• Title/Summary/Keyword: resin cements

Search Result 226, Processing Time 0.023 seconds

EFFECT OF DENTIN DESENSITIZERS ON SHEAR BOND STRENGTH OF RESIN CEMENTS (상아질 지각완화제가 레진시멘트의 전단결합강도에 미치는 영향)

  • Lee Ho;Jin Tai-Ho;Son Oe-Soo;Ahn Hee-Young
    • The Journal of Korean Academy of Prosthodontics
    • /
    • v.40 no.4
    • /
    • pp.365-373
    • /
    • 2002
  • The purpose of this study was to investigate the effects of desensitizer on shear bond strength of adhesive resin cements for all ceramic crown. For this study, Gluma $desensitizer^{(R)}$(Heraeus Kulzer, Germany) and MS $Coat^{(R)}$(Sun medical, Japan) were used as desensitizer, and Bistite $II^{(R)}$ resin cement(Tokuyama, Japan) and Variolink $II^{(R)}$ resin cement (Ivoclar, Liechtenstein) were used. IPS Empress ceramics were bonded to dentin surfaces after application of desensitizer and shear bond strength of specimens were measured using UTM(Zwick 1456 41. Zwick, Germany) at a crosshead speed of 1mm/min. The obtained results were as follows : 1. The shear bond strength of both resin cements were not affected by Gluma $desensitizer^{(R)}$ containing HEMA 2. The shear bond strength of Bistite $II^{(R)}$ resin cement was significantly decreased by MS $Coat^{(R)}$. 3. The failure mode in MS $Coat^{(R)}-Bistite \;II^{(R)}$ group was mainly adhesive type between dentin and resin cement. but that of Gluma $desensitizer^{(R)}$-Variolink $II^{(R)}$ group was mainly mixed type, combined adhesive failures between dentin and resin cement or porcelain and resin cement.

Impact on Retrievability by Cement Variety for Implant Restorations Equipped with a Lingual Slot

  • Lee, Ji-Hong;Lee, Kyu-Bok
    • Journal of Korean Dental Science
    • /
    • v.11 no.1
    • /
    • pp.14-20
    • /
    • 2018
  • Purpose: The purpose of this study is to measure and compare the removal torques of different cements applied in attachments of zirconia restorations on titanium (Ti) abutments fitted with retrievable cement-type slot (RCS) on the lingual side for the better retrievablity by use of a slot driver. Materials and Methods: Three types of cements were used in the experiment: two permanent cements in $RelyX^{TM}$ U200 (RU) (3M ESPE) which is a resin cement and $FujiCem^{TM}$ (FC) (GC) which is a resin-modified glass ionomer cement, and a temporary cement in $Freegenol^{TM}$ temporary cement (TC) (GC). Measurements of removal torques were conducted as follows; an attached sample was fixed on the equipment customized for the experiment; a slot driver was connected to a MGT12 (Mark-10 Corp.), a torque measurement instrument; the sample had the driver fitted to its RCS and then was rotated until the it was removed; and finally, the maximum torque value was recorded. Result: As for the removal torque measurement results, the average values were $47.9{\pm}2.6Ncm$ for RU, $43.4{\pm}1.5Ncm$ for FC, and $20.9{\pm}1.0Ncm$ for TC. The statistical analysis using Kruskal-Wallis test yielded the significance probability of P<0.05 (P=0.002), which confirmed the presence of significant differences between the three groups. Conclusion: All three cements exhibit clinically acceptable levels of removal torque when applied to an upper zirconia implant restoration fitted with a lingual slot, with RU and FC, the two permanent cements, having the significantly higher values than that of TC, the temporary cement.

Cytotoxic effects of different self-adhesive resin cements: Cell viability and induction of apoptosis

