• Macromolecular Research
• /
• v.12 no.4
• /
• pp.399-406
• /
• 2004

Glass-like carbon precursors shrink significantly during curing and carbonization, which leads to crack formation and bending. Cured furan resin powder and ethanol were added to furan resin to diminish the weight loss, to suppress the shrinkage and bending, and to readily release the gases evolved during polymerization and curing. Curing and carbonization were controlled by pressure and slow heating to avoid damage to the samples. The effect of the filler and ethanol on the fabrication process was examined by measuring the properties of the glass-like carbon, such as the specific gravity, bending strength, electrical resistivity, and microstructural change. The specific gravities of the filler-added glass-like carbons were higher than those of the ethanol-added samples because of the formation of macropores from the vaporization of ethanol during the curing and polymerization processes. Although the ethanol-added glass-like carbons exhibited lower bending strengths after carbonization than did the filler-added samples, the opposite result was observed after aging at 2,600$^{\circ}C$. We found that the macropores created from ethanol were contracted and removed upon heat treatment. The electrical resistivity of the glass-like carbon aged at 2,600$^{\circ}C$ was lower than those of the samples carbonized at 1,000$^{\circ}C$. We attribute this phenomenon to the fact that aging at high temperature led to well-developed microstructures, the removal of macropores, and the reduction of the surface area.

• Resources Recycling
• /
• v.8 no.4
• /
• pp.57-63
• /
• 1999

Wood-Polymer Composites (WPC) m s prepared irom recycled films of agricullural use and wood wastes, and LLDPE and neal PE resin mlxlurr war also utilized in order to cornpiue the praperlies. Molc~ca nhydride (MA) and dicumyl peroxide were used as an adheslon pmmoler and an il~lliatotor~, .espcmivelyT. ensile prapenies of W Cw zrc measured via lenslle test as a funclieu of woad lille~m d MA contmt, and rractu1.e surface was also mvestigaled wilh SEM. As the content of wwd tiller mcreased, clongauon deneased bul modulus increased However, tensile slrength OI WPC increased only when MA war used, and 1 wt.% of MA may be hgh enough to increase the tensile properties. The tensilc ptopcrlies af WPC prepwed from recycled PE films were &nost same as thosc of neal PE resin mixture.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.4 no.2
• /
• pp.133-138
• /
• 2006

Chemical wastes containing small amounts of uranium can not be disposed of them after treatment as an industrial waste, because the uranium concentration in the final dry cake exceeds the exemption level. Especially for the removal of uranium in this study, the method for immobilizing Diphosil powder within alginate beads is adopted to make a bead form from a powdered resin. Sodium alginate bead itself showed a capability to uptake uranium to above 60%, but the value was decreased to below 30% after equilibrium. The adsorption rate of uranium increased with the increasing content of Diphosil in the sodium alginate bead. Diphosil resin itself showed very fast uptake of uranium from early stages, and then the rates were leveled off. Diphosil bead showed an improved capability to uptake uranium considering the pure Diphosil content in the composite bead, and provide a considerable potential for further applications of a continuous process by using Diphosil as a bead form.

• Journal of Conservation Science
• /
• v.26 no.3
• /
• pp.325-334
• /
• 2010

In order to clarify the effect of consolidant, the artificial porous material with low intensity was manufactured using granite powder and Portland cement. We have prepared four kinds of alkoxysilane system consolidants, a acrylic resin and a epoxy resin and investigated about characteristics before and after consolidation. As a result of the research, Silres BS OH 100 was effective for density and surface hardness. SS-101 with hydrophobicity and Site SX-RO with hydrophilicity had the good durability over salts weathering. On the other hand, Syton HT-50 and Paraloid B72 were easily destructed by salt weathering because they were concentrated on surface area by the low penetration depth. Araldite 2020 was the most effective consolidant for improvement of physical properties.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.5
• /
• pp.1161-1171
• /
• 1993

Model materials are developed to achieve similarity of flow patterns for mild steels in forming processes at high temperatures. The model materials consist of pure plasticine and one or two additives such as resin and lanolin. To verify the similarity of flow patterns between physical modeling and compression of mild steels at high temperatures, ring and compression tests have been carried out with the developed-model materials at various strain rates, temperatures and lubricants. The test results are in good agreement with the flow patterns obtained from upsetting of a mild steel at high temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.12
• /
• pp.792-796
• /
• 2015

