• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.322-323
• /
• 2012

This study discussed the formation of phosphate conversion coatings on AZ31 Mg alloy (AZ31) from the zinc phosphating bath with various concentrations of sodium fluoride (NaF). The effects of NaF on the formation, structure, composition and electrochemical behavior of the phosphate coatings were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD) weight balances, open circuit potential (OCP) transients, potentiodynamic polarization curves and immersion test. The coatings were composed of two layers: an outer $Zn_2(PO_4)_3.4H_2O$ (hopeite) crystal layer and an inner amorphous of $MgZn_2(PO_4)_2$. NaF concentration is emphasized to be highly effective in the formation of the hopeite crystal and etching and coating rates. Potentiodynamic polarization and immersion test showed that the coatings formed in the zinc phosphating bath with addition of NaF have much higher corrosion resistance than bare AZ31.

• 대한금속재료학회지
• /
• 제47권9호
• /
• pp.558-566
• /
• 2009

The alloying effect of a small amount of nickel on low alloy steel for application to flue gas desulfurization(FGD) systems was studied. The structural characteristics of the rust layer were investigated by scanning electron microscopy(SEM). The electrochemical properties were examined by means of potentiostatic polarization test, potentiodynamic polarization test, and electrochemical impedance spectroscopy(EIS) in a modified green death solution of 16.9 vol.% $H_2SO_4$+0.35 vol.% HCl at $60^{\circ}C$ and an acid rain solution of $6.25{\times}10^{-5}M\;H_2SO_4+5.5{\times}10^{-3}M\;NaCl$ at room temperature. It was found that as the amount of nickel increased, the corrosion rate increased in the modified green death solution, which seemed to result from micro-galvanic corrosion between NiS and alloy matrix. In acid rain solution, the corrosion rate decreased as the amount of nickel increased due to the repulsive force of $NiFe_2O_4$ rust against $Cl^-$ ions by electronegativity.

• Corrosion Science and Technology
• /
• 제20권6호
• /
• pp.475-483
• /
• 2021

Additively manufactured titanium alloy is one of the promising materials in advanced medical industries. However, these additively manufactured alloys show corrosion properties different from those of conventional materials due to their unique microstructure. In this study, the effect of surface roughness and masking conditions on the results of the potentiodynamic polarization tests on additively manufactured or conventional Ti-6Al-4V alloys in artificial saliva solution with or without fluoride was investigated. The results showed that the corrosion potential was slightly lower with a flat cell with an O-ring than with masking tape. The corrosion rate was decreased with decreases in the surface roughness. Localized corrosion involving delamination of the surface layer occurred at 7 ~ 9 V (SSC) on the additively manufactured alloy in solution with or without fluoride when the samples were finished with 1000-grit SiC paper, whereas localized corrosion was not observed in the specimens finished with 1-㎛ alumina paste.

• Nuclear Engineering and Technology
• /
• 제54권6호
• /
• pp.2329-2333
• /
• 2022

Base metal corrosion forms a significant issue during the chemical decontamination of the primary coolant loop in nuclear power plants as it is directly related to the economic and safety viability of decommissioning. In this technical note, potentiodynamic evaluations of several base metals (304 stainless steel, SA106 Grade B carbon steel, and alloy 600) were performed to determine their corrosion behavior during the hydrazine (N₂H₄)-based reductive ion decontamination (HyBRID) process. The results suggested that N₂H₄ protected the surface of the base metals in the HyBRID solution, which is primarily composed of H₂SO₄. The corrosion resistance of the carbon steel was further improved through the addition of CuSO₄ to the solution. The corrosion rate of carbon steel in the H₂SO₄-N₂H₄-CuSO₄ solution was lower than that exhibited in an oxalic acid solution, a commonly used reaction medium during commercial decontamination processes. These results indicate the superiority of the HyBRID process with respect to the base metal stability.

• Corrosion Science and Technology
• /
• 제21권2호
• /
• pp.138-146
• /
• 2022

The cavitation and potentiodynamic polarization experiments were conducted simultaneously to investigate the effect of cavitation amplitude on the super austenitic stainless steel (UNS N08367) electrochemical behavior in seawater. The results of the potentiodynamic polarization experiment under cavitation condition showed that the corrosion current density increased with cavitation amplitude increase. Above oxygen evolution potential, the current density in a static condition was the largest because the anodic dissolution reaction by intergranular corrosion was promoted. In the static condition, intergranular corrosion was mainly observed. However, damage caused by erosion was observed in the cavitation environment. The micro-jet generated by cavity collapse destroyed the corrosion product and promoted the repassivation. So, weight loss occurred the most in static conditions. After the experiment, wave patterns were formed on the surface due to the compressive residual stress caused by the impact pressure of the cavity. Surface hardness was improved by the water cavitation peening effect, and the hardness value was the highest at 30 ㎛ amplitude. UNS N08367 with excellent mechanical performance due to its high hardness showed that cavitation inhibited corrosion damage.

• Corrosion Science and Technology
• /
• 제21권2호
• /
• pp.147-157
• /
• 2022

Electrochemical characteristics and damage behavior of 6061-T6 aluminum alloy used as a battery housing material for electric vehicles were investigated in solution simulating the acid rain environment with chloride concentrations. Potentiodynamic polarization test was performed to analyze electrochemical characteristics. Damage behavior was analyzed through Tafel analysis, measurement of damage area, weight loss, and surface observation. Results described that corrosion current density was increased rapidly when chloride concentration excceded 600 PPM, and it was increased about 7.7 times in the case of 1000 PPM compared with 0 PPM. Potentiodynamic polarization experiment revealed that corrosion damage area and mass loss of specimen increased with chloride concentrations. When chloride concentration was further increased, the corrosion damage area extended to the entire surface. To determine damage tendency of pitting corrosion according to chloride concentration, the ratio of damage depth to width was calculated. It was found that the damage tendency decreased with chloride concentrations. Thus, 6061-T6 aluminum alloy damage becomes larger in the width direction than in the depth direction when a small amount of chloride is contained in an acid rain environment.

