• Bulletin of the Korean Chemical Society
• /
• 제16권11호
• /
• pp.1099-1104
• /
• 1995

The catalyzed polycondensations of bis(2-hydroxyethyl) naphthalate were kinetically investigated in the presence of various antimony compounds as a catalyst. The polymerization were investigated with various ligand types of antimony oxides, various concentrations of antimony triacetate and titanium/antimony mixed catalysts. The time to reach the maximum molecular weight was remarkably changed in each case. With increasing the concentration of antimony acetate, the propagation rate was largely increased, while the degradation rate was slightly decreased. It also can be seen that the propagation and degradation rate were larger influenced by the equimolecular titanium/antimony mixed catalyst than other mixed catalysts. The temperature dependence of bis(2-hydroxyethyl) naphthalate with antimony triacetate also has been studied. From the results, it was found that the propagation rate was less influenced by a temperature change than the degradation rate.

• 한국식품위생안전성학회지
• /
• 제28권1호
• /
• pp.56-62
• /
• 2013

연구에서는 PEN 수지 안전관리를 위하여 HPLC-UV 검출기를 이용한 2,6-NDC 및 2,6-NDA 분석법을 확립하였다. 분석법 검증 결과, 2,6-NDC 및 2,6-NDA 모두 $0.002{\mu}g/mL$ 검출한계, $0.005{\mu}g/mL$ 정량한계 및 $0.05{\sim}1{\mu}g/mL$의 농도 범위에서 $r^2$= 0.999 이상의 직선성을 확인할 수 있었다. 또한 회수율도 90~110%임을 확인할 수 있었다.

• 한국염색가공학회:학술대회논문집
• /
• 한국염색가공학회 2011년도 제45차 학술발표회
• /
• pp.7-7
• /
• 2011

Poly(ethylene terephthalate)(PET) is one of the most widely used materials in textile industry. It can have a low cost, silk-like handle, and excellent mechanical properties. Low thermal stability of PET had been a common problem limiting its high temperature application. The polyester have been known to have the disadvantage of degradation under ionized irradiation compared to crosslikable polymers such as polyethylene, polypropylene and polystylene. To improve thermal stability of PET, the PET films were photocrosslinked by UV irradiation. A hydrogen-abstractable photoinitiator was used to photocrosslink of PET by continuous UV irradiation. Photoinitiator addition increased the gel fraction. The photocrosslinking was attributed to the recombination of PET radicals generated upon UV irradiation, which was enhanced by the hydrogen abstraction of the PET polymer chains by the added photoinitiator. Also the crosslinked PET showed higher thermal stability and mechanical strength with increasing UV energy. Polyester type films such as poly(ethylene naphthalate)(PEN) and poly(butylene terephthalte)(PBT) were also increased the gel fraction and improved thermal stability and mechanical properties by UV irradiation.

• Journal of the Optical Society of Korea
• /
• 제18권3호
• /
• pp.251-255
• /
• 2014

A fiber diffuser sheet based on poly (ethylene naphthalate) (PEN) and poly (methylpentene) (PMP) has shown potential for liquid crystal display backlight units, but these materials have an interfacial adhesion problem. To improve the interfacial adhesion between the fibers and matrix components, we have proposed the use of amorphous poly (cyclohexane-1,4-dimethylene terephthalate) (Tritan) instead of PEN. Furthermore, the fabrication processes have been optimized and simplified to improve the optical and mechanical properties of the sheet. As a result, the most effective fiber content for achieving the best haze characteristics of a sample consisting of Tritan and PMP has been identified.

• 폴리머
• /
• 제37권6호
• /
• pp.711-716
• /
• 2013

폴리(에틸렌 나프탈레이트)(PEN)의 사슬 배향과 이완이 PEN 유연기판의 치수안정성 및 광학 특성에 미치는 영향에 대하여 살펴보았다. 사슬이 배향된 PEN 기판은 사용온도 증가 시 PEN 분자 유동성을 감소시켜 $100^{\circ}C$ 이하에서 PEN의 열팽창계수(CTE)를 $20ppm/^{\circ}C$까지 감소시키나, 유리전이온도 근처에서 연신된 사슬의 이완에 의하여 열수축이 발생됨을 알 수 있었다. 유리전이온도 근처에서의 열처리는 이러한 열수축을 최소화시킬 수 있으나 사슬이완에 따른 PEN 분자의 경직성 또한 감소되어 열팽창계수가 연신 전 PEN의 고유 CTE의 65% 정도인 $70ppm/^{\circ}C$까지 다시 증가함을 확인하였다. 열처리 과정에서 연신된 필름에 응력을 가하지 않는 경우, 열수축 시작 온도 증가와 함께 열수축을 최소화할 수 있으며 연신에 의해 얻어진 낮은 CTE 또한 유지할 수 있었다. 배향에 의한 광 투과도 감소는 없는 반면 열처리는 미약한 결정화를 발현시켜 5% 정도의 광 투과도가 감소됨을 알 수 있었다.

• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2002년도 International Meeting on Information Display
• /
• pp.746-749
• /
• 2002

Aluminum oxide thin films were grown on a poly ethylene naphthalate (PEN) substrate at the temperature of 100$^{\circ}C$ using atomic layer deposition method. The film showed very flat morphology and good adhesion to the substrate. The visible spectrum showed higher transmittance in the range from 400 nm to 800 nm than that of PEN. The water vapor transmission value measured with MOCON for 230nm oxide-deposited PEN was 0.62g/$m^2$/day @ 38$^{\circ}C$, while that of PEN substrate was 1.4g/$m^2$/day @ 38$^{\circ}C$.

• 대한기계학회논문집B
• /
• 제37권6호
• /
• pp.577-582
• /
• 2013

AZO(Aluminium-doped Zinc Oxide)는 기존의 LCD, OLED, 광센서, 유기태양전지 등의 투명전극에 널리 사용되는 ITO(Indium Tin Oxide)를 대체하기 위한 물질로 주목받고 있다. 본 연구에서는 유기태양전지의 투명 전극으로 많이 사용되는 ITO 를 대체하기 위해 원자층 증착(ALD) 공정의 저온 선택적 증착 특성을 이용하여 유연성 폴리머인 PEN 기판상에 AZO 투명전극을 직접 패턴방식으로 제조하고, 그 투명전극의 구조적, 전기적, 광학적 특성을 평가하였다. 전기적, 광학적 특성 결과들로부터 원자층 증작공정의 저온 선택적 증착 특성을 통해 형성된 AZO 투명전극의 유기태양전지로의 적용 가능성을 확인할 수 있었다.

• Elastomers and Composites
• /
• 제37권4호
• /
• pp.244-257
• /
• 2002

주사슬에 나프탈렌고리와 테트라메틸렌 및 헥사메틸렌 유연격자를 가지면서 트라이어드메소겐을 갖는 새로운 열방성 방향족 액정 폴리에스테르(TLCP)를 용액중합법에 의하여 합성하였다. TLCP의 함량을 달리하는 TLCP/PEN in situ 복합재료를 용융방사하여 연신비가 각각 다른 단섬유를 제조하고 그들의 열적, 기계적 특성 및 모폴로지를 조사하였다. 합성된 TLCP는 네마틱 액정중합체였으며 고체상에서 액정상으로의 전이 온도는 249 ℃였다. 블렌드내의 TLCP 도메인들은 매트릭스 고분자인 PEN에 잘 분산 되었으며 어떠한 거대 상 분리 현상도 보여 주지 않았다. TLCP 함량의 증가에 따른 블렌드내 PEN의 cold crystallization 온도가 낮아진 것으로 보아서 TLCP가 PEN에 대한 조핵제 역할을 하였음을 알 수 있었다. 블렌드 섬유내의 TLCP의 도메인 크기는 대략 40 ~ 50 nm정도의 미세한 크기였으며 매트릭스와의 사이에 좋은 계면 접착력을 보였다. 또한 cold 및 hot-drawing 과정을 거친 낮은 draw ratio(DR)에서는 거의 fibril이 형성되지 않았지만, 높은 DR에서는 잘 발달된 fibril들을 보여 주었다. TLCP의 강화효과로 인하여 10 wt% TLCP/ PEN 블렌드 섬유의 초기 모듈러스는 270 %, 인장강도는 235 %의 증가를 보여주었다. 반면에 신장률은 DR의 증가와 함께 감소 하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.283-284
• /
• 2008

Electrical and optical characteristics of indium tin oxide (ITO) and indium zinc oxide (IZO) films without and with $(SiO_2)_3(ZnO)_7$ at.% (SZO) film deposited on poly(ethylene naphthalate) (PEN) and poly(ethylene terephthalate (PET) substrates as a gas barrier layer for flexible display were studied. The ITO and IZO films with SZO gas barrier layer showed the improved properties which were both the high transmittance of average 80% in the visible light range and the decreased sheet resistance as compared to those of ITO and IZO films without SZO layer. Particularly, the PEN substrate with only SZO gas barrier layer had a low water vapor transmission rate (WVTR) of $\sim10^{-3}g/m^2$/day. Thus, we suggest that the SZO film with protection ability against the water vapor permeation can be applied to gas barrier layer for flexible display.

• 폴리머
• /
• 제35권3호
• /
• pp.249-253
• /
• 2011

PET/PEN 블렌딩에 의하여 발현되는 형태학적 변화가 PET/PEN 블렌드 유연기관 특성에 미치는 영향을 살펴보았다. PET와 PEN의 용융 블렌딩에 따른 two phase 형태학적 변화는 블렌드의 유연기관으로서의 치수안정성을 증가시킴을 알 수 있었다. PET/PEN 필름의 가공조건에 따른 상호에스테르 교환반응은 블렌드의 two phase 형태와 결정화도를 변화시키며 이러한 거시적 형태학적 변화는 유연기관으로서의 PET/PEN 필름의 치수안정성에 영향을 미침을 확인하였다. 결정화도가 높을수록 상호에스테르 교환반응이 낮을수록 PET/PEN 블렌드 필름의 치수안정성이 우수해짐을 알 수 있었다.