• The Journal of Advanced Prosthodontics
• /
• 제13권5호
• /
• pp.292-303
• /
• 2021

PURPOSE. The aim of this in vitro study was to evaluate the effect of silane and universal adhesive applications on the micro-shear bond strength (µSBS) of different resin-matrix ceramics (RMCs). MATERIALS AND METHODS. A total of 120 slides (14 × 12 × 1 mm) were produced from 5 different RMC materials (GC Cerasmart [GC]; Brilliant Crios [BC]; Grandio blocs [GB]; Katana Avencia [KA]; and KZR-CAD HR 2 [KZR]) and sandblasted using 50 ㎛ Al₂O₃ particles. Each RMC material was divided into six groups according to the surface conditioning (SC) method as follows: control (G1), silane primer (G2), silane-free universal adhesive (G3), silane-containing universal adhesive (G4), silane primer and silane-free universal adhesive (G5), and silane primer and silane-containing universal adhesive (G6). Three cylindric specimens made from resin cement (Bifix QM) were polymerized over the treated surface of each slide (n = 12). After thermal cycling (10000 cycles, 5 - 55℃), µSBS test was performed and failure types were evaluated using a stereomicroscope. Data were analyzed using 2-way ANOVA and Tukey tests (α = .05). RESULTS. µSBS values of specimens were significantly affected by the RMC type and SC protocols (P < .001) except the interaction (P = .119). Except for G2, all SC protocols showed a significant increase in µSBS values (P < .05). For all RMCs, the highest µSBS values were obtained in G4 and G6 groups. CONCLUSION. Only silane application did not affect the µSBS values regardless of the RMC type. Moreover, the application of a separate silane in addition to the universal adhesives did not improve the µSBS values. Silane-containing universal adhesive was found to be the best conditioning method for RMCs.

• 한국재료학회지
• /
• 제9권12호
• /
• pp.1160-1169
• /
• 1999

본 연구에서 FPC에 사용되는 동박과 접착제의 이종 재료간에 계면접착력을 향상시키기 위해 silane primer를 도입하였다. 또한 동박표면 및 에폭시 접착제를 개질하여 개질조건이 접착강도에 미치는 영향도 조사하였다. 본 실험은 접착제층과의 상용성을 고려하여 silane primer로 triethoxyvinylsilane을 용액 및 무유화제 유화중합한 고분자형태와 3-aminopropyl-triethoxysilane (3-APTES), 3-glycidoxypropylmethoxysilane (3-GPTMS)을 사용하여 접착제층과의 접착력 증진을 도모하였다. 동박표면은 1,1,1-trichloroethane을 사용하여 개질 시간에 따른 동박 표면의 지형변화와 그에 따른 접착강도를 조사하였다. 결과에 따르면 silane을 사용한 경우 동박-접착제간의 접착력이 약2 ~ 5배 정도 증진되었고, 동박표면의 개질시간은 약 10분 정도가 최적의 접착조건임을 알 수 있었다. 또한 저분자량 실란의 농도에 따른 접착력은 3-APTES는 약 0.5 vol.%에서 최고 접착력을 보였고, 3-GPTMS의 경우 약 0.2 vol.%에서 최고의 접착력을 보였다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1480-1481
• /
• 2008

In this paper, we present surface treatments for achieving bonds between PMMA and PDMS substrates. Silane primer is used for the formation of hydroxyl group on PMMA surfaces. The formed hydroxyl groups enhance the bonding strength of PDMS-PMMA substrates without channel clogging and structure deformation. The bonding strength on the different surface treatments (include oxygen plasma, 3-APTES, and corona discharge) is evaluated to find optimal bonding condition. The maximum bonding strength at the optimal surface treatment is over 300 kPa. The surface treatment using silane primer can be used to the bonding process of Micro-TAS and Lab-on-a-Chip.

