• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.102-106
• /
• 2007

YBCO films have been synthesized using a spray pyrolysis method. We used nitrates of Y, Ba, Cu as precursors. Deposition was made on $LaAlO_3$ (100) single crystal substrate by spraying the mist of aqueous precursor solution generated by a concentric nozzle. The distance between concentric nozzle and substrate was 15 cm. C-axis oriented films were obtained at deposition temperature of $740{\sim}800^{\circ}C$ and working pressure of 20 Torr. Oxygen partial pressure was 3 Torr and substrate was transported with the speed ranging from 0.23 cm/min to 0.7 cm/min by reel to reel. Scanning electron microscope (SEM) and X-ray diffraction (XRD) observation revealed that films are smooth and highly textured with (001) planes parallel to substrate. Highest critical current density (Jc) was $1.38\;MA/cm^2$ at 77K and self-field for the film with a thickness of $0.5\;{\mu}m$ prepared at a substrate temperature of $780^{\circ}C$ and $PO_2\;=3\;Torr$. The effect of temperature on the microstructure and YBCO phase formation will be discussed.

• 한국초전도학회:학술대회논문집
• /
• v.10
• /
• pp.56-60
• /
• 2000

Cube texture를 갖는 Ni기판위에 MOCVD(Metal Chemical Vapor Deposition)를 이용하여 NiO, CeO$_2$, YBCO 박막을 제조하였다. NiO(200)와 CeO$_2$(200) buffer layer는 450${\sim}$470$^{\circ}$C에서 10분간 MOCVD방법으로 (100)<001>Ni 기판위에 직접 증착하였다. 제조된 NiO, CeO$_2$ buffer layer는 조직이 치밀하며 표면의 상태가 매우 좋으며 Ni기판 위에 epitaxial하게 성장하였다. NiO는 Ni기판과 NiO<100>//Ni<100>의 방위관계를 가지고 성장하였으며, CeO$_2$는 증착조건에 따라 CeO$_2$ <100>//Ni<100> 및 CeO$_2$ <110>//Ni<100> 의 방위관계를 가지고 성장하였다. 증착된 NiO막과 CeO$_2$막에서 균열은 발생하지 않았다. MOCVD법으로 표면에 biaxial texture를 갖는 ceramic buffer를 증착시킨 NiO/Ni및 CeO$_2$/Ni 기판위에 YBCO박막을 MOCVD법으로 제조하였다. YBCO막은 기판온도 800$^{\circ}$C,증착압력 10torr, 산소분압을 0.7torr로 하여 10분간 행하였다. 공급원료의 조성에 따라 YBCO의 막의 texture와 형성되는 상이 변화되었다. NiO/Ni및 CeO$_2$/Ni 기판 위에 증착된 YBCO막은 c축 배향성을 가지고 성장하였으며, -scan 및 ${\varphi}$ -scan으로 측정한 (500)면의 in-plane과 (110)면의 out-of-plane의 FWHM(Full Width Half Maximum)값은 각각 10$^{\circ}$ 미만으로 우수하였다.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.145-151
• /
• 2006

Nickel and nickel-tungsten alloy were electroplated on a cold rolled and heat treated copper(Cu) substrate. 4 mm-thick high purity commercial grade Cu was rolled to various thicknesses of 50, 70, 100 and 150 micron. High reduction ratio of 30% was applied down to 150 micron. Rolled texture was converted into cube texture via high temperature heat treatment at $400-800^{\circ}C$. Grain size of Cu was about 50 micron which is much smaller compared to >300 micron for the Cu prepared using smaller reduction pass of 5%. 1.5 km-long 150 micron Cu was fabricated with a rolling speed of 33 m/min and texture of Cu was uniform along length. Abnormal grain growth and non-cube texture appeared for the specimen anneal above $900^{\circ}C$. 1-10 micron thick Ni and Ni-W film was electroplated onto an annealed cube-textured Cu or directly on a cold rolled Cu. Both specimens were annealed and the degree of texture was measured. For electroplating of Ni on annealed Cu, Ni layer duplicated the cube-texture of Cu substrate and the FWHM of in plane XRD measurement for annealed Cu layer and electroplated layer was $9.9^{\circ}\;and\;13.4^{\irc}$, respectively. But the FWHM of in plane XRD measurement of the specimen which electroplated Ni directly on cold rolled Cu was $8.6^{\circ}$, which is better texture than that of nickel electroplated on annealed Cu and it might be caused by the suppression of secondary recrystallization and abnormal grain growth of Cu at high temperature above $900^{\circ}C$ by electroplated nickel.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.2
• /
• pp.86-92
• /
• 2013

$SF_6/O_2$ inductively coupled plasmas were employed to texture Si surface as a pretreatment for nanocrystalline diamond film growth. It was found that the $SF_6/O_2$ plasma texturing provided a very wide process window where normalized roughness values in the range of 2~16 could be obtained. Significantly improved nucleation densities of ${\sim}6.5{\times}10^{10}cm^{-2}$ compared to conventional mechanical abrasion were achieved after seeding for the textured Si substrate.

