• Elastomers and Composites
• /
• 제51권4호
• /
• pp.269-274
• /
• 2016

Two different reactive silicone oligomers, hydroxylpropyl terminated PDMS (PDMS-L) and 1-(2,3-dihydroxy-propoxy)propyl terminated PDMS (PDMS-B), were synthesized through hydrosilylation reaction under Karstedt's catalyst. Using the reactive silicone oligomers, two different silicone-modified gel-coat series were prepared to investigate their thermal and mechanical properties as well as surface characteristics according to reactive silicone oligomer contents. In case of thermal stabilities and mechanical properties, the gel-coat series containing PDMS-B showed higher values than that of the gel-coat series containing the PDMS-L. The contact angle for the gel-coat containing both silicone oligomers/was increased with reactive silicone oligomer contents but there was similar surface tension between PDMS-L and PDMS-B.

• Elastomers and Composites
• /
• 제48권4호
• /
• pp.249-255
• /
• 2013

Hydrogen terminated PDMS와 allyl alcohol를 Karstedt's 촉매 존재하에서 hydrosilylation 반응을 이용하여 hydroxypropyl terminated PDMS를 합성한 후, 3관능 HDI isocyanurate trimer와 hydroxyethyl methacrylate를 one-pot 반응으로 초분지 형태의 다관능 실리콘 변성 우레탄 아크릴레이트 올리고머(PUA 올리고머)를 합성하였다. 합성된 PUA 올리고머의 특성은 FT-IR과 GPC를 사용하여 분석하였으며, 그들의 중량평균 분자량은 약 9000 g/mol 이었다. 합성된 PUA 올리고머와 반응성 모노머인 phenylthioethyl acrylate를 여러 가지 조성비로 혼합하고 UV-광경화반응을 이용하여 연성 경화물을 제조하였다. 연성 경화물의 굴절률은 phenylthioethyl acrylate 첨가함에 따라 증가하였으나 반응성 모노머 함량과 관계가 없었다. 또한, 연성 경화필름의 광투과도 변화도 없었다.

• 폴리머
• /
• 제27권5호
• /
• pp.421-428
• /
• 2003

반응성 올리고머 및 메타아크릴레이트/SBS블렌드의 확산에 의해 제어되는 광중합 반응 특성을 ATR-FTR을 이용하여 고찰하였다. 광중합 속도는 반응 초기 단계에서는 자가 가속 현상을 보이며 반응 속도가 급격하게 증가하여 반응이 진행함에 따라 확산에 의한 반응 지연 현상이 관찰된다. 확산 제어항이 도입된 반응 기구 속도식으로 반응 속도를 해석한 결과 전체 반응 구간에서 실험 결과와 잘 일치하였다. SBS의 도입을 위해 사용된 반응성 용매인 N-비닐피롤리돈 (NVP)의 첨가에 의해서 최종 전환율에 이르는 시간은 거의 일정하였으나 전환율은 NVP의 높은 반응성으로 인하여 증가하는 경향을 보였다. 중합 반응 속도도 NVP 첨가에 의하여 증가하는 경향을 보였다. SBS의 첨가시 NVP-SBS의 함량이 10 phr까지는 동일한 전환율 거동을 보이나 NVP-SBS의 함량이 20 phr에서는 현저히 떨어지게 되는데 이는 NVP-SBS의 함량이 20 phr에서는 블렌드의 점도가 증가하여 반응에 영향을 주는 것으로 보인다. NVP-SBS의 함량이 증가함에 따라 중합 반응 속도는 점진적으로 감소함을 알 수 있었다. 메타아크릴레이트./SBS의 블렌드는 상온과 여러 높은 온도 범위에서 상분리가 관찰되지 않았으며 광중합 반응 후에도 투명한 준-IPN을 형성하여 성공적으로 필름 및 코팅에 적용할 수 있었다.

• 한국응용과학기술학회지
• /
• 제32권4호
• /
• pp.718-723
• /
• 2015

For the fabrication of the Si negative electrode in Li-ion batteries (LIBs) containing the cross-linking polymer binder, in this work, the urethane acrylate (UA) oligomer was synthesized via a simple synthetic process. The cross-linked poly(urethane acrylate) (CPUA)/carbone black (CB)/Si composite (CPUA/CB/Si composite) was fabricated through reactions between their reactive vinyl segments in the UA oligomer. Interestingly, the CPUA/CB/Si composite showed better cycle performance than the poly(vinylidene fluoride) (PVdF)/CB/Si composite (PVdF/CB/Si composite) and the polyurethane (PU)/CB/Si composite (PU/CB/Si composite). The CPUA/CB/Si composite had the best lithiation of about $2586mAh\;g^{-1}$. The UA oligomer showed a good compatibility with the electrode materials and current collector after and before a curing process.