With high integration of electronic components, power inductors are also miniaturized. Recently, thick film processes for small size power inductors were developed and commercialized. However, the thick film process to prepare soft magnetic green sheets was not reported enough. In this study, we used Fe-Si magnetic and CIP (carbonyl iron powders) as starting materials to lead to a bimodal particle size distribution in the sheet. We proposed a newly developed 'Modified slurry preparation process' to get well dispersed condition even at high solid contents. Using the new process, it was possible to prepare a well dispersed slurry over 70 vol% of solid. BYK-103 was better than BYK-111 as dispersant in this slurry and the optimum amount was 0.6 wt%. The optimized slurry was formed into a sheet by tape casting process and then the sheet was laminated. We conformed that small size powder, large size powder, and epoxy resin were well dispersed in the green sheet.

• Polymer(Korea)
• /
• v.24 no.6
• /
• pp.845-853
• /
• 2000

The optimum cure cycle and carbonization condition were selected by the DSC and TGA analysis and green bodies were prepared by the method of hot press molding and then carbonized up to 140$0^{\circ}C$. Additives such as graphite powder, carbon black, milled carbon fiber and carbon fiber mat, which were considered to be effective in improving the interlaminar shear strength, were also added to check their effects on the density and porosity of products. Then, their relations with mechanical properties such as ILSS and flexural strength were investigated. The composites added 9 vol% of graphite powder showed the greatest values of ILSS and flexural strength. Otherwise, in case of adding carbon black, the composites showed the slight improvement of ILSS at its contents of 3 vol% but the flexural strength was decreased. When milled carbon fiber and carbon fiber mat were added, the lack of resin and the heat shrinkage during the carbonization caused the delamination, resulting in decreasing the density, ILSS and flexural strength.

• Journal of the Korean Society of Safety
• /
• v.27 no.6
• /
• pp.78-83
• /
• 2012

In this study, some experimental results of the peroxide-degradation process of polypropylene(PP) in a co-rotating twin-screw extruder to produce controlled rheology polypropylene(CRPP) are presented. The peroxide was dicumyl peroxide(DCP) and the concentration of DCP was in the range 0-0.3 wt%. It was found that the rheological properties of PP change significantly during reactive extrusion. Melt flow index(MFI) increased with DCP concentration. Intrinsic viscosity decreases with increasing DCP concentration. From dynamic rheological data, number average molecular weight(Mn), weight average molecular weight(Mn) and molecular weight distribution(MWD) were calculated. Results indicated that Mw decreases and MWD becomes narrower with increasing peroxide concentration. Especially, particle size distribution of CRPP decreases with increasing DCP concentration by chemical powdering process, and anti-slip floor paint, CRPP(DCP 0.2 wt%) powder by 10phr was friction coefficient 2.15 ${\mu}$, abrasion resistance 511.18%.

• Proceedings of the SAREK Conference
• /
• 2008.11a
• /
• pp.369-374
• /
• 2008

This study is an inorganic foaming ceramic by sol-gel reaction in order to overcome weak point of insulator using in construction equipment. We shall be able to confirm as the existing product substitute is possible result of this study. The solution where the silicate, the ceramic powder and the additive are included which makes foaming ceramic slurry, then the insulator made by used $CO_2$ Sol-Gel reaction. There being will be able to manufacture the insulator where the economical efficiency is excellent confirmed at the start product which is completed. The recording gel time decreases when the silicate will increase. Uses the hydrogen peroxide and fe make foam, when additionally surface preparation the fluorine resin, the water tolerance increases and will be able to complement the weak point of the silicate which omits in the water. The case which will use the loess powder with the research method which sees specially was environment-friendly product and according to appearing, the physical properties of nonflammability.

• Composites Research
• /
• v.20 no.5
• /
• pp.49-55
• /
• 2007

Nanocomposite blade for dicing semiconductor wafer is investigated for micro/nano-device and micro/nano-fabrication. While metal blade has been used for dicing of silicon wafer, polymer composite blades are used for machining of quartz wafer in semiconductor and cellular phone industry in these days. Organic-inorganic material selection is important to provide the blade with machinability, electrical conductivity, strength, ductility and wear resistance. Maintaining constant thickness with micro-dimension during shaping is one of the important technologies fer machining micro/nano fabrication. In this study the fabrication of blade by wet processing of mixing conducting nano ceramic powder, abrasive powder phenol resin and polyimide has been investigated using an experimental approach in which the thickness differential as the primary design criterion. The effect of drying conduction and post pressure are investigated. As a result wet processing techniques reveal that reliable results are achievable with improved dimension tolerance.