• Macromolecular Research
• /
• v.13 no.6
• /
• pp.521-528
• /
• 2005

Electrospun polyacrylonitrile (PAN) nanofibers were carbonized with or without iron (III) acetylacetonate to induce catalytic graphitization within the range of 900-1,500$^{circ}C$, resulting in ultrafine carbon fibers with a diameter of about 90-300 nm. Their structural properties and morphologies were investigated. The carbon nanofibers (CNF) prepared without a catalyst showed amorphous structures and very low surface areas of 22-31 $m^{2}$/g. The carbonization in the presence of the catalyst produced graphite nanofibers (GNF). The hydrogen storage capacities of these CNF and GNF materials were evaluated through the gravimetric method using magnetic suspension balance (MSB) at room temperature and 100 bar. The CNFs showed hydrogen storage capacities which increased in the range of 0.16-0.50 wt$\%$ with increasing carbonization temperature. The hydrogen storage capacities of the GNFs with low surface areas of 60-253 $m^{2}$/g were 0.14-1.01 wt$\%$. Micropore and mesopore, as calculated using the nitrogen gas adsorption-desorption isotherms, were not the effective pore for hydrogen storage.

• Corrosion Science and Technology
• /
• v.11 no.1
• /
• pp.9-14
• /
• 2012

The formation of the Fe-Al inhibition layer in hot-dip galvanizing is a confusing issue for a long time. This study presents a characterization result on the inhibition layer formed on C-Mn-Cr and C-Mn-Si dual-phase steels after a short time galvanizing. The samples were annealed at $800^{\circ}C$ for 60 s in $N_{2}$-10% $H_{2}$ atmosphere with a dew point of $-30^{\circ}C$, and were then galvanized in a bath containing 0.2 %Al. X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) was employed for characterization. The TEM electron diffraction shows that only $Fe_{2}Al_{5}$ intermetallic phase was formed. No orientation relationship between the $Fe_{2}Al_{5}$ phase and the steel substrate could be identified. Two peaks of Al 2p photoelectrons, one from metallic aluminum and the other from $Al^{3+}$ ions, were detected in the inhibition layer, indicating that the layer is in fact a mixture of $Fe_{2}Al_{5}$ and $Al_{2}O_{3}$. TEM/EDS analysis verifies the existence of $Al_{2}O_{3}$ in the boundaries of $Fe_{2}Al_{5}$ grains. The nucleation of $Fe_{2}Al_{5}$ and the reduction of the surface oxide probably proceeded concurrently on galvanizing, and the residual oxides prohibited the heteroepitaxial growth of $Fe_{2}Al_{5}$.

• Journal of Photoscience
• /
• v.10 no.2
• /
• pp.203-208
• /
• 2003

Two coupled molecules were successfully synthesized by condensation of amine-donor-substituted barbituric acid derivativies as nonlinear optical chromophores. A flexible spacer of the alkyl chain with different lengths of carbon chains (5 and 6 carbons) was introduced between two chromophores, which prevented crystallization and aggregation of molecules. Two coupled molecules (B-Cn-B, n=5, 6) had glass-transition temperatures on a second heating around 81 and 76$^{\circ}C$ without melting points, respectively. To explore the linear optical properties, thin-films were prepared and examined by a photometry method using Nd:YVO$_4$ CW laser. Also, microscopic and macroscopic nonlinear optical properties were measured by Hyper-Rayleigh Scattering (HRS) and the Maker Fringes method using Nd:YAG ps pulse laser, respectively. In spite of the moderate hyperpolarizabilities of coupled molecules, the second order NLO coefficient (d$\_$33/) was larger than the conventional Disperse Red 1 doped PMMA polymeric system.

• Transactions of the Korean hydrogen and new energy society
• /
• v.16 no.4
• /
• pp.334-342
• /
• 2005

200-300 nm 직경을 지닌 폴리비닐리덴 플루오라이드 초극세 섬유를 전기방사법으로 제조하였다. 이들을 불응화시킨 후, $800-1800^{\circ}C$ 온도에서 탄화시켜 PVdF 계 탄소나노 섬유를 제조하여 구조 및 기공분석을 하였다. 이들은 20-30 nm 크기의 탄소입자로 이루어져 있으며 탄소나노입자는 1 nm이하의 슬릿형 나노기공을 지니고 있었다. 탄화온도가 증가함에 따라 비표면적은 $1500^{\circ}C$에서 $414\;m^2/g$로 감소하였으나, $1800^{\circ}C$에서는 $1300\;m^2/g$로 급격히 다시 증가하였으며 1 nm 이하의 나노기공만을 지닌 탄소섬유가 얻어졌다. 비표면적 및 기공특성과 수소저장특성을 관계를 조사하기 위하여 Magnetic Syspension Balance(MSB)를 사용한 중량법으로 평가한 이들의 수소저장능은 0.04-0.4wt%이었다.

