• 열처리공학회지
• /
• 제25권4호
• /
• pp.196-205
• /
• 2012

The purpose of this study is to enhance the hardenability and the mechanical properties by the addition of alloying elements such as Ni, Cr, Mo and B for the development of Cr-Mo plastic mold steel with uniform hardness and microstructure. The ingots were prepared by vacuum induction melting and forged to ${\Phi}35mm$ round bar. Forged bars were quenched and tempered at $200{\sim}600^{\circ}C$ for 1.5 hour. Jominy test, boron distribution observation, microstructual observation, tensile test and charpy impact test were conducted. It was confirmed that the hardenablity of these steels was improved by increasing of alloying elements and further promoted by the addition of boron. The critical rate of cooling required to obtain the bainitic structure for 0.27C-1.23Cr-0.28Mo-B steel was $0.5^{\circ}C/sec$. Hardness and strength of Cr-Mo steels decreased with increasing tempering temperature, but elongation and reduction of area increased with increasing tempering temperature. However, impact energy tempered at $400^{\circ}C$ showed the lowest value in the range $200{\sim}600^{\circ}C$ due to the temper embrittlement.

• 한국재료학회지
• /
• 제28권2호
• /
• pp.113-117
• /
• 2018

Effects of annealing temperature on the microstructure and mechanical properties through thickness of a cold-rolled Cu-3.0Ni-0.7Si alloy were investigated in detail. The copper alloy with thickness of 3 mm was rolled to 50 % reduction at ambient temperature without lubricant and subsequently annealed for 0.5h at $200{\sim}900^{\circ}C$. The microstructure of the copper alloy after annealing was different in thickness direction depending on an amount of the shear and compressive strain introduced by rolling; the recrystallization occurred first in surface regions shear-deformed largely. The hardness distribution of the specimens annealed at $500{\sim}700^{\circ}C$ was not uniform in thickness direction due to partial recrystallization. This ununiformity of hardness corresponded well with an amount of shear strain in thickness direction. The average hardness and ultimate tensile strength showed the maximum values of 250Hv and 450MPa in specimen annealed at $400^{\circ}C$, respectively. It is considered that the complex mode of strain introduced by rolling effected directly on the microstructure and the mechanical properties of the annealed specimens.

• 한국재료학회지
• /
• 제30권3호
• /
• pp.149-154
• /
• 2020

A powder-in-sheath rolling method is applied to the fabrication of a carbon nano tube (CNT) reinforced copper composite. A copper tube with outer diameter of 30 mm and wall thickness of 2 mm is used as sheath material. A mixture of pure copper powder and CNTs with a volume content of 3 % is filled in a tube by tap filling and then processed to an 93.3 % reduction using multi-pass rolling after heating for 0.5 h at 400 ℃. The specimen is then sintered for 1h at 500 ℃. The relative density of the 3 vol%CNT/Cu composite fabricated using powder in sheath rolling is 98 %, while that of the Cu powder compact is 99 %. The microstructure is somewhat heterogeneous in width direction in the composite, but is relatively homogeneous in the Cu powder compact. The hardness distribution is also ununiform in the width direction for the composite. The average hardness of the composites is higher by 8Hv than that of Cu powder compact. The tensile strength of the composite is 280 MPa, which is 20 MPa higher than that of the Cu powder compact. It is concluded that the powder in sheath rolling method is an effective process for fabrication of sound CNT reinforced Cu matrix composites.

• 동아시아식생활학회지
• /
• 제25권4호
• /
• pp.681-690
• /
• 2015

In this study, gluten-free noodles were developed and the physicochemical quality of gluten-free noodles added with nondigestible maltodextrin (NMD) was also investigated. The gluten-free noodles were prepared by addition of 0, 5, 7, and 9% NMD of total ingredients except water. Inhibition activities for ${alpha}$-amylase and ${alpha}$-glucosidase according to the addition amounts of NMD were evaluated. As a result, activities of carbohydrate-digestive enzymes decreased with an increase of the added NMD amounts. Water binding capacity and solubility of raw noodles increased upon NMD addition. Swelling power also increased as temperature rose. L value of raw noodles decreased with the addition of NMD, but b value increased. Texture profile analysis of cooked noodles showed reduction of hardness, springiness, and chewiness of noodles with NMD. On the other hand, tensile strength of cooked noodles containing up to 7% NMD was not significantly different from that of noodle without NMD. In the sensory evaluation, elasticity of noodles with 9% NMD was lower than that of other noodles, whereas other characteristics of noodles were not significantly different among noodles. Therefore, it was confirmed that the addition of 5~7% NMD had little effect on the sensory quality of noodles.

• 콘크리트학회지
• /
• 제9권2호
• /
• pp.137-144
• /
• 1997

발수제의 유무와 알루미늄분말의 분말도 및 첨가량을 조절하여 비중을 0.4에서 0.7로 변화시켜 비중과 ALC의 기초물성, 내동해성 및 내구성과의 관계를 조사하였다. 압축 및 인장강도는 비중이 0.4에서 0.7로 증가함에 따라 발수제의 첨가량에 관계없이 증가하였고 발수제의 첨가량이 증가하면 내동해성은 개선되었으며 흡수율은 감소하였다. 입경이 작은 AI분말을 이용항 제조한 ALC의 박리에 의한 체적감소율은 낮게 나타났으며 일면동결지속시험 및 기중동결수중융해시험에서도 내동해성이 우수한 것으로 나타났다.