  • Sismanoglu, Soner;Demirci, Mustafa;Schweikl, Helmut;Ozen-Eroglu, Gunes;Cetin-Aktas, Esin;Kuruca, Serap;Tuncer, Safa;Tekce, Neslihan
    • The Journal of Advanced Prosthodontics
    • /
    • v.12 no.2
    • /
    • pp.89-99
    • /
    • 2020
  • PURPOSE. The effects of four different self-adhesive resin cement materials on cell viability and apoptosis after direct and indirect exposure were evaluated using different cell culture techniques. MATERIALS AND METHODS. Self-adhesive cements were applied to NIH/3T3 mouse fibroblasts by the extract test method, cell culture inserts, and dentin barrier test method. After exposure periods of 24 h and 72 h, the cytotoxicity of these self-adhesive materials was evaluated using the MTT assay (viability) and the Annexin-V-FITC/PI staining (apoptosis). RESULTS. The lowest cell viability was found in cells exposed to BeautiCem SA for 24 h in the extract test method. Cell viability was reduced to 70.6% compared to negative controls. After the 72 h exposure period, viability rate of cell cultures exposed to BeautiCem SA decreased more than 2- fold (29.5%) while cells exposed to RelyX U200 showed the highest viability rate of 71.4%. In the dentin barrier test method, BeautiCem SA induced the highest number of cells in apoptosis after a 24 h exposure (4.1%). Panavia SA Cement Plus was the material that caused the lowest number of cells in apoptosis (1.5%). CONCLUSION. The used self-adhesive cements have showed different cytotoxic effects based on the evaluation method. As exposure time increased, the materials showed more cytotoxic and apoptotic effects. BeautiCem SA caused significantly more severe cytotoxic and apoptotic effects than other cements tested. Moreover, cements other than BeautiCem SA have caused necrotic cell death rather than apoptotic cell death.

Effect of Accelerated Aging on the Color Stability of Dual-Cured Self-Adhesive Resin Cements

  • Kim, Ah-Rang;Jeon, Yong-Chan;Jeong, Chang-Mo;Yun, Mi-Jung;Huh, Jung-Bo
    • Journal of Korean Dental Science
    • /
    • v.8 no.2
    • /
    • pp.49-56
    • /
    • 2015
  • Purpose: The effect of accelerated aging on color stability of various dual-cured self-adhesive resin cements were evaluated in this study. Materials and Methods: Color stability was examined using three different brands of dual-cured self-adhesive resin cements: G-CEM LinkAce (GC America), MaxCem Elite (Kerr), and PermaCem 2.0 (DMG) with the equivalent color shade. Each resin cement was filled with Teflon mold which has 6 mm diameter and 2 mm thickness. Each specimen was light cured for 20 seconds using light emitting diode (LED) light curing unit. In order to evaluate the effect of accelerated aging on color stability, color parameters (Commission Internationale de l'Eclairage, CIE $L^*$, $a^*$, $b^*$) and color differences (${\Delta}E^*$) were measured at three times: immediately, after 24 hours, and after thermocycling. The $L^*$, $a^*$, $b^*$ values were analyzed using Friedman test and ${\Delta}E^*$ values on the effect of 24 hours and accelerated aging were analyzed using t-test. These values were compared with the limit value of color difference (${\Delta}E^*=3.7$) for dental restoration. One-way ANOVA and Scheff's test (P<0.05) were performed to analyze each ${\Delta}E^*$ values between cements at each test period. Result: There was statistically significant difference in comparison of color specification ($L^*$, $a^*$, $b^*$) values after accelerated aging except $L^*$ value of G-CEM LinkAce (P<0.05). After 24 hours, color difference (${\Delta}E^*$) values were ranged from 2.47 to 3.48 and $L^*$ values decreased and $b^*$ values increased in all types of cement and MaxCem Elite had high color stability (P<0.05). After thermocycling, color change's tendency of cement was varied and color difference (${\Delta}E^*$) values were ranged from 0.82 to 2.87 and G-CEM LinkAce had high color stability (P<0.05). Conclusion: Color stability of dual-cured self-adhesive resin cements after accelerated aging was evaluated and statistically significant color changes occurred within clinically acceptable range.

Shear bond strength between universal adhesives with various pH and dual-cured resin cements (다양한 pH를 가지는 Universal adhesives와 이원 중합 레진 세멘트 간의 전단결합강도)

  • Kwon, Sung-Joo;Park, Jeong-Kil;Son, Sung-Ae
    • Korean Journal of Dental Materials
    • /
    • v.45 no.4
    • /
    • pp.301-310
    • /
    • 2018
  • The purpose of this study is to evaluate the compatibility of universal adhesives with two dual-cured resin cements. Eighty human molars were divided into eight groups. Tooth was embedded in self-curing acrylic resin and sectioned horizontally to exposure dentine surface. After polishing with 600-grit SiC paper, adhesives were applied. All-Bond Universal (Bisco), G-premio bond (GC), Scotch-bond universal (3M ESPE), Scotch-bond Multipurpose (3M ESPE) were used in this study. Calibra (Dentsply) as a conventional dual-curing resin cement and RelyX Ultimate (3M ESPE) as an amine free resin cement were used. The adhesives and the cements were applied according to the manufacturer's instructions. Final specimens were cylinder (diameter 2mm, height 3mm) shape. After storing in distilled water at $37^{\circ}C$ for 7 days the shear bond strength (SBS) test was performed. There was no significant difference in shear bond strength between the adhesives when RelyX Ultimate was used (p>0.05). However, when Calibra used with Scotch-bond Multipurpose and All-Bond Universal were used, statistically higher SBS was observed, as compared to the groups which Calibra cements with G-premio bond and Scotch-bond universal adhesive (p<0.05) were used. Within the limitations of this study, RelyX Ultimate resin cement was compatible with universal adhesives of various pH. All-Bond Universal adhesive was compatible with a resin cement containing the tertiary amine.

