• Journal of Powder Materials
• /
• v.17 no.3
• /
• pp.230-234
• /
• 2010

Homogenous silica-coated $CoFe_2O_4$ samples with controlled silica thickness were synthesized by the reverse microemulsion method. First, 7 nm size cobalt ferrite nanoparticles were prepared by thermal decomposition methods. Hydrophobic cobalt ferrites were coated with controlled $SiO_2$ using polyoxyethylene(5)nonylphenylether (Igepal) as a surfactant, $NH_4OH$ and tetraethyl orthosilicate (TEOS). The well controlled thickness of the silica shell was found to depend on the reaction time and the amount of surfactant used during production. Thick shell was prepared by increasing reaction time and small amount of surfactant.

• Macromolecular Research
• /
• v.17 no.5
• /
• pp.307-312
• /
• 2009

Core-shell hydrogel nanocomposite was fabricated by encapsulating a silica-gold nanoshell (SGNS) with poly(N-isopropylacrylamide-co-acrylic acid) (PNIPAM-co-AAc) copolymer. The oleylamine-functionalized SONS was used as a nanotemplate for the shell-layer growth of hydrogel copolymer. APS (ammonium persulfate) was used as a polymerization initiator to produce a hydrogel-encapsulated SGNS (H-SGNS). The amounts of NIPAM (N-isopropylacrylamide) monomers were optimized to reproduce the hydrogel-encapsulated SGNS. The shell-layer thickness was increased with the increase of polymerization time and no further increase in the shell-layer thickness was clearly observed over 16 h. H-SGNS exhibited the systematic changes of particle size corresponding to the variation of pH and temperature, which was originated from hydrogen-bonding interaction between PNIPAM amide groups and water, as well as electrostatic forces attributed by the ionization of carboxylic groups in acrylic acid.

• Polymer(Korea)
• /
• v.28 no.6
• /
• pp.487-493
• /
• 2004

The distribution of particles, in the mixture of poly(ethyl acrylate-co-t-butyl acrylate) (PEB) emulsion polymer and silica nanoparticles, was determined mainly depending on the pH of the mixture. The weak interfacial interaction was responsible for the severe coagulation of silica particles and the irregular dispersion for these nanocomposites. Methacryloxypropyltrimethoxysilane (MPS) was used to modify both the polymer and the silica. The nanocomposites which were prepared with these modified components had finer dispersion of silica nanoparticles and core-shell morphology due to the strong interfacial interaction. The strong hydrogen bonds were identified for these nanocomposites with FT-IR. The nanocomposites having strong interfacial interaction showed the increased glass transition temperature, the decreased ΔC$_{p}$ , and the increased decomposition temperature of the polymer chains. polymer chains.

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.415-421
• /
• 2000

The effect of silica binder content on the mechanical properties of zircon shell mold was investigated. Content of binder silica sol to refractory powder in weight[$R_W$] was adjusted from 0.18 to 0.43. Sintering of the shell mold was carried out in the temperature range of $871^{\circ}C$ to $1400^{\circ}C$. Green strength of the shell mold at room temperature increased with increasing $R_W$ and sintering temperature up to $1300^{\circ}C$. However, the mold with $R_W$ of 0.43 that sintered at $1400^{\circ}C$ for 3 hours showed relatively low strength and large level of porosity. The mechanical behavior of the shells is supposed to attributed to the difference in thermal expansion coefficient between refractory powder and binder silica. The optimum value of $R_W$ for zircon-based shell molds was found to be 0.33.

• Polymer(Korea)
• /
• v.33 no.5
• /
• pp.452-457
• /
• 2009

Hybrid nanomaterials consisting of multi-walled carbon nanotube(MWNT) and/or PEDOT of conductive polymer were prepared in this study. In the presence of catalyst and ligand, the MWNT-Br compound prepared by the successive surface treatment reaction was mixed with MMA to initiate the atom transfer radical polymerization process. PMMA was covalently linked to the surface of MWNT for the formation of MWNT/PMMA nanocomposites. The EDOT and oxidant were added in the aqueous emulsion of PS produced via a miniemulsion polymerization process and then it proceeded to carry out the oxidative chemical polymerization of EDOT for the preparation of PEDOT/PS nanoparticles with the core-shell structure. The aqueous dispersion of PEDOT:poly(styrene sulfonate) (PSS) was mixed with the silica particles treated with a silane compound and thus PEDOT:PSS-clad silica nanoparticles were prepared by the surface chemistry reaction. The hybrid nanomaterials were analyzed by using TEM, FE-SEM, TGA, EDX, UV, and FT-IR.

• Journal of the Korean Society of Tobacco Science
• /
• v.16 no.2
• /
• pp.181-190
• /
• 1994

