• 한국염색가공학회지
• /
• 제24권1호
• /
• pp.91-96
• /
• 2012

The physical properties of recycled polyester yarns according to recycling methods were investigated. Virgin polyester draw texturized yarn(DTY), material-recycled(MR) polyester DTY and chemical-recycled(CR) polyester DTY were prepared. Surface morphology, thermal property, micro-structure and mechanical property of recycled polyester yarns were estimated. SEM-EDS analysis showed that the CR PET yarn had better crimp and more stable structure than MR PET yarn. Tm of the MR PET yarn was higher than that of the CR PET yarn. The intensity of the crystallization peak of the CR PET yarn was a little higher than that of the MR PET yarn. Tensile strength of the MR PET yarn was slightly higher than that of the CR PET yarn. Breaking elongation of the CR PET yarn was slightly higher than that of the MR PET yarn.

• 한국농공학회논문집
• /
• 제51권6호
• /
• pp.97-103
• /
• 2009

This study was performed to evaluate the strength and durability properties of recycled polymer concrete using unsaturated polyester resin and recycled aggregates. Unsaturated polyester resin, natural and recycled aggregates and fly ash were used. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate sizes (5-10 and 5-25 mm) and unit binder contents (10% and 12%). Tests for the compressive and flexural strength, freezing and thawing and durability for 20% sulfuric solution were performed. The compressive and flexural strength of recycled polymer concrete were in the range of 85~97 MPa and 17.9~20.8 MPa, respectively. The strengths of recycled polymer concrete using recycled aggregate have similar or slightly decreased compared to polymer concrete using natural aggregate. After 300 cycles of freezing and thawing, weight decrease ratio and durability factor of recycled polymer concrete were in the range of 0.13~1.42% and 94~99, respectively.

• 한국염색가공학회지
• /
• 제35권3호
• /
• pp.169-178
• /
• 2023

The extended use of polyester nowadays has increased the amount of waste polyester (PET) released into the environment. Although these materials don't directly harm living things or the ecosystem, their inability to biodegrade remains one of the major global threats, driving up the amount of solid waste made up of PET. Environmental concerns have approved an increasing interest in recycled PET however the production of recycled PET with sufficient mechanical properties is still a challenge. Recycled Polyester (rPET) yarns are inexpensive and have the potential to acquire better mechanical characteristics through physical treatments, particularly by using technically simple method like uniaxial drawing. This study inspected the drawn behavior of virgin PET yarns and rPET yarns under various drawing parameters by first analyzing the initial material characteristics of both yarn. The impact of stretching on mechanical and morphological properties was also investigated. The results showed that virgin PET has better properties than rPET yarn; however, mechanical properties resembling virgin PET are achieved after optimizing the draw ratio.

• 농업과학연구
• /
• 제37권1호
• /
• pp.87-96
• /
• 2010

This study was performed to evaluate the planting properties of herbaceous plant and cool-season grass in porous polymer blocks that were manufactured by using recycled coarse aggregates and unsaturated polyester resin to develop environmentally friendly planting blocks. Unsaturated polyester resin, natural and recycled coarse aggregates and $CaCO_3$ were used. The mix proportions were determined to satisfy the requirement for the workability and slump according to aggregate sizes(5-10 and 5-20mm). Tests for the void ratio and compressive strength of porous polymer concrete were performed at curing age 7 days. Also, porous polymer block using recycled coarse aggregates were applied to kinds of plants such as tall fescue, Perennial ryegrass, Lesedeza and Alfalfa. After seed, initial germination, germination ratio, cover view and growth length for planting blocks were estimated by various methods.

• KCI Concrete Journal
• /
• 제11권3호
• /
• pp.89-97
• /
• 1999

The purpose of this research is to investigate the utilization of recycled fine aggregates as a material to apply to a building finished walls or as a decorating material in combination with a polymer. The strengths of two resin mortars using recycled fine aggregates and natural fine aggregates was made. In order to improve the workability and the strength of the resin mortar with recycled fine aggregates, partial replacement of recycled fine aggregates with natural ones was made with the application of various type of fillers. The results, it show that the compressive strength and flexural strength of resin mortar using the recycled fine aggregates were about 70% to 100% of those of resin mortar using natural fine aggregates. It was enough to assure the utilization of the recycled fine aggregates as a material for the production of resin mortar. From the result of partial replacement of recycled fine aggregates with natural ones, the compressive strength was Increased from 5% to 15% and the flexural strength was much as 5% to 20% as a result of 70% substitution It was also found that the use of garnet powder shows a similar tendency in the compressive strength and slag powder does in the flexural strength and tensile strength.