Influence of nano-structured alumina coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements

  • Lee, Jung-Jin;Choi, Jung-Yun;Seo, Jae-Min
    • The Journal of Advanced Prosthodontics
    • /
    • v.9 no.2
    • /
    • pp.130-137
    • /
    • 2017
  • PURPOSE. The purpose of this study was to evaluate the effect of nano-structured alumina surface coating on shear bond strength between Y-TZP ceramic and various dual-cured resin cements. MATERIALS AND METHODS. A total of 90 disk-shaped zirconia specimens (HASS CO., Gangneung, Korea) were divided into three groups by surface treatment method: (1) airborne particle abrasion, (2) tribochemicalsilica coating, and (3) nano-structured alumina coating. Each group was categorized into three subgroups of ten specimens and bonded with three different types of dual-cured resin cements. After thermocycling, shear bond strength was measured and failure modes were observed through FE-SEM. Two-way ANOVA and the Tukey's HSD test were performed to determine the effects of surface treatment method and type of cement on bond strength (P<.05). To confirm the correlation of surface treatment and failure mode, the Chi-square test was used. RESULTS. Groups treated with the nano-structured alumina coating showed significantly higher shear bond strength compared to other groups treated with airborne particle abrasion or tribochemical silica coating. Clearfil SA Luting showed a significantly higher shear bond strength compared to RelyX ARC and RelyX Unicem. The cohesive failure mode was observed to be dominant in the groups treated with nano-structured alumina coating, while the adhesive failure mode was prevalent in the groups treated with either airborne particle abrasion or tribochemical silica coating. CONCLUSION. Nano-structured alumina coating is an effective zirconia surface treatment method for enhancing the bond strength between Y-TZP ceramic and various dual-cured resin cements.

Degree of conversion of two dual-cured resin cements light-irradiated through zirconia ceramic disks

  • Kim, Min-Jeong;Kim, Kyo-Han;Kim, Young-Kyung;Kwon, Tae-Yub
    • The Journal of Advanced Prosthodontics
    • /
    • v.5 no.4
    • /
    • pp.464-470
    • /
    • 2013
  • PURPOSE. The aim of this Fourier transform infrared (FTIR) spectroscopic study was to measure the degree of conversion (DC) of dual-cured resin cements light-irradiated through zirconia ceramic disks with different thicknesses using various light-curing methods. MATERIALS AND METHODS. Zirconia ceramic disks (KT12) with three different thicknesses (1.0, 2.0, and 4.0 mm) were prepared. The light transmittance of the disks was measured using ultraviolet visible near-infrared spectroscopy. Four different light-curing protocols were used by combining two curing light modes (Elipar TriLight (standard mode) and bluephase G2 (high power mode)) with light-exposure times of 40 and 120 seconds. The DCs of the two dual-cured resin cements (Duo-Link and Panavia F2.0) light-irradiated through the disks was analyzed at three time intervals (3, 7, and 10 minutes) by FTIR spectroscopy. The data was analyzed using repeated measures ANOVA (${\alpha}$=.05).Two-way ANOVA and Tukey post hoc test were used to analyze the 10 minute DC results. RESULTS. The 1.0 mm thick disk exhibited low light transmittance (<25%), and the transmittance decreased considerably with increasing disk thickness. All groups exhibited significantly higher 10 minute DC values than the 3 or 7 minute values (P<.05), but some exceptions were observed in Duo-Link. Two-way ANOVA revealed that the influence of the zirconia disk thickness on the 10 minute DC was dependent on the light-curing methods (P<.001). This finding was still valid even at 4.0 mm thickness, where substantial light attenuation took place. CONCLUSION. The curing of the dual-cured resin cements was affected significantly by the light-curing technique, even though the additional chemical polymerization mechanism worked effectively.

