• Journal of Periodontal and Implant Science
• /
• 제29권1호
• /
• pp.209-231
• /
• 1999

Even though titanium(Ti) and its alloys are the most used dental implant materials, there are some problems that Ti wears easily and interferes normal osteogenesis due to the metal ions. Ti coated with bioactive ceramics such as hydroxyapatite has also such problems as the exfoliation or resorption of the coated layer, Recent studies on implant materials have been proceeding to improve physical properties of the implant substrate and biocompatibility of the implant surfaces. The purpose of the present study was to examine the physical property and bone tissue compatibility of bioinert nitrides ion plated Ti, Button type specimens(14mm in diameter, 2.32rrun in height) for the abrasion test and cytotoxicity test and thread type implants(3.75mm in diameter, 6mm in length) for the animal experiments were made from Ti(grade 2) and 316LVM stainless steel. Ti specimens were ion plated with TiN, ZrN by the low temperature arc vapor deposition, and the depth profile of the TiN/Ti, ZrN/Ti ion plated surface was examined by Auger Electron Spectroscopy. Three kind of button type specimens .of TiN/Ti, ZrN/Ti and Ti were used for abrasion test, and HEPAlClC7 cells and CCD cells were cultivated for 4 days with the specimens for cytotoxicity test. Thread type implants of TiN/Ti, ZrN/Ti, Ti, 316LVM were implanted on the femur of 6 adult dogs weighing 10kg-13kg. Two dogs were sacrified for histological examination after 45 days and 90 days, and four dogs were sacrified for the removal torque test of the implant') after 90 days. The removal torque force was measured by Autograph (Shimadzu Co., AGS-1000D series, Japan). Abrasion resistance of TiN/Ti was the highest, and that of ZrN/Ti and Ti were followed. The bioinert nitride ion plated Ti had much better abrasion resistance, compared with Ti, In the cytotoxicity test, the number of both cells were increased in all specimens, and there were no significant difference in cytotoxic reaction among all groups (p>0.1), In histological examination, 316LVM showed the soft tissue engagement in interface between the implant and bone, but the other materials after 45 days noted immature new bone formation in the medullary portion along the implant surface, and those after 90 days showed implant support by new bone formation in both the cortical and the medullary portion, The removal torque force of Tilv/Ti showed significantly higher than that of Ti(p(O,05). The difference in removal torque force between TiN/Ti and ZrN/Ti was not significant(p>0.05), and that of 316LVM was lowest among all groups(p<0.05). These results suggest that bioinert nitrides ion plated Ti can resolve the existing problems of Ti and bioactive ceramics, and it may be clinically applicable to human.

• 자원리싸이클링
• /
• 제12권6호
• /
• pp.13-18
• /
• 2003

Fe($NO_3$)$_3$ㆍ$9H_2$O, Zn($NO_3$)$_2$ㆍ$6H_2$O, Ni($NO_3$3)$_2$ㆍ $6H_2$O, Cu($NO_3$)$_2$ㆍ $3H_2$O와 같은 질산 금속염들을 $150^{\circ}C$로 24시간 동안 열분해하여 최초 NiCuZn ferrite 분체를 얻었으며, 이 분체 시료를 $500^{\circ}C$로 가소한 후 각각 볼밀 분쇄를 행하고 $700∼1000^{\circ}C$까지 각각 1시간씩 소결을 행하여 이에 대한 자기적 특성을 조사하였다. 일반 세라믹스 공정 보다 질산금속염들의 $ 200^{\circ}C$이하의 저 융점인 것을 이용하여 이들 출발 시료를 $150^{\circ}C$의 저온에서 액상의 화학결합이 가능하게 입자간의 거리를 분자적 거리로 좁힐 수 있었으며, 이로 인해 소결반응 점을 최소한 200∼ $300^{\circ}C$ 이상 낮출 수 있었다. 또한 이들의 초투자율은 50∼490, 포화자속밀도 및 보자력은 각각 2,400G와 0.3∼1.2 Oe정도로 보통의 ferrite 소결체의 특성과 유사하게 나타났다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2002년도 제3회 최신 분말제품 응용기술 Workshop
• /
• pp.25-37
• /
• 2002

