• 자원환경지질
• /
• 제32권4호
• /
• pp.399-409
• /
• 1999

Mullitization of kaolinite and dickite was examined with special attention to the influence of polytypism and impurities on the phase transformation. The phase transformation sequence in dickite is identical with that in kaolinite except that cristobalite is crystallized at $50^{\circ}C$ higher temperature in dickite. Difference in phase transformation above $1000^{\circ}C$ in kaolin minerals is attributed to the different crystal structures of metadickite and metakaolinite on the effect of impurities. A part of quartz is transformaed into cristobalite. Spinel-type phase produced in disordered kaolins including illite occurs over a short range of temperatures. Primary mullite is transformed into orthorhombic mullite at higher temperature as well. These results sustain the idea that disintegration of methkaolin and the spinel-type phase supplies extra sillica and promotes the growth of mullite cristobalite.

• The Korean Journal of Ceramics
• /
• 제7권1호
• /
• pp.41-44
• /
• 2001

A composite of $Ca_3$(PO$_4$)$_2$ and MgAl$_2$O$_4$ spinel is biologically active and has enduring strength. Its strength depends on the spinel phase. The flaws in the spinel depend on the grain size of the calcium phosphate phase and are not altered by dissolution. The calcium phosphate, ${\alpha}$ tri-calcium phosphate, controls the tissue response. Bone bonds to the implant. A design for a bone graft as a replacement for a section of the diaphysis of a canine femur provides for tensile, compressive, torsional and bending load; and for the physiological processes of bonding and remodeling. A bone plate, used to stabilize the implant at time of surgery was removed after about one year. Over seven years of service have been achieved without internal or external fixation.

• 한국세라믹학회지
• /
• 제37권6호
• /
• pp.564-568
• /
• 2000

Spinel LiMn2O4 catalyst with submicron and single phase particles was synthesized at 48$0^{\circ}C$ for 12 hr in air by a sol-gel method. The spinel LiMn2O4 was deoxidized by hydrogen at various temperatures. Effects of physiochemical properties of the catalyst reduced by hydrogen were examined with X-ray diffractometer, thermogravimetric analysis and scanning electron microscope. The decomposition rate of carbon dioxide was measrued using the catalyst deosidized at 35$0^{\circ}C$.

• 한국자기학회지
• /
• 제5권2호
• /
• pp.123-127
• /
• 1995

Copper ferrite $CuFe_{2}O_{4}$를 화학적인 방법을 사용한 미세입자 상태에서 시료를 제조한 후 이에 대한 결정학적 및 자기적 성질을 X-선 회절, $M\"{o}ssbauer$ 분광법 등을 사용하여 연구하였다. 결정구조는 서냉하여 제조한 결과 tetragonal phase spinel 구조로서 결정 상수는 $a=8.26{\pm}0.05{\AA},\;c=8.75{{\pm}}0.05{\AA}$로 측정되 었다. 실내 온도에서 부터 Curie 온도 이상까지 여러 온도범위에서 $M\"{o}ssbauer$ spectrum 을 측정, 분석한 결과 $Cu_{2+}$는 저온에서 spinel 구조의 8면체 자리에 위치하여 Jahn-Teller 효과를 나타내고, 이에 따라 630K 근방에서 결정구조상의 변화가 일어나고 있음을 알았다. Curie 온도는 690K로 세라믹 방법으로 제조한 시료에 비해 낮은 것으로 나타났다.

• 한국결정성장학회지
• /
• 제9권3호
• /
• pp.320-326
• /
• 1999

금속 Al과 산화물{{{{{Al}_{2}{O}_{3}}}}}를 사용하여 Al의 직접질화법에 의한 ALON 합성실험을 행하여 Al의 첨가량의 변화에 따른 질화반응 거동과 ALON 반응소결체의 특성을 조사하였다. Al과{{{{{Al}_{2}{O}_{3}}}}}의 직접질화법에 의한 ALON 합성이 가능함을 확인하였다. 소결온도가 증가함에 따라 ALON의 생성량이 증가하였으며, Al 첨가량 10wt%까지는 $1750^{\circ}C$ 이상의 소결온도에서 ALON상만이 존재하였다. Al 첨가량 13wt% 이상의 조성에서는 약간의 AlN상이 ALON상과 공존하였다. 반응소결체의 밀도는 소결온도가 증가함에 따라 증가하였으나, AlN이 잔존하는 시편의 소결밀도는 $1750^{\circ}C$를 넘으면 약간 감소하였다. Al 첨가량이 증가할수록 입내파괴현상이 현저히 증가하였다.

