• Membrane Journal
• /
• v.10 no.3
• /
• pp.121-129
• /
• 2000

The membrane requires both high in selectivity and flux. However, the permselective membrane has low flux. In this study, the porous alumina membrane was coated with silane coupling agent in order to enhance the flux with proper selectivity. The contact angle of water to the surface-modified alumina membrane was greater than 90$^{\circ}$, which indicated the high hydrophobicity. The modified membrane was tested in vapor permeation for the concentration of aqueous ethanol, isopropanol, and n-butanol. With the increase of ethanol, isopropanol, butanol concentration in the feed, permeation flux increased due to the greater affinity of ethanol, isopropanol, butanol with surface-modified alumina membrane than that of water. The experimental results showed that the permeation tate of surface-modified alumina membrane was 20~1000 times greater than that of a polymer membranes.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.2
• /
• pp.349-352
• /
• 2014

Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i.e., meshed pore, was produced.

• Membrane Journal
• /
• v.10 no.4
• /
• pp.186-191
• /
• 2000

The recovery of three ethyl esters (aroma model compounds; ethyl acetate, ethyl propionate. ethyl butyrate) from aqueous solutions was studied for vapor permeation with surface-modified hydrophobic alumina membrane, Although the driving force of ethyl butyrate is the highest, the ethyl butyrate concentration in permeate is lower than those of propionate and acetate. Since the solubility of aroma compounds for water is very low, phase separation occurred in permeate, and we could obtain pure ethyl esters. The experimental results showed that the porous hydrophobic alumina membrane had high selectivity and permeation flux on the ester-model compounds.

• Journal of Environmental Science International
• /
• v.9 no.4
• /
• pp.311-318
• /
• 2000

To improve $CO_2$pemselectivity, a modified silica membrane was prepared by chemical vapor deposition with tetraethoxysilane(TEOS)-ethanol-water, and TEOS-ethanol-water-HCI solution at 300-$600^{\circ}C$. The silica was effectively deposited in the mesopores of a ${\gamma}$-alumina film coated on a porous $\alpha$-alumina tube by evacuating the reactants through the porous wall. In this membrane, $CO_2$interacts, to some extent, with the pore wall, and $CO_2$/$N_2$selectivity then exceeds the value of the Knudsen diffusion mechanism, while the membrane derived from TEOS alone has no $CO_2$selectivity. The silica membrane prepared from TEOS-ethanol-water-HCI solution showed that $CO_2$permeance was $2.5$\times$10^{-7}mol/s^{-1}.m^{-2}.Pa^{-1} at 30{\circ}C$ and $CO_2$/$N_2$selectivity was approximately 3. The $CO_2$permeance and selectivity was improved by enlarging the surface diffusion with modification of chemical affinity of the silica pores.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.205-210
• /
• 2002

The HPS(High Porosity Support, 39.3%) and the LPS( Low Porosity Support, 18.7%) were fabricated to investigate the phase transformation and the chance of microstructure with porosity of alumina support. Alumina sol was made using aluminum tri-sec $butoxide(ATSB,\; Al(O-Bu)_3)$, the membrane on porous support with different porosity and the membrane without support were fabricated. The $\theta$-to ${\alpha}-A1_2O_3$ phase transformation in the membranes was investigated using thin film X-ray diffraction (XRD), and the change of microstructure was observed using scanning electron microscopy(SEM). XRD patterns showed that the membrane on LPS and HPS had 10$0^{\circ}C$, 5$0^{\circ}C$ higher $\theta$-to ${\alpha}-A1_2O_3$ transformation temperature compared to the unsupported membrane. A similar effect was also observed in microstructure of the membranes, theoritical temperature difference were 97$^{\circ}C$ and 44$^{\circ}C$ by Crapeyron equation.

