• Geomechanics and Engineering
• /
• 제31권2호
• /
• pp.149-158
• /
• 2022

Ladle furnace (LF) slag, waste from the steel-making process, was incorporated to improve the compressive strength of soil cement. LF slag was mixed to replace the cement in the soil-cement samples with wt% ratio 20:0, 15:5, and 10:10 of cement and slag, respectively. LF slag in the range of 5, 10, and 20 wt% was also separately added to the 20-wt% cement-treated soil samples. The soil-cement mixed LF slag samples were incubated in a plastic wrapping for 7, 14, and 28 days. The strength of soil cement was highly developed to be higher than the standard acceptable value (0.6 MPa) after incorporating slag into soil cement. The mixing of LF slag resulted in more hydration products for bonding soil particles, and hence improved the strength of soil cement. With the LF slag mixing either a replacement or additive materials in soil cement, the LF slag to cement ratio is considered to be less than 1, while the cement content should be more than 10 wt%. This is to promote a predominant effect of cement hydration by preventing the partially absorbed water on slag particles and keeping sufficient water content for the cement hydration in soil cement.

• 한국세라믹학회지
• /
• 제40권3호
• /
• pp.273-278
• /
• 2003

다공질 세라믹스 흡음재료의 흡음특성과 물리.기계적 특성에 미치는 하수슬러지 슬래그 첨가량과 입경 효과에 대하여 조사하였다. 시편의 물리.기계적 특성은 슬래그 입경과 관계 없이 소성온도가 증가하고 슬래그 함량이 감소함에 따라 증가하였으며, 슬래그의 함량이 일정한 시편은 물유리 첨가량이 증가하고 슬래그 입경이 감소함에 따라 증가하였다. 1~3mm 크기의 슬래그를 약 77~89 wt% 함유하고 1,05$0^{\circ}C$에서 2시간 소성한 시편의 부피비중은 1.48~1.71, 압축강도 85~163 kgf/$\textrm{cm}^2$을 나타내었으며, 1~3mm의 슬래그를 이용한 시편은 저주파영역, 슬래그 입경이 1 mm이하인 시편은 고주파영역의 흡음특성이 향상되었으며, 시편의 두께가 증가함에 따라 저주파영역의 흡음특성이 향상되었다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.671-674
• /
• 1999

With increasing content of granulated blase furnace slag in cement, the content of capillary pores in the mortar decreases and later age strength of the concrete. Therefore, this provides greater reserves study is carried out to estimate frost resistance of high-strength concrete specimens with water cement ratios using blast-furnace slag. 1. Blast furnace concrete is comparatively more good frost resistance than normal concrete. 2. As the blast furnace slag increases, the quantity of pores with a radius of more than 30nanometer decreses.

• 한국농공학회:학술대회논문집
• /
• 한국농공학회 2003년도 학술발표논문집
• /
• pp.391-394
• /
• 2003

Effects of the polymer-binder ratio and slag content on the properties of combined wet/dry-cured polymer-modified mortars using granulated blast-furnace slag are examined. Results shows that the flexural, compressive, tensile and adhesion in tension strengths of polymer-modified mortar using the slag tend to increase with increasing slag content, and is inclined to increase with increasing polymer-binder ratio. In particular, the polymer-modified mortars with slag content of 40% provide about 20% higher tensile strength than unmodified mortars. Such high strength development is attributed to the high tensile strength of polymer and the improved bond between cement hydrates and aggregates because of the addition of polymer.

• 한국건설순환자원학회논문집
• /
• 제4권3호
• /
• pp.276-283
• /
• 2016

레드머드는 보오크사이트 원광석에서 생산되는 알루미나의 선광과정에서 발생되는 무기질 부산물이다. 인 레드머드를 활용하고자 하는 연구가 국내에서 이루어지고 있다. 강알카리성의 레드머드를 건설산업용 촉진제로서 활용하고자 하는 연구로서 알칼리활성화 슬래그-레드머드 시멘트가 국내외적으로 발표되고 있다. 본 논문은 순환골재 대체율에 따른 알칼리활성화 슬래그-레드머드 건식 흙포장재의 최적함수율, 압축강도, 흡수율, 백화발생 특성에 대하여 비교 검토하였다. 그 결과 순환골재 대체율이 증가할수록 알칼리활성화 슬래그-레드머드 흙포장재의 최적 함수비, 물흡수계수, 백화면적은 증가하고 압축강도는 감소하였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2007년도 추계 학술논문 발표대회
• /
• pp.75-78
• /
• 2007

