• Steel and Composite Structures
• /
• v.43 no.4
• /
• pp.465-481
• /
• 2022

This paper presents a comprehensive integrity assessment of welded structural components, including uniform high- and low-cycle fatigue assessment of welded plate joints and fatigue-induced fracture assessment of welded plate joints. This study reports a series of fatigue and fracture tests of welded plate joints under three-point bending. To unify the assessment protocol for high- and low-cycle fatigue of welded plate joints, this study develops a numerical damage assessment framework for both high- and low-cycle fatigue. The calibrated damage material parameters are validated through the smooth coupon specimens. The proposed damage-based fatigue assessment approach describes, with reasonable accuracy, the total fatigue life of welded plate joints under high- and low-cycle fatigue actions. Subsequently, the study performs a tearing assessment on the ductile crack extension of the fatigue-induced crack. The tearing assessment diagram derives from the load-deformation curve of a single-edge notched bend, SE(B) specimen and successfully predicts the load-crack extension relation for the reported welded plate joints during the stable tearing process.

• Restorative Dentistry and Endodontics
• /
• v.24 no.4
• /
• pp.604-613
• /
• 1999

This study was performed to evaluate the effect of resin and filler type on the fracture toughness of light-activated composites. Experimental composites were prepared using urethane tetramethacrylate(UTMA) and bisphenol glycidylmethacrylate(Bis-GMA) monomers and five different types of silica fillers. Fracture toughness was measured by a single edge V-notched beam(SEVNB) method, which was discussed from ASTM E399-78. Rectangular bars of $2.5{\times}5{\times}26mm$ were prepared with experimental composites and a notch about 2.25mm deep was carved at the center of the long axis of the specimen using a dental diamond disk driven by a dental micro engine. The flexural test was carried out at a crosshead speed of 0.05mm/min and fracture surfaces were observed under scanning electron microscope. The results obtained were summarized as follows: 1. The fracture toughness values of UTMA-based composites were relatively higher than those of Bis-GMA-based composites. 2. The highest fracture toughness value was observed in the UTMA-based composite containing the $1.5{\mu}m$-spherical fillers. 3 Aging in the distilled water at $37^{\circ}C$ for 10 days showed the increase of fracture toughness, which was severer in the Bis-GMA-based composites than those of UTMA-based composites. 4. The AE amplitude occurring during the fracture toughness tests was the highest at the point of macroscopic fracture.

• The Journal of Advanced Prosthodontics
• /
• v.5 no.1
• /
• pp.36-43
• /
• 2013

PURPOSE. The objective of this study was to compare the fracture toughness ($K_{Ic}$) obtained from the single edge V-notched beam (SEVNB) and the fractographic analysis (FTA) of a glass-infiltrated and a zirconia ceramic. MATERIALS AND METHODS. For each material, ten bar-shaped specimens were prepared for the SEVNB method ($3mm{\times}4mm{\times}25mm$) and the FTA method ($2mm{\times}4mm{\times}25mm$). The starter V-notch was prepared as the fracture initiating flaw for the SEVNB method. A Vickers indentation load of 49 N was used to create a controlled surface flaw on each FTA specimen. All specimens were loaded to fracture using a universal testing machine at a crosshead speed of 0.5-1 mm/min. The independent-samples t-test was used for the statistical analysis of the $K_{Ic}$ values at ${\alpha}$=0.05. RESULTS. The mean $K_{Ic}$ of zirconia ceramic obtained from SEVNB method ($5.4{\pm}1.6\;MPa{\cdot}m^{1/2}$) was comparable to that obtained from FTA method ($6.3{\pm}1.6\;MPa{\cdot}m^{1/2}$). The mean $K_{Ic}$ of glass-infiltrated ceramic obtained from SEVNB method ($4.1{\pm}0.6\;MPa{\cdot}m^{1/2}$) was significantly lower than that obtained from FTA method ($5.1{\pm}0.7\;MPa{\cdot}m^{1/2}$). CONCLUSION. The mean $K_{Ic}$ of the glass-infiltrated and zirconia ceramics obtained from the SEVNB method were lower than those obtained from FTA method even they were not significantly different for the zirconia material. The differences in the $K_{Ic}$ values could be a result of the differences in the characteristics of fracture initiating flaws of these two methods.

• The Journal of Korean Academy of Prosthodontics
• /
• v.52 no.4
• /
• pp.312-316
• /
• 2014

Purpose: The aim of this study was to compare the fracture toughness of currently available resin cements for zirconia restorations and evaluate the effect of water storage on fracture toughness of those resin cements. Materials and methods: Single-edge notched specimens ($3mm{\times}6mm{\times}25mm$) were prepared from three currently available dual cure resin cements for zirconia restorations (Panavia F 2.0, Clearfil SA luting and Zirconite). Each resin cement was divided into four groups: immersed in distilled water at $37^{\circ}C$ for 1 (Control group), 30, 90, or 180 days (n=5). Specimens were loaded in three point bending at a cross-head speed of 0.1 mm/s. The maximum load at specimen failure was recorded and the fracture toughness ($K_{IC}$) was calculated. Data were analyzed using one-way ANOVA and multiple comparison $Scheff{\acute{e}}$ test (${\alpha}$=.05). Results: In control group, the mean $K_{IC}$ was $3.41{\pm}0.64MN{\cdot}m^{-1.5}$ for Panavia F, 2.0, $3.07{\pm}0.41MN{\cdot}m^{-1.5}$ for Zirconite, $2.58{\pm}0.30MN{\cdot}m^{-1.5}$ for Clearfil SA luting respectively, but statistical analysis revealed no significant difference between them. Although a gradual decrease of $K_{IC}$ in Panavia F 2.0 and gradual increases of KIC in Clearfil SA luting and Zirconite were observed with storage time, there were no significant differences between immersion time for each cement. Conclusion: The resin cements for zirconia restorations exhibit much higher $K_{IC}$ values than conventional resin cements. The fracture toughness of resin cement for zirconia restoration would not be affected by water storage.

• The Journal of Korean Academy of Prosthodontics
• /
• v.43 no.1
• /
• pp.52-60
• /
• 2005

Purpose. The intent of this study was to evaluate the effects of curing conditions on self-curing denture base resins to find out proper condition in self-curing resin polymerization. Materials and methods, In this study, 3 commercial self-curing denture base resins are used Vertex SC, Tokuso Rebase and Jet Denture Repair Acrylic. After mixing the self curing resin, it was placed in a stainless steel mold(3$\times$6$\times$60mm). The mold containing the resin was placed under the following conditions: in air at 23$^{\circ}C$; or in water at 23$^{\circ}C$; or in water at 23$^{\circ}C$ under pressure(20psi); or in water at 37$^{\circ}C$ under pressure(20psi) or in water at 50$^{\circ}C$ under pressure(20psi) , or in water at 65$^{\circ}C$ under pressure(20psi), respectively. Also heat-curing denture base resin is polymerized according to manufactures' instructions as control. Fracture toughness was measured by a single edge notched beam(SENB) method. Notch about 3mm deep was carved at the center of the long axis of the specimen using a dental diamond disk driven by a dental micro engine. The flexural test was carried out at a crosshead speed 0.5mm/min and fracture surface were observed under measuring microscope. Results and conclusion . The results obtained were summarized as follows : 1. The fracture toughness value of self-curing denture base resins were relatively lower than that of heat-curing denture base resin. 2. In Vertex SC and Jet Denture Repair Acrylic, higher fracture toughness value was observed in the curing environment with pressure but in Tokuso Rebase, low fracture toughness value was observed but there was no statistical difference. 3. Higher fracture toughness value was observed in the curing environment with water than air but there was no statistical difference. 4. Raising the temperature in water showed the increase of fracture toughness.