• Fibers and Polymers
• /
• v.7 no.4
• /
• pp.372-379
• /
• 2006

The surface topography, tensile properties, and thermal properties of ramie fibers were investigated as reinforcement for fully biodegradable and environmental-friendly 'green' composites. SEM micrographs of a longitudinal and cross sectional view of a single ramie fiber showed a fibrillar structure and rough surface with irregular cross-section, which is considered to provide good interfacial adhesion with polymer resin in composites. An average tensile strength, Young's modulus, and fracture strain of ramie fibers were measured to be 627 MPa, 31.8 GPa, and 2.7 %, respectively. The specific tensile properties of the ramie fiber calculated per unit density were found to be comparable to those of E-glass fibers. Ramie fibers exhibited good thermal stability after aging up to $160^{\circ}C$ with no decrease in tensile strength or Young's modulus. However, at temperatures higher than $160^{\circ}C$ the tensile strength decreased significantly and its fracture behavior was also affected. The moisture content of the ramie fiber was 9.9 %. These properties make ramie fibers suitable as reinforcement for 'green' composites. Also, the green composites can be fabricated at temperatures up to $160^{\circ}C$ without reducing the fiber properties.

• Journal of Adhesion and Interface
• /
• v.10 no.2
• /
• pp.98-105
• /
• 2009

Poly(amic acid) was synthesized from the reaction of p-PDA/ODA and PMDA/BPDA and silane oligomer containing epoxy group was also synthesized from the reaction of tetramethylorthosilicate (TMOS) and glycidol. After hybridizing poly (amic acid) and silane oligomer, they were effectively converted into polyimide/silica hybrid films by thermal imidization process. As the silica contents in hybrid films increased, CTE values decreased from 17 ppm/K to 10 ppm/K and the tensile modulus increased, in spite of decreasing tensile strength. In addition, the peel test showed that the adhesion strength of hybrid film was enhanced from $0.43kg_f/cm$ to $1.02kg_f/cm$. Therefore, it could be concluded that the polyimide/silica hybrid film is effective to enhance adhesion strength for FCCL films.

• Journal of Adhesion and Interface
• /
• v.14 no.2
• /
• pp.68-74
• /
• 2013

We synthesized polyurethane elastomer containing acid groups. We measured the adhesion, grip, tensile strength and mechanical properties. Casting polyurethane elastomers were prepared with the contents of acid. The adhesive strength and the wet slip were increased. Also, the tensile strength and abrasion properties were increased. We measured the properties with different acid contents. Increasing the acid content, the mechanical properties were increased. But the mechanical properties were decreased above 0.20 wt% of acid content. The wet slip was increased and the contact angle was decreased as the acid content increased.

• Journal of Adhesion and Interface
• /
• v.7 no.2
• /
• pp.26-31
• /
• 2006

In order to effectively improve interfacial adhesion strength between polypropylene (PP) and jute fiber, we particularly incorporated maleic anhydride grafted PP (MAPP) into the matrix through the environment-friendly process without an additional method of process and had better mechanical performances by providing the alignment into the natural fiber than those of the conventional fabrication technology such as an extrusion or injection molding. We also proposed hot pressing method which applied relatively low shear to the composites and confirmed the chemical bonds among the functional groups of MAPP and jute using FT-IR approach. The concentration of MAPP for maximum tensile strength and modulus was optimized at 3 wt%. Flexural properties had no noticeable tendency to increase with MAPP contents compared to tensile strength, which could probably be explained by the degree in wetting of PP/MAPP matrix.

• Journal of Adhesion and Interface
• /
• v.22 no.3
• /
• pp.85-90
• /
• 2021

Generally, the tensile strength of carbon fiber reinforced composite (CFRP) should be determined to produce this material. The tensile strength was performed based on ASTM D3039, and this test could cause the error by specimens and human. In this research, the CFRP tensile test was performed with different thickness of specimens and tap, adhesive for attaching tap, and pressure of jig to hold the specimens, while the test was performed based on ASTM D3039. The tensile stress and modulus exhibited differently with different specimen thicknesses, and the 1~1.5 mm thickness of the specimen was optimized. In the case of 0.28 MPa jig pressure, the slip or fracture at the clamping area of the specimen has not occurred, and specimens were fractured to the center section of the specimen. The adhesive to attach jig on specimen should be used to exhibit high adhesive stress. Experimental parameters could cause errors. It is expected to achieve an accurate tensile property evaluation of composite materials via improvements in adhesives, tabs, and jigs.

