• Journal of the Korea institute for structural maintenance and inspection
• /
• v.3 no.4
• /
• pp.179-189
• /
• 1999

This study attempts to propose an evaluation considering the property of concrete pore which affects the deterioration of neutralization and the rebar resistance of concrete. Understanding pore property of concrete in using extent, for practical using of concrete manufacturing condition. basic quality property and durability estimation etc, the results of the experiment are as follows. 1) The result of analysis pore property of every specimen with the method of area ratio, in limitation of $10^{-6}{\sim}10^{-5}m$, the pore distribution ratio was maximum. It was high value as W/C was increased and the unit cement content was decreased. 2) In case of using admixture. the volume of pores was some increased as variation of mixing content. In high W/C range, it was very increased compared with plain concrete. 3) Concerned with compressive strength and volume of pores in hardened concrete, it is possible compressive strength estimation using the property of concrete pores. 4) Direct measurement of concrete pore property is difficult. the valuation of the dynamic modulus of elasticity using ultrasonic wave velocity was available. 5) Quantitatively evaluation of concrete structure durability by past result of pore distribution estimation, and it can be estimative scale of property study on the concrete materials.

• Textile Coloration and Finishing
• /
• v.26 no.3
• /
• pp.218-229
• /
• 2014

The wearing comfort of garment is governed by two kinds of characteristics such as moisture and thermal transport properties and mechanical properties of fabrics. The porosity influenced by yarn and fabric structural parameters is known as main factor for wearing comfort of garment related to the moisture and thermal transport properties. This study investigated effect of porosity of composite yarns to the moisture and thermal comfort properties of composite fabrics made of hollow composite DTY and ATY yarns. The theoretical porosity and pore size were inversely proportional to cover factor of fabric, but cover factor was not correlated with experimental pore size. The wicking property of hydrophobic PET filament fabric showed inferior result irrespective of porosity, pore size and cover factor. The drying rate was superior at composite fabrics with high pore size and low cover factor, and pore size was dominant factor for drying property. On the other hand, thermal conductivity of composite fabric was mainly influenced by cover factor and not influenced by porosity. Air permeability was influenced by both porosity and cover factor and was highly increased with increasing porosity and decreasing fabric cover factor.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.6
• /
• pp.703-712
• /
• 2018

The sound absorption property, hand feel, air permeability and pore size of 25 kinds of traditional Korean natural wallpapers (Hanji) were measured and analyzed in this study. The sound absorption rate of Hanji became larger with increasing of frequency beginning from 3.2 kHz, reached 2 times in frequency range of nearby 4 kHz. The sound absorption rate of Hanji was increased as the permeability was lowered and the pore size was decreased. The sound absorption property of Hanji wallpaper could be improved by manufacturing process such as super calendering process.

• Science of Emotion and Sensibility
• /
• v.17 no.4
• /
• pp.71-78
• /
• 2014

Composite draw textured yarns(DTY) and air jet textured yarns(ATY) with hollow PET filament have been used for making high emotional fabrics including light weight sports wear garments. This study investigated effect of hollow composite yarns and fabric structural parameters to the comfort properties related to the moisture and thermal transport phenomena for the composite fabrics made of DTY and ATY with hollow PET filament. Wicking property of hollow composite fabric was superior at the high pore size fabric and was not influenced by fabric cover factor. Wicking property of the fabric with ATY was better than that of the fabric with DTY. On the other hand, drying rate of fine pore sized fabric was shorter than that of large pore sized fabric and drying rate of high multi yarn fabric with low cover factor and small pore size was superior than that of hollow composite fabric. The pore size of the fabric was dominant factor in the air permeability and thermal conductivity of hollow composite fabric. High pore sized fabric showed high air permeability and thermal conductivity of hollow composite fabric was nonlinearly inversely proportional to pore size of the fabric.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2003.05a
• /
• pp.711-714
• /
• 2003

Factors causing deterioration of concrete structures under marine environment are various, especially penetration and diffusion of chloride ion, carbon dioxide, and water through pore effects on the durability of concrete as well as mechanical properties of concrete. Pore of porous materials like concrete can be classified as micro-, meso-, and macro-pore. And pore of cement matrix is classified as pore which occupied by water, air void, and ITZ between cement paste and aggregates. In this study, to verify the relationship between pore of cement matrix and the property of chloride ion diffusivity, the regression analysis is producted. From the result of regression analysis, the average pore diameter more than total pore volume effects on the diffusivity of chloride ion.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2007.11a
• /
• pp.27-30
• /
• 2007

