• Journal of the Korean Magnetics Society
• /
• v.25 no.5
• /
• pp.144-148
• /
• 2015

We grew spinel structured $CoMn_2O_4$ thin films and have studied post-growth annealing effects on their physical properties. After post-growth annealing at $700^{\circ}C$ that is lower than the growth temperature ($720^{\circ}C$), crystal structure became cleared accompanying a change of surface structure. In the temperature dependences of magnetization, phase transitions were observed at ~100 K for both before and after post-growth treated samples which were not observed for the bulk. For both samples, ferromagnetic behaviors were observed above 100 K while it turned to ferrimagnetism at low temperature below 100 K. In particular, the ferrimagnetic behavior became strong after the post-growth treatment. These results indicate that the post-growth annealing process plays an important role in determining the physical properties of spinel $CoMn_2O_4$ thin film.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.1
• /
• pp.28-32
• /
• 2000

Structural and electrical properties of (Ba, Sr)TiO\ulcorner (BST) thin films prepared by pulsed laser depositon were investigated to verify the influences of post-annealing in oxygen ambient. Increase of post-anneal-ing time in oxygen ambient resulted in not only grain growth but also improvement of crystallinity of BST films. Although the post-annealing in oxygen ambient resulted in the increase of surface roughness, it assisted the dielectric constant increase by eliminating oxygen vacancies. The electrical property enhancement including high dielectric constant and low leakage current density was associated with introducing high pressure of oxygen during the post-annealing.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.5
• /
• pp.247-252
• /
• 2002

$(Pb_{1-x}La_x)TiO_3$ (x = 0.1) thin films were prepared on ITO-coated glass substrates by metal organic chemical vapor deposition using ultrasonic spraying. Effects of the post-annealing and the seeding layer on crystallization, microstructures and electrical properties of thin films were investigated. Dielectric constants of films increased due to the modification of crystallization and the changing of a surface morphology by applying the post-annealing. In addition, as the application of PT seed- ing layer offered nucleation sites to PLT thin films, electrical properties of films were enhanced by the increase of crys-tallinity and grain size. The dielectric constant of the films post-heated for 60 min and with a seeding layer was 213 at 1 kHz.

• Journal of the Korean Magnetics Society
• /
• v.21 no.3
• /
• pp.93-98
• /
• 2011

We successfully grew $La_{0.35}Pr_{0.35}Ca_{0.3}MnO_3$(LPCMO)/$LaAlO_3$(LAO) thin film using Laser Molecular-Beam Epitaxy and studied post-growth annealing effects ($750^{\circ}C$, 5 h) on its crystal structural and magnetic properties. Whereas the single-layered LPCMO and LPCMO/STO superlattice thin films show rough surface before and after the post-growth annealing, LPCMO/LAO superlattice shows a relatively very flat surface even after the post-growth annealing. The enhancement of ferromagnetism of LPCMO/LAO superlattice after the post-growth annealing was remarkable compared to the single-layered LPCMO thin film. The coercive and saturation magnetic field of the single-layed LPCMO thin film were decreased after the post-annealing. However, for LPCMO/LAO superlattice, a same coercive and increased saturation magnetic field were exhibited after post-growth annealing. We suggest that these peculiar observations are originate from the super-structure of LPCMO and LAO.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.61-62
• /
• 2005

The present article deals with in situ post annealing of ZnO in sputtering system. The ZnO thin films were grown at low temperature of $100^{\circ}C$ and at working pressure of 15 mTorr with RF magnetron sputtering. Having been gown, ZnO thin films were annealed in situ at different temperatures, at annealing ambient pressure of 15 mTorr and in ambients of oxygen and argon respectively. Through analyses of XRDs, it is can be concluded that the crystallinity of annealed ZnO thin films becomes much better than that of as-grown ZnO thin film.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.203-203
• /
• 2015

Gallium Oxide (Ga2O3) has been widely investigated for the optoelectronic applications due to its wide bandgap and the optical transparency. Recently, with the development of fabrication techniques in nanometer scale semiconductor materials, there have been an increasing number of extensive reports on the synthesis and characterization of Ga2O3 nano-structures such as nano-wires, nano-belts, and nano-dots. In contrast to typical vapor-liquid-solid growth mode with metal catalysts to synthesis 1-dimensional nano-wires, there are several difficulties in fabricating the nano-structures by using sputtering techniques. This is attributed to the fact that relatively low growth temperatures and higher growth rate compared with chemical vapor deposition method. In this study, Ga2O3 nanowires (NWs) were synthesized by using radio-frequency magnetron sputtering method. The NWs were then coated by Au thin films and annealed under Ar or N2 gas enviroment with no supply of Gallium and Oxygen source. Several samples were prepared with varying the post annealing parameters such as gas environment annealing time, annealing temperature. Samples were characterized by using XRD, SEM, and PL measurements. In this presentation, the details of fabrication process and physical properties of branched Ga2O3 NWs will be reported.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.18 no.1
• /
• pp.50-55
• /
• 2008