• Membrane Journal
• /
• v.15 no.2
• /
• pp.105-113
• /
• 2005

Silica membranes were prepared on a porous metal sheet by ultrasonic spray pyrolysis method for gas separation at high temperatures. In order to improve the permselectivity, silica was deposited in the sol-gel derived $silica/\gamma-alumina$ intermediate layer by pyrolysis of tetraethyl orthosilicate (TEOS) at 873 K. The pyrolysis with forced cross flow through the porous wall of the support was very effective in plugging mesopores, Knudsen diffusion regime, that were left unplugged in the membranes. At permeation temperature of 523 K, the silica/alumina composite membrane showed $H_2/N_2$ and water/methanol selectivity as high as 17 and 16, respectively, by molecular sieve effect.

• Applied Chemistry for Engineering
• /
• v.10 no.2
• /
• pp.212-217
• /
• 1999

Porous alumina membrane with asymmetrical structure was prepared by anodic oxidation under constant DC current mode in aqueous solution of sulfuric acid. In order to produce membrane with improved properties, the aluminium plate was pre-treated with thermal oxidation, chemical polishing and electrochemical polishing before anodic oxidation. The thickness and pore diameter of the membrane were controlled by current density and charge density, respectively. The upper layer of 20 nm under of pore diameter was produced under very low current density while the lower layer of 36 nm pore diameter was produced under higher current density. The thickness of the membrane was about $80{\sim}90{\mu}m$ and that of the upper layer was $6{\mu}m$. We found that the mechanism of gas permeation through the membrane depended on Knudsen diffusion.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.364-365
• /
• 2006

One of the promising routes for producing highly ordered nanostructures is a template method using the porous alumina membrane (PAM). Because the PAM is mechanically, chemically, thermally stabile with highly ordered structure, many researchers have studied under various experimental conditions to fabricate nanostructures. We present the information on the fabrication of about 300 nm nano-mask which have important applications for various patterned nanostructures.

• Journal of the Korean Ceramic Society
• /
• v.39 no.12
• /
• pp.1153-1157
• /
• 2002

The fabrication of a three-layered asymmetric ceramic membrane was performed by slip casting of the porous alumina support and dip coating of the alumina intermediate layer using high purity ${\alpha}-Al_2O_3$ powders that have different particle size, followed by screen printing-pyrolysis of the $Tio_2$ layer as an ultrafilteration membrane using Ti-naphthenate solution. The bending strength, porosity and mean pore size of the alumina support were 231 kg/$cm^2$s, 30.26% and 0.19 ${mu}m$, respectively. The thickness of the intermediate layer was 30 ${mu}m$ and the mean pore size of that was 0.063 ${mu}m$. Also, the top layer was 0.5 ${mu}m$ thick and micropores with about 20 nm size were formed uniformly.

• Journal of Hydrogen and New Energy
• /
• v.31 no.2
• /
• pp.177-183
• /
• 2020

To utilize hydrogen energy, high-yield, high-purity hydrogen needs to be produced; therefore, hydrogen separation membrane studies are being conducted. The membrane reactor that fabricates hydrogen needs to have high hydrogen permeability, selective permeability, heatresistant and a stable mechanical membrane. Dense membranes of Pd and Pd alloys are usually used, but these have drawbacks associated with high cost and durability. Therefore, many researchers have studied replacing Pd and Pd alloys. Dense TiN membrane is highly selective and can separate high-purity hydrogen. The porous alumina has a high permeation rate but low selectivity; therefore, separating high-purity hydrogen is difficult. To overcome this drawback, the two materials are combined as composite reclamations to produce a separation membrane with a high penetration rate and high selectivity. Accordingly, TiN-alumina was manufactured using a high-energy ball mill. The TiN-alumina membrane was characterized by X-ray diffraction analysis, scanning electron microscopy, and energy dispersive spectroscopy. The hydrogen permeability of the TiN-alumina membrane was estimated by a Sievert-type hydrogen permeation membrane apparatus. Due to the change in the diffusion mechanism, the transmittance value was lower than that of the general TiN ceramic separator.