• Korean Journal of Materials Research
• /
• v.10 no.1
• /
• pp.29-33
• /
• 2000

The amorphous tungsten nitrides, WNx, film could be fabricated by reactive sputtering process. The nitrogen concentration for the amorphization ranges from 10 at% to 40at%. The amorphous $W_{67}N_{33}$ film was crystallized into low resistivity $\alpha$-tungsten phase with equiaxed grains and excess nitrogen after the rapid thermal annealing for 1min at 1273K, which was similar to the resistivity of the sputtered pure tungsten film. The excess nitrogen was depleted from $\alpha$-tungsten crystals and then segregated at $\alpha$-tungsten/poly-Si interface. The segregated nitrogen has favored the formation of the homogeneous diffusion barrier layer comprised of silicon nitride, $Si_3N_4$, nano-crystals, which undertaken the inhibition of the high resistivity tungsten silicide reaction.

• Journal of the Korean Vacuum Society
• /
• v.11 no.1
• /
• pp.22-27
• /
• 2002

We investigated the crystal structure, resistivity, and chemical states change of the tungsten nitride $(WN_x)$ films prepared by reactive sputtering method with various $N_2$ flow ratios. Crystal structures of $WN_x$ films deposited at the $N_2$ flow ratios of 20%, 40%, and 60% were bcc $\beta$-W, amorphous, and fcc $W_2$N, respectively. Surface roughness of $WN_x$ film was smallest when the $WN_x$ film is amorphous. After the air exposure of $WN_x$ films, $WO_3$ layer was formed at the surface of all samples. Both the nitrogen content of $WN_x$ film and the binding energy of W $4f_{7/2}$ peaks increased with increasing $N_2$ flow ratio. However, after $Ar^+$ ion etching, the shift of W $4f_{7/2}$ peaks was not observed with $N_2$ flow ratio due to the amorphization of the $WN_x$ film surface. The resistivity of $WN_x$ films increased with increasing $N_2$ flow ratio.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.386-386
• /
• 2013

반도체 소자의 소형화, 고집적화로 박막의 다층화 및 선폭의 감소 등의 복잡한 제조 공정이 불가피하고, 따라서 공정 중 실리콘 웨이퍼와 금속 박막사이의 확산을 방지하기 위한 많은 연구가 이루어지고 있다. 하지만 현재까지의 연구는 확산방지막의 nano-mechanics 특성 분석에 대한 연구는 전무하다. 본 논문에서 tungsten (W)을 주 물질로, nitrogen (N)을 첨가한 확산방지막을 질소 유량을 2.5, 5, 7.5, 10 sccm으로 변화시켜가면서 rf magnetron sputter 방법으로 tungsten-nitride (W-N) 박막을 증착하였다. 박막의 기본 물성인 증착율, 비저항 및 결정학적 특성을 ${\beta}$-ray, 4-point probe, X-ray diffraction (XRD)를 이용하여 측정하였고, 측정결과 증착 중 질소 유량이 증가할수록 W-N 박막의 비저항은 증가하였고 반대로 증착율과 결정성은 감소하였다. 이는 기존의 연구 결과와 비교하여 일치한 결과로 증착된 박막이 신뢰성을 가짐을 확인하였다. 이후 가장 관심사인 nano-mechanics 특성은 nano-indenter를 이용하여 측정하였다. 측정 결과 시료는 증착 중 질소 유량이 2.5 sccm인 시료를 기준으로 5 sccm 포함된 박막에서 load force-depth 그래프가 급격히 변화하는 경향을 나타내었고, 표면강도(surface hardness)는 10.07 GPa에서 15.55 GPa로 증가하였다. 이후 질소 유량이 7.5 sccm과 10 sccm에서는 12.65 GPa와 12.77 GPa로 질소 유량이 5 sccm 포함된 박막보다 상대적으로 감소하였다. 이는 박막내 결정상으로 존재하는 질소와 비정질 상태로 존재하는 질소의 비율에 의한 것이고, 압축력에 기인하는 스트레스 증가로 판단된다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.87-88
• /
• 2007

반도체 소자가 초고집적화 되어감에 따라 반도체 공정에서 선폭은 줄어들고 박막은 다층화 되어가고 있다. 이와 같은 제조 공정 하에서는 Si 기판과 금속 박막간의 확산이 커다란 문제로 부각되어 왔다. 특히 Cu는 높은 확산성에 의하여 Si 기판과 접합에서 많은 확산에 의한 문제가 발생하게 되며, 또한 선폭이 줄어듦에 따라 고열이 발생하여 실리콘으로 spiking이 발생하게 된다. 이러한 확산을 방지하기 위하여 이 논문에서는 Tungsten - Carbon - Nitrogen (W-C-N)에 Boron (B)을 첨가하였고, Boron 타겟 power을 조절하여 다양한 조성을 가지는 W-B-C-N 확산방지막을 제작하여 각 조성에 따른 증착률을 조서하였고 $1000^{\circ}C$까지 열처리하여 그 비저항을 측정하여 각 특성을 확인하였다.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.36D no.7
• /
• pp.17-25
• /
• 1999

Tungsten nitride($WN_x$) films were deposited by PECVD method on silicon nitride($WSi_3N_4$) substrate. The characteristics of $WN_x$ film were investigated with changing various processing parameters ; substrate temperature, gas flow rate, rf power, and different nitrogen sources. The nitrogen composition in $WN_x$ film varied from 0 to 45% according to the $NH_3$ and $N_2$ flow rate. The highest deposition rate of 160 nm/min was obtained for the $NH_3$ gas and relatively low deposition rate of $WN_x$ films were formed by $N_2$ gas. $WN_x$ films deposited on $WSi_3N_4$ substrate had higher deposition rate than that of TiN and Si substrates. The purity of $WN_x$ film were analyzed by AES and higher purity $WN_x$ films were deposited using $NH_3$ gas. The XRD analysis indicates a phase transition from polycrystalline tungsten(W) to amorphous tungsten nitride($WN_x$), showing improved etching profile of $WN_x$ films Thick $WN_x$ films were deposited on various substrates such as Tin, NiCr and Al and maximum thickness of $1.6 {\mu}m$ was obtained on the Al adhesion layer.

