• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.577-584
• /
• 1991

Among various forming techniques for ceramics, we have studied the slip casting method for the binary system of SiC and carbon. The stability of the slip of silicon carbide and carbon were investigated by measurements of zeta potential, viscosity, sedimentation height, and also studied as functions of PH and amounts of dispersants. A preform of SiC and C was prepared by slip casting and heat treatment at 400∼600$^{\circ}C$ under N2 gas. The preform was reacted with Si metal at 1550$^{\circ}C$, 10-1 mmHg to give rise a reaction bonded SiC with a density of 3.0g/㎤ and a bending strength of 580 MPa.

• Journal of the Korean Ceramic Society
• /
• v.34 no.5
• /
• pp.528-534
• /
• 1997

There have been many studies on the preparation of slip, forming and drying in the slip casting process. However, is has not been yet on the rheological properties of consolidated body which largely affect on the workability. It was investugated that the rheological properties of the consolidated bodies formed by slip casting in the form of cakes from well dispersed(slip C) and weakly agglomerated slip(slip B) in the clay and clay-fly ash systems. The state of dispersion of slip was found to affected the critical moisture content which was largely affected by the pore and moisture distribution of the consolidated body. The cake C show lower critical moisture content than cake B in the clay system. However, the cake B gives lower critical moisture content than cake C in the clay-fly ash system.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2002.10a
• /
• pp.126.2-126
• /
• 2002

• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.209-216
• /
• 1995

In order to investigate the effect o green microstructure on the sintering behavior and properties of AlN ceramics, samples were prepared by slip casting and dry pressing. The slip cast samples had high green density, fine pore size and narrow pore size distribution. They showed much higher sinterability and more homogeneous sintered microstructure compared to the dry pressed samples. Both increased thermal conductivity and flexural strength for samples prepared by slip casting could be attributed to the improved microstructural homogeneity with isolated second phase(s).

• Applied Chemistry for Engineering
• /
• v.20 no.3
• /
• pp.317-321
• /
• 2009

In order to analyze the high temperature phase formation and the sinterability of super ionic conductor $K^+-{\beta}/{\beta}"-Al_2O_3$ which is commonly used as a solid oxide electrolyte, the pure $K^+-{\beta}/{\beta}"-Al_2O_3$ powder in the ternary system $K_2O-LiO_2-Al_2O_3$ was synthesized by solid state reaction and formed to tube and disk using slip casting method and cold isostatic pressing (CIP), respectively. The slip casting was conducted in an alumina mold with the slurry containing 40 wt% of solid contents and the CIP was carried out under 20 MPa. The samples were sintered at $1600^{\circ}C$, $1700^{\circ}C$ and $1750^{\circ}C$, respectively, and their phase formation and the sintering density were investigated according to the forming method. The samples produced by CIP showed far higher ${\beta}"-Al_2O_3$ fraction as compared with those by slip casting. On the other hand, the samples by slip casting showed slightly higher sintering density. The relative density reached to about 83% at $1750^{\circ}C$ and for 1 h, independent of the forming method. In the case of 90 min socking time, the density was decreased owing to the exaggerated grain growth and the pores by $K_2O$ evaporation.

• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.519-526
• /
• 2006

A full-factorial design of experiments with three input factors and two levels for each factor including center points was utilized for the preparation and characterization of twelve types of $BaTiO_3$ slips for tape casting. Ceramic powders with different particle sizes, different milling methods such as high energy milling and conventional ball milling, and two types of dispersant with different polymeric species were chosen as input factors in order to investigate their effects on slip and on green tape properties. Tape casting, a small rectangular-shaped K-square preparation, characterization and quantitative data analysis using statistical software were followed. Ceramic powder was the most significant among three input factors for the output responses of slip viscosity and green tape density, showing more favorable results with large particles than with very fine ones. In addition, high energy milling for only 30 min was more efficient than 24h of conventional ball milling in terms of powder dispersion and milling. The optimum condition based on the experimental results was a slip exposed to high energy milling with large ceramic particles along with a methylethyl acetate dispersant.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.70-78
• /
• 1997

3Y-TZP/SUS316 Functionally Graded Material (FGM) was fabricated by slip casting method. Alumina mold was used to overcome problems of gypsum mold in slip casting process, and the optimal dispersion con-ditions of 3Y-TZP/SUS316 binary slurries was determined using electrokinetic sonic amplitude and a viscometer, and observing sedimentation behavior. The properties of the specimens casted by gypsum mold and alumina mold were compared in terms of changes in shrinkage rate, drying and sintering conditions, and microstructure. It was found that the specimens obtaine from the alumina mold showed a clean surface, easier thickness control of each layer, and higher productivity. Especially, no degradation was observed in the SUS316 prepared using alumina mold. Thus it is desirable to use porous alumina mold rather than gyp-sum mold for the slip casting of 3Y-TZP/SUS316-FGM.

• Journal of Technologic Dentistry
• /
• v.34 no.2
• /
• pp.75-81
• /
• 2012

Purpose: All ceramic crown, made from zirconia instead of metal for core material, is recognized the best esthetical prosthesis. Recently, high-priced zirconia blocks and expensive CAD/CAM machines come into use for making zirconia core. In this study, slip casting process is adapted to evaluate the possibility of the recycling the remained parts of zirconia block after machining. Methods: Remained zirconia blocks were reduced to powders with zirconia mortar, and screened with 180 mesh sieve. Passed powders were ball milled under various conditions to obtain the optimum zirconia slip for casting. Solid casting method was used for casting the specimens with plaster mold. Formed specimens were dried and biscuit fired at $1,000^{\circ}C$ for 1 hour. Biscuit fired specimens were finished with exact shape of square pillar. Finished specimens were fired from $1,200^{\circ}C$ to $1,550^{\circ}C$ at $50^{\circ}C$ intervals for 1 hour. Linear shrinkage, apparent porosity, water absorption, bulk density, and flexural strength were tested. Microstructures were observed by SEM. Results: Above examinations indicated that the optimum firing temperture was $1,500^{\circ}C$, and when fired at this temperature for 1 hour, apparent porosity was 0% and flexural strength was 680MPa. SEM photomicrographs showed uniform 200~300nm grain size, which is equal with microcture of sintered commercial zirconia block. when compare 24% linear shrinkage of cast specimen with 20% linear shrinkage of CAD/CAM machined block, it was estimated that the size controlling of cast core was not so difficult. Conclusion: According to the all of this experimental results, the cast zirconia core produced from the remained parts of zirconia block was possible to use for all ceramic denture.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1099-1100
• /
• 2006

The mechanical properties of ceramics materials can be tailored by designing their microstructures. We have reported that development of texture can be controlled by slip casting in a strong magnetic field followed by heating even for diamagnetic ceramics such as alumina. A strong magnetic field of 12T was applied to the suspension indcuding alumina powder to rotate each particle during slip casting. The sintering was conducted at the desired temperature in air without a magnetic field. C-axis of alumina was parallel to the magnetic field. Bending strength of textured alumina depended on the direction of oriented microstructure.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.327-328
• /
• 2006

We have demonstrated that textured $Al_2O_3-mullite-SiC$ nanocomposites can be fabricated by slip casting followed by partial oxidation - reaction sintering of mixed suspensions of $Al_2O_3$ and SiC powders in a high magnetic field. The sintered density was changed by the degree of oxidation at 1200C and 1300C. The degree of orientation of alumina in the nanocomposite was examined on the basis of the X-ray diffraction patterns and scanning electron micrographs. It is confirmed that alumina-oriented nanocomposites were fabricated. The three-point bending strength at room temperature was observed for the nanocomposites.