• Journal of Adhesion and Interface
• /
• v.23 no.4
• /
• pp.137-143
• /
• 2022

In this study, the polyurethane acrylates (PUA) resin with good adhesive and flexibility for adhesive for shoes and clothing were synthesized using that poly(tetramethylene adiphate glycol) (PTAd), poly(tetramethylene ether glycol) (PTMG) as polyester polyol and polyether polyol respectively, including 4,4'-methylene diphenyl diisocyanate (MDI), isophorone diisocyanate (IPDI), 1,4-butandiol (1,4-BD), 2-hydroxyethyl methacrylate (2-HEMA) and dibutyl amine (DBA). The effect of polyol blend in the polyurethane acrylate on thermal and mechanical properties, adhesion strength and flexural strength were studied. The glass transition temperature (T_g) of PUA was confirmed in range of -70~-40 ℃. In addition, the glass transition temperature (T_g), decomposition temperature (T_d), tensile strength adhesion strength and heat resistance were increased as increasing of PTAd amount while the elongation, water resistance and flexural properties were decreased. The synthesized polyurethane acrylate with 5:5 ratio of PTAd and PTMG indicated the highest adhesion strength and flexural properties.

• Journal of Adhesion and Interface
• /
• v.15 no.3
• /
• pp.109-115
• /
• 2014

In this study, we synthesized and identified microcapsule containing isocyanate, and investigated the mechanical and adhesion properties of polyurethane resin by adding microcapsule. We found out that the core material of microcapsule and the component weight fraction of microcapsule from the FT-IR and TGA analysis. From the results of adhesion and mechanical property tests, we confirmed that in case of using microcapsule for adhesive resin composition, adhesion strength, tensile strength and abrasion were improved by cross-linking reaction between urethane and IPDI in microcapsule.

• International Journal of Highway Engineering
• /
• v.10 no.3
• /
• pp.239-246
• /
• 2008

In this study, the influence of reaction temperatures, mixing time and flexible modifier for crumb rubber modified asphalt(CRMA) as processing conditions were investigated. The temperature susceptibility and adhesion properties of neat and modified asphalts at low temperature measured using the penetration and tensile adhesion test. It was found that processing temperatures and flexible modifier were important factors for tensile adhesion strength and toughness energy at low temperature. The CRMA in the higher processing temperature and flexible modifier exhibited improved tensile adhesion properties which indicated the flexible structure of neat and modified asphalt binder. In general, the improvements of the physical properties in the CRMAs were due to the improvements of miscibility between CR and asphalt binder. It was found that the adhesion properties of the flexible agent modified CRMA were higher than CRMA were related to the flexible agent tend to penetrate into CR particles and asphalt binder.

• Restorative Dentistry and Endodontics
• /
• v.16 no.1
• /
• pp.60-73
• /
• 1991

The purpose of this study is to evaluate the effects of etching time, environmental temperature and humidity on the adhesion of composite resin to glass-ionomer cement. Two chemical cure composite resins (Clearfil F II and Microrest AP) and two glass-ionomer cements (Fuji ionomer Type I and KET AC-CEM) were used as the experimental materials. The experiment is performed in 3 stages: The first stage is to bond composite resins to glass-ionomer cements, and the surface was not etched, and etched for 20 seconds, 40 seconds, and 60 seconds. Then specimens are stored in distilled water at $37^{\circ}C$ for 24 hours to measure tensile strength. The second stage is to choose the one group that had the highest tensile strength from the first stage and prepare two experimental groups: One group with composite resin bonded to glass-ionomer cement without etching and bonding agent application and the other with composite resin bonded to glass-ionomer cement with etching but without any bonding agent application. The specimens are stored in distilled water at $37^{\circ}C$ for 24 hours and tensile strength is measured. The third stage is to choose group that had the highest tensile strength from the first stage experiment, and bond composite resin to glass-ionomer cement at $24^{\circ}C$ 44%, $30^{\circ}C$ 44%, $30^{\circ}C$ 80%, and $32^{\circ}C$ 92%. The storage time of specimens is to bond immediately after storage, then changed to 30 sec., 60 sec., and 120 sec.. Specimens are stored in distilled water at $37^{\circ}C$ for 24 hours and their tensile strength are measured again. The following results were obtained: 1. As the etching time increases, the tensile bond strength between glass-ionomer cement and composite resin increase, and the tensile bond strength is the highest when acid etched for 60 minutes (P < 0.05). 2. After acid etching for 60 minutes, the tensile strength of the group with bonding agent was stronger than that without bonding agent application (P < 0.05). 3. The tensile strength of Clearfil F II was stronger than that of Microrest AP. 4. It was observed that the tensile bond strength is not affected by different storage time with different temperature and humidity. 5. As the humidity was increased, the tensile bond strength between glass-ionomer cement and composite resin decreased (P < 0.05).

• Journal of Adhesion and Interface
• /
• v.8 no.4
• /
• pp.8-13
• /
• 2007

In this study, solvent-free waterborne polyurethanes (SWPU) were synthesized with teramethylxylene diisocyanate (TMXDI), poly(tetramethylene glycol) (PTMG) and polycarprolactone (PCL) and different mole ratio of dimethylol proponicacid (DMPA). The effect of ionic contents in the solvent-free waterborn polyurethane on thermal, mechanical properties and adhesion strength were studied. Glass transition temperature (Tg) were in range of $-70{\sim}-50^{\circ}C$ and increased as PCL contents increased in polyol. With more incorporation of PCL and DMPA contents in SWPU, tensile strength, adhesion strength and heat resistance of SWPU increased, while the elongation decreased.