• Journal of the Korean Magnetics Society
• /
• v.4 no.3
• /
• pp.282-284
• /
• 1994

A theoretical expression for determining the effective magnetic moment of hematite(${\alpha}-Fe_{2}O_{3}$) particle of the parasitic ferromagnetism by the proton relaxation in water is derived. In deriving the expression it is found that the mathematical procedures are exactly the same as those applied for aqueous solutions containing free paramagnetic ions, except that the distance between the proton spin of water molecule and the corresponding electronic spin of the particle must be considered to be a radius vector rather than a relative distance. And it is also found that the average effective magnetic moment of the particle calculated by the expression is in good agreement with the experimental value determined by Hirai.

• Journal of Magnetics
• /
• v.17 no.4
• /
• pp.251-254
• /
• 2012

The electron paramagnetic resonance (EPR) of the $Eu^{2+}$ ion in $SrCl_2$:Eu single crystal has been investigated using an X-band spectrometer. The angular dependence of magnetic resonance positions for the $Eu^{2+}$ impurity ion in the crystallographic aa-plane is analyzed with effective spin-Hamiltonian. The EPR spectra of the isolated $Eu^{2+}$ center merged to each other. The hyperfine splitting of the isolated $Eu^{2+}$ center due to the $^{151}Eu$ nucleus is approximately 35 G. Three kinds of $Eu^{2+}$ centers except the isolated $Eu^{2+}$ center, $Eu^{2+}$ pairs, $Eu^{2+}$ triples, and other $Eu^{2+}$ clusters, are split from the fitting of the integrated experimental spectrum with the Gaussian curve. The calculated spectroscopic splitting parameters of the $Eu^{2+}$ pairs, $Eu^{2+}$ triples, and other $Eu^{2+}$ clusters in $SrCl_2$:Eu crystal are $g_1$ = 2.06, $g_2$ = 1.94, and $g_3$ = 1.93, respectively.

• Journal of Magnetics
• /
• v.14 no.4
• /
• pp.161-164
• /
• 2009

Iron-doped $Sn_{1-x}Fe_xO_2$ (x = 0.0, 0.05, 0.1, 0.2, 0.33) thin films on Si(100) substrates and powders were prepared by a chemical solution process. The x-ray diffraction (XRD) patterns of the $Sn_{1-x}Fe_xO_2$ thin films and powders showed a polycrystalline rutile tetragonal structure. Thermo gravimetric (TG) - differential thermal analysis (DTA) showed the final weight loss above $430{^{\circ}C}$ for all powder samples. According to XRD Rietveld refinement of the powders, the lattice parameters and unit cell volume decreased with increasing Fe content. The magnetic properties were characterized using a vibrating sample magnetometer (VSM) and M$\ddot{o}$ssbauer spectroscopy. The thin film samples with x = 0.1 and 0.2 showed paramagnetic properties but thin films with x = 0.33 exhibited ferromagnetic properties at room temperature. Mossbauer studies revealed the $Fe^{3+}$ valence state in the samples. The ferromagnetism in the samples can be interpreted in terms of the direct ferromagnetic coupling of ferric ions via an electron trapped in a bridging oxygen deficiency, which can be explained using the F-center exchange model.

• Bulletin of the Korean Chemical Society
• /
• v.21 no.7
• /
• pp.679-684
• /
• 2000

The Sr2Co0.5Nb(Ta)0.5O4 and Sr3CoNb(Ta)O7 compounds, both with Ruddlesden-Popper structures, have been synthesized by the ceramic method at $1150^{\circ}C$ under atmospheric pressure. The crystallographic structure of the compounds was assigned to the tetr agonal system with space group 14/mmm by X-ray diffraction(XRD) Rietveld refinement. The reduced lattice volume and lattice parameters increased as the Ta with 5d substitutes for the Nb with 4d in the compounds. The Co/Nb(Ta)O bond length has been determined by X-ray absorption spectroscopic(EXAFS/XANES) analysis and the XRD refinement. The CoO6,octahedra were tetragonally distorted by elongation of Co-O bond along the c-axis. The magnetic measurement shows the compounds Sr2Co0.5Nb(Ta)0.5O4 and Sr3CoNb(Ta)O7 have paramagnetic properties and the Co ions with intermediate spin sates between high and low spins in D4h symmetry. All the compounds showed semiconducting behavior whose electrical conductivity increased with temperature up to 1000 K. The electrical conductiviy increased and the activation energy for the conduction decreased as the number of perovskite layers increased in the compounds with chemical formula An+1BnO3n+1.

