An all-transparent photodetector was fabricated by structuring $Cu_2O$/ZnO/AZO/ITO on a glass substrate. The visible-range transmittance was as high as 80%, which ensures clear vision forhuman eyes. High-transparency metal conductive oxides (p-type $Cu_2O$ and n-type ZnO) were appliedto form the transparent p/n junction. The functional AZO layer was adopted to improve the transparent photodetector performance between the ZnO and ITO, improving the photoresponses because of its electrical conductivity. To clarify the AZO functionality, a comparator device was prepared without the AZO layer in the formation of $Cu_2O$/ZnO/ITO/Glass. The $Cu_2O$/ZnO/AZO/ITO device provided a rectifying ratio of 113.46, significantly better than the 9.44 of the $Cu_2O$/ZnO/ITO device. In addition, the $Cu_2O$/ZnO/AZO/ITO device's photoresponses at short wavelengths were better than those of the comparator. The functioning AZO layer provides ahigh-performing transparent Cu oxide photodetector and may suggest a route for the design of efficient photoelectric devices.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.68-69
• /
• 2007

We have prepared p-type ZnO:Al films in pure oxygen ambient on n-type Si (100) and homo buffer layers by RF magnetron sputtering system. Hall effect measurement shows that the film annealed at $600^{\circ}C$ possesses p-type conductivity and the film annealed $800^{\circ}C$ does not. PL spectra show different properties of p- and n-type ZnO film. The corresponding peaks of PL spectra of p- and n-type show at about same positions. The intensities of high photon energy of n-type film on buffer shows decreasing tendency.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.122-122
• /
• 2010

ZnO is a widely investigated material for the blue and ultraviolet solid-state emitters and detectors. It has been promoted due to a wide-band gap semiconductor which has large exciton binding energy of 60 meV, chemical stability and low radiation damage. However, there are many problems to be solved for the growth of p-type ZnO for practical device applications. Many researchers have made an efforts to achieve p-type conductivity using group-V element of N, P, As, and Sb. In this letter, we have studied the optical characteristics of the antimony-doped ZnO (ZnO:Sb) thin films by means of photoluminescence (PL), PL excitation, temperature-dependent PL, and time-resolved PL techniques. We observed donor-to-acceptor-pair transition at about 3.24 eV with its phonon replicas with a periodic spacing of about 72 meV in the PL spectra of antimony-doped ZnO (ZnO:Sb) thin films at 12 K. We also investigate thermal activation energy and carrier recombination lifetime for the samples. Our result reflects that the antimony doping can generate shallow acceptor states, leading to a good p-type conductivity in ZnO.

• Transactions on Electrical and Electronic Materials
• /
• v.9 no.2
• /
• pp.67-72
• /
• 2008

Al-doped p-type ZnO thin films were fabricated by RF magnetron sputtering on n-Si (100) and homo-buffer layers in pure oxygen ambient. ZnO ceramic mixed with 2 wt% $Al_2O_3$ was selected as a sputtering target. XRD spectra show that the Al-doped ZnO thin films have ZnO crystal structure. Hall Effect experiments with Van der Pauw configuration show that p-type carrier concentrations are arranged from $1.66{\times}10^{16}$ to $4.04{\times}10^{18}\;cm^{-2}$, mobilities from 0.194 to $198\;cm^2V{-1}s^{-1}$ and resistivities from 0.0963 to $18.4\;{\Omega}cm$. FESEM cross section images of different parts of a p-type ZnO:Al thin film annealed at $800^{\circ}C$ show a compact structure. Measurement for same sample shows that density is $5.40\;cm^{-3}$ which is smaller than theoretically calculated value of $5.67\;cm^{-3}$. Photoluminescence (PL) spectra at 10 K show a shoulder peak of p-type ZnO film at about 3.117 eV which is ascribed to electron transition from donor level to acceptor level (DAP).

• Journal of Sensor Science and Technology
• /
• v.15 no.2
• /
• pp.84-89
• /
• 2006

Highly concentrated p-type ZnO thin films can be obtained by doping of N, P and As elements. In this study, undoped ZnO buffer layers were prepared on a (0001) sapphire substrate by a ultra high vaccum pulsed laser deposition(UHV-PLD) method. ZnO buffer layers were deposited with various deposition temperature($400{\sim}700^{\circ}C$) at 350 mtorr of oxygen working pressure. Arsenic doped(1 wt%) ZnO thin films were deposited on the ZnO buffer layers by UHV-PLD. Crystallinity of the samples were evaluated by X-ray diffractometer and scanning electron microscopy. Optical, electrical properties of the ZnO thin films were estimated by photoluminescence(PL) and Hall measurements. The optimal condition of the undoped ZnO buffer layer for the deposition of As-doped ZnO thin films was at $600^{\circ}C$ of deposition temperature.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.121-121
• /
• 2008

