Fabrication and Mechanical Properties of ultra fine WC-6wt.%Co by Spark Plasma Sintering Process

Using the spark plasma sintering process (SPS process), the WC-6wt.%Co hard materials were densified using an ultra fine WC-Co powder. The WC-Co was almost completely dense with a relative density of up to 100% after the simultaneous application of a pressure of 60 MPa and the DC pulse current for 3 min without any significant change in the grain size. The average grain size of WC that was produced through this experiment was about $0.2{\sim}0.8{\mu}m$. The hardness and fracture toughness were about $1816kg/mm^2$ and $15.1MPa{\cdot}m^{1/2}$, respectively, for 60 MPa at $1200^{\circ}C$.

방전플라즈마 소결 공정을 이용한 WC-6wt.%Co 소결체 제조 및 기계적 특성 평가