• 한국생활과학회지
• /
• 제21권4호
• /
• pp.781-790
• /
• 2012

In midst of growing interest and awareness towards sustainability and being "green", there has been increased demand for sustainable clothing. In the purpose of boosting eco-friendly textiles industry, this research was conducted by investigating environmentally-conscious clothing behavior of university students and assessing their views on eco-friendliness of fibers. Thus, their awareness on recycled polyester fiber was evaluated. The research was conducted by surveying 257 university students residing in Daejeon. The data were analyzed with descriptive statistics, factor analysis, and reliability analysis, using SPSS 19.0. The results were as follows. 1) The majority of the subjects answered "Disposing clothing in the clothing recycling container" to reduce environmental impact. 2) Six factors of eco-friendliness of fiber were extracted as reutilization, unfinishedness, economics, environment preservation, natural materials, and slow fashion by using factor analysis. 3) Subjects scored organic cotton as most eco-friendly among various fibers. Recycled polyester fiber was graded less sustainable than natural fiber, but more eco-friendly than artificial one. 4) In assessment of subject's awareness of recycled polyester fiber, they highly valued on resource-reutilization and economics, but less valued on its hygiene, thermal insulation and health-functionality.

• 콘크리트학회논문집
• /
• 제14권3호
• /
• pp.283-290
• /
• 2002

일반적으로 불포화 폴리에스테르 모르타르 및 콘크리트는 강도가 우수하고 내약품성이 좋지만, 취성적이어서, 내충격성이 요구되는 용도로는 사용하기 어렵다. 그러므로, 본 연구에서는 재생골재와 불포화 폴리에스테르 액상수지를 사용한 바닥마감재를 개발하기 위해 불포화 폴리에스테르 모르타르의 취성을 개선시켜보고자 하였다. 불포화 폴리에스테르 모르타르의 취성을 개선하기 위한 재료로 폴리우레탄 액상고무를 사용하였으며, 폴리올의 분자량과 폴리우레탄 액상고무의 치환율에 따른 모르타르의 특성을 검토했다. 실험결과, 폴리우레탄 액상고무의 사용에 따라 불포화 폴리에스테르 모르타르의 점도가 증가하였고, 경화수축은 감소하였다. 그리고, 모르타르내에 생성된 고무입자에 의해 압축강도 및 휨강도는 다소 저하하였지만, 내충격성이 향상되고, 휨파괴시험결과에서 파괴하중이후에도 급격한 파괴를 보이지 않는 결과를 얻을 수 있었다. 따라서, 본 연구의 결과는 폴리올의 분자량 2000, 3000인 폴리우레탄 액상고무를 불포화 폴리에스테르 모르타르에 사용하여 취성의 개선효과를 얻을 수 있다는 것을 제시하고 있다.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 춘계 학술발표회 제16권1호
• /
• pp.324-327
• /
• 2004

In this paper, fundamental properties of Polymer Concrete made from unsaturated polyester resin based on recycled PET and recycled aggregate(RPC) were investigated. Resins based on recycled PET and recycled aggregate offer the possibility of low source cost for forming useful products, and would also help alleviate an environmental problem and save energy. The results of test for resin contents and recycled aggregate ratio are showed that the strength of RPC increases with resin contents relatively, however beyond a certain resin content the strength does not change appreciably, and the relationship between the compressive strength and aggregate contents at resin $9\%$ has a close correlation linearly whereas there is no correlation between the compressive strength and the flexural strength of RPC with recycled concrete aggregate.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2004년도 추계 학술발표회 제16권2호
• /
• pp.719-722
• /
• 2004

Resins using recycled PET offer the possibility of a lower source cost of materials for making useful polymer concrete products. The purposed of this paper is to form a part of reducing the damage of sulfuric acid, through investigating recycled PET polymer concrete, . immersed at sulfuric acid solution for 84 days. Recycled PET PC is excellent chemical resistance, resulting in the role of unsaturated polyester resin which consists of polymer chain structure accomplishes bond of aggregates and filler strongly. Also, Recycled PET PC, used fly-ash as filler, is stronger resistance of sulfuric acid corrosion than $CaCO_3$, because it is composed of $SiO_2$ and very strong glassy crystal structure. Therefore, Recycled PET PC, used fly-ash as filler, is available under corrosion circumstances like sewer pipe or waste disposal plant.

• 한국환경과학회지
• /
• 제12권6호
• /
• pp.635-641
• /
• 2003

A recycling process for the waste FRP from boats was developed. The recycling process is composed of decomposition of waste FRP with propylene glycol and synthesis of recycled unsaturated polyester resin from the decomposed liquid material. Prior to the decomposition, waste FRP was cut into 2cm x 5cm segments and mechanical impact was applied by press roller to give gaps between cumulated laminates. Propylene glycol effectively decomposed the waste FRP segments and glass fibers were easily separated from decomposed liquid material. Recycled unsaturated polyester resin could be made from the decomposed liquid material by reaction with maleic anhydride and phthalic anhydride.