• Corrosion Science and Technology
• /
• 제6권4호
• /
• pp.206-210
• /
• 2007

Aerospace aluminum alloys such as Al alloy 2024-T3 and 7075-T6 are subject to localized corrosion due the existence of intermetallics containing Cu, Mg or Zn. Chromate is currently widely used in the aerospace industry as the corrosion inhibitor for these alloys. However, chromate needs to be replaced due to its strong carcinogenicity. In this study, an extensive pigment screening has been performed to find replacements for chromates. Different categories of inhibitors were evaluated by immersion tests, DC polarization tests and other methods. Phosphates, zinc salts, cerium salts, vanadates and benzotriazole were found to be effective inhibitors for AA7075. Among those inhibitors, zinc phosphate was found to be the most effective in our novel, silane-based, one-step aqueous primer system. The performance of this primer is comparable to that of currently used chromate primers in accelerated corrosion tests, while it is completely chromate-free and its VOC is about 80% less than that of current primers. Studies by SEM/EDS showed that the unique structure of the superprimer accounts for the strong anti-corrosion performance of the zinc phosphate pigment. The self-assembled stratified double-layer structure of the superprimer is characterized by a less-penetrable hydrophobic layer at the top and a hydrophilic layer accommodating the inhibitors underneath. The top layer functions as the physical barrier against water ingress, while the lower layer functions as a reservoirfor the inhibitor, which is leached out only if the coating is damaged by a scratch or scribe. The presence of a silane in the primer further improves the adhesion and anti-corrosion performance of the primer.

• 한국구조물진단유지관리공학회 논문집
• /
• 제21권4호
• /
• pp.39-46
• /
• 2017

본 연구에서는 프라이머 도포 여 부 및 압축강도수준 그리고 바닥 마감재 시공재령에 따른 주차장용 바닥 마감재 부착성능을 평가하였다. 또한 현행 KS 기준에서는 바닥 마감재 부착성능을 모르타르 공시체를 활용하여 평가하도록 제안하고 있지만, 실제 현장에서 바닥 마감재는 콘크리트 상부면에 시공되기 때문에 바탕면 변화에 따른 부착성능을 추가변수로 계획하여 평가를 진행하였다. 모르타르는 현행기준에서 제안하고 있는 배합표에 준하여 제작하였으며, 콘크리트 설계기준강도는 18, 30, 50 MPa로 계획하였다. 프라이머는 모르타르 및 콘크리트 재령 28일 변수에 따라 바닥 마감재와 함께 도포되었으며, KS 기준에 준하여 바닥 마감재 재령 일에 따라 부착성능을 평가하였다. 변수에 따른 부착성능 평가결과 바닥 마감재 재령이 경과함에 따라 바닥 마감재 부착성능은 향상되는 것으로 나타났으며, 압축강도가 높아짐에 따라 바닥 마감재 부착성능 또한 향상되는 것으로 나타났다. 이는 파괴양상을 고려하였을 때 콘크리트 쪼갬 인장강도의 영향을 받은 것으로 판단된다. 프라이머 도포에 따른 부착성능은 유사한 것으로 나타났으며, 프라이머의 사용은 부착강도에 문제없이 콘크리트 표면의 내구성을 향상시킬 수 있을 것으로 판단된다. 또한 콘크리트 및 모르타르 바탕면의 부착강도 특성을 비교한 결과 바닥재의 부착강도는 구성재료 보다 압축강도에 큰 영향을 받는 것으로 나타났다. 따라서 현행 KS 기준의 모르타르 바탕면 실험체의 부착강도를 근거로 실제현장의 부착강도를 예측할 수 있을 것으로 판단된다.

• 대한치과교정학회지
• /
• 제45권4호
• /
• pp.164-170
• /
• 2015

Objective: The aim of this study was to compare the shear bond strength (SBS) of orthodontic brackets bonded to zirconia surfaces using three different zirconia primers and one silane primer, and subjected to thermocycling. Methods: We designed 10 experimental groups following the surface treatment and thermocycling. The surface was treated with one of the following method: no-primer (NP), Porcelain Conditioner (PC), Z-PRIME Plus (ZP), Monobond Plus (MP) and Zirconia Liner Premium (ZL) (n=20). Then each group was subdivided to non-thermocycled and thermocycled groups (NPT, PC, ZPT, MPT, ZLT) (n=10). Orthodontic brackets were bonded to the specimens using $Transbond^{TM}$ XT Paste and light cured for 15 s at $1,100mW/cm^2$. The SBS was measured at a 1 mm/min crosshead speed. The failure mode was assessed by examination with a stereomicroscope and the amount of bonding resin remaining on the zirconia surface was scored using the modified adhesive remnant index (ARI). Results: The SBS of all experimental groups decreased after thermocycling. Before thermocycling, the SBS was ZL, $ZP{\geq}MP{\geq}PC>NP$ but after thermocycling, the SBS was $ZLT{\geq}MPT{\geq}ZPT>PCT=NPT$ (p > 0.05). For the ARI score, both of the groups lacking primer (NP and NPT) displayed adhesive failure modes, but the groups with zirconia primers (ZP, ZPT, MP, MPT, ZL, and ZLT) were associated with mixed failure modes. Conclusions: Surface treatment with a zirconia primer increases the SBS relative to no-primer or silane primer application between orthodontic brackets and zirconia prostheses.