The steel slag, a by-product which is produced by refining pig iron during the manufacture of steel, is mainly used as road materials after aging. It is necessary to age steel slag for long time in air because the reaction with water and free-CaO in steel slag could make the expansion of volume. This problem prevents steel slag from being used as aggregate for concrete. However, steel slag used in this study was controled by a air-jet method which rapidly cools substance melted at a high temperature. The rapidly-chilled method would prevent from generation of free-CaO in steel slag. Also, Molten steel slag rapidly-chilled by air in high speed becomes a fine aggregate of nearly spherical shape. This study dealt with the influence of the using rate of rapidly-chilled steel slag and polymer resin on fluidity of polymer concrete, as a results Since RCSS has spherical shape and high density, up to replacement ratio of 100%, increases concrete fluidity under same polymer content and decrease polymer content in order to secure the same fluidity

• 콘크리트학회논문집
• /
• 제25권3호
• /
• pp.305-312
• /
• 2013

이 연구는 물-결합재(W/B) 비에 따른 실리카 퓸이 알칼리 활성화 슬래그 시멘트(AASC)에 미치는 유동성과 강도 특성에 대한 연구이다. W/B비는 0.50에서 0.60까지 0.05 단위로 일정하게 변화시켰다. 실리카 퓸은 고로슬래그 중량의 0%에서 50%까지 치환시켰다. 활성화제는 수산화나트륨(NaOH)를 사용하였고, 농도는 3M로 하였다. W/B 비에 따른 강도는 1, 3, 7 그리고 28일을 측정하였다. 유동성 측정 결과는 실리카 퓸의 치환율이 증가할수록 감소하였다. 압축강도는 실리카 퓸의 치환율이 증가할수록 증가하였다. 또한 W/B 비가 증가할수록 모든 재령에서 강도는 감소하였다. 실리카 퓸은 W/B 비와 실리카 퓸의 치환율에 따라서 활성화 반응을 증대시켜 강도를 증가시키는 것을 알 수 있었다.

• 자원리싸이클링
• /
• 제17권5호
• /
• pp.11-18
• /
• 2008

본 연구에서는 고로슬래그 미분말 혼입률에 따른 라텍스개질 콘크리트의 역학적 특성과 탄산화 특성을 평가하였다. 이를 위해 라텍스 혼입률 변화(0%, 15%)와 고로슬래그 혼입률 변화(0%, 30%, 50%)를 실험변수로 하였으며, LMC와 BS-LMC의 특성분석을 위하여 압축강도, 황산, 염산에 대한 화학저항성 및 탄산가스에 의한 탄산화 촉진 시험을 실시하였다. 실험결과, 고로슬래그 혼입률이 30%일 경우 일반콘크리트와 동일한 강도발현 특성을 나타내었다. 고로슬래그 혼입율 50%의 조건은 탄산화에 의한 구조적 품질 저하가 예상되었으나 혼입률 30%이하에서는 일반콘크리트보다 우수한 탄산화 억제 효과가 있는 것으로 평가되었다. 특히 황산 및 염산용액 침지에 따른 강도저하 문제는 라텍스를 혼입함으로써 저감할 수 있었으며 탄산가스에 의한 중성화 진행도 라텍스를 혼입함으로서 개선되는 것으로 나타났다.

• 한국건축시공학회지
• /
• 제11권5호
• /
• pp.442-451
• /
• 2011

Blast furnace slag is recycled as a high value-added material, while steel slag is difficult to recycle or is recycled as a low-grade filler material due to its expansive characteristics. Its property is caused by the high content of free lime and instable steel oxides. Recently, an innovative and rapid cooling method for melting steel slag has been developed in Korea, which reduces free lime content to a minimum level and increases the stability of steel oxides. However, researches on the long-term stability are not sufficient so far. Therefore, this study, focusing on the electric arc furnace oxidizing slag in the steel slag, aims to investigate the properties of the steel slag aggregate, its long-term volume stability and the engineering strength of mortar, and using it as a fine aggregate. This study result indicated that it was possible for it to be used as concrete aggregate because the volume change of the steel slag appeared to be stable.

• Advances in concrete construction
• /
• 제7권4호
• /
• pp.231-239
• /
• 2019

The present study deals with the development of metakaolin-based geopolymer concrete (GPC) and thereafter studying the effects of adding ultra-fine slag on its mechanical and permeability characteristics. The mechanical characteristics including compressive, split tensile, flexural strengths and elastic modulus were studied. In addition, permeability characteristics including water absorption, porosity, sorptivity and chloride permeability were studied up to 90 days. The results showed the effective utilization of metakaolin for the development of elevated temperature cured geopolymer concrete having high 3-day compressive strength of 42.6 MPa. The addition of ultra-fine slag up to 15%, as partial replacement of metakaolin resulted in an increase in strength characteristics. Similar improvement in durability properties was also observed with the inclusion of ultra-fine slag up to 15%. Beyond this optimum content of 15%, further increase in ultra-fine slag content affected the mechanical as well as permeability parameters in a negative way. In addition, the relationship between various properties of GPC was also derived.