Adhesion of 10-MDP containing resin cements to dentin with and without the etch-and-rinse technique

  • Turp, Volkan;Sen, Deniz;Tuncelli, Betul;Ozcan, Mutlu
    • The Journal of Advanced Prosthodontics
    • /
    • v.5 no.3
    • /
    • pp.226-233
    • /
    • 2013
  • PURPOSE. This study evaluated the adhesion of 10-MDP containing self-etch and self-adhesive resin cements to dentin with and without the use of etch-and-rinse technique. MATERIALS AND METHODS. Human third molars (N=180) were randomly divided into 6 groups (n=30 per group). Conventional (Panavia F2.0, Kuraray-PAN) and self-adhesive resin cements (Clearfil SA, Kuraray-CSA) were bonded to dentin surfaces either after application of 3-step etch-and-rinse (35% $H_3PO_4$ + ED Primer) or two-step self-etch adhesive resin (Clearfil SE Bond). Specimens were subjected to shear bond strength test using the universal testing machine (0.5 mm/min). The failure types were analyzed using a stereomicroscope and quality of hybrid layer was observed under a scanning electron microscope. The data (MPa) were analyzed using two-way ANOVA and Tukey's tests (${\alpha}$=.05). RESULTS. Overall, PAN adhesive cement showed significantly higher mean bond strength ($12.5{\pm}2.3-14.1{\pm}2.4$ MPa) than CSA cement ($9.3{\pm}1.4-13.9{\pm}1.9$ MPa) (P<.001). Adhesive failures were more frequent in CSA cement groups when used in conjunction with two-step self-adhesive (68%) or no adhesive at all (66%). Hybrid layer quality was inferior in CSA compared to PAN cement in all conditions. CONCLUSION. In clinical situations where bonding to dentin substrate is crucial, both conventional and self-adhesive resin cements based on 10-MDP can benefit from etch-and-rinse technique to achieve better quality of adhesion in the early clinical period.

Effect of non-thermal plasma on the shear bond strength of resin cements to Polyetherketoneketone (PEKK)

  • Labriaga, Wilmart;Song, So-Yeon;Park, Jin-Hong;Ryu, Jae-Jun;Lee, Jeong-Yol;Shin, Sang-Wan
    • The Journal of Advanced Prosthodontics
    • /
    • v.10 no.6
    • /
    • pp.408-414
    • /
    • 2018
  • PURPOSE. This study aimed to assess the effect of non-thermal plasma on the shear bond strength of resin cements to polyetherketoneketone (PEKK) in comparison to other surface treatment methods. MATERIALS AND METHODS. Eighty PEKK discs were subjected to different surface treatments: (1) Untreated (UT); (2) Non-thermal plasma (NTP); (3) Sandblasting with $50{\mu}m$ $Al_2O_3$ particles (SB); and (4) Sandblasting + Non-thermal plasma (SB+NTP). After each surface treatment, the contact angle was measured. Surface conditioning with Visio.Link was applied in all groups after pre-treatment. RelyX Unicem resin cement was bonded onto the PEKK specimens. After fabrication of the specimens, half of each group (n=10) was initially tested, while the other half was subjected to thermocycling ($5^{\circ}C$ to $55^{\circ}C$ at 10,000 cycles). Shear bond strength (SBS) testing was performed using a universal testing machine, and failure modes were assessed using stereomicroscopy. The SBS results were analyzed statistically using one-way ANOVA followed by Tukey's post hoc test. Independent t-test was used to examine the effect of thermocycling (P<.05). RESULTS. The highest SBS values with or without thermocycling were observed with PEKK specimens that were treated with SB+NTP followed by the SB group. The lowest SBS results were observed in the UT groups. CONCLUSION. The shear bond strength between PEKK and resin cements was improved using non-thermal plasma treatment in combination with sandblasting.

Bonding to zirconia with resin cements (지르코니아와 레진 시멘트의 결합)

  • Lim, Bum-Soon;Her, Soo-Bok
    • The Journal of the Korean dental association
    • /
    • v.49 no.5
    • /
    • pp.265-278
    • /
    • 2011
  • The introduction of zirconia-based materials to the dental field broadened the design and application limits of, all-ceramic restorations. Most ceramic restorations are adhesively luted to the prepared tooth, however, resin bonding to zirconia components is less reliable than those to other dental ceramic systems. It is important for high retention, prevention of microleakage, and increased fracture resistance, that bonding techniques be improved for zirconia systems. Strong resin bonding relies on micromechanical interlocking and adhesive chemical bonding to the ceramic surface, requiring surface roughening for mechanical bonding and surface activation for chemical adhesion. In many cases, high strength ceramic restorations do not require adhesive bonding to tooth structure and can be placed using conventional cements which rely only on micromechanical retention. However, resin bonding is desirable in some clinical situations. In addition, it is likely that strong chemical adhesion would lead to enhanced long-term fracture and fatigue resistance in the oral environment.