• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.10
• /
• pp.608-612
• /
• 2016

In this study, in order to develop relaxor ferroelectric ceramics for refrigeration device application with large electrocaloric effect and low sintering temperature, PLZT(8/65/35) ceramics was fabricated using conventional solid-state method with the variation of sintering temperature ($1,050^{\circ}C$, $1,100^{\circ}C$, $1,200^{\circ}C$). The XRD pattern of all specimens indicated general perovskite structure with secondary phase. From the results of temperature dependence of dielectric constant, the $T_C$ (ferroelectric-paraelectric phase transition temperature) was shifted toward high temperature with increasing sintering temperature. When the specimen was sintered at $1,100^{\circ}C$, the optimal value of ${\Delta}T{\sim}0.349^{\circ}C$ in ambient temperature of $215^{\circ}C$ was appeared. It is considered that PLZT(8/65/35) ceramics possess the possibility of refrigeration device application.

• Applied Science and Convergence Technology
• /
• v.24 no.6
• /
• pp.224-227
• /
• 2015

Ferroelectric $Pb_2(Sc,Nb)O_6$ were prepared under two different sintering conditions using the oxide mixing method and the electrical properties were measured. The sintering conditions were $1350^{\circ}C$ for 25 minutes and $1400^{\circ}C$ for 20 minutes. EDX spectroscopy and XRD were used to determine the crystalline characteristic of the $Pb_2(Sc,Nb)O_6$ compositions Pyrochlore phase showed about 2% in all $Pb_2(Sc,Nb)O_6$ specimens. It expands the growth of crystals in samples sintered at $1400^{\circ}C$ than $1350^{\circ}C$, but all samples were the optimal crystallization. The temperature and frequency dependence of the complex dielectric constant and admittance were measured to analyze the electrical properties. The high dielectric constant of the specimens reflects the good stoichiometry and crystallization. The maximum value of the dielectric constant in the two specimens treated with sintering at $1350^{\circ}C$ and $1400^{\circ}C$ were more than 27,000, and the dielectric loss at room temperature is smaller than 0.05. The maximum dielectric constant decreased with increasing frequency, the transition temperature also increased in $Pb_2(Sc,Nb)O_6$ compositions. The admittance and susceptance values reach a peak at all temperatures, and the magnitude of the peak increases with increasing measuring temperature. Strong frequency dependent of maximum admittance, susceptance, dielectric constant and dielectric loss were observed.

• Proceedings of the KIEE Conference
• /
• 1997.07d
• /
• pp.1330-1332
• /
• 1997

In this paper, PNN-PZN-PZT ceramics were fabricated with various mole ratio of the PZT[$Pb(Zr_{1/2}Tid_{1/2})O_3$]. PNN [$Pb(Ni_{1/3}Nb_{2/3})O_3$] and PZN[$Pb(Ni_{1/3}Nb_{2/3})O_3$ powders prepared by double calcination and PZT powders prepared by molten-salt synthesis method. The formation rate of perovskite phase in PNN-PZN-PZT ceramics could be obtained about 92% at PZT 0.3 mole ratio. The relative permittivity of specimen with PZT 0.3 mole ratio was shown 5,320 and appeared the relaxor ferroelectric feature. The maximum piezoelectric coefficient $d_{31}$ to be used for evaluation the displacement of piezoceramics in PNN-PZN-PZT ceramics was $324{\times}10^{-12}$(C/V) at the vicinity of morphotropic phase boundary and was larger than that of solid PZT ceramics($120{\times}10^{-12}C/V$).

• Journal of the Korean Ceramic Society
• /
• v.55 no.5
• /
• pp.419-439
• /
• 2018

Piezoelectric materials are essential parts of the electronics and electrical equipment used for consumer and industrial applications, such as ultrasonic piezoelectric transducers, sensors, actuators, transformers, and resonators. In this review, the development of piezoelectric materials and the figures of merit for various electromechanical applications are surveyed, focusing on piezoelectric crystals, i.e., the high-performance relaxor-$PbTiO_3$-based perovskite ferroelectric crystals and nonferroelectric high-temperature piezoelectric crystals. The uniqueness of these crystals is discussed with respect to different usages. Finally, the existing challenges and perspective for the piezoelectric crystals are discussed, with an emphasis on the temperature-dependent properties, from cryogenic temperatures up to the ultrahigh-temperature usage range.

• Proceedings of the Korea Association of Crystal Growth Conference
• /
• 1996.06b
• /
• pp.185-217
• /
• 1996

Pb(Mg1/3Nb2/3)O3은 높은 유전율과 전기저항 및 유전율의 온도변화율이 적은 Pb계 relaxor의 대표적인 재료로서 적층 세라믹 콘덴서 재료에의 응용이 크게 기대되고 있다. 그러나 산화물 분말을 이용하는 일반적인 세라믹스 합성방법으로는 Pb(Mg1/3Nb2/3)O3의 단일상의 합성이 어렵고, 합성과정에서 저유전율상인 pyrochlore상이 합성이 어렵고, 합성과정에서 저유전율상인 pyrochlore상이 공존하여 Pb(Mg1/3Nb2/3)O3의 전기적 특성을 저하시킨다. 본연구에서는 용액을 이용하여 Pb(Mg1/3Nb2/3)O3의 단일상을 합성하고자 하였다. 출발물질로는 값싼 금속염인 Niobium Oxalate, magnesium Nitrate 및 Lead Nitrate를 선정하고 증류수에 용해하여 혼합용액을 제좋고, 합성방법으로는 초음파 분무 열분해법과 에멀젼법을 이용하였다. 초음파 분무 열분해법에서는 75$0^{\circ}C$에서 합성한 분말을 다시 75$0^{\circ}C$에서 하소하여 Pb(Mg1/3Nb2/3)O3 단일상을 합성할 수 있었으며, 에멀젼법에서는 80$0^{\circ}C$에서 Pb(Mg1/3Nb2/3)O3 단일상을 합성할 수 있었다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.206-210
• /
• 1997