• Macromolecular Research
• /
• 제16권2호
• /
• pp.149-154
• /
• 2008

UV-curable electrolytes inks were prepared by dissolving [2-[(methacryloyloxy)ethyl]dimethyl]propylaminium bromide (MEPAB), 1,5-[bis(2-methacryloxyethyl)dimethyl ammono]penthane dibromide (MDAPD), hexafunctional reactive oligomer (SP1013), trimethylolpropane triacrylate (TMPTA) and a photoinitiator in methanol/2-methoxyethanol. The compositions of the electrolyte inks were MEPAB/MDAPD/SP1013/TMPTA=6/24/17.2/12.8, 15/15/17.2/12.8 and 24/6/17.2/12.8. Humid-membranes were deposited on a gold electrode/alumina electrode using an ink-jet printer equipped with a UV lamp followed by immediate UV curing. The humidity-sensing characteristics including hysteresis, frequency and temperature dependence, response time and water durability were estimated.

• 공업화학
• /
• 제17권1호
• /
• pp.33-36
• /
• 2006

광경화 접착제로 많이 사용되는 우레탄-아크릴레이트 올리고머의 광경화 거동을 자체촉매화 반응모델식을 통해 중합온도 및 올리고머의 관능성에 따른 영향을 확인하여 보았다. 중합온도가 증가함에 따라 최대중합속도는 감소하여 중합온도가 경화 거동에 대한 영향인자임을 확인할 수 있었으며, 반응속도상수 k는 온도증가에 따라 거의 일정한 값을 보이나 반응차수 m과 n은 증가하는 경향을 보였는데 이는 가교구조에 의한 반응성 기의 확산제한 및 유동성의 제한으로 인한 것으로 판단되어진다. 온도증가에 따른 중합속도의 감소는 주로 반응차수 n의 증가에 의해 진행되었다.

• 접착 및 계면
• /
• 제17권2호
• /
• pp.67-71
• /
• 2016

본 연구에서는 반응성 희석제 함량에 따라 접착강도 및 물성을 향상시키기 위해 polyether polyol/polyester polyol, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), 2-butanone oxime (MEKO)를 사용하여 저점도 폴리우레탄 핫멜트를 합성하였다. 합성된 저점도 폴리우레탄 핫멜트의 물성은 FT-IR, viscosity meter 및 UTM 등을 통해 확인하였다. 반응성 희석제의 함량이 증가하고 NCO-blocked prepolymer가 감소함에 따라 저점도 폴리우레탄 핫멜트 접착제의 점도는 증가하였으며, OH-terminated oligomer, NCO-blocked prepolymer, 반응성 희석제 함량의 비가 1 : 0.5 : 0.5일 때 1.1 kgf/cm 접착강도를 나타내었다.

• 폴리머
• /
• 제33권1호
• /
• pp.19-25
• /
• 2009

내수성 감습막으로 사용하기 위하여 이온넨을 포함하는 광경화성 반응성 올리고머(PIDM)로부터 새로운 종류의 전해질 고분자를 제조하였다. PIDM, hexamethylene dimethacrylate(HDM), pentaerythritol triacrylate dimer(SP1013) 및 광개시제를 혼합하여 전극에 광개시 라디칼 중합과 동시에 도포하였다. 또한, 센서의 내수성 그리고 고온/고습에서의 안정성을 증진시키기 위하여 전극 기판에 비닐기를 가지는 실란 카플링제를 사용하여 전처리 하였다. 가교화된 이온넨으로 이루어진 습도센서의 상대습도에 대한 저항을 측정하였을 때, 저항은 20%$\sim$90%RH 상대습도 영역에서 $10^3$의 값이 변화하였으며 이것은 대기의 습도를 측정하는데 요구되는 특성을 만족시키고 있다. 그 밖에 온도의존성, 히스테리시스 응답 및 회복속도, 내수성 그리고 고온/고습에서 장기 안정성을 측정하여 습도센서로서 특성을 평가하였다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2003년도 International Meeting on Information Display
• /
• pp.520-523
• /
• 2003

We used three types of reactive diluents with different chemical structures, N-vinyl-pyrrollidone(NVP), ethyl hexyl acrylate(EHA) and hydroxyehtyl methacrylate(HEMA). It was founded that N-vinylpyrrollidone(NVP) and ethyl hexyl acrylate(EHA) based PUA with low molecular weight polypropylene glycol(PPG) at low oligomer content give high diffraction efficiency. The morphology of the resultant gratings was analyzed by using scanning electron microscopy(SEM) and Tg of the polymer matrix by dynamic mechanical thermal analysis(DMTA).

• 대한화학회지
• /
• 제38권7호
• /
• pp.480-484
• /
• 1994

자외선 경화코팅 필름-기질 계면에서의 견딤성에 대하여 조사하였다. 특히, UV 경화 우레탄 아크릴레이트계 배합물에서 모노머 및 올리고머의 코팅필름 주름현상에 미치는 영향은 조사하였다. 실험결과, 주름현상은 DMTA이 손실모듈러스 피크가 넓고 shouldr가 있을수록 덜 나타났다. 특히, 변성된 방향족 우레탄 아크릴레이트를 지방족계에 첨가하므로서 hard하면서도 flexible한 코팅필름을 얻을 수 있음을 알 수 있었다. 따라서 주름현상 방지효과는 높은 손실모듈러스값 때문인 것으로 나타났다. SEM 및 instron 실험결과도 위의 결론을 입증하고 있음을 알 수 있었다.