• Restorative Dentistry and Endodontics
• /
• 제33권5호
• /
• pp.419-427
• /
• 2008

본 연구는 레진시멘트의 레진인레이에 대한 접착 시 접착제 혹은 primer의 사용이 결합력에 영향을 미치는지 평가하기 위해 시행하였다. 직경 5mm,높이 4.5mm의 원기둥 형태로 제작한 레진인레이 (Tescera, Bisco, USA)의 표면을 1000번, 1500번 그리고 2000번 사포로 주수 하에서 연마하여 평편한 면을 형성한 후 레진인레이의 표면에 sandblasting을 시행한 후 표면에 1분 동안 silane을 도포하였다. 2군으로 나누어 한 군은 대조군으로, 다른 한 군은 표면에 동일한 제조사의 접착제나 프라이머를 도포한 후 중합하였다. 레진인레이 상에 3mm 직경의 구멍이 형성된 아크릴판을 고정하고, 구멍에 레진 시멘트를 주입하여 경화시켰다. 레진 시멘트는 Panavia-F (Kurary), Varolink-II(Ivoclar-Vivadent), RelyX Unicem(3M ESPE), Duolink(Bisco)와 자가중합형인 Multilink (Ivoclar-Vivadent)를 사용하였다. 제작된 시편을 만능물성시험기에 위치시고 전단결합강도를 측정하였다. 측정 결과 접착제나 프라이머를 도포한 군은 대조군에 비해 전단결합강도가 증가하였다 (p<0.05). 하지만 Variolink-II와 Panavia-F는 전단결합강도의 차이를 보이지 않았다. 대조군에서는 각 레진 시멘트간에 전단결합강도의 유의한 차이를 보였으며 (p<0.01) Variolink-II가 가장 높은 결합강도를 보인 반면, 자가중합형인 Multilink가 가장 낮은 결합강도를 보였다. 하지만, 접착제나 프라이머를 도포한 군에서는 각 제품간에 전단결합강토의 차이를 보이지 않았다. 이상의 결과 이원중합형이나 자가중합형 레진시멘을 이용하여 레진인레이 부착 시 silane 처리 후 접착제나 프라이머의 도포가 결합 강도의 증가를 위해 필요하리라 사료된다.

• 대한치과보철학회지
• /
• 제53권4호
• /
• pp.295-300
• /
• 2015

목적: 레진과 니켈-크롬 합금의 결합력에 미치는 금속 프라이머 및 다용도 접착제의 영향에 대하여 비교 평가하고자 한다. 재료 및 방법: 실험을 위해 120개의 니켈-크롬 합금(Vera Bond 2V) 디스크를 제작하여 아크릴 레진 실린더에 포매하였다. 시편의 표면은 220 grit, 600 grit의 실리콘 카바이드지로 연마한 뒤 $50{\mu}m$의 알루미늄옥사이드 입자를 분사하여 처리하였다. 실험군은 메탈 프라이머의 적용(Metal primer II, Alloy primer, Metal & Zirconia primer, MKZ primer)과 다용도 접착 시스템(Single Bond Universal, All Bond Universal)에 따라 6개 군으로 나뉘었다. 각 시편의 중앙에 높이 2 mm, 직경 3 mm로 복합레진을 충전하였으며, 제작된 모든 시편은 $37^{\circ}C$ 증류수에서 24시간 보관하였다. 만능시험기에 시편을 위치시킨 후 1 mm/min cross head speed로 전단결합강도를 측정하였다. 통계분석은0.05의 유의수준으로 일원분산분석을 시행하였고 Tukey's multiple coMParison test로 사후검정을 하였다. 결과: Single Bond Universal, All Bond Universal, Metal Primer II 3개 군과 Alloy Primer, MKZ Primer, Metal & Zirconia Primer 3개 군 사이에 통계학적으로 유의한 차이를 보였다(P<.001). 결론: 니켈-크롬 합금에 대한 다용도 접착 시스템의 전단결합강도는 Metal Primer II를 제외한 기존의 금속 프라이머를 적용했을 때 보다 높게 나타났다. 본 실험에서 더 나아가 다용도 접착 시스템 내 실란(Silane) 포함 여부에 따른 효과를 평가할 수 있는 연구가 필요할 것이다.