AI-doped ZnO(AZO) thin films have been fabricated on glass substrate by sol-gel method, and the effect of Al precursors and post-annealing temperature on the characteristics of AZO thin films was investigated. The sol was prepared with zinc acetate, EtOH, MEA and Al precursors. In order to dope Al in ZnO, two types of aluminum nitrate and aluminum chloride were used as Al precursor. Zinc concentration was 0.5 mol/l and the content of Al precursor was 1 at% of Zn in the sol. The sol was spin-coated on glass substrate, and the coated films were annealed at 550ue for 2 hand were post-annealed at temperature ranges of $300{\sim}500^{\circ}C$ for 2 h in reducing atmosphere ($N_2/H_2$= 9/1). Structural, electrical and optical propertis of the fabricated AZO thin films were analyzed by XRD, FE-SEM, AFM, hall effect measurement system and UV-visible spectroscopy. Optical and electrical properties of AZO thin films prepared with aluminum nitrate as Al precursor were better than those of films prepared with aluminum chloride. The electrical resistivity and the optical transmittance of films decreased with increasing post-annealing temperatures. The minimum electrical resistivity of $2{\times}10^{-3}$ and the maximum optical transmittance of 91% were obtained for the AZO thin films post-annealed at $550^{\circ}C\;and\;300^{\circ}C$, respectively.

• The Korean Journal of Ceramics
• /
• v.6 no.2
• /
• pp.110-115
• /
• 2000

$SrBi_2Ta_2O_9$ thin films were deposited at room temperature on the usual (111) oriented Pt bottom electrodes using r.f. magnetron sputtering, and then post-annealed at 650-$800^{\circ}C$ for 30min in oxygen flow. Low temperature processing which shows the preferred oriented SBT thin films was obtained by controlling the sputtering pressure and/or Sr content in target. The orientation and grain growth behavior of SBT thin films were dependent on Sr contents in films. With increasing the excess Bi content up to 50% in SBT thin films, it was possible to lower the onset temperature of grain growth. The c-axis preferred oriented SBT thin films were well-grown under the condition of low post-annealing($650^{\circ}C$) by lowering post-annealing pressure. After $10^{11}$ switching cycles, no polarization degradation was observed in both preferred oriented SBT capacitors.

• Korean Journal of Materials Research
• /
• v.31 no.6
• /
• pp.320-324
• /
• 2021

Effects of growth variables and post-growth annealing on the optical, structural and electrical properties of magnetron-sputtered Ga_0.04Mg_0.10Zn_0.86O films are characterized in detail. It is observed that films grown from pure oxygen plasma showed high resistivity, ~10² Ω·cm, whereas films grown in Ar plasma showed much lower resistivity, 2.0 × 10^-2 ~ 1.0 × 10^-1 Ω·cm. Post-growth annealing significantly improved the electrical resistivity, to 4.3 ~ 9.0 × 10^-3 Ω·cm for the vacuum annealed samples and to 1.3 ~ 3.0 × 10^-3 Ω·cm for the films annealed in Zn vapor. It is proposed that these phenomena may be attributed to the improved crystalline quality and to changes in the defect chemistry. It is suggested that growth within oxygen environments leads to suppression of oxygen vacancy (Vo) donors and formation of Zn vacancy (V_Zn) acceptors, resulting in highly resistive films. After annealing treatment, the activation of Ga donors is enhanced, Vo donors are annihilated, and crystalline quality is improved, increasing the electron mobility and the concentration. After annealing in Zn vapor, Zn interstitial donors are introduced, further increasing the electron concentration.

• Korean Journal of Materials Research
• /
• v.15 no.11
• /
• pp.741-744
• /
• 2005

Atomic layer deposition (ALD) is a very promising deposition technique for ZnO thin films. However, there have been very few reports on ZnO grown by ALD. Effects of substrate temperature in both ALD and post annealing on the microstructure and PL properties of ZnO thin films were investigated using X-ray diffraction, photoluminescence, and scanning electron microscopy. The temperature window of ALD is found to be between $130-180^{\circ}C$. The growth rate of ZnO thin film increases as the substrate temperature increases in the temperature range except the temperature window. The crystal quality depends most strongly on the substrate temperature among all the growth parameters of ALD. The crystallinity of the film is improved by increasing the growth thine per ALD cycle or doing post-annealing treatment. The grain size of the film tends to increase and the grain shape tends to change from a worm-like longish shape to a round one as the annealing temperature increases from $600^{\circ}C\;to\;1,000^{\circ}C$.