The most important industrial application of gamma radiation in characterizing green compacts is the determination of the density. Examples are given where this method is applied in manufacturing technical components in powder metallurgy. The requirements imposed by modern quality management systems and operation by the workforce in industrial production are described. The accuracy of measurement achieved with this method is demonstrated and a comparison is given with other test methods to measure the density. The advantages and limitations of gamma ray densitometry are outlined. The gamma ray densitometer measures the attenuation of gamma radiation penetrating the test parts (Fig. 1). As the capability of compacts to absorb this type of radiation depends on their density, the attenuation of gamma radiation can serve as a measure of the density. The volume of the part being tested is defined by the size of the aperture screeniing out the radiation. It is a channel with the cross section of the aperture whose length is the height of the test part. The intensity of the radiation identified by the detector is the quantity used to determine the material density. Gamma ray densitometry can equally be performed on green compacts as well as on sintered components. Neither special preparation of test parts nor skilled personnel is required to perform the measurement; neither liquids nor other harmful substances are involved. When parts are exhibiting local density variations, which is normally the case in powder compaction, sectional densities can be determined in different parts of the sample without cutting it into pieces. The test is non-destructive, i.e. the parts can still be used after the measurement and do not have to be scrapped. The measurement is controlled by a special PC based software. All results are available for further processing by in-house quality documentation and supervision of measurements. Tool setting for multi-level components can be much improved by using this test method. When a densitometer is installed on the press shop floor, it can be operated by the tool setter himself. Then he can return to the press and immediately implement the corrections. Transfer of sample parts to the lab for density testing can be eliminated and results for the correction of tool settings are more readily available. This helps to reduce the time required for tool setting and clearly improves the productivity of powder presses. The range of materials where this method can be successfully applied covers almost the entire periodic system of the elements. It reaches from the light elements such as graphite via light metals (AI, Mg, Li, Ti) and their alloys, ceramics ($AI_20_3$, SiC, Si_3N_4, $Zr0_2$, ...), magnetic materials (hard and soft ferrites, AlNiCo, Nd-Fe-B, ...), metals including iron and alloy steels, Cu, Ni and Co based alloys to refractory and heavy metals (W, Mo, ...) as well as hardmetals. The gamma radiation required for the measurement is generated by radioactive sources which are produced by nuclear technology. These nuclear materials are safely encapsulated in stainless steel capsules so that no radioactive material can escape from the protective shielding container. The gamma ray densitometer is subject to the strict regulations for the use of radioactive materials. The radiation shield is so effective that there is no elevation of the natural radiation level outside the instrument. Personal dosimetry by the operating personnel is not required. Even in case of malfunction, loss of power and incorrect operation, the escape of gamma radiation from the instrument is positively prevented.

• 대한치과보철학회지
• /
• 제37권4호
• /
• pp.516-530
• /
• 1999

The current clinical technique for occlusal vertical dimension recording is based on marking the skin reference points on the patient's face and measuring between these points using caliper-like device. And it is difficult to achieve reliable measurements by this technique because of movable soft tissue. The purpose of this study is to reveal the stability of skin reference points by comparing the relative movement between extra-oral skin reference points and intra-oral reference points using X-ray fluoroscope. 10 test subjects were divided into 2 groups : Group I (natural dentition) and Group II (denture-wearer whose vertical dimension was lost) and Group III consists of identical test subjects to Group II with their upper denture removed and record base inserted. Attaching the 3 mm diameter steel ball to nose tip, lower lip, chin and to existing denture (or record base), fluoroscopic examination and recording were taken during 2 jaw opening and closing movements. After subsequent digitization using personal computer, 1219 still pictures with 0.1 second interval were made. Using the 2 dimensional graphic software, measurements between reference points were executed. Dividing the entire jaw movement into 3 ranges (total, 1st half opening, 2nd half opening), rate of movement and relative movement between extra-oral and intra-oral reference points were calculated and statistically analyzed. The results of this study are as follows. 1 Within the same experimental group, no statistical difference was found in the stability of skin reference between lower lip point and chin point during total range of jaw opening and closing movement (p>.05) 2. In the first half range of jaw opening, statistical difference was found between Group I (natural dentition) and Group II (denture wearer) (p<.05) Group I has greater skin reference stability than Group II. 3. In the first half range of jaw opening, statistical difference was found between Group I and Group III (record base wearer) (p<.05). Group I has greater skin reference stability than Group III. 4. In the first half range of jaw opening, no statistical difference was found in the stability of skin reference between Group II and Group III (p>.05). 5. In the second half range of jaw opening, no statistical difference was found in the stability of skin reference between any experimental groups (p>.05). 6. In patients with their occlusal vertical dimension lost, employing other measuring references rather than skin is recommended because of low stability.

