• Journal of Powder Materials
• /
• v.5 no.4
• /
• pp.329-333
• /
• 1998

Copper-10 wt. % tungsten alloyed powder was obtained by co-reduction of mixed tungsten-trioxide and copper oxide powders at 973 K for 7.2 Ks. In the alloy obtained by pressure-assisted sintering of this co-reduced powder, ultra fine tungsten particles (about 100nm) were dispersed uniformly in the copper matrix. At room temperature, the hardness of this alloy was Hv151 and the electrical conductivity was 85% IACS. After annealing at 1173 K for 3.6 Ks, the hardness and electrical conductivity were Hv147 and 84% IACS, respectively, and were same as before annealing. It was confirmed that the hardness and electrical conductivity of this alloy were hardly influenced by annealing condition since the microstructure of this alloy is highly stabilized.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.1-5
• /
• 2003

Nano-sized WC powders were synthesized by vapor phase reaction using the precusor of tungsten ethoxide under helium and hydrogen atmosphere. The phases of the powder were varied with reaction Bone and gas flow rate. The powder size was about 30nm in diameter, and the tungsten carbide powder was coated by carbon layer. The synthesis of nano-sized WC powders was promoted as the hydrogen gas flow rate became higher. Inversely, tungsten oxide was formed by increasing the flow rate of helium gas. The synthesized powders were analyzed by XRD, FE-SEM, carbon analyzer etc.

• Nuclear Engineering and Technology
• /
• v.53 no.5
• /
• pp.1642-1651
• /
• 2021

In this study, isophtalic neopentyl glycol polyester (NPG-PES) based composites with different loading ratios of pure tungsten metal (W), tungsten (VI) oxide (WO₃), tungsten boron (WB) and tungsten carbide (WC) composites were prepared as alternative shielding materials for ionizing electromagnetic radiation (IEMR) shielding. Structural characterizations of the composites were done. Gamma spectrometric analysis of composites for 80-2000 keV energy range was performed and their usability as IEMR shielding was discussed. As a result, the produced composites showed a shielding performance of 60-100% of the lead (the most widely used IEMR shielding material) depending on the reinforcement material, reinforcement loading rate and experimental conditions. Thus, it was reported that produced composites could be an alternative to lead shieldings that have several disadvantages as toxic properties, difficulty of processing and inelasticity.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.5
• /
• pp.257-264
• /
• 2020

Anodization of Fe and Fe alloys is one of the most promising techniques to obtain iron oxide films applying to the various electrochemical devices due to their electrochemical catalytic properties. In this study, we investigate on the preparation of anodic iron oxide composite incorporated with WO₃ through a single-step anodization of stainless steel type-304 (STS304) as a substrate. The effects of applied voltage and tungsten precursor on the structural characteristics of iron oxide composite with different amount of incorporated WO₃ were observed. It is demonstrated that when the voltage of 60 V applied with 20 mM of Na₂WO₄ as a precursor, anodic iron oxide composite with a large pore diameter and a thick oxide length in which WO₃ is uniformly incorporated is obtained.

• Korean Journal of Materials Research
• /
• v.28 no.7
• /
• pp.411-416
• /
• 2018

Tungsten oxide($WO_3$) films with uniform surface morphology are fabricated using a spin-coating method for applications of electrochromic(EC) devices. To improve the EC performances of the $WO_3$ films, we control the heating rate of the annealing process to 10, 5, and $1^{\circ}C/min$. Compared to the other samples, the $WO_3$ films fabricated at a heating rate of $5^{\circ}C/min$ shows superior EC performances for transmittance modulation(49.5 %), response speeds(8.3 s in a colored state and 11.2 s in a bleached state), and coloration efficiency($37.3cm^2/C$). This performance improvement is mainly related to formation of a uniform surface morphology with increased particle size without any cracks by an optimized annealing heating rate, which improves the electrical conductivity and electrochemical activity of the $WO_3$ films. Thus, the $WO_3$ films with a uniform surface morphology prepared by the optimized annealing heating rate can be used as a potential candidate for performance improvement of the EC devices.

• Solar Energy
• /
• v.15 no.3
• /
• pp.141-149
• /
• 1995

The tungsten oxide thin films were prepared on $s_i$ wafer by using an electron-beam evaporation technique. Thickness and structure of tungsten oxide film degraded in various electrolytes were analyzed by Rutherford backscattering spectroscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and scanning electron microscope. Thickness of $WO_3$ film was the most dissolved in 1M $H_2SO_4$ electrolytye. We have confirmed that the degradation of this films was accelerated by $H_2O$ in electrolytes. But the electronic structure of film degraded by electrolyte contained of glycerol was not changed as comparision with as-deposited film. The degradation may be attributed to a change of thickness and the surface morphology of the film.