• Journal of the Korean Magnetics Society
• /
• v.18 no.1
• /
• pp.32-35
• /
• 2008

Thermally stable diffusion barrier of tungsten carbon nitride(W-C-N) and of tungsten boron carbon nitride(W-B-C-N) thin films have studied to investigate the impurity behaviors of boron and nitrogen. In this paper we newly deposited tungsten boron carbon nitride(W-B-C-N) thin film for various $W_2B$ target power on silicon substrate. The impurities of the 100nm-thick W-C-N and W-B-C-N thin films provide stuffing effect for preventing the inter-diffusion between W-C-N or W-B-C-N thin films and silicon during the high temperature($700^{\circ}C{\sim}1000^{\circ}C$) annealing process.

• Korean Journal of Materials Research
• /
• v.8 no.2
• /
• pp.147-153
• /
• 1998

Tungsten nitride is very attractive as absorber for X-ray lithographic mask and as a diffusion barrier for interconnecting metallization in Si VLSI technology. Microstructure of tungsten nitride films prepared by RF magnetron sputtering has been investigated as a function of deposition parameter. The crystal structure of sputtered films on silicon nitride membrane depends strongly on the NJAr gas flow ratio(0~18%1, gas pressure(l0~43mTorr). RF power (60~150W), target-substrate distance(4~8cm). Tungsten nitride films deposited at the $N_2/Ar$ gas flow ratio(- 10%). gas pressure(~10mmTorr), RF power(~150W) and target-substrate distance(6cm) are amorphous, but at other conditions are almost rough -surfaced polycrystalline. Amorphous films are very smooth($3.1\AA$ rms) and expected to be excellent absorber for X-ray mask.

• Journal of the Korean Vacuum Society
• /
• v.22 no.4
• /
• pp.188-192
• /
• 2013

Many studies have been conducted for preventing from diffusion between silicon wafer and metallic thin film due to a decrease of line-width and multi-layer thin film for miniaturization and high integration of semiconductor. This paper has focused on the nano-mechanical property of diffusion barrier which sample is prepared for various gas flow rate of nitrogen with tungsten (W) base from 2.5 to 10 sccm. The deposition rate, resistivity and crystallographic properties were measured by a ${\beta}$-ray back-scattering spectroscopy, 4-point probe and x-ray diffraction (XRD), respectively. We also has investigated the nano-mechanical property using the nano-indenter. As a result, the surface hardness of W-N thin film was increased rapidly from 10.07 to 15.55 GPa when the nitrogen gas flow was increased from 2.5 to 5 sccm. And the surface hardness of W-N thin film had 12.65 and 12.77 GPa at the nitrogen gas flow of 7.5 and 10 sccm respectively. These results were decreased by the comparison with the W-N thin film at nitrogen gas flow of 5 sccm. It was inferred that these severe changes were caused by the stoichiometric difference between the crystalline and amorphous state in W-N thin film. In addition, these results were caused by increased compressive stress.

• Journal of the Korean Vacuum Society
• /
• v.20 no.3
• /
• pp.200-204
• /
• 2011

In this paper, we deposited the tungsten carbon nitride (W-C-N; nitrogen gas flow of 2 sccm) and tungsten carbon (W-C) thin film on silicon substrate using rf magnetron sputter. Then the thin films annealed at $800^{\circ}C$ during 30 minute ($N_2$ gas ambient) for thermal damage. Nano-indenter was executed 16 points on thin film surface to measure the thermal stability, and we also propose the elastic modulus and the Weibull distribution, respectively. This nanotribology method provides statistically reliable information. From these results, the W-C-N thin film included nitrogen gas flow is more stable for film uniformities, physical properties and crystallinities than that of not included nitrogen gas flow.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.318-326
• /
• 1996

This study is to investigate a chemical vapor deposition technique of copper film which is expected to be more useful as metallizations of microcircuit fabrication. An experimental equipment was designed and set-up for this study, and a Cu-precursor used that is a metal-organic compound, named (hfac)Cu(I)VTMS ; (hevaflouoroacetylacetonate trimethyvinylsilane copper). Base pressure of the experimental system is in $10^{-6}$ Torr, and the chamber pressure and the substrate temperature can be controlled in the system. Before the deposition of copper thin film, tungsten or titanium nitride film was deposited onto the silicon wafer. Helium has been used as carrier gas to control the deposition rate. As a result, deposition rate was measured as $1,800\;{\AA}/min$ at $220^{\circ}C$ which is higher than the results of previous studies, and the average surface roughness was measured as about $200\;{\AA}$. A deposition selectivity was observed between W or TiN and $SiO_{2}$ substrates below $250^{\circ}C$, and optimum results are observed at $180^{\circ}C$ of substrate temperature and 0.8 Torr of chamber pressure.