• KEPCO Journal on Electric Power and Energy
• /
• 제1권1호
• /
• pp.175-180
• /
• 2015

본 연구에서는 간단한 화학적 합성 방법을 통하여 스테인레스 기판 위에 nano-bud 형태의 수산화 구리 박막을 형성하였다. 그리고 또 다른 합성 방법인 chemical bath deposition을 이용하여 수산화 구리 나노 구조를 간단하고 친환경적으로 형성하였다. 수산화 구리 박막의 구조적 연구는 X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM) 방법을 통하여 이루어졌으며 다결정의 nano-bud 형상을 확인할 수 있었다. 또한 나노 구조로 합성된 수산화구리 전극의 전기화학적 측정은 1M KOH의 전해질 조건에서 cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD)에서 측정되었으며 $340Fg^{-1}$의 높은 비 용량을 보였다. 또한 $1mA\;cm^{-2}$ 의 전력 밀도에서 ${\sim}83Wh\;kg^{-1}$의 높은 에너지 밀도와 ${\sim}3.1kW\;kg^{-1}$의 높은 출력 밀도를 가지며 향상된 전극의 성능을 보였다. 이러한 뛰어난 의사 캐패시터의 성능은 수산화 구리의 nano-bud 형상에 의한 효과로 확인할 수 있었다. 본 연구를 통하여 화학적 합성 방법의 확장을 통하여 수산화 구리 전극의 에너지 저장 장치로써의 성능을 확인할 수 있었다.

• 한국지반신소재학회논문집
• /
• 제20권3호
• /
• pp.1-10
• /
• 2021

본 연구는 성토구조체 현장실험을 통해 포항 지역의 제3기 이암을 도로 노체 재료로 활용하기 위한 가능성을 검토하는 제시하는 것이다. 이 이암은 신생대 제 3기층인 연암퇴적층에 분포하고 있는 미고결화 암석으로 슬레이킹, 팽윤 현상, 전단강도 저하와 같은 물리적 문제와 산성배수라는 화학적 문제가 발생한다. 여러 복합적 문제 해결하기 위해 실내 배합 시험을 진행하였으며 제 3기 이암(90%)과 복합슬래그(제강 70%, 고로 30%)와 중화·코팅제 처리의 최적 배합 조건을 도출했으며, 이를 실증하기 위해 실제 규모의 도로 성토구조체를 시공하여 구간별 현장 시험을 진행했다. 사전처리구간은 최적 배합 조건 설계로 인해 안정이 유지되는 반면, 무처리구간은 자연 풍화가 빠르게 진행되어 구조적 문제 발생이 우려되었으며, 가적치구간은 중화·코팅제 효과가 확인됨에 따라 임시 적치 시기에 적용 가능함을 확인했다.

• 한국전산구조공학회논문집
• /
• 제33권6호
• /
• pp.419-426
• /
• 2020

본 연구에서는 철골편심가새골조 시스템을 대상으로 다목적최적화기법을 통해 설계를 수행하고 그 결과를 분석하였다. 최적화 설계를 위해 유전 알고리즘의 일종인 NSGA-II를 활용하였다. 여기서, 목적함수는 이율배반적 관계를 갖는 구조물량과 층간변위로 하여 최소화되고, 제약조건에는 구조기준에서 요구하는 내력비, 링크의 회전각 등을 포함하였다. 제약조건은 최적화 알고리즘 내에서 각 항목을 위반할수록 목적함수 값을 크게 증가시키는 벌금함수의 형태를 가지고 있다. 설계기준에서 EBF 시스템의 설계규정은 링크 부재만 항복이 허용되며 나머지 부재는 링크 항복 시 발생되는 부재력을 탄성상태에서 견디도록 의도한 역량설계법에 기초한다. 그러나 최적화를 통해 도출된 결과 중 일부는 구조기준의 설계조항은 만족하지만 특정층 링크에 소성변형이 집중되어 연약층을 형성함으로써 기준에서 의도하는 역량설계의 원칙을 위배하는 결과가 나타났다. 이를 해결하기 위해 모든 링크의 전단 초과강도계수 중 최대값이 최소값의 1.25배를 넘지 않도록 하는 제약식을 추가하였다. 새로운 제약식을 추가한 경우 모든 최적해는 설계기준과 역량설계의 원칙을 준수하는 것으로 나타났다. 모든 설계안에서 보 경간에 대한 링크의 길이비는 전단링크의 범주에 해당하는 10% ~ 14%였다. 전체적으로 설계안들은 링크의 초과강도 계수비가 가장 지배적인 제약으로 작용하였으며, 구조기준의 요구사항 중 층간변위와 내력비 등의 항목에서 허용치에 비해 매우 보수적으로 설계되었다.