• Journal of the Korean Magnetics Society
• /
• v.8 no.5
• /
• pp.282-287
• /
• 1998

Dependence of magnetoresistance on base pressure and deposition rates of each Fe, Co, Cu layers in the $Fe(50{\AA}/[Co(17{\AA})/Cu(24{\AA})]_20$ multilayer thin films, prepared by dc magnetron sputtering on Corning glass, were investigated. AFM analysis, X-ray diffraction analysis, vibrating sample magnetometer analysis, and magnetoresustance measurement (4-probe method) were performed. The multilayer films deposited under low base pressure increases magnetoresistance ratio by preventing oxidation. Annealing for the samples at a moderate temperature allowed larger textured grain with no loss in the periodicity. Magnetoresistance ratio of the annealed multilayers was increased due to the increase antiferromagnetically coupled fraction of the film after annealing. Optimization of deposition rate was greater than 1 $\AA$/s for Fe, and 2.8 $\AA$/s for Cu. Deposition rate of Co showed a tendency of increasing of magnetoresistance ratio due to the formation of flat magnetic layer in case of high deposition rate of Co.

• Journal of the Korean Ceramic Society
• /
• v.43 no.11 s.294
• /
• pp.715-723
• /
• 2006

Perovskite oxide materials are very important for the electronics industry, because they exhibit promising properties. With an interest in the obvious applications, significant effort has been invested in the growth of highly crystalline epitaxial perovskite oxide thin films in our laboratory. And the desired structure of films was formed to achieve excellent properties. $Y_1Ba_2Cu_3O_{7-x}$ (YBCO) superconducting thin films were simultaneously deposited on both sides of 3 inch wafer by inverted cylindrical sputtering. Values of microwave surface resistance R$_2$ (75 K, 145 GHz, 0 T) smaller than 100 m$\Omega$ were reached over the whole area of YBCO thin films by pre-seeded a self-template layer. For implementation of voltage tunable high-quality varactor, A tri-layer structured SrTiO$_3$ (STO) thin films with different tetragonal distortion degree was prepared in order to simultaneously achieve a large relative capacitance change and a small dielectric loss. Highly a-axis textured $Ba_{0.65}Sr_{0.35}TiO_3$ (BST65/35) thin films was grown on Pt/Ti/SiO$_2$/Si substrate for monolithic bolometers by introducing $Ba_{0.65}Sr_{0.35}RuO_3$ (BSR65/35) thin films as buffer layer. With the buffer layer, the leakage current density of BST65/35 thin films were greatly reduced, and the pyroelectric coefficient of $7.6\times10_{-7}$ C $cm^{-2}$ $K^{-1}$ was achieved at 6 V/$\mu$m bias and room temperature.

• Korean Journal of Soil Science and Fertilizer
• /
• v.33 no.1
• /
• pp.1-7
• /
• 2000

Management of phosphorus availability in the plastic film house soils in Korea merits attention because salts have been accumulated for last decades due to the heavy application of fertilizers and intensive cropping practices. In an attempt to characterize the P availability, available phosphorus contents and electrical conductivity of the saturated extracts ($EC_e$) were measured for soils collected from the 169 plastic film houses in Kangwon-do. Soil phosphorus contents were analyzed by methods of Lancaster, Bray No. 1, Olsen, Truog, water extractable and saturation extracts. Phosphorus concentrations in the saturated extracts of the plastic film house soils ranged from 0.02 to $34mg\;L^{-1}$, with the average of $8mg\;L^{-1}$. The available $P_2O_5$ of the soils ranged from 136 to $3,689mg\;Kg^{-1}$, with the average of $1,261mg\;Kg^{-1}$. The water soluble $P_2O_5$ ranged from 2 to $118mg\;L^{-1}$, with the average of $39mg\;L^{-1}$. A significant correlation existed between saturation extract P (Y) and available $P_2O_5$ (X) [Y = -5.075 + 0.018X, $r=0.662^{***}$] indicating $1.0mg\;P\;L^{-1}$ of in the saturated extract was equivalent to $337mg\;Kg^{-1}$ of the available $P_2O_5$ by Lancaster method. Electrical conductivity of the saturated pastes ($EC_e$) was highly significantly correlated with EC (1:5), yielding the slope of 12.2 for the coarse textured plastic film house soils. Results of higher concentrations of available P in soil solution and dilution factor of 12.2 for $EC_e$ demonstrate that a special care must be taken in terms of fertilizer management and data interpretation for soils under this specific condition.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2003.11a
• /
• pp.235-235
• /
• 2003

