• 대한기계학회논문집B
• /
• 제23권3호
• /
• pp.311-319
• /
• 1999

The thermal conductivity ${\lambda}_b$, thermal diffusivity ${\alpha}_b$ of the thin black paint layer sprayed on solid surface and absorptivity a for laser beam are measured by applying a non-contact measurement method of the thermophysical properties of solids. The values of a=0.67, ${\lambda}_b=1.45W/mK$ and ${\alpha}_b=1.24{\times}10^{-6}m^2/s$ are obtained for the sprayed lay~ thickness $z_b{\fallingdotseq}40\;{\mu}m$. Furthermore, for the $z_b{\fallingdotseq}24\;{\mu}m$ thick layers which arc formed by rubbing with a glass rod after spraying, the values of a=0.73, ${\lambda}_b=1.85W/mK$. and ${\alpha}_b=1.09{\times}10^{-6}m^2/s$ are obtained. It is also shown that the present thermal diffusivity ${\alpha}_b$ for $z_b{\fallingdotseq}40\;{\mu}m$ Is about 30~80% larger than those obtained by Araki et al. for the thicker layer $z_b{\fallingdotseq}150{\sim}248\;{\mu}m$. This method could be applied to the measurement of thermophysical properties of thin layer on solids.

• 한국응용과학기술학회지
• /
• 제31권2호
• /
• pp.176-182
• /
• 2014

Using alkali treatment solution, neutrality treatment solution and acid treatment solution, the surface corrosion layer of copper plates and bronze plates that have been artificially corroded using HCl, $H_2SO_4$ and $HNO_3$ solutions were removed. In the case of alkali treatment solution, only air oxidation in the form of black tenorite and white cuproous chloride remained without being removed. In the case of using a neutrality treatment solution, a anhydrous type layer of reddish brown cupric chloride remained without being removed, together with this black and white corrosion substance. In the case of using an acid treatment solution, this red corrosion substance also remained, but all of the oxide was removed on the surface of the specimen that was treated by alternatively using alkali treatment solution and acid treatment solution. In the case of this treatment solution with the order of alkali-acid, oxidation no longer proceeded only through the distilled water cleaning process after treatment, thereby showing that oxidation from the cleaning solution no longer proceeded.

• 한국표면공학회지
• /
• 제43권2호
• /
• pp.97-104
• /
• 2010

In this paper, we conducted MATLAB simulation using the reflectance formula and the Planck's black body radiation principle, for the purpose of identifying the opimum material and thickness of anti-reflective coating from double layered structures. We found that the optimum condition was obtained when refractive index of upper layer is 1.44 and that of lower layer is 2.29. As materials close to these refractive indices, $MgF_2$ as the upper layer and $HfO_2$, ZnS, $TiO_2$ as the lower layer were suggested. The best result in an average reflectance of 2.759% was obtained from a double layered structure of $MgF_2$ 94 nm/ZnS 55 nm.

• Applied Microscopy
• /
• 제26권3호
• /
• pp.277-291
• /
• 1996

The structures of the egg envelope in fertilized eggs of three species of characidae, head and tail light fish (Hemigrammus ocellifer), black tetra (Gymnocorymbus ternetzi), and buenos aires tetra (Hemigrammus caudovittatus) were studied using light and electron microscopes. The fertilized eggs in all species were colorless, transparent, spherical and non-floted type. The egg envelopes have a single micropyle resembling the pathway of sperm in the area of the animal pole. The micropyle was surrounded by protruded lines of the egg envelope in a radiated form. Egg envelopes of fertilized eggs in both head and tail light fish and buenos aires tetra consisted of three distinct layers; an outer layer, a middle layer and an inner layer. And that of blacktetra consisted of two layers; an outer layer and an inner layer. Also, an outer layers of both head and tail light fish and black tetra were adhesive types but, in that of buenous aires tetra was non-adhesive type. An outer surface of egg envelope in black tetra was arranged by pores regularly. In that of head and tail light fish and buenos aires tetra have a rough side. An inner layer of egg envelope in fertilized eggs consisted of lamellae alternating with interlamellae of lower electron density; an inner layer of fertilized eggs in head and tail light fish consisted of three layers, that of black tetra was four layers, and that of buenos aires tetra was five layers.

• 보존과학회지
• /
• 제26권3호
• /
• pp.247-258
• /
• 2010

무령왕릉 출토 목관재 6점의 칠도막 편에 대하여 광학 현미경 관찰, 적외선 분광분석 및 SEM-EDS 분석을 실시하였다. 목관재에 도장된 옻칠 기법은 크게 네 가지 방법으로 분류되었다. 목재 표면에 그을음(미립자의 흑색 안료)을 혼합한 흑색 안료층이 밑층으로 존재하면서 그 위로 칠이 1회(그룹 II) 도장된 것과 3회(그룹 I) 도장된 것, 흑색 안료층이 존재하지 않으면서 칠 도장이 1회(그룹 IV)와 2회(그룹 III) 되어있는 것으로 분류되었다. 이는 목관의 제작기법과 부재의 결구 방법을 밝히는데 좋은 정보가 될 것으로 생각된다. 적외선 분광분석을 통해 무령왕릉 칠도막은 자외선에 의한 열화 요인이 적은 것으로 나타났다. 이는 이동이 어려운 목관의 크기와 무덤이라는 매장 환경 등에 기인한 결과로 보인다. 또한 SEM-EDS 분석결과 현재까지 고대 칠분석에서 보고된 바 없는 Ca, Fe, Cu의 성분이 확인되어 의미가 있다.