• 생물환경조절학회지
• /
• 제22권3호
• /
• pp.284-290
• /
• 2013

본 연구는 시설재배에서 참외를 수확할 수 있는 로봇의 엔드이펙터를 개발하기 위한 전단계로서, 참외의 엔드이펙트 중에서 소프트 핸드링이 가능한 그립퍼와 참외줄기를 절단하는 커터를 설계하기 위해 참외의 기하학, 압축, 절단, 마찰 특성 등을 분석하였다. 그 결과 참외의 길이는 평균 108mm, 직경은 중간지점에서 평균 70mm, 중량은 평균 188g, 부피는 평균 333mL, 진원도는 평균 3.8mm로 나타났다. 참외의 중량(W)에 대하여 길이(L)와 직경(D2)을 변수로 하는 식 $W=L^a{\times}D_2^b$로부터 비선형 회귀분석을 실시한 결과 a는 2.0279, b는 -0.9998의 상수값을 가지는 상관관계가 있는 것으로 나타났다. 참외줄기의 지름은 평균 3.8mm이며, 참외 줄기는 중심으로부터 반경 5mm 범위 내에서 대부분 분포하였다. 참외의 항복치와 압축강도, 경도의 평균값은 각각 $36.5N/cm^2$, $185.7N/cm^2$, $636.7N/cm^2$이며, 참외 줄기의 절단력과 절단강도는 각각 $2.87{\times}10^{-2}N$와 $5.60N/cm^2$로 나타났다. 참외의 마찰계수는 고무가 0.609으로 가장 높게 나타났고, 그 다음으로 알루미늄이 0.393, 스테인레스강이 0.177, 테프론이 0.079로 나타났다. 분석된 자료를 토대로 엔드이펙터 설계시 동작에 따른 위치 오차와 안전율을 감안하여, 그립퍼의 및 커터의 크기, 선회반경, 설치위치, 구동모터의 동력, 재료 및 재질의 선정 등에 적용할 수 있을 것으로 판단되었다.

• 한국진공학회지
• /
• 제20권6호
• /
• pp.395-402
• /
• 2011

원자힘 현미경을 이용하여 실리콘 기판 위에 증착된 실리콘 나노선과 리튬화된 실리콘 나노선의 나노기계적 성질을 연구했다. 금 촉매를 사용하여 스테인리스 기판 위에서 증기-액체-고체 과정을 통해 실리콘 나노선을 합성하였다. 완전히 리튬화된 실리콘 나노선을 얻기 위해서 전기 화학적 방법을 사용했고, 이를 실리콘 기판 위에 증착하였다. 접촉모드 원자힘 현미경으로 측정된 표면 거칠기는 실리콘 나노선에서 $0.65{\pm}0.05$ nm에 비해 리튬화된 실리콘 나노선에서 $1.72{\pm}0.16$ nm으로 더 큰 값을 보여주었다. 탐침과 표면 사이의 접착력에서 리튬화의 영향을 조사하기 위해 힘 분광기법을 사용했다. 실리콘 나노선의 접착력이 실리콘 기판과 ~60 nN으로 흡사한 반면에, 리튬화된 실리콘 나노선은 ~15 nN으로 더 작은 값을 나타냈다. 또한, 탄성적으로 부드러운 무정형 구조 때문에 국부적 탄성 스프링 상수도 실리콘 나노선 66.30 N/m보다 완전히 리튬화된 실리콘 나노선이 16.98 N/m으로 상대적으로 작았다. 실리콘 나노선과 완전히 리튬화된 실리콘 나노선에서 탐침과 표면 사이에 마찰력의 수직항력 의존성과 스캔 속도 의존성을 조사하기 위하여 각 0.5~4.0 Hz와 0.01~200 nN으로 측정했다. 본 연구에서 실리콘과 리튬화된 실리콘의 기계적 성질에 관련된 접착력과 마찰력의 경향성이 보여졌고 이러한 방향의 연구는 충-방전 동안 리튬화된 나노수준의 영역의 화학적 맵핑에 응용성을 보여준다.