• Journal of Magnetics
• /
• v.5 no.4
• /
• pp.111-115
• /
• 2000

Ultrafine $Co_{0.9}Mn_{0.1}Fe_2O_4$ powders have been fabricated by a sol-gel method. Structural and magnetic properties of the powders were investigated by x-ray diffractometry, transmission electron microscopy (TEM), Mossbauer spectroscopy, and vibrating sample magnetometry (VSM). Co-Mn ferrite powders that were fired at and above 773 K contained only a single spinel phase and behaved ferrimagnetically. Powders fired at 673 and 723 K had a spinel structure and were mixed paramagnetic and ferrimagnetic in nature. The magnetic behavior of Co-Mn ferrite powders fired at and above 873 K showed that an increase of the firing temperature yielded a decrease in the coercivity and an increase in the saturation magnetization. The maximum saturation magnetization and coercivity of Co-Mn ferrite powders were 66.7 emu/g and 1523 Oe, respectively, Mossbauer spectra of the powder fired at 923 K were taken at various temperatures ranging from 13 to 850 K. The iron ions.at both A (tetrahedral) and B (octahedral) sites were found to be in ferric high-spin states. The Nel temperature $T_N$ was found to be 850 $\pm$ 2 K. Debye temperatures far A and B sites were found to be $\Theta_A = 757 \pm$5K and $Theta_B = 282 \pm$5 K, respectively.

• Journal of the Korean Chemical Society
• /
• v.37 no.11
• /
• pp.923-928
• /
• 1993

The series of solid solutions in the $Sr_{1+x}Ho_{1-x}FeO_{4-y}$ (x = 0.00, 0.25, 0.50, 0.75 and 1.00) systems with $K_2NiF_4$ type structure have been prepared at 1550$^{\circ}$C under an atmospheric air pressure. The X-ray powder diffraction spectra of these samples assign that the crystallographic phases are tetragonal system over the whole x range. The lattice volume was increased with increasing the substitution amount of the $Sr^{2+}$ ion. The mole ratio of the $Fe^{4+}$ ion to total iron ions or ${\tau}$ value has been determined by Mohr salt titration of the sample and then the y value was calculated from x and ${\tau}$ values. The ${\tau}$ and y values have been increased with x values. The nonstoichiometric chemical formula are formulated from the general formula of $Sr_{1+x}Ho_{1-x}Fe^3_{1-}\;^+_{\tau}Fe_{\tau}^{4+}O_{4-y}$ replaced by x,${\tau}$ and y values. Mossbauer spectra show the mixed valence state and coordination state of $Fe^{3+}\;and\;Fe^{4+}$ ions. It is found out that the magnetic property of the samples is paramagnetic at room temperature. Electrical conductivity varied within the semiconductivity range of 1.0 to 1 ${\times}\;10^{-9}{\Omega}^{-1}cm^{-1}$. Activation energy of the electrical conductivity was decreased with the $\tau$ value. The conduction mechanism should be explained by the hopping model of the conduction electrons between the valence states of $Fe^{3+}\;and\;Fe^{4+}$ ions.

• Journal of the Korean Chemical Society
• /
• v.55 no.3
• /
• pp.502-508
• /
• 2011

Synthesis of $Nd_{2x}Cd_{2-3x}SiO_4$ ($0.01{\leq}x{\leq}0.21$) [S1-S3: x=0.01, 0.11 and 0.21] solid solutions were prepared by solgel method. Powder x-ray diffraction (XRD) results show monoclinic unit cell with space group P21/m. The average crystallite sizes are found to be 20 to 45 nm. The Scanning Electron Microcopy (SEM) images show morphology of the sample is in globular nature. The energy dispersive analysis of x-rays (EDX) and X-ray mapping results confirmed that all the constituent elements of the composites were present and that were distributed in uniformly. The optical absorption band at ~750 nm was due to $^4I_{9/2}{\rightarrow}^4F_{7/2}+^4S_{3/2}$ transition optically active $Nd^{3+}$ ions. Electron Paramagnetic Resonance (EPR) lineshapes of S1-S3 at 10, 40, 77 and 300 K show a broad unresolved isotropic lineshapes were observed due to rapid spin lattice relaxation of $Nd^{3+}$.