• Journal of Powder Materials
• /
• v.24 no.2
• /
• pp.153-163
• /
• 2017

Transparent conducting electrodes (TCEs) are attracting considerable attention as an important component for emerging optoelectronic applications such as liquid crystal displays, touch panels, and solar cells owing to their attractive combination of low resistivity (<$10^{-3}{\Omega}cm$) and high transparency (>80%) in the visible region. The solution-based process has unique properties of an easy fabrication procedure, scalability, and low cost compared to the conventional vacuum-based process and may prove to be a useful process for fabricating TCEs for future optoelectronic applications demanding large scale and flexibility. In this paper, we focus on the introduction of a solution-based process for TCEs. In addition, we consider the powder materials used to fabricate solution-based TCEs and strategies to improve their transparent conducting properties.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.05a
• /
• pp.65-65
• /
• 2011

Single-well carbon nanotubes (SWNT) have been proposed as a promising candidate for various applications owing to their excellent properties. In particular, their fascinating electrical and mechanical properties could provide a new area for the development of advanced engineering materials. A transparent conductive thin film (TCF) has increased for applications such as liquid crystal displays, touch panels, and flexible displays. Indium tin oxide (ITO) thin films, which have been traditionally used as the TCFs, have a serious obstacle in TCFs applications. SWNTs are the most appropriate materials for conductive films for displays due to their excellent high mechanical strength and electrical conductivity. But, a bundle of CNTs has different electrical properties than their individual counterparts. In this work, the fabrication by the spraying process of transparent SWNT films and reduction of its sheet resistance on PET substrates is researched. Arc-discharge SWNTs were dispersed in deionized water by adding sodum dodecyl sulfate (SDS) as surfactant and sonicated, followed by the centrifugation. The dispersed SWNT was spray-coated on PET substrate and dried on a hotplate at $100^{\circ}C$. When the spray process was terminated, the TCF was immersed into deionized water to remove the surfactant and then it was dried on hotplate. The TCF film was then treated with ionic doping treatment, rinsed with deionized water and dried. The surface morphology of TCF was characterized by field emission scanning electron microscopy. The sheet resistance and optical transmission properties of the TCF were measured with a four-point probe method and a UV-visible spectrometry, respectively. Results, we show that 97 ${\Omega}$/> sheet resistance can be achieved with 81% transmittance at the wavelength of 550 nm. The changes in electrical and optical conductivity of SWNT film before and after ionic doping treatments were discussed.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1996.11a
• /
• pp.143-143
• /
• 1996

• Proceedings of the Materials Research Society of Korea Conference
• /
• 1998.08a
• /
• pp.93.3-93
• /
• 1998

• Korean Journal of Materials Research
• /
• v.27 no.11
• /
• pp.631-635
• /
• 2017

We report facile solution processing of mesoporous hematite (${\alpha}-Fe_2O_3$) thin films for high efficiency solar-driven water splitting. $Fe_2O_3$ thin films were prepared on fluorine doped tin oxide(FTO) conducting substrates by spin coating of a precursor solution followed by annealing at $550^{\circ}C$ for 30 min. in air ambient. Specifically, the precursor solution was prepared by dissolving non-toxic $FeCl_3$ as an Fe source in highly versatile dimethyl sulfoxide(DMSO) as a solvent. The as-deposited and annealed thin films were characterized for their morphological, structural and optical properties using field-emission scanning electron microscopy(FE-SEM), X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS) and UV-Vis absorption spectroscopy. The photoelectrochemical performance of the precursor (${\alpha}-FeOOH$) and annealed (${\alpha}-Fe_2O_3$) films were characterized and it was found that the ${\alpha}-Fe_2O_3$ film exhibited an increased photocurrent density of ${\sim}0.78mA/cm^2$ at 1.23 V vs. RHE, which is about 3.4 times higher than that of the ${\alpha}-FeOOH$ films ($0.23mA/cm^2$ at 1.23 V vs. RHE). The improved performance can be attributed to the improved crystallinity and porosity of ${\alpha}-Fe_2O_3$ thin films after annealing treatment at higher temperatures. Detailed electrical characterization was further carried out to elucidate the enhanced PEC performance of ${\alpha}-Fe_2O_3$ thin films.

• Korean Journal of Materials Research
• /
• v.20 no.12
• /
• pp.629-635
• /
• 2010

Abstract In this study characteristics of Al-doped ZnO thin film by HIPIMS (High power impulse sputtering) are discussed. Deposition speed of HIPIMS with conventional balanced magnetic field is measured at about 3 nm/min, which is 30% of that of conventional RF sputtering process with the same working pressure. To generate additional magnetic flux and increase sputtering speed, electromagnetic coil is mounted at the back side of target. Under unbalanced magnetic flux from electromagnet with 1.5A coil current, deposition speed of AZO thin film is increased from 3 nm/min to 4.4 nm/min. This new value originates from the decline of particles near target surface due to the local magnetic flux going toward substrate from electromagnet. AZO film sputtered by HIPIMS process shows very smooth and dense film surface for which surface roughness is measured from 0.4 nm to 1 nm. There are no voids or defects in morphology of AZO films with varying of magnetic field. When coil current is increased from 0A to 1A, transmittance of AZO thin film decreases from 80% to 77%. Specific resistance is measured at about $2.9{\times}10-2