In the fields of the optics, precise machine, semiconductors, the micro-positioning actuators are required for the control of position in the submicron range. PNN-P2N-PZT ceramics were fabricated with various mole ratio of the PZT[Pb(Zr$_{1}$2//Ti$_{1}$2)O$_3$]. PNN (Pb(Ni$_{1}$3/Nb$_{2}$3/)O$_3$]and PZN[Pb(Zn$_{1}$3//Nb/sbu 2/3/)O$_3$] powders prepared by double calcination and PZT powders prepared by molten- salt synthesis method. The relative permittivity of specimen with PZT 0.3 mole ratio was shown 5,320 and appeared the relaxor ferroelectric feature. The maximum Piezoelectric coefficient d$_{31}$ to be used for evaluation the displacement of piezoceramics in PNN-PZN-PZT ceramics was 324$\times$10$^{-12}$ (C/V) at the vicinity of morphotropic phase boundary and was larger than that of solid PZT ceramics(120$\times$10$^{-12}$ C/V).

• Korean Journal of Materials Research
• /
• v.19 no.6
• /
• pp.300-304
• /
• 2009

The domain structures of annealed (001)-oriented $Pb(Mg_{1/3}Nb_{2/3})O_3-x%PbTiO_3$ (PMN-x%PT) crystals for x = 10, 20, 30, 35, and 40 at% were investigated by Polarized Optical Microscopy (POM) and Scanning Force Microscopy (SFM) in the piezoresponse mode. Both Polar Nano-Domains (PND) and long strip-like domains were clearly observed. The results also showed how the domain structure changed between phases with an increasing x in the PMN-x%PT crystals and the domain hierarchy on various length scales ranging from 40 nm to 0.1 mm. Distorted pseudo-cubic phase (x < 20%) consisted of PNDs that did not self-assemble into macro-domain plates. The rhombohedral phase (x = 30%) consisted of PNDs that began to self-assemble into colonies along preferred {110} planes. The monoclinic phase (x = 35%) consisted of miniature polar domains on the nm scale, whereas, the tetragonal phase (x = 40%) consisted of {001} oriented lamella domains on the mm scale that had internal nano-scale heterogeneities, which self-assembled into macro-domain plates oriented along {001} the mm scale.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.34 no.5
• /
• pp.382-385
• /
• 2021

Electrical poling is a crucial step to convert ferroelectrics to piezoelectrics. Nevertheless, no systematic investigation on the effect of poling has been reported. Given that the poling involves an alignment of spontaneous polarization, the condition for poling should be different when a material has an internal bias field that influences the domain stability. Here, we present the effect of poling profile on the dielectric and piezoelectric properties in Mn-doped Pb(Mg_1/3Nb_2/3)O₃-29 mol%PbTiO₃ single crystal with an internal bias field. We showed that both the dielectric permittivity and the piezoelectric coefficient were further enhanced when the poling procedure ends with a field application along the opposite direction to the internal bias field. We expect that the current finding would give a clue to understanding the true mechanism for the electrical poling.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.30 no.5
• /
• pp.183-188
• /
• 2020

Lead zinc niobate (PZN)-added lead zirconate titanate (PZT) thick films with thickness of 5~10 ㎛ were fabricated on silicon and sapphire substrates using aerosol deposition method. The contents of PZN were varied from 0 %, 20 % and to 40 %. The PZN-added PZT film showed poorer electrical properties than pure PZT film when the films were coated on silicon substrate and annealed at 700℃. On the other hand, the PZN-added PZT film showed higher remanent polarization and dielectric constant values than pure PZT film when the films were coated on sapphire and annealed at 900℃. The ferroelectric and dielectric characteristics of 20 % PZN-added PZT films annealed at 900℃ were compared with the result values obtained from bulk ceramic specimen with same composition sintered at 1200℃. As annealing temperature increased, dielectric constant increased. These came from enhanced crystallization and grain growth by post heat treatment.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.4
• /
• pp.667-672
• /
• 1998

Pyroelectric properties of $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3$ ceramics prepared by the columbite precursor method have been investigated as a function of the sintering temperature in the range of $1000^{\circ}C$ to $1250^{\circ}C$. The $Pb(Mg_{1/3}Nb_{2/3})O_3-PbTiO_3$ ceramics show typical relaxor ferroelectric behavior. The optimum condition for obtaining samples with high densities and improved pyroelectric properties occur at a sintering temperature of $1250^{\circ}C$ and sintering times of 2 hours. The $Pb(Mg_{1/3}Nb_{2/3}O_3-PbTiO_3$ ceramics show the possibility for pyroelectric sensors with pyrostat.