Preparation of Porous Ceramics Sound Absorbent Material Using Sewage Sludge Slag

The effects of content and particle size of sewage sludge slag on the sound absorption was investigated and the physical$.$mechanical properties of porous ceramics for sound absorbent material was studied. The physical$.$mechanical properties of specimens have depended on sintering temperature and slag content without particle size effect of slag. As water glass content increase and particle size of slag decrease at the same slag content, physical$.$mechanical properties of them have been improved. The bulk density and compressive strength of specimens with the batch composition of 77∼89 wt% of slag content and particles with 1∼3 mm, and sintered at 1,050$^{\circ}C$ for 2 h were 1.48∼1.71 and 86∼163 kgf/$\textrm{cm}^2$, respectively. The specimens with 1∼3 mm and <1 mm of particles size showed good sound absorption property at low frequency and high frequency region. With increasing thickness of specimens, sound absorption properties at low frequency region were increased.

하수슬러지 슬래그를 이용한 다공성 세라믹스 흡음재료 제조

다공질 세라믹스 흡음재료의 흡음특성과 물리.기계적 특성에 미치는 하수슬러지 슬래그 첨가량과 입경 효과에 대하여 조사하였다. 시편의 물리.기계적 특성은 슬래그 입경과 관계 없이 소성온도가 증가하고 슬래그 함량이 감소함에 따라 증가하였으며, 슬래그의 함량이 일정한 시편은 물유리 첨가량이 증가하고 슬래그 입경이 감소함에 따라 증가하였다. 1~3mm 크기의 슬래그를 약 77~89 wt% 함유하고 1,05$0^{\circ}C$에서 2시간 소성한 시편의 부피비중은 1.48~1.71, 압축강도 85~163 kgf/$\textrm{cm}^2$을 나타내었으며, 1~3mm의 슬래그를 이용한 시편은 저주파영역, 슬래그 입경이 1 mm이하인 시편은 고주파영역의 흡음특성이 향상되었으며, 시편의 두께가 증가함에 따라 저주파영역의 흡음특성이 향상되었다.