• 대한치과보철학회지
• /
• 제52권2호
• /
• pp.113-120
• /
• 2014

연구 목적: 본 연구는 근관치료된 치아에 레진 시멘트로 fiber reinforced composite post (FRC) post의 접착시 포스트의 다양한 표면처리를 비교하여, 새롭게 제안되고 있는 다용도 프라이머의 효용성에 대해 평가하고자 하였다. 연구 재료 및 방법: 근관치료된 소구치 중 치근길이 1.8 cm 이상 되는 치아만을 총 24개 선택하였다. 표면 처리하지 않은 대조군과 표면처리를 시행한 FRC posts (DT Light Post, Size3, Bisco Inc., Schaumburg, IL, US)를 다음과 같이 6개의 그룹으로 무작위 분류하였다: Group A: airborne-particle abrasion (Cojet sand, 3M ESPE), Group S: silanization (Bis-silane, Bisco Inc.), Group M: universal primer (Monobond-plus primer, Ivoclar Vivadent Inc.), Group AS: silanization after airborne-particle abrasion, Group AM: universal primer treatment after airborne-particle abrasion. 하였다. CEJ에서 1.5 cm 근관성형 후 레진 시멘트를 이용하여 표면처리된 총 24개의 FRC post를 접착하고 광중합하였다. 생리식염수에 24시간 보관한 후 포스트 장축에 수직으로 1 mm 두께로 절단하여 만능시험기로 push-out test를 시행하였다. 포스트가 탈락되는 접착 실패 강도를 측정하고 SEM을 관찰하여 접착 실패 양상을 분류하고, 접착 강도를 Kruskal-Wallis test와 Tukey HSD value of rank test를 이용하여 통계 분석하였다(${\alpha}=0.05$). 결과: Airborne-particle abrasion후 실란 처리한 실험군에서 유의할만하게 높은 접착 강도를 보였다. 실란 처리, airborne-particle abrasion후 다용도 프라이머를 처리한 실험군의 순서로 접착 강도가 높게 나타났다. FRC post의 표면에 특정 전처리를 하지 않은 대조군에서 가장 낮은 결합 강도를 보이고, 이어서 다용도 프라이머, airborne-particle abrasion 순으로 낮은 평균 접착 강도를 보였다. 결론: FRC post의 접착 전 표면 처리 과정으로서 실란 처리를 거친 실험군에서 높은 결합 강도를 보였으며, 다용도 프라이머를 이용한 표면 처리는 실란과 비교하여 유의성 있는 접착 강도의 변화를 보이지 않았다.

• Restorative Dentistry and Endodontics
• /
• 제36권2호
• /
• pp.125-131
• /
• 2011

연구목적: Silane 처리가 FRC-포스트와 레진 시멘트 간의 결합강도에 미치는 영향을 알아보고자 하였다. 연구 재료 및 방법: FRC-포스트로 LuxaPost (DMG)와 Rely-X Fiber Post (3M ESPE)를 사용하였으며 자가 접착 레진 시멘트인 Rely-X Unicem (3M ESPE)과 전통형 레진시멘트인 Rely-X ARC (3M ESPE)와의 Rely-X Ceramic Primer (3M ESPE)를 이용한 표면처리 유무에 따른 결합강도를 push-out test를 실시하여 측정하고 independent samples t-test 및 one-way ANOVA와 Scheffe 사후검정을 95% 유의수준에서 실시하였다. 결과: 실험 결과 Rely-X Fiber Post를 사용한 실험군에서 silane 처리와 관계없이 Rely-X ARC를 적용하였을 때, 다른 실험군들에 비해 높은 결합 강도가 나타났으며 LuxaPost를 사용한 실험군에서 각각의 레진 시멘트에 대해 silane 처리를 하였을 때 시행하지 않은 실험군에 비해 높은 결합 강도가 나타났다. 결론: 이상의 실험 결과로 볼 때 미리 silane 처리된 LuxaPost를 사용하더라도 silane 처리를 시행하는 것이 좋은 것으로 생각된다.