• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.27-28
• /
• 2018

In this study, water vapor pressure and restrained stress were evaluated by ring-type restrained condition for compressive strength 60 and 80MPa concrete. Experimental results show that the 80MPa concrete has higher water vapor pressure and restraint stress than the 60MPa concrete, resulting in spalling occurrence. It is because, the higher the compressive strength of the concrete, the more dense the internal structure is formed.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.04a
• /
• pp.821-824
• /
• 2008

In this study, it is willing to present that fundamental data for proposing quantitatively shrinkage cracking evaluation method such as plat-ring type restrained test method. It is possible to decide that specimen diameter is s 150mm with evaluating restrained shrinkage crack properties of concrete according to change of ring diameter in specimen. Also, effectiveness of test method according to mixing of PVA fiber is evaluated as part of a repeatability verification experiment of plat-ring type restrained test method using ring which diameter is 150mm. As a result, it is possible to measure the crack due to the plastic shrinkage which was occurred within 48hours at early age with plat-ring type restrained test method. Hereafter, it is considered that the study concerning environmental condition and mixing factor in plat-ring type restrained test method is need.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.581-584
• /
• 2008

In this study, it is willing to present that fundamental data for proposing quantitatively shrinkage cracking evaluation method such as plat-ring type restrained test method. To examine suitable size of specimen of plat-ring type restrained test method, Evaluated concrete about restrained shrinkage crack properties of numerical analysis of 3D solid element using the MIDAS program, drying shrinkage deformation, restrained shrinkage stress, crack area and crack point with inside ring diameter of specimen in 100mm, 150mm, 200mm and high of Specimen in 30mm, 50mm after curing in condition of constant temperature and usual habit of temperature 20${\pm}$3$^{\circ}$C, humidity 60${\pm}$5%. As a result, it was available about suitable estimation with inside ring diameter of specimen in more than 150mm and high of Specimen in 50mm. Hereafter, it is considered that the study concerning environmental condition and mixing factor in plat-ring type restrained test method is need.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.13 no.3 s.55
• /
• pp.188-196
• /
• 2009

In Concrete, shrinkages occur like plastic shrinkage and drying shrinkage in the early age because of evaporation and transfer of moisture. Within the country, the crack test standardized by KS is used to test the drying shrinkage of the concrete by using the restricted drying shrinkage of Dumbbell type mold, but this test is for the cracking-point and the restricted shrinkage stress. Thus it is difficult to valuate the crack quantitative test. In this study, it is intended to develop the Flat-ring type restrained test method for the shrinkage deformation movement of the concrete and to provide the quantitative data for evaluating the cracks in concrete. And it suggest the proper specimen diameter and quantitative test method about shrinkage crack properties on Flat-ring type restrained test method. And Verified the suitability.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.155-156
• /
• 2018

In this study, surface spalling and explosive spalling of ring-type ultra-high strength concrete under rapid heating and slow heating were investigated. In rapid heating, the internal temperature difference of the concrete is large, so that continuous surface spalling occurs. However, in slow heating, the difference in the internal temperature of the concrete is small, resulting in explosive spalling at a time. Since the heating condition has a great influence on the internal temperature of the concrete, it is necessary to consider the spalling of the concrete under various heating conditions.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.124-125
• /
• 2017

In this study, the spalling properties of Polypropylene reinforced concrete were evaluated by the restrained ring-type test. As a result of the experiment with the fiber mixture ratio set at 0, 0.15 vol.%, The PP fiber reinforced specimen showed lower water vapor pressure as a whole than the Plain specimen, but the restraint stress was measured to be higher. This is thought to be due to the fact that higher thermal stresses were applied in the PP fiber reinforced test specimen.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.224-225
• /
• 2017

Ultra-high-strength concrete exposed to high temperature is likely to cause spalling. Spalling is caused by the vapor pressure of the concrete, and the vapor pressure may be different depending on the heating conditions of the concrete. Therefore, in this study, a ring-type restrained specimen was fabricated using ultra-high-strength concrete and the vapor pressure generated in the concrete by heating condition(rapid and slow heating) was evaluated.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.174-175
• /
• 2019

In this study, the spalling and ultrasonic pulse transmission time of concrete were investigated according to compressive strength during heating. As a result, the higher the compressive strength of the concrete, the more the explosion occurs, which affects the cross-sectional loss and the spalling fragment size. Also, ultrasonic pulse transmission time was found to be strongly influenced by the section loss of concrete.

• International Journal of Concrete Structures and Materials
• /
• v.1 no.1
• /
• pp.3-9
• /
• 2007

Fiber-reinforced self-compacting concrete (FRSCC) is a new type of concrete mix that can mitigate two opposing weaknesses: poor workability in fiber-reinforced concrete and cracking resistance in plain SCC concrete. This study focused on early-age cracking of FRSCC due to restrained drying shrinkage, one of the most common causes of cracking. In order to investigate the effect of fiber on shrinkage cracking of FRSCC, ring shrinkage tests were performed for polypropylene and steel fiber-reinforced SCC. In addition, finite element analyses for those specimens were carried out considering drying shrinkage based on moisture diffusion, creep, cracking resistance of concrete, and the effect of fiber. The analysis results were verified via a comparison between the measured and calculated crack width. From the test and analysis results, the effectiveness of fiber with respect to reducing cracking was confirmed and some salient features on the shrinkage cracking of FRSCC were obtained.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.237-238
• /
• 2021

This study evaluated the vapor pressure and thermal stress of high-strength concrete according to spalling type. As a result, it was confirmed that the internal temperature gradient of the concrete varies depending on the heating rate, and the vapor pressure and thermal stress of the concrete are the main factors of spalling. In addition, it was confirmed that spalling type varies depending on the vapor pressure and thermal stress of the concrete.