• Advances in materials Research
• /
• v.6 no.1
• /
• pp.79-91
• /
• 2017

In the present work, a design of experiment (DOE) technique using Taguchi method, has been applied to optimize the properties of ODS tungsten heavy alloys(WHAs). In this work Taguchi method involves nine experiments groups for four processing parameters (compaction pressure, sintering temperature, binding material type, and oxide type) with three levels was implemented. The signal-to-noise (S/N) ratio and analysis of variance (ANOVA) were employed to obtain the optimal process parameter levels and to analyze the effect of these parameters on density, electrical conductivity, hardness and compressive strength values. The results showed that all the chosen factors have significant effects on all properties of ODS tungsten heavy alloys samples. The density, electrical conductivity and hardness increases with the increase in sintering temperature. The analysis of the verification experiments for the physical properties (density and Electrical conductivity) has shown that Taguchi parameter design can successfully verify the optimal parameters, where the difference between the predicted and the verified values of relative density and electrical conductivity is about 1.01% and 1.15% respectively.

• Journal of Powder Materials
• /
• v.29 no.1
• /
• pp.47-55
• /
• 2022

Tungsten carbide is widely used in carbide tools. However, its production process generates a significant number of end-of-life products and by-products. Therefore, it is necessary to develop efficient recycling methods and investigate the remanufacturing of tungsten carbide using recycled materials. Herein, we have recovered 99.9% of the tungsten in cemented carbide hard scrap as tungsten oxide via an alkali leaching process. Subsequently, using the recovered tungsten oxide as a starting material, tungsten carbide has been produced by employing a self-propagating high-temperature synthesis (SHS) method. SHS is advantageous as it reduces the reaction time and is energy-efficient. Tungsten carbide with a carbon content of 6.18 wt % and a particle size of 116 nm has been successfully synthesized by optimizing the SHS process parameters, pulverization, and mixing. In this study, a series of processes for the high-efficiency recycling and quality improvement of tungsten-based materials have been developed.

• Journal of the Korean Institute of Telematics and Electronics A
• /
• v.33A no.3
• /
• pp.126-134
• /
• 1996

Tungsten silicide films were deposited on the phosphorus-doped poly-Si/SiO$_{2}$/Si-substrates by LPCVD (low pressue chemical vapor deposition). The formation and various properties of tungsten silicide processed by furnace annealing in N$_{2}$ ambient were evaluated by using XRD. AFM, 4-point probe and SEM. And the redistribution of phosphorus atoms has been observed by SIMS. The crystal structure of the as-deposited tungsten silicide films were transformed from the hexagonal to the tetragonal structure upon annealing at 550.deg. C. The surface roughness of tungsten polycide films were found to very smoothly upon annelaing at 850.deg. C and low phosphorus concentration in polysilicon layer. The sheet resistance of tungsten polycide low phosphorus concentration in polysilicon layer. The sheet resistance of tungsten polycide films are measured to be 2.4 .ohm./ㅁafter furnace annealing at 1100.deg. C, 30min. It was found that the sheet resistance of tungsten polycide films upon annealing above 1050.deg. C were independant on the phosphorus concentration of polysilicon layer and furnace annealing times. An out-diffusion of phosphorus impurity through tungsten silicide film after annealing in $O_{2}$ ambient revealed a remarkably low content of dopant by oxide capping.

• Economic and Environmental Geology
• /
• v.18 no.4
• /
• pp.331-342
• /
• 1985

The Dongbo tungsten-molybdenum deposits are fissure-filling veins emplaced in granites of late Cretaceous age. Integrated field, mineralogic and fluid inclusion studies were undertaken to illuminate the characters and origin of the ore deposits. Mineral paragenesis is complicated by repeated fracturing, but four distinct depositional stages can be recognized; (I) tungsten-molybdenum minerals-quartz-chlorite stage, (II) iron-oxide and sulfides-quartz stage, (III) iron -oxide-base metal sulfides-sulfosalts-quartz-carbonates stage, (IV) barren rhodochrosite-zeolite stage. Fluid inclusion studies were carried out for stage I quartz and stage III quartz, sphalerite and calcite. Fluid inclusion studies reveals highly systematic trends of homogenization temperature and salinity throughout the mineralization. Ore fluids during stage I were complex, NaCl rich brine and salinity reached values as high as 34.4 weight percent equivalent NaCl, but the later ore fluids were more dilute and reached to 9.7 weight percent equivalent NaCl during stage III. Intermittent boiling of ore fluid during stage I is indicated by the fluid inclusions in stage I quartz. Depositional temperatures and pressures during stage I range from $520^{\circ}C$ to $265^{\circ}C$and from 600 to 400 bars. Homogenization temperatures of the stage III quartz, sphalerite and calcite range from $305^{\circ}C$ to $190^{\circ}C$. Fluid inclusion data from the Dongbo mine are nearly similar to those from other hydrothermal tungsten deposits in the Kyeongsang basin. Depositional temperature and salinity of ore fluids during precipitation of tungsten-molybdenum minerals in Dongbo mine were much higher, but $CO_2$ contents were much lower than those from hydrothermal tungsten-molybdenum deposits of late Cretaceous plutonic association in central parts of Korean peninsula.