• Transactions on Electrical and Electronic Materials
• /
• 제1권3호
• /
• pp.23-28
• /
• 2000

A block-oxide layer was formed on the surface of Cu-based leadframe by chamical oxidation method in order to enhance the adhesion strength between Cu-based leadframe and epoxy molding compound (EMC) Using sandwiched double cantilever beam (SDCB) specimens, the adesion strength was measured in terms of interfacial fracture toughness, G$\sub$IC//Results showed that the black-oxide layer was composed of two kinds of layers: pebble-like Cu$_2$O layer and acicular CuO layer, At the initial stage of oxidation the Cu$_2$O layer was preferentially formed and thickened up to around 200 nm whithin 1 minute of the oxidation time. Then the CuO layer started to from atop of the Cu$_2$O layer and thickened up to around 1300 nm until 20 minutes. As soon as the CuO layer formed, the thickness of Cu$_2$O layer began to reduce and finally reached to around 150 nm. The pre-cleaned and the Cu$_2$O coated leadframes showed almost no adhesion of EMC, however, as the CuO precipitates appeared and became continuous, G$\sub$IC/ increased up to around 80 J/㎡. Further oxidation raised G$\sub$IC/ up. to around 100 J/㎡.

• 연구논문집
• /
• 통권28호
• /
• pp.219-227
• /
• 1998

In order to investigate the interfacial structure between TiN and iron nitride, an AISI 4140 steel was nitrided to form a layer of thickness 15$\mum$ by DC ion nitriding, then the surface was bombarded with Ti ions and subsequently coated a TiN film of 5$\mum$ by arc ion plating method. The interfacial microstructure between TiN and iron nitride was characterized by optical microscope, SEM and XRD. So called black layer was observed in the duplex treatment. It was resulted from the decomposition of iron nitride during the bombardment. Its thickness was increased with increasing bombardment time at high bias voltage. But the thickness was greatly decreased when the iron nitride was bombarded with a nitrogen gas or at a reduced bias voltage. The adhesion strength of the top TiN coating was decreased with increasing thickness of the black layer. Furthermore, the reduced adhesion strength in this system was discussed in view of the interfacial structural relationship between TiN and iron nitride.

• 보존과학회지
• /
• 제35권5호
• /
• pp.385-391
• /
• 2019

인도네시아 보로부두르 보존처리소에서 촬영한 보로부두르 사원 흑백 사진의 재질 특성을 조사하기 위해 과학적 분석을 수행하였다. 흑백 사진에서 시료를 채취하여 현미경 조사, 성분 및 재질 분석을 진행한 결과 흑백 사진은 지지체, 바리타층, 바인더층, 표면층 등 4개의 층으로 구성되어 있는 것을 확인하였다. 지지체는 마섬유로 구성된 종이, 바리타층은 분말상태의 황산바륨(BaSO₄), 바인더층은 할로겐화은이 함유된 유제, 표면보호층은 젤라틴을 사용하여 제작된 것으로 판단하였다. 사진은 구성 재질에 따라 특성 및 보존 환경이 다르므로 시대에 따른 다양한 흑백 사진 재질 특성에 대한 연구가 필요하다.

• Applied Microscopy
• /
• 제47권3호
• /
• pp.176-186
• /
• 2017

Two-dimensional (2D) materials have been studied widely owing to their outstanding properties since monolayer graphene was isolated in 2004. Especially, among 2D materials, phosphorene, a single atomic layer of black phosphorus (BP), has been highlighted for its electrical properties. This material can serve as a substitute for graphene, which has been revealed as a "semi-metal", in next-generation semiconductors. However, few-layer BP is prone to degradation under ambient conditions owing to its reactivity with oxygen and water, which results in the condensation of water droplets on the surface of the BP flakes. This causes charge transfer from the phosphorus atom to oxygen, resulting in the formation of phosphoric acid (oxide) and degrades the various properties of BP. Therefore, it is necessary to find passivation methods to prevent BP flakes from being degraded under ambient conditions. This review article deals with recent studies on passivation methods for BP and their performance against oxygen and water, effects on the electrical properties of BP, and the extent to how they protect BP.

• 센서학회지
• /
• 제15권2호
• /
• pp.90-96
• /
• 2006

We have fabricated the Pd-blck/NiCr gate MISFET-type $H_2$ sensor to detect the hydrogen in atmosphere. A differential pair-type structure was used to minimize the intrinsic voltage drift of the MISFET. The Pd-black film was deposited in the argon environment by thermal evaporation. In order to eliminate the blister formation in the surface of the hydrogen sensing gate metal, Pd-black/NiCr double metal layer was deposited on the gate insulator. The scanning electron microscopy and the auger electron spectroscopy was used to analyze their surface morphology and basic structure. The Pd-black/NiCr gate MISFET has been shown high sensitivity and stability more than Pd-planar/NiCr gate MISFET.