Manufacturing of YBCO coated conductor deposited on RABiTS by pulsed laser deposition method

RABiTS 위에 PLD 방법으로 증착된 YBCO 초전도 박막 선재의 제조

YBCO coated conductor is one of the most promising materials as a new generations wire especially for practical power applications. In this work, $YBa_2$$Cu_3$$O_{7}$ -$\delta$/(YBCO) coated conductors (CC) were deposited by pulsed laser deposition (PLD) from buffer layers to superconducting layer on hi-axially textured metal tape. The oxide multilayer buffered substrate of architectures of $CeO_2$/$YSZ/Y_2$$O_3$ was fabricated by PLD at steady status. Then YBCO layer was deposited on RABiTS substrate by stationary and reel-to-reel (R2R) continuous process and we compared with deposition conditions of both processes. The degree of texture of each layer was investigated using X-ray diffraction including $\theta$-2$\theta$ scans, $\omega$-scans and $\Phi$-scans analysis. Their surface morphology was observed by scanning electron microscopy (SEM). The FWHM of the X-ray $\Phi$-scans and $\Phi$-scans indicated that YBCO and buffer layers closely replicate the in-plane and out-of-plane texture of metal tape. Critical current (Ic) at 77 K, self-field of 75.8 A/cm-width, critical temperature (Tc) of 85 K, and critical current density (Ic) of 3.7 MA/$\textrm{cm}^2$ were measured from coated conductor deposited by stationary process. And coated conductor deposited by R2R continuous process had Ic of 57.5 A/cm-width, Tc of 86.5 K and Jc of 2.0 MA/$\textrm{cm}^2$. The film also exhibits a homogeneous and dense surface morphology.