We propose a novel nanomaterial-based pn diode which constructed with an n-type ZnO nanowire (NW) and a p-type HgTe nanoparticle (NP) thin film. The photo current characteristics of a ZnO NW, a HgTe NP thin film and pn diode constructed with a ZnO NW and a HgTe NP thin film were investigated under illumination of the 325 nm and 633 nm wavelength light. The conductivities of a ZnO NW exposed to the 325 nm and 633 nm wavelength light increased, while the photocurrents taken from the HgTe NP thin film was very close to the dark currents. Moreover, The pn diode exhibited the rectifying characteristics of the dark current and of the photocurrent excited by the 633 nm wavelength light. In contrast, the ohmic characteristics for the photocurrent were observed due to the junction barrier lowering in the conduction band of the ZnO nanowire under the illumination of the 325 nm wavelength light.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1270-1271
• /
• 2008

Effects of thin ZnO/Mg interlayers on electrical and optical properties between p-GaN and ITO were characterized for its application to GaN-LEDs. The ZnO and Mg layers were deposited to have various thicknesses (1${\sim}$6nm for ZnO and 1${\sim}$2nm for Mg) by sputtering. After RTA process, the atomic migration between Mg and ZnO and the formation of Ga vacancy were observed from SIMS depth profile, resulting in the increase of hole concentration and the reduction of band bending at the surface region of p-GaN. The sample using ZnO(2nm)/Mg(2nm) interlayer produced the lowest contact resistance with SBH(Schottky barrier height) of 0.576 eV and the transmittance higher than 83% at a wavelength of 460nm when annealed at 500$^{\circ}C$ for 3min in air ambient.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.141-142
• /
• 2005

To investigate the ZnO thin films which is interested in the next generation of short wavelength LEDs and Lasers, our ZnO thin films were deposited by RF sputtering system. At sputtering process of ZnO thin films, substrate temperature, work pressure respectively is $300^{\circ}C$ and 5.2 mTorr, and the purity of target is ZnO 5N. The thickness of ZnO thin films was about $1.9{\mu}m$ at SEM analysis after sputtering process. Phosphorus (P) and arsenic (As) were diffused into ZnO thin films sputtered by RF magnetron sputtering system in ampoule tube which was below $5\times10^{-7}$ Torr. The dopant sources of phosphorus and arsenic were $Zn_3P_2$ and $ZnAs_2$. Those diffusion was perform at 500, 600, and $700^{\circ}C$ during 3hr. We find the condition of p-type ZnO whose diffusion condition is $700^{\circ}C$, 3hr. Our p-type ZnO thin film has not only very high carrier concentration of above $10^{19}/cm^3$ but also low resistivity of $5\times10^{-3}{\Omega}cm$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.315-315
• /
• 2013

We report the electronic structure modification in the swift heavy ion (SHI) irradiated N-doped ZnO thin films prepared by RF sputtering from ZnO target in different ratio of Ar/$N_2$ gas mixture using highly pure $N_2$ gas. The different N-ZnO thin lms were then irradiated with 120 MeV Ag ion beam with different doses ranging from $1{\times}10^{11}$ to $5{\times}10^{12}$ ions/$cm^2$ and characterized by XRD and near edge X-ray absorption ne structure (NEXAFS) at N and O K-edges. The NEXAFS measurements provide direct evidence of O 2p and Zn 3d orbital hybridization and also the bonding of N ions with Zn and O ions. The minimum value of resistivity of $790{\Omega}cm$, a Hall mobility of $22cm^2V^-1s^-1$ and the carrier concentration of $3.6{\times}10^{14}cm^{-3}$ were yielded at 75% $N_2$. X-ray diffraction (XRD) measurements revealed that N-doped ZnO films had the preferential orientation of (002) plane for all samples, while crystallinity start decreasing at 32.5% $N_2$. The average crystallite size varies from 5.7 to 8.2 nm for 75% and then decreases to 7.8 nm for 80% $Ar:N_2$ ratio.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.30 no.8
• /
• pp.508-513
• /
• 2017

Ultraviolet (UV) photodetectors are used in various industries and fields of research, including optical communication, flame sensing, missile plume detection, astronomical studies, biological sensors, and environmental research. However, general UV detectors that employ Schottky junction diodes and p-n junctions have high fabrication cost and low quantum efficiency. In this study, we investigated the characteristics of materials used to manufacture UV photodetectors in a low-cost solution process that requires easy fabrication of flexible substrates. We fabricated p-type NiO and n-type ZnO substrates with wide band gap by the sol-gel method and compared the characteristics of substrates prepared under different spin-coating and heat-treatment conditions.