• Journal of the Korean Chemical Society
• /
• v.63 no.6
• /
• pp.453-458
• /
• 2019

Synthesis of ZnCo₂O₃ oxide is performed by sol-gel method via nitrate-citrate route. Powder X-ray diffraction (XRD) study shows monoclinic unit cell having lattice parameters: a = 5.721(1) Å, b = 8.073(2) Å, c = 5.670(1) Å, β = 93.221(8)°, space group P_2/m and Z = 4. Average crystallite sizes determined by Scherrer equation are the range ~14-32 nm, whereas SEM micrographs show nano-micro meter size particles formed in ZnCo₂O₃. Endothermic peak at ~798 K in the Differential scanning calorimetric (DSC) trace without weight loss could be due to structural transformation and the endothermic peak ~1143 K with weight loss is due to reversible loss of O₂ in air atmosphere. Energy Dispersive X-ray (EDX) analysis profile shows the presence of elements Zn, Co and O which indicates the purity of the sample. Magnetic measurements in the range of +12 kOe to -12 kOe at 10 K, 77 K, 120 K and at 300 K by PPMS-II Physical Property Measurement System (PPMS) shows hysteresis loops having very low values of the coercivity and retentivity which indicates the weakly ferromagnetic nature of the oxide. Observed X-band EPR isotropic lineshapes at 300 K and 77 K show positive g-shift at g_iso ~2.230 and g_iso ~2.217, respectively which is in agreement with the presence of paramagnetic site Co²⁺(3d⁷) in the oxide. DC conductivity value of 2.875 ×10^-8 S/cm indicates very weakly semiconducting nature of ZnCo₂O₃ at 300 K. DRS absorption bands ~357 nm, ~572 nm, ~619 nm and ~654 nm are due to the d-d transitions ⁴T_1g(⁴F)→²E_g(²G), ⁴T_1g(⁴F)→⁴T_1g(⁴P), ⁴T_1g(⁴F)→⁴A_2g(⁴F), ⁴T_1g(⁴F)→⁴T_2g(⁴F), respectively in octahedral ligand field around Co²⁺ ions. Direct band gap energy, E_g~ 1.5 eV in the oxide is obtained by extrapolating the linear part of the Tauc plot to the energy axis indicates fairly strong semiconducting nature of ZnCo₂O₃.

• Journal of the Korean Magnetics Society
• /
• v.15 no.4
• /
• pp.246-249
• /
• 2005

The blue-color emitting phosphor powder, $CaMgSi_{2}O_6:Eu^{2+}(CMS:Eu^{2+})$ was synthesized by the solid-state reaction method. The synthesized powder was annealed from room temperature to $1,100^{\circ}C$ in air. Its PL property and valence state of Eu atoms was measured by the photoluminescence (PL) and the electron paramagnetic resonance (EPR) spectrometers, respectively. The PL intensity was stable to $700^{\circ}C$, but drastically decreased to $1,100^{\circ}C$. The behavior of EPR intensity was very similar to the PL intensity. The EPR measurement showed that decreased intensity of the PL was caused to the oxidation from the ion $Eu^{2+}$ to $Eu^{3+}$ ions. The EPR spectrometer was powerful as a tool that could distinguish between the valence states of Eu atom as a dopant in various phosphors.

• Analytical Science and Technology
• /
• v.11 no.3
• /
• pp.189-193
• /
• 1998

Binary alloys, $MoRu_3$ and $MoRh_3$, have been prepared using arc melting furnace. Mo and the noble metals Ru and Rh are the constituents of metallic insoluble residues, which were found in the early days of the post-irradiation studies on uranium oxide fuels. Detailed structural informations about these alloys have not been reported on JCPDS files of ICDD (International Centre for Diffraction Data). The results of X-ray diffraction study showed that the alloy was crystallized in hexagonal close-packing, well known as ${\varepsilon}$-phase. The X-ray diffraction patterns of these alloys matched well to that of $WRh_3$ with $P6_3/mmc$ of space group. The lattice parameters, a and c, were calculated using the least squares extrapolation. It was found from X-ray photoelectron spectroscopic measurements that Mo on the surface of the alloy was oxidized to Mo(6+), which could be removed by sputtering with Ar ions for approximately 15 minutes. The changes in binding energy of Mo, Ru, and Rh on the surface of the alloy were not observed. Magnetic susceptibility measurements resulted in the typical Pauli-paramagnetic behavior in the temperature range of 2 to 300 K.