• Metals and materials international
• /
• v.24 no.6
• /
• pp.1232-1240
• /
• 2018

Corrosion properties of dissimilar friction stir welded 6061 aluminum and HT590 steel were investigated to understand effects of galvanic corrosion. As cathode when coupled, HT590 was cathodically protected. However, the passivation of AA6061 made the aluminum alloy cathode temporarily, which leaded to corrosion of HT590. From the EIS analysis showing Warburg diffusion plot in Nyquist plots, it can be inferred that the stable passivation layer was formed on AA6061. However, the weld as well as HT590 did not show Warburg diffusion plot in Nyquist plots, suggesting that there was no barrier for corrosion or even if it exists, the barrier had no function for preventing and/or retarding charge transport through the passivation layer. The open circuit potential measurements showed that the potential of the weld was similar to that of HT590, which lied in the pitting region for AA6061, making the aluminum alloy part of the weld keep corrosion state. That resulted in the cracked oxide film on AA6061 of the weld, which could not play a role of corrosion barrier.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.21 no.1
• /
• pp.56-65
• /
• 2022

The electrochemical corrosion properties of austenitic AISI 304 steel subjected to a long-term-aging heat treatment were investigated. AISI 304 steel was aged at 700 ℃ for up to 10,000 h. The variation in the microstructure of the aged specimens was observed by optical microscopy and scanning electron microscopy. Electrochemical polarization experiments were performed to obtain the corrosion current density (Icorr) and corrosion potential (Ecorr). Analyses indicated that the metastable intermetallic carbide M₂₃C₆ formed near the γ/γ grain boundary and coarsened with increasing aging time; meanwhile, the δ-ferrite decomposed into the σ phase and into M₂₃C₆ carbide. As the aging time increased, the current density increased, but the corrosion potential of the austenitic specimen remained high (at least 0.04 ㎛/cm²). Because intergranular carbide was absent, the austenitic annealed specimen exhibited the highest pitting resistance. Consequently, the corrosion resistance of austenitic AISI 304 steel decreased as the aging heat treatment time increased.

• Corrosion Science and Technology
• /
• v.22 no.1
• /
• pp.64-72
• /
• 2023

Ni-Ti shape memory alloy for dental nerve treatment devices was prepared by adding Mo to Ni-Ti alloy to improve flexibility and fatigue fracture characteristics and simultaneously increase corrosion resistance. Surface properties of the alloy were evaluated. Microstructure analysis of the Ni-Ti-xMo alloy revealed that the amount of needle-like structure increased with increasing Mo content. The shape of the precipitate showed a pattern in which a long needle-like structure gradually disappeared and changed into a small spherical shape. As a result of XRD analysis of the Ni-Ti-xMo alloy, R-phase structure appeared as Mo was added. R-phase and B2 structure were mainly observed. As a result of DSC analysis, phase transformation of the Ti-Ni-Mo alloy showed a two-step phase change of B2-R-B19' transformation with two exothermic peaks and one endothermic peak. As Mo content increased, R-phase formation temperature gradually decreased. As a result of measuring surface hardness of the Ti-Ni-Mo alloy, change in hardness value due to the phase change tended to decrease with increasing Mo content. As a result of the corrosion test, the corrosion potential and pitting potential increased while the current density tended to decrease with increasing Mo content.

• Corrosion Science and Technology
• /
• v.7 no.2
• /
• pp.85-91
• /
• 2008

By operation in aqueous environment at high temperature and pressure, the structural materials from Primary Heat Transport System (PHTS) cover with protective oxide films, which maintain the corrosion rate in admissible limits. A lot of potential factors exist, which conduct to degradation of the protective films and consequently to intensification of the corrosion processes. The existing experience of different nuclear reactors shows that the water chemistry has an important role in integrity maintaining of the protective oxide films. To investigate the influence of water chemistry (pH, O2 dissolved, $Cl^-$, $F^-$) on corrosion of some structural materials (carbon and martensitic steel, Zr and Ni alloys) and to establish the maximum permissible values, corrosion experiments by static autoclaving and electrochemical methods were performed. The experimental results allowed us to establish the contribution of the water chemistry in initiation and evolution of some accelerated corrosion processes.