The development of a buffer layer is an important issue for the second -generation wire, YBCO coated metal wire. The buffer layer demands not only on the prohibition of the reaction between YBCO and metal substrate, but also the proper lattice match and conductivity for high critical current density (Jc) of YBCO superconductor, In order to satisfy these demands, we suggested CaRuO3 as a useful candidate having that the lattice mismatches with Ni (200) and with YBCO are 8.2% and 8.0%, respectively. The CaRuO3 thin films were deposited on Ni substrates using various methods, such as e-beam evaporation and DC and RF magnetron sputtering. These films were investigated using SEM, XRD, pole-figure and AES. In e-beam evaporation, the deposition temperature of CaRuO3 was the most important since both hi-axial texturing and NiO formation between Ni and CaRuO3 depended on it. Also, the oxygen flow rate had i[n effect on the growth of CaRuO3 on Ni substrates. The optimal conditions of crystal growth and film uniformity were 400$^{\circ}C$, 50 ㎃ and 7 ㎸ when oxygen flow rate was 70∼100sccm In RF magnetron sputtering, CaRuO3 was deposited on Ni substrates with various conditions and annealing temperatures. As a result, the conductivity of CaRuO3 thin films was dependent on CaRuO3 layer thickness and fabrication temperature. We suggested the multi-step deposition, such as two-step deposition with different temperature, to prohibit the NiO formation and to control the hi-axial texture.

• Progress in Superconductivity
• /
• v.6 no.1
• /
• pp.74-78
• /
• 2004

YBCO coated conductor is one of the most promising materials as a new generations wire especially for practical power applications. In this work, $YBa_2$$Cu_3$$O_{7}$ -$\delta$/(YBCO) coated conductors (CC) were deposited by pulsed laser deposition (PLD) from buffer layers to superconducting layer on hi-axially textured metal tape. The oxide multilayer buffered substrate of architectures of $CeO_2$/$YSZ/Y_2$$O_3$ was fabricated by PLD at steady status. Then YBCO layer was deposited on RABiTS substrate by stationary and reel-to-reel (R2R) continuous process and we compared with deposition conditions of both processes. The degree of texture of each layer was investigated using X-ray diffraction including $\theta$-2$\theta$ scans, $\omega$-scans and $\Phi$-scans analysis. Their surface morphology was observed by scanning electron microscopy (SEM). The FWHM of the X-ray $\Phi$-scans and $\Phi$-scans indicated that YBCO and buffer layers closely replicate the in-plane and out-of-plane texture of metal tape. Critical current (Ic) at 77 K, self-field of 75.8 A/cm-width, critical temperature (Tc) of 85 K, and critical current density (Ic) of 3.7 MA/$\textrm{cm}^2$ were measured from coated conductor deposited by stationary process. And coated conductor deposited by R2R continuous process had Ic of 57.5 A/cm-width, Tc of 86.5 K and Jc of 2.0 MA/$\textrm{cm}^2$. The film also exhibits a homogeneous and dense surface morphology.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.6
• /
• pp.580-586
• /
• 2016

Cr-Si-Al-N coating with different Si content were deposited by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The deposition temperature was $300^{\circ}C$, and the gas ratio of $Ar/N_2$ were 9:1. The CrSi alloy and aluminum targets used for arc ion plating and sputtering process, respectively. Si content of the CrSi alloy targets were varied with 1 at%, 5 at%, and 10 at%. The phase analysis, composition and microstructural analysis performed using x-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) including energy dispersive spectroscopy (EDS), respectively. All of the coatings grown with textured CrN phase (200) plane. The thickness of the Cr-Si-Al-N films were measured about $2{\mu}m$. The friction coefficient and removal rate of films were measured by a ball-on-disk test under 20N load. The friction coefficient of all samples were 0.6 ~ 0.8. Among all of the samples, the removal rate of CrSiAlN (10 at% Si) film shows the lowest values, $4.827{\times}10^{-12}mm^3/Nm$. As increasing of Si contents of the CrSiAlN coatings, the hardness and elastic modulus of CrSiAlN coatings were increased. The morphology and composition of wear track of the films was examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy, respectively. The surface energy of the films were obtained by measuring of contact angle of water drop. Among all of the samples, the CrSiAlN (10 at% Si) films shows the highest value of the surface energy, 41 N/m.