• 한국분말재료학회지
• /
• 제9권6호
• /
• pp.449-454
• /
• 2002

$MnxZn_{1-x}Fe_2O_4$ (x=0.69~0.74) powders synthesized by the thermal decomposition of organic acid salts. The obtained powders were uniform in composition and ultra-fine particle with about 400 nm. The amount of spinel phase of these powders was about 50% in X-ray diffraction patterns. The calcination of powder was carried out at $900^{\circ}C$ for 2 hours in air. After the powders were calcined. the mean size of powder was about 500 nm and the amount of spinel phase was increased over about 65%. The maximum amount of spinel phase was about 75% in the specimen of X=0.72. The magnetic properties of calcined $Mn_{0.72}Zn_{0.28}Fe_2O_4$ powders were the best among the different among the different compositions.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.281-285
• /
• 1998

The microstructure and conduction characteristics of ZnO varistor fabricated in the range of 0.0 ~ 4.0mol% $Y_20_3$ were investigated. With increasing$Y_20_3$ content, distribution of spinel phase decreased, whereas Y-rich phase segregated to the nodal point increased, as a result, the average grain size decreased in the range of $20.0 ~ 4.8{\mu}m$. $Y_20_3$ content showing relatively good conduction characteristics was l.Omol%, then nonlinear exponent and leakage current was 55.3, 0.66mA.respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1998년도 추계학술대회 논문집
• /
• pp.275-279
• /
• 1998

The influence of $WO_3$ (0.5-4.0mol%) on the microstructural and electrical properties of ZnO varistors was investigated. The major part of a tungsten segregated to the nodal point. SEM, EDAX, and XRD analysis revealed that three phase, such as W-rich phase, Bi-rich phase, and spinel phase, coexist at the nodal point. The average grain size increased in the range of 15.5-29.9pm with increasing $WO_3$ content. This may be probably attributed to liquid phase formed by $WO_3$, $WO_3$ acted as promotion additive of grain growth. As $WO_3$ content increase, the varistor voltage greatly decreased in the range 186.82-35.87V/mm due to the increase of grain growth. The barrier height decreased in the range 1.93-0.42eV with increasing $WO_3$content.

• Journal of Magnetics
• /
• 제19권2호
• /
• pp.111-115
• /
• 2014

X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and vibrating sample magnetometry (VSM) were used to investigate the influence of Ni ions on the structural, electronic, and magnetic properties of nickel-ferrites ($Ni_xFe_{3-x}O_4$). Spinel $Ni_xFe_{3-x}O_4$ ($x{\leq}0.96$) samples were prepared as polycrystalline thin films on $Al_2O_3$ (0001) substrates, using a sol-gel method. XRD patterns of the nickel-ferrites indicate that as the Ni composition increases (x > 0.3), a structural phase transition takes place from cubic to tetragonal lattice. The XPS results imply that the Ni ions in $Ni_xFe_{3-x}O_4$ substitute for the octahedral sites of the spinel lattice, mostly with the ionic valence of +2. The minority-spin d-electrons of the $Ni^{2+}$ ions are mainly distributed below the Fermi level ($E_F$), at around 3 eV; while those of the $Fe^{2+}$ ions are distributed closer to $E_F$ (~1 eV below $E_F$). The magnetic hysteresis curves of the $Ni_xFe_{3-x}O_4$ films measured by VSM show that as x increases, the saturation magnetization ($M_s$) linearly decreases. The decreasing trend is primarily attributable to the decrease in net spin magnetic moment, by the $Ni^{2+}$ ($2{\mu}_B$) substitution for octahedral $Fe^{2+}$ ($4{\mu}_B$) site.

• 한국결정성장학회지
• /
• 제13권6호
• /
• pp.297-303
• /
• 2003

rf magnetron sputtering법을 이용하여 Mn-Ni-Co계 써미스터 박막을 증착하였다. $300^{\circ}C$ 및 $Ar/O_2$ = 10/0에서, cubic spinel 상형성이 이루어졌으며 공정가스에 산소 첨가 시, cubic spinel 상은 열처리를 통해서도 형성되지 않았다. 써미스터 박막은 Mn, Ni, Co 성분 외 다른 이종 성분은 포함되어 있지 않았다. 써미스터 박막에 대한 적외선 반사 특성을 분석으로 증착된 박막은 일정 각도로 입사되는 적외선에 대해 비교적 높은 반사율을 가짐을 관찰할 수 있었다. DI water : $HNO_3$: HCI=60 : 30 : 10 vo1%에서 써미스터 박막의 식각 속도는 약 63 nm/min였다. 박막 써미스터의 B상수는 약 3500 K였으며 TCR은 약 -3.95%/K였다 전압감도는 약 108.5 V/W였으며 NEP와 specific detectivity는 각각 $5.1\times 10^{-7}$ W/$Hz^{-1/2}$ $0.2\times 10^6$cm $Hz^{1/2}$/W였다.