• Corrosion Science and Technology
• /
• v.3 no.3
• /
• pp.102-106
• /
• 2004

Al foil used was 99.9 and 99.99 %. Test solution used was NaCl solution. The noise was determined using controlled potential electrolysis at -200 and -700 mV vs. NHE. The current fluctuation was caused by breakdown and repaired process of aluminum oxide film. The current fluctuation value of noise was proportion to degree of growth. The number of noise was proportion to the number of pit. The examining of current flutulation value and number of noise could be evaluated corrosion. A 99.99 % Al foil was the mostly crystal of {100} plane, and showed three-dimensional, as azimuth pit with along the direction of this place piled up. A 99.9 % Al foil was polycrystal, and in order of (311) >(222) >(200) >(111) plane. The azimuth pit did not occurred as the dissolution was occurred from each plane.

• Journal of Surface Science and Engineering
• /
• v.36 no.5
• /
• pp.398-405
• /
• 2003

The stainless steel wire requires good corrosion resistance and mechanical properties, such as drawing ability, combined with a high resistance to corrosion. For increasing drawing ability of stainless steel, Ni coating methods have been used in this study. However, there is no information on the electrochemical corrosion behavior of drawed wires after Ni coating. To investigate corrosion resistance and mechanical property of drawed wire, the characteristics of Ni coated wires have been determined by tensile strength tester, hardness tester, field emission scanning microscope, energy dispersive x-ray analysis and potentiodynamic method in 0.1 M HCl. The drawed stainless steel wires showed the strain-induced martensitic structure, whereas non-drawed stainless steel wire showed annealing twin in the matrix of austenitic structure. The hardness and tensile strength of drawed stainless steel wire were higer than that of non-drawed stainless steel wire. Electrochemical measurements showed that, in the case of drawed stainless steel o ire after Ni coating, the corrosion resistance and pitting potential increased compared with non-coated and drawed stainless steel wire due to decrease in the surface roughness.

• Corrosion Science and Technology
• /
• v.11 no.4
• /
• pp.108-111
• /
• 2012

The effects of volume fraction (15-30%) of SiC particulate reinforcements on the corrosion behavior of SiCp/7091 Al composites in the 3.5% NaCl solution were studied by electrochemical techniques and scanning electron microscopy. The results showed that the amount of SiC particulate reinforcements did not cause much difference in the corrosion behavior of SiCp/7091 Al composites but the corrosion rate was proportional to the amount of SiCp reinforcement. And numerous pits and severe dissolution of the matrix was observed probably due to the discontinuities and galvanic effects between Al matrix and SiC reinforcements.

• Corrosion Science and Technology
• /
• v.9 no.6
• /
• pp.300-309
• /
• 2010

The influences of sensitization on localized corrosion resistance of 304 stainless steel, were investigated, using micro-dropletcell techniques. Micro-droplet cell allows one to align the micro-electrode to the desired spot of the working electrode and measure directly local current with the potentiodynamic polarization, linear polarization and a.c. impedance. Micro-electrochemical tests were carried out inside of the grain and on grain boundaries separately. It was found that sensitization decreased the pitting potential, increasing corrosion current density around grain boundaries. Galvanic current density was also measured between grain and grain boundaries.

• Journal of Surface Science and Engineering
• /
• v.50 no.6
• /
• pp.432-438
• /
• 2017

AZ91D casting alloy requires an advanced plasma anodizing processing because large amount of defects are liable to generate during anodization. In this study, plasma electrolytic oxidation (PEO) of AZ91D Mg alloy was conducted by the application of either constant voltage or current using a pulse mode and its effects on pore formation, surface roughness and corrosion resistance were investigated. The PEO films showed a three-layer structure. The PEO film thickness was found to increase linearly with voltage. The surface roughness, Ra, ranged between $0.2{\mu}m$ and $0.3{\mu}m$. The corrosion resistance increased from RN 3.5 to 9.5 by the PEO treatment when evaluated according to the 72 hour salt spray test. The PEO-treated surface exhibited higher pitting potential than the raw material.

• Journal of Surface Science and Engineering
• /
• v.36 no.4
• /
• pp.339-346
• /
• 2003

Stainless steel wire has been used in industry, dental and medical parts. Especially, it has been used widely for the dental orthodontic materials. The orthodontic wire requires good mechanical properties, such as elastic strength, combined with a high resistance to corrosion. To increase elastic strength and good corrosion resistance, drawing methods(one-step and two-step drawing) have been used and the electrochemical characteristics of drawed wire have been researched using potentiodynamic method in 0.9％NaCl and field emission scanning electron microscope. The one-step drawed wire showed the formation of rough surface. The hardness and tensile strength of two-step drawed wire increased. For the case of two-step drawed wire, the corrosion resistance and pitting potential increased compared with one-step drawed wire due to the drawing induced small surface roughness, such as scratch. The passivation and active current density decreased as the reduction in area for drawing increased.