• 한국의류산업학회지
• /
• 제8권3호
• /
• pp.363-369
• /
• 2006

In this the study, Lyocell fabrics for blanket were developed to get high value added goods for elder and Infant. Therefore, the purpose of the study was determine the effect of twist per inch on the physical properties of developed fabrics, including compression property and abrasion resistance on the process for making Lyocell combined yarns. For comparison, commonly used cotton blanket was used. The results were as the follows: 1) Dimensional changes of Lyocell fabrics was in -3% which value was pretty stable, and antistatic property was very good with 10V of electric propensity voltage which means there was no static electricity at all. Pilling property of Lyocell fabrics showed 3 grade which was good and air permeability and moisture vapor transmission rate of Lyocell fabrics were higher than those of cotton fabric and keeping warmth rate of Lyocell fabrics was about 50% which means it very warms. 2) Twist per inch of Lyocell combined yarns increased with tensile strength and elongation of Lyocell fabrics. 3) Twist per inch of Lyocell combined yarns increased with decreasing thickness reduction rate and therefore, compression property of those was pretty good. Specially, compression property of Lyocell fabrics made with yarns of 3.9TPI was better than those of cotton fabric. 4) Twist per inch of Lyocell combined yarns increased with abrasion resistance of Lyocell fabrics.

• 한국수소및신에너지학회논문집
• /
• 제27권3호
• /
• pp.270-275
• /
• 2016

A simple solid state incorporation method was employed in order to incorporate Pd nanocatalyst into a Nafion film for polymer electrolyte membrane fuel cell (PEMFC) via the reduction of palladium (II) bis (acetylacetonate), $Pd(acac)_2$. It was sublimed, penetrated into Nafion film and then reduced to Pd nanoparticles simultaneously in a glass reactor of N2 atmosphere at $180^{\circ}C$ for 1, 3 and 5 min. This reaction was took place without any reducing agent and any solvent. The morphology of the Pd nanoparticles was observed by transmission electron microscopy (TEM), and Pd distribution was analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). And 23% modification of tensile strength of Pd/Nafion composite film was measured by universal testing machine and I-V curve was estimated by using a unit cell with $5{\times}5cm^2$ active area.

• Computers and Concrete
• /
• 제11권4호
• /
• pp.271-289
• /
• 2013

In this research, a developed microstructural model of cement particles was presented to describe the cement hydration procedure. To simplify the hydration process, the whole hydration was analyzed in a series of sub-steps. In each step, the hydration degree, as well as the microstructural size of the hydration cell, was calculated as a function of the radius of the unreacted cement particles. With the consideration of the water consumption and the reduction of the interfacial area between water and hydration products, the micro-level expressions of the cement hydration kinetics were established. Then the heat released and temperature history of the concrete was carried out with the hydration degree obtained from each sub-steps. The equivalent age method based on the Arrhenius law was introduced in this research. Based on the equivalent age method, a maturity model was applied to describe the evolution of the mechanical properties of the material during the hydration process. The finite element program ANSYS was used to analyze the temperature field in concrete structures. Then thermal stress field was calculated using the elasticity modulus obtained from code formulate. And the risk of thermal cracking was estimated by the comparison of thermal stress and concrete tensile strength.

• 한국분말재료학회지
• /
• 제11권3호
• /
• pp.259-264
• /
• 2004

Aluminum based metal matrix composite reinforced with SiC particles was fabricated by the powder-in sheath rolling method. A stainless steel tube with outer diameter of 12 mm and wall thickness of 1mm was used as a sheath. Mixture of aluminum powder and SiC particles of which volume content was varied from 5 to 20vol.% was filled in the tube by tap filling and then rolled to 75% reduction at ambient temperature. The rolled specimen was sintered at 56$0^{\circ}C$ for 0.5hr. The tensile strength of the (SiC)$_{p}$/Al composite increased with the volume content of SiC particles, and at 20vol.% it reached a maximum of 100㎫ which is 1.6 times higher than unreinforced material. The elongation decreased with the volume content of $Al_{2}$O$_{3}$ particles. The mechanical properties of the (SiC)$_{p}$/Al composite fabricated by the powder-in sheath rolling is compared with that of (Al$_{2}$O$_{3}$)$_{p}$/Al composite by the same process.ess.

• 한국분말재료학회지
• /
• 제14권4호
• /
• pp.251-255
• /
• 2007

This work is to report not only the effect of rapid solidification of $MgZn_{4.3}Y_{0.7}$ alloys on the micro-structure, but also the extrusion behavior on the materials properties. The average grain size of the atomized powders was about $3-4{\mu}m$. The alloy powders of $Mg_{97}Zn_{4.3}Y_{0.7}$, consisted of I-Phase (Icosahedral, $Mg_{3}Zn_{6}Y_{1}$) as well as Cubic structured W-Phase ($Mg_{3}Zn_{3}Y_{2}$), which was finely distributed within ${\alpha}-Mg$ matrix. The oxide layer formed along the Mg surface was about 48 nm in thickness. In order to study the consolidation behavior of Mg alloy powders, extrusion was carried out with the area reduction ratio of 10:1 to 20:1. As the ratio increased, fully deformed and homogeneous microstructure could be obtained, and the mechanical properties such as tensile strength and elongation were simultaneously increased.