• 한국표면공학회지
• /
• 제55권4호
• /
• pp.236-246
• /
• 2022

Electropolishing is a surface finishing treatment that compensates for the disadvantages of the mechanical polishing process. It not only has a smooth surface, but also improves corrosion resistance. Therefore, the purpose of this investigation is to examine the corrosion resistance and electrochemical characteristics in seawater of UNS S31603 with electropolishing process time. The roughness improvement rate after electropolishing was improved by about 78% compared to before polishing, indicating that the electropolishing is effective. As a result of potential measuring of mechanical polishing and electropolishing, the potential of electropolishing was nobler than the mechanical polishing condition. As a result of calculating the corrosion current density after potentiodynamic polarization experiment with electropolishing conditions, the corrosion current density of mechanical polishing was about 6.4 times higher than that of electropolishing. After potentiodynamic polarization experiment with electropolishing conditions, the maximum damage depth of mechanical polishing was about 2.2 times higher than that of electropolishing(7 minutes). In addition, the charge transfer resistance of the specimen electropolished for 7 minutes was the highest, indicating improved corrosion resistance.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 봄 학술논문 발표대회
• /
• pp.281-282
• /
• 2023

The solid-state reference electrodes made of polyaniline-coated MnO₂ (SSRE-PAM) and their electrochemical characteristics were studied in simulated concrete pore solutions (SCPS) containing 0 and 3.5% NaCl. Saturated calomel electrodes (SCE) have been used to conduct electrochemical studies on the stability behavior of SSRE-PAM. Open circuit potential (OCP) and potentiodynamic polarization techniques were used to assess the corrosion performance of steel rebar exposed in SCPS with 0 and 3.5% NaCl using SSRE-PAM. The results demonstrate that the SSRE-PAM was capable of identifying steel rebar in a concrete environment that was either passive or active. Potentiodynamic polarization parameters such as E_corr and I_corr for steel rebar in SCPS containing 0 and 3.5%)NaCl are greater than that of the passive condition (0% NaCl). All the studies validate the importance of using SSRE-PAM for corrosion monitoring applications in concrete structures.

• Corrosion Science and Technology
• /
• 제22권5호
• /
• pp.314-321
• /
• 2023

The aim of the present study was to investigate the effect of thymus extract on corrosion inhibition of aluminum 5083 alloy in a 0.1 M NaCl medium prepared using a mixture of ethylene glycol and water using potentiodynamic and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic electrochemical technique showed an increase in corrosion inhibition efficiency starting from 49.63% at a concentration of 0.25 g/L to 92.71% at a maximum concentration of 1.25 g/L of the extract. These results were consistent with those obtained via EIS analysis. Spectral characterization of the tested plant extract using the Fourier-transform infrared spectroscopy (FTIR) technique confirmed the presence of organic compounds having different oxygen and aromatic functionalities in the extract that could help enhance the adsorption of these compounds on the aluminum surface. This study reveals possible adsorption isotherm of the thymus extract on the aluminum surface, supporting a Langmuir isotherm for the adsorption of inhibitor molecules on this surface.

• 대한치과기공학회지
• /
• 제30권1호
• /
• pp.25-31
• /
• 2008

Cp-Ti and Ti-6Al-4V alloys commonly used dental implant materials, particularly for orthopaedic and osteosynthesis because of its suitable mechanical properties and excellent biocompatibility. This alloys have excellent corrosion behavior in the clinical environment. The first factor to decide the success of dental implantation is sufficient osseointegration and high corrosion resistance between on implant fixture and its surrounding bone tissue. In this study, in order to increase corrosion resistance and biocompatibility of Cp-Ti and Ti-6Al-4V alloy that surface of manufactured alloy was coated with TiN by RF-magnetron sputtering method. The electrochemical behavior of TiN coated Cp-Ti and Ti-6Al-4V alloy were investigated using potentiodynamic (EG&G Co, PARSTAT 2273. USA) and potentiostatic test (250mV) in 0.9% NaCl solution at 36.5 $\pm$ 1$^{\circ}C$. These results are as follows : 1. From the microstructure analysis, Cp-Ti showed the acicular structure of $\alpha$-phase and Ti-6Al-4V showed the micro-acicular structure of ${\alpha}+{\beta}$ phase. 2. From the potentiodynamic test, Ecorr value of Cp-Ti and Ti-6Al-4V alloys showed -702.48mV and -319.87mV, respectively. Ti-6Al-4V alloy value was higher than Cp-Ti alloy. 3. From the analysis of TiN and coated layer, TIN coated surface showed columnar structure with 800 nm thickness. 4. The corrosion resistance of TiN coated Cp-Ti and Ti-6Al-4V alloys were higher than those of the non-coated Ti alloys in 0.9% NaCl solution from potentiodynamic test, indicating better protective effect. 5. The passivation current density of TiN coated Cp-Ti and Ti-6Al-4V alloys were smaller than that of the noncoated implant fixture in 0.9% NaCl solution, indicating the good protective effect resulting from more compact and homogeneous layer formation.