Recently, use of light-weight panel is increasing in building. Styrofoam sandwich panel is inexpensive and it is excellent in insulation ability and constructability. But styrofoam of panel inside is low ignition point. Consequently, when panel is fired, it is occur in poisonous gas. On the other hand, light-weight foamed concrete is excellent in insulation ability, fire resistance due to inner pore. Properties of light-weight concrete is influenced by foaming agent type. Accordingly, this study investigate in insulation property of according to foaming agent type in order to using light-weight foamed concrete instead of styrofoam. As a results, Non-heating zone temperature of light-weight foamed concrete of using AP, FP are lower than light-weight foamed concrete of using AES. Light-weight foamed concrete of using AES, FP are satisfied with fire performance of two hours at foam ratio 50, 100. Light-weight foamed concrete of using AP is satisfied with fire performance of two hours at AP ratio 0.1, 0.15. Insulation property is better closed pore by made AP, FP than open pore by made AES.

• Journal of the Korean Ceramic Society
• /
• v.32 no.4
• /
• pp.462-470
• /
• 1995

The characteristics of spray-dried granules are important for dry pressing operation since they have great influences on die-filling, compaction ratio, and resulting green microstructure. An attempt was made to control granule morphology and the packing structure of fine Si3N4 particles in granules by adjusting suspension property. Mercury porosimetry was used to characterize the pore structures of both granules and green compacts. Finally, the effects of particle packing structure in granules and green microstructure on sintering behavior were investigated.

• Korean Journal of Materials Research
• /
• v.28 no.1
• /
• pp.50-61
• /
• 2018

Various carbon aerogels (CAs) were prepared from polymerization of resorcinol and formaldehyde and applied as the electrode materials of an electric double layer capacitor (EDLC) with the aim of controlling the textural and electrochemical properties of CAs by the type of base catalyst and the ratio of resorcinol to catalyst (R/C). The CAs from $NaHCO_3$ and $KHCO_3$ with $H^+$ ions had higher specific surface areas but exhibited lower electrochemical properties than those from $K_2CO_3$ and $Na_2CO_3$, which had more uniform pore size distributions. The electrochemical properties of $Na_2CO_3$ were superior to those of $K_2CO_3$ probably because the polarizing power of $Na^+$ ions was higher than $K^+$ ions. With an increasing R/C ratio, the pore sizes of CA showed a tendency to increase but the uniformity of the pore size distribution got worse. For the four base catalysts, the highest electrochemical property was obtained at the R/C ratio of 500.

• Journal of environmental and Sanitary engineering
• /
• v.13 no.3
• /
• pp.19-29
• /
• 1998

The calcination reactivity of limestone and physical property changes of calcined lime were investigated with a temperature($720~1000^{\circ}C$ under atmospheric gas($N_2$, $CO_2$) conditions. The mechanisms of mass transport in a lime matrix were represented by the evaporation and condensation (${\gamma}=1.7$) at $1000^{\circ}C$ and the volume diffusion (${\gamma}=2.7$) at $800^{\circ}C$, which was obtained by the specific surface area of calcined lime with sintering conditions. Also, the effect of physical property on the reactivity of sulfation reaction was determined by the changes of pore size with $lime-SO_2$ reaction in this work. The initial sulfation rate of calcined lime increased with increasing temperature, whereas the capture capacity of $SO_2$ exhibited a maximum value at $900^{\circ}C$. The pore volume of sulfated lime was decreased with increasing sulfation time, but the major pores shifted to the distribution of larger size at a temperature of $850{\;}~{\;}1000^{\circ}C$. The mean pore size of sulfated lime based on pore volume decreased gradually at $1000^{\circ}C$; however, it increased with sulfation time up to 40 min and rapidly decreased thereafter.

• Journal of Powder Materials
• /
• v.10 no.1
• /
• pp.34-39
• /
• 2003

Porous TiNi bodies were produced by Self-propagating High-temperature Synthesis (SHS) method from a powder mixture of Ti and Ni. Porosity, pore size and structure, mechanical property, and transformation temperature of TiNi product were investigated. The average porosity and pore size of produced porous TiNi body are 63% and $216\mutextrm{m}$, respectively. XRD analysis showed that the major phase of produced TiNi body is B2 phase. Its average fracture strength and elastic modulus measured under dry condition were $22\pm2$ MPa and $0.18\pm0.01$GPa, respectively. It could be strained up to 7.3 %. The transformation temperatures determined by DSC showed the $M_s$ temperature of $67^{\circ}C$ and $A_f$ temperature of $99^{\circ}C$.