope than that of large particle (900nm), giving IEP (isoelectric point) value of pH=1.6 for small particle and pH=1.9 for large particle respectively, which means that it is more difficult to control zeta potential with pH fur small particle than large particle. The dispersion stability of $BaTiO_3$ particles in aqueous medium was found to be strongly related with the agglomeration of colloidal suspensions with time through the sedimentation behaviors of colloidal particles with time and pH value.

• 한국자기학회지
• /
• 제5권5호
• /
• pp.819-823
• /
• 1995

The oil-based magnetic fluids were sysnthesized using ultra-fine $Fe_{3}O_{4}$ powder dispersed in hydrocarbon oil. To synthesize ultra-fine $Fe_{3}O_{4}$, we carried out the experiments varying the pH of reacting medium and the initial concentration of $Fe^{2+}$. We also investigated the amount of oleic acid to obtain a stable dispersion and the proper base oil of MF for loudspeaker application. The limits of adsorbed amount of oleic acid on the $Fe_{3}O_{4}$ surface were approximately 35~40 percents of the total magnetite weight. As the $Fe_{3}O_{4}$ content increased from 0.1g/cc to 0.6g/cc, the viscosity of oil-based magnetic fluid increased from 1,063cP to 1,828cP, and its saturation magnetization at 10kOe increased from 66G to 242G. When we tested the MF sample to a commercial speaker, improvements were noted.

• 대한금속재료학회지
• /
• 제49권1호
• /
• pp.40-45
• /
• 2011

Using the spark plasma sintering process (SPS process), the WC-6wt.%Co hard materials were densified using an ultra fine WC-Co powder. The WC-Co was almost completely dense with a relative density of up to 100% after the simultaneous application of a pressure of 60 MPa and the DC pulse current for 3 min without any significant change in the grain size. The average grain size of WC that was produced through this experiment was about $0.2{\sim}0.8{\mu}m$. The hardness and fracture toughness were about $1816kg/mm^2$ and $15.1MPa{\cdot}m^{1/2}$, respectively, for 60 MPa at $1200^{\circ}C$.

• 한국분말재료학회지
• /
• 제21권5호
• /
• pp.382-388
• /
• 2014

Fe-TiC composite powder was fabricated by high-energy milling of powder mixture of (Fe, TiC) and (FeO, $TiH_2$, C) as starting materials, respectively. The latter one was heat-treated for reaction synthesis of TiC phase after milling. Both powders were spark-plasma sintered at various temperatures of $680-1070^{\circ}C$ for 10 min. with sintering pressure of 70 MPa and the heating rate of $50^{\circ}C/min$. under vacuum of 0.133 Pa. Density and hardness of the sintered compact was investigated. Fe-TiC composite fabricated from (FeO, $TiH_2$, C) as starting materials showed better sintered properties. It seems to be resulted from ultra-fine TiC particle size and its uniform distribution in Fe-matrix compared to the simply mixed (Fe, TiC) powder.

• 한국분말재료학회지
• /
• 제12권5호
• /
• pp.336-344
• /
• 2005

In the present study, the focus is on the effect of cobalt oxide powder in the carbothermal reduction of the titanium-cobalt-oxygen based oxide powder by solid carbon for the optimizing synthesis process of ultra fine TiC/Co composite powder. The titanium-cobalt-oxygen based oxide powder was prepared by the combination of the spray drying and desalting processes using the titanium dioxide powder and cobalt nitrate as the raw materials. The titanium-cobalt-oxygen based oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under flowing argon atmosphere. Changes in the phase structure and thermal gravity of the mixture during carbothermal reduction were analysed using XRD and TGA. Titanium-cobalt-oxygen based oxide powder desalted at $600^{\circ}C$ had a mixture of $TiO_2\;and\;Co_{3}O_4$. And the one desalted at $800^{\circ}C$ had a mixture of $TiO_2\;and\;CoTiO_3$. In the case of the former powder, the reduction of cobalt oxide powder in the titanium-cobalt-oxygen based oxide powder occurred at lower temperature than the latter one. However, the carbothermal reduction of titanium dioxide powder in the titanium-cobalt-oxygen based oxide powder with a mixture of $TiO_2\;and\;Co_{3}O_4$ occurred at higher temperature than the one with a mixture of $TiO_2\;and\;CoTiO_3$. And also, the former powder showed a lower TiC formation ability than the latter one.

• 한국세라믹학회지
• /
• 제28권2호
• /
• pp.146-152
• /
• 1991

Ultra fine and homogeneous (Ni0.4Zn0.6)Fe2O4 ferrite powders were prepared by direct-wet, Hydrothermal and coprecipitation methods. In case that specific surface areas of Ni-Zn ferrite powders were over 220㎡/g, 100㎡/g, 30㎡/g individually direct-wet, hydrothermal and coprecipitation methods. The Ni-Zn ferrite magnetic fluids of which Solvents were benzene or kerosene was prepared by making cation surfactant adsorbed on the surface of the (Ni0.4Zn0.6)Fe2O4. The results that measured dispersion and viscosity by making cation surfactant adsorbed were as follows. 1. The adsorption amount of Oleric acid be proportioned the specific surface area of powders. 2. The maximum amount of Oleric acid was 36wt% of dried powders which has 220㎡/g of specific surface area. 3. The stability of fluid by direct-wet synthesis emthod in benzene or kerosene solvent excellent.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 봄 학술발표회 논문집(I)
• /
• pp.285-291
• /
• 1998

During recent years, the durability of concrete structures has been considered in concret practice and material research. To preserve the brittleness of concrete as well as energy absorption and impact resistance, amount of fiber usage has greatly increased in the field of public works. Ultra fine powder, silica fume, mixed into concrete, it reduce void of concrete structure. Especially, there's a great effect for strength improvement of concrete by initial pozzolanic reactions. For these reasons, if silica fume mixed into concrete, it decrease the total void by microfilter effect . Pozzolan reaction, between cement particle and silica powder, can elaborate the micro structure of matrix. And so, in this paper, we deal SFRC for the purpose of efficiently using of industrial by-products(silica fume). Also we performed the test for durability such as freeze-thaw resistance and accelerated carbonation of SFRC using silica fume.