• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.455-458
• /
• 2001

The thin films of high pemitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)$TiO_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/$SiO_2/Si$ substrate at 4,000 [rpm] for 10 seconds. The devices of BST thin films to composite $(Ba_{0.7},Sr_{0.3})TiO_3$ were fabricated by changing of the depositing layer number on $Pt/Ti/SiO_2/Si$ substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was $2500[\AA]$, $3500[\AA]$, $3800[\AA]$. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency l[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07a
• /
• pp.151-154
• /
• 2003

AlN/Al/SiO$_2$/Si thin films for application to FBAR(Film Bulk Acoustic Resonator) devices were prepared by FTS(Facing Targets sputtering system) apparatus which provides a stable discharge at low gas pressures and can deposit high quality thin films because of the substrate located apart from the plasma. The AlN thin films were deposited on a $SiO_2(1{\mu}m)/Si(100)$ substrate using an Al bottom electrode. The process parameters were fixed such as sputering power of 200W, working pressures of 1mTorr and AlN thin film thickness of 800nm, respectively and crytallographic characteristics of AlN thin films were investigated as a function of $N_2$ gas flow rate$[N_2/(N_2+Ar)]$. Thickness of AlN thin films were measured by $\alpha$-step, the crystallographic characteristics and c-axis preferred orientation were evaluated by XRD.

• Journal of Welding and Joining
• /
• v.19 no.3
• /
• pp.305-310
• /
• 2001

UBM-coated Si-wafer was fluxlessly soldered with glass substrate in $N_2$ atmosphere using plasma cleaning method. The bulk Sn-37wt.%Pb solder was rolled to the sheet of $100\mu\textrm{m}$ thickness in order to bond a solder disk by fluxless 1st reflow process. The oxide layer on the solder surface was analysed by AES(Auger Electron Spectroscopy). Through rolling, the oxide layer on the solder surface became thin, and it was possible to bond a solder disk on the Si-wafer with fluxless process in $N_2$ gas. The Si-wafer with a solder disk was plasma-cleaned in order to remove oxide layer formed during 1st reflow and soldered to glass by 2nd reflow process without flux in $N_2$ atmosphere. The thickness of oxide layer decreased with increasing plasma power and cleaning time. The optimum plasma cleaning condition for soldering was 500W 12min. The joint was sound and the thicknesses of intermetallic compounds were less than $1\mu\textrm{m}$.

• Journal of the Korean institute of surface engineering
• /
• v.27 no.3
• /
• pp.158-165
• /
• 1994

Cu-Cr alloy thin film requires good quality of etching be used for TAB technology. The etched cross sec-tion was clean enough when the etching was performed in 0.1M $FeCl_3$ solution at $50^{\circ}C$. The etching rate was increased with the amount of $KMnO_4$. For enhanced profile of cross section and rate, the spray etchning was found to be superior compared to the immersion etching. A series of experiments were performed to improve the uniformity of the current distribution in electrodeposition onto the substrate with lithographic patterns. Copper was electrodeposited from quiescent-solution, paddle-agitated-solution, and air-bubbled-solution to in-vestigate the effect of the fluid flow. The thickness profile of the specimen measured by profilmetry has the non uniformity at feature scale in quiescent-solution, because of the longitudinal vortex roll caused by the natural convection. However, uniform thickness profile was achieved in paddle-agitated or air bubbled solu-tion.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.8
• /
• pp.319-324
• /
• 2003

AIN thin films are deposited on Si (100) and $SiO_2$/Si substrates by using an RF magnetron sputtering method and by changing the conditions of deposition variables, such as RF power, $N_2$/Ar flow ratio, and substrate temperature ($T_sub$). For all the deposited AIN films, XRD Peak patterns are monitored to examine the effect of deposition condition on the crystal orientation. Highly (002)-oriented AIN films are obtained at following nominal deposition conditions; RF Power : 350W, $N_2$/Ar ratio = 10/20, T$_{sub}$ : $250^{\circ}C$, and working pressure = 5mTorr, respectively. AIN-based SAW devices are fabricated using a lift-off method by varying the thickness of AIN layer. Insertion losses and side-lobe rejection levels of fabricated SAW devices are extracted from their frequency response characteristics, which are also compared in terms of AIN thickness and substrate. Relationships between the film properties of AIN films and the frequency responses of SAW devices are discussed. It is concluded from the experimental results that the (002)-preferred orientation as well as the surface roughness of AIN film may play a crucial role of determining the device performances of AIN-SAW devices.s.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.103-106
• /
• 2002

We prepared $Co_{77}Cr_{20}Ta_{3}$ thin film with Facing Targets Sputtering Apparatus. which can deposit a high quality thin film CoCrTa magnetic layer for Perpendicular magnetic recording media. In order to obtain Good Crystal orientation of CoCrTa thin films. We prepared Thin Films on slide glass substrate. The thickness of Buffer-layer were varied from 10 to 50 nm and Magnetic layer thickness fixed 100[nm]. input current was varied from 0.2[A] to 0.5[A]. Substrate temperature was varied from room temperature to ${250^{\circ}C}$ respectively. The crystal orientation of the CoCrTa film were examined with XRD. Introduce Buffer-layer thin films showed improvement of dispersion angle of c-axis orientation (${\Delta\theta}_{50}$).

• ETRI Journal
• /
• v.33 no.3
• /
• pp.335-343
• /
• 2011

The pad pitch of modern radio frequency integrated circuits is in the order of few tens of micrometers. Connecting a large number of high-speed I/Os to the outside world with good signal fidelity at low cost is an extremely challenging task. To cope with this requirement, we need reflection-free transmission lines from an on-chip pad to on-board SMA connectors. Such a transmission line is very hard to design due to the difference in on-chip and on-board feature size and the requirement for extremely large bandwidth. In this paper, we propose the use of narrow tracks close to chip and wide tracks away from the chip. This narrow-to-wide transition in width results in impedance discontinuity. A step change in substrate thickness is utilized to cancel the effect of the width discontinuity, thus achieving a reflection-free microstrip. To verify the concept, several microstrips were designed on multilayer FR4 PCB without any additional manufacturing steps. The TDR measurements reveal that the impedance variation is less than 3 ${\Omega}$ for a 50 ${\Omega}$ microstrip and S11 better than -9 dB for the frequency range 1 GHz to 6 GHz when the width changes from 165 ${\mu}m$ to 940 ${\mu}m$, and substrate thickness changes from 100 ${\mu}m$ to 500 ${\mu}m$.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.6 s.261
• /
• pp.665-670
• /
• 2007

Alpha-phase alumina TGO(Thermally Grown Oxide) forms on the interface between zirconia top coat and bond coat of thermal barrier coating system for superalloys during exposure to high temperature over $1000^{\circ}C$. It is known to provide a good protection against hot corrosion and to cause surface failure such as rumpling and cracking due to difference in thermal expansion coefficient from the substrate metal and the lateral growth. Consequently, mechanical properties of the alumina TGO at the high temperature are the key parameters determining the integrity of TBC system. In this work, by using Fecralloy foils as the alumina forming substrate, creep tests and tensile tests have been performed with various TGO thicknesses$(h=0{\sim}4{\mu}m)$ and yttrium contents(0, 200ppm) at $1200^{\circ}C$. Displacement-time curves and load-displacement curves for each TGO thickness(h=1,2,..) were measured from the creep and tensile tests, respectively, and compared with the curves without TGO thickness(h=0). As the result, the intrinsic tensile and creep properties of TGO itself were determined.

• Journal of Magnetics
• /
• v.6 no.3
• /
• pp.90-93
• /
• 2001

Co/$Al_O_3$/NiFe and CO/$Al_O_3$/Co tunnel junctions were fabricated by a radio frequency magnetron sputtering at room temperature with hard mask on glass and $4^{\circ}$ tilt cut Si (111) substrates. The barrier layer was formed through two steps. After the Al layer was deposited, it was oxidized in the chamber of a reactive ion etching system (RIE) with $O_2$plasma at various conditions. The dependence of the TMR value and junction resistance on the thickness of Al layer (before oxidation) and oxidation parameters were investigated. Magnetoresistance value of 7% at room temperature was obtained by optimizing the Al layer thickness and oxidation conditions. Circular shape junctions on $4^{\circ}$tilt cut Si (111) substrate showed 4% magnetoresistance. Photovoltaic energy conversion effect was observed with the cross-strip geometry junctions on Si substrate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.455-458
• /
• 2001

The thin films of high permitivity in ferroelectric materials using a capacitor are applied to DRAMs and FRAMs. (Ba, Sr)TiO$_3$ thin films as ferroelectric materials were prepared by the sol-gel method and made by spin-coating on the Pt/Ti/SiO$_2$/Si substrate at 4,700 [rpm] for 10 seconds. The devices of BST thin films to composite (Ba$\_$0.7/Sr$\_$0.3/)TiO$_3$ were fabricated by changing of the depositing layer number on Pt/Ti/SiO$_2$/Si substrate. The thin film capacitor to be ferroelectric devices was investigated by structural and electrical properties. The thickness of BST thin films at each coating numbers 3, 4 and 5 times was 2500[${\AA}$], 3500[${\AA}$], 3800[${\AA}$]. The dielectric factor of thin film when the coating numbers were 3, 4 and 5 times was 190, 400 and 460 on frequency 1[MHz]. The dielectric loss of BST thin film was linearly increased by increasing of the specimen area.