• Journal of the Korean institute of surface engineering
• /
• v.42 no.1
• /
• pp.47-52
• /
• 2009

Cu-Ag powder having Core-Shell structure was prepared from by electroless plating method using agents such as $AgNO_3$, $NH_{4}OH$, Hydroquinone. Ag coated copper powders were analyzed using scanning electron microscopy(SEM) and energy dispersive X-ray spectrometer(EDX). The silver coating layer of copper powder was affected from various reaction conditions such as molar ratio of $NH_{4}OH$, $AgNO_3$, and pulp density. Free silver was generated below 0.1M or 0.3M and above of $NH_{4}OH$ mole ratio. Silver coating layer thickened as addition of $AgNO_3$. When the pulp density reached 12% with 0.2M $NH_{4}OH$, and 0.15M $AgNO_3$ at $4^{\circ}C$, silver was homogeneously distributed around the copper particles and free silver particles were not generated.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.4
• /
• pp.93-99
• /
• 2016

In this paper, we investigated the mechanical and electrical reliability of silver nanowire (AgNW) films. In particular, the durability and reliability of AgNW films were studied when the AgNW film was subjected to the bending deformation under current flow. The electrical durability of AgNW was evaluated by observing changes in heat generation and current density occurring in AgNW through voltage and current tests. The AgNW film showed a constant resistance change up to a bending radius of 2 mm and 200,000 cycles in the bending fatigue tests. The over-coating layer has an effect of improving the durability of the AgNW film. In the case of AgNW with the over-coating layer, heat was uniformly dissipated on the surface of AgNW film, whereas in the case of AgNW film without the over-coating layer, heat was generated locally. In the bending test under the current flow, the current density of the AgNW film was continuously decreased up to 52.4%. During bending, the AgNW was deformed due to mechanical deformation such as tensile, bending and sliding of the AgNW, consequently contact resistance of the AgNW was increased, leading to a electrical breakdown of AgNW by Joule heating. It was found that the application of the over-coating layer can improve the electrical and mechanical reliability of the AgNW film.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.4
• /
• pp.182-189
• /
• 2020

Indium tin oxide (ITO) used a transparent electrode of a photoelectric device has a low sheet resistance and a high transmittance. However, ITO is disadvantageous in that the process cost is expensive, and the process time is long. Silver nanowires (AgNWs) transparent electrodes are based on a low cost solution process. In addition, it has attracted attention as a next-generation transparent electrode material that replaces ITO because it has similar electrical and optical characteristic to ITO, it is noted as a. AgNW thin films are mainly produced by spin-coating. However, the spin-coating process has a disadvantage of high material loss. In this study, the material loss was reduced by using about 2~10 ㎕ of AgNW solution on a (25 × 25) ㎟ substrate using the shear-coating method. It was also possible to align AgNWs in the drag direction by dragging the meniscus of the solution. The electro-optical properties of the AgNW thin film were adjusted by changing the experimental parameters that the amount of AgNWs suspension, the gap between the substrate and the blade, and the coating speed. As a result, AgNW thin films with a transmittance of 90.7 % at a wavelength of 550 nm and a sheet resistance of 15 Ω/□ was deposited and exhibited similar properties to similar AgNW transparent electrodes studied by other researchers.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1998.04a
• /
• pp.47-54
• /
• 1998

An experimental study was performed to discover the effect of environmental conditions on the rolling resistance behavior of pure silver and lead coated 52100 bearing steel. Pure silver and lead coating were produced by a thermal evaporation coating method. Experiments using a thrust ball bearing-typed rolling test-rig were performed under vacuum, dry air and controlled humidity conditions. Results showed that agglomeration of particles were prevented in vacuum environment and as it showed low and stable rolling resistance by shakedown phenomena. Also, humidity relates closely to the agglomeration of particles and increased the rolling resistance after the failure of coated layer.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.217-220
• /
• 2009

Conductive adhesives have been investigated for use in microelectronics packaging as a lead-free solder substitute due to their advantages, such as low bonding temperature. However, high resistivity and poor mechanical behavior may be the limiting factors for the development of conductive adhesives. The metal fillers and the polymer resins provide electrical and mechanical interconnections between surface mount device components and a substrate. As metal fillers used in conductive adhesives, silver is the most commonly used due to its high conductivity and the stability. However the cost of conductive adhesives with silver fillers is much higher than usual lead-free solders and silver has poor electro-migration performance. So, copper can be a promising candidate for conductive filler metal due to its low resistivity and low cost, but oxidation causes this metal to lose its conductivity. In this study, electrically conductive adhesives (ECAs) using surface modified copper fillers were developed. Especially, in order to overcome the problem associated with the oxidation of copper, copper particles were coated with silver, and the silver-coated copper was tested as a filler metal. Especially the effect of silver coating on the electrical resistance just after curing and after aging was investigated. As a result, it was found that the electrical resistance of ECA with silver-coated copper filler was clearly lower and more stable than that of ECA with pure copper filler after curing process. And, during high temperature storage test, the degradation rate of electrical resistance for ECA with silver coated copper filler was quite slower than that for ECA with pure copper filler.

• 한국초전도학회:학술대회논문집
• /
• 2009.07a
• /
• pp.94-94
• /
• 2009

• Molecular & Cellular Toxicology
• /
• v.5 no.1
• /
• pp.23-31
• /
• 2009

To compare the effects of nanometer-sized silver ions and support materials (nano-silver coating material, NM-silver) and silver ions, we exposed zebrafish embryos to both types of nano-silver ions and compared the acute responses during embryogenesis. The amount of silver in the NM-silver (17.16%) was greater than that in the silver ion (4.56%). Both of these materials have different atomic compositions. The silver ion-exposed groups (10 and 20 ppt) showed lower survival rates than the NM-silver-exposed groups (10 and 20 ppt). NM-silver penetrated the skin and blood tube of zebrafish larvae as aggregated particles, whereas, silver ions penetrated the organelles, nucleus and yolk in a spread-out pattern. Micro-array analysis of RNA from zebrafish larvae (72 hours post-fertilization) that were treated with either NM-silver or silver ions, showed alteration in expression of the BMP, activin, TGF-$\beta$, and $GSK3{\beta}$ genes pathway. Additionally, $GSK3{\beta}$ gene pathway for apoptosis that was related with left-right asymmetry. Gene expression changes in the NM-silver or silver ions-treated zebrafish embryo led to phenotypic changes in the hatched larvae, reflecting increased apoptosis and incomplete formation of an axis.

• Tribology and Lubricants
• /
• v.18 no.1
• /
• pp.1-8
• /
• 2002

Nano adhesion and friction between a $Si_{3}N_{4}$ AFM(atomic force microscope) tip and thin silver films were experimentally studied. Tests were performed to measure the nano adhesion and friction in both AFM and LFM(lateral force microscope) modes in various range of normal loads. Thin silver films deposited by IBAD (ion beam assisted deposition) on Si-wafer (100) and other Si-wafers of different surface roughness were used. Results showed that nano adhesion and friction decreased with the surface roughness. When the Si surfaces were coated by pure silver, the adhesion and friction decreased. But the adhesion and friction were not affected by the thickness of IBAD silver coating. As the normal force increased, the adhesion forces of bare Si-wafer and IBAD silver coating film remained constant, but the friction forces increased linearly. Test results suggested that the friction was mainly governed by the adhesion as long as the load was low.

• The Journal of Korean Academy of Prosthodontics
• /
• v.29 no.3
• /
• pp.111-119
• /
• 1991

This study was performed to investigate the effect of gold electrodepositoin on porcelain color of palladium-silver alloy. The specimens were made by firing porcelain on the metal plates cast respectively in Au-Pt alloy, and Pd-Ag alloy. In the case of Pd-Ag alloy specimens, porcelain were fired under three different conditions of the metal plate: 1) without gold coating, 2) firing opaque beforehand on one side, gold coating on the other side, 3) gold coating on both sides of the metal plate. Color change was measured with fiber-optic colorimeter(Model TC-6FX, Tokyo Denshoku Co., Japan). The obtained results were as follows: 1. In the group of firing opaque beforehand on one side and gold coating on the other side, there was no significant differences in their color in comparison to the color of the control group of the Au-Pt alloys. 2. In the group of gold coating on both sides on metal plate, there were no significant differences except their value to the group of firing poaque beforehand on one side and gold coating on the other side.

• The Journal of the Institute of Internet, Broadcasting and Communication
• /
• v.18 no.4
• /
• pp.79-83
• /
• 2018

An accurate method to measure shielding effectiveness(SE) of EMI spray coating film is presented. After high frequency simulating, Circular coaxial standard test fixture is fabricated. A sample of EMI spray coating film was fabricated for insertion into a circular coaxial standard test fixture. The measuring instrument used an Agilent 8722ES vector network analyzer for the SE measurement. The exact SE of copper and silver mixed spray coating sample was measured by the composition of the measuring instrument and the measuring sample. The SE of copper sample was measured at 70 dB and the SE of copper and silver mixed spray coating sample was measured at 60 dB. As a result of the measurement, the reliability of the circular coaxial standard test fixture was confirmed.