Various active carbons were made from plant sources of coconut shell, pine tree, oak tree and lignite coal. Pore characteristics of these adsorbents were investigated. 1, With increasing activation time, specific surface area and pore volume increased, but the development of micropores was limited at a certain level. The average pore diameter, by BET, of coconut active carbon was 15.5-21.8$\AA$ and that of lignite carbon was 15.6-31.3$\AA$. The pore diameters of silica-gel, sepiolite and zeolite was 30.9$\AA$, 58.6$\AA$ and 55.7$\AA$, respectively. 2. The Horvath - Kawazoe micropore diameter of coconut shell active carbon was under 10.5$\AA$ and that of the other active carbon was under 20.9$\AA$ but silica-gel 33$\AA$, sepiolite 103 $\AA$ and zeolite was unexpectedly large to be 175$\AA$. From the difference between BET micropore diameter and Howath - Kawazoe diameter, it could be said that silica - gel has comparatively uniform pore diameter but sepiolite and zeolite have very uneven diameter. 3. Total pore volume of coconut shell active carbon was 0.27-1.04 cm3/g but that of the other active carbon, 0.23-0.62 cm3/g, was much lower than that of coconut shell active carbon. Hydrophilic adsorbent silica - gel and sepiolite showed big difference in specific surface area, but pore volumes of these were 0.47 and 0.56 cm3/g showing similar value and micropore volumes of these were, respectively, 0.06 cm3/g and 0.04 cm3/g. Total pore volume of zeolite was 0.1 cm3/g and that of micropore was only 0.02 cm3/g.

• Journal of Industrial Technology
• /
• v.23 no.A
• /
• pp.199-206
• /
• 2003

The charcoal-encapsulated methyl silica microcapsules were prepared by a O/W microemulsion sol-gel method, and the adsorption properties on aquatic humic acid were investigated. The capsules prepared were spherical, $100{\sim}1000{\mu}m$ in size. The size distribution was controllable by adjusting the size of charcoal powder, charcoal/methyl silica ratio, and agitating speed in O/W sol-gel process. Adsorption efficiency of charcoal for aquatic humic acid was decreased after encapsulation by methyl silica shell. The decreased adsorption efficiency can be dependent on the decrease of the BET surface area and pore volume after encapsulation. Diffusion properties of humic acid through the capsule shell also played an important role on adsorption efficiency. Therefore, the reasonable target pollutants for the capsules can be VOC or odor molecules which can overcome diffusion barrier through shell of capsules in air condition. Functionalization methods for the charcoal-encapsulated $CH_3(SiO)_n$ microcapsules by incorporation of $TiO_3$ as a phtocatalytic function and by incorporation of inorganic pigment as a color function were also investigated. $TiO_2$ coating properties were controllable by adjusting pH, temperature, and the concentration of $TiOSO_4$. In XRD measurement, the crystal form of the coated $TiO_2$ was anatase. For the colorization of the capsules, inorganic pigments were more efficient than organic dyes, and various color was introduced to the capsules using inorganic pigments.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.553-553
• /
• 2012

The artificial shells of hard inorganic nanocomposites on individual cells would protect the cells physically and chemically, and control cell division. These emerging properties could be combined with cell-surface functionalizations for applications to cell-based sensors and assays as well as for fundamental studies on single-cell biology. In this work, individual Chlorella cells were encapsulated within a silica/titania nanocomposite shell in a biocompatible fashion that utilized a designed peptide, RKKRKKRKKRKKDDDDDDDD, as a catalytic template for formation of both $SiO_2$ and $TiO_2$ on the cell surface. The cell viability was maintained, and the division of the encapsulated Chlorella cells was controlled. The cell viability was enhanced compared with the $TiO_2$-shell formation. In addition, the incorporation of $TiO_2$ to the shell made it possible to anchor the ligands of interest to the shell via catechol chemistry. All in all, the combination of biological $SiO_2$ and abiolgical $TiO_2$ for the shell formation gave more tunability of the artificial shells compared with the $SiO_2$ or $TiO_2$ shells only.

• Conservation Science in Museum
• /
• v.27
• /
• pp.91-102
• /
• 2022

Silica-based inorganic fillers for restoration of iron objects have been used for the reduction of thermal expansivity and the improvement of melt flow index. However, the higher the amount of filler is applied, the more degradation of mechanical properties and the yellowing occur, which could cause retreatment of the objects with adding stress to them. Thus, research on not only the quantification of a mixture of resin and filler but also the yellowing should be emphasized. Experiments on mechanical properties were carried out with a silica-based light filler, Micro Shell as a comparison group. The results of the experiment showed Micro Shell reduced the number of occurrences of the yellowing by 34% compared to existing fillers. The value of adhesion and specific gravity was also improved depending on the filler amount. The results of this research indicate the possibility of using Micro Shell as a new filler.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.10
• /
• pp.3707-3711
• /
• 2011

Silver nanoparticles coated with silica can be obtained by the reduction of $AgNO_3$ with hydrazine in the presence of NaOH-stabilized, active silicic acid (polysilicic acid). The size of the silver nanoparticles and the silica shell thicknesses were affected by varying the hydrazine content, the active silicic acid content and the experimental method (e.g. hydrothermal method). Typically, silver nanoparticles sized around 40 nm were aggregated, connected by silica. The presence of peaks centered around 400 nm in UV-vis spectra corresponds to the surface plasmon resonance of silver nanoparticles. The size of the aggregated silver nanoparticles increased with increasing hydrazine concentration. Under hydrothermal conditions at $150^{\circ}C$ the formation of individual silica particles was observed and the sizes of the silver nanoparticles were reduced. The hydrothermal treatment of silver nanoparticles at $180^{\circ}C$ gives a well-defined Ag@$SiO_2$ core-shell in aggregated silica sol particles. The absorption band observed at around 412 nm were red-shifted with respect to the uncoated silver nanoparticles (${\lambda}_{max}$ = 399 nm) due to the larger refractive index of silica compared to that of water. The formation of silver nanoparticles coated with silica is confirmed by UV-visible absorption spectra, transmission electron microscopy (TEM) and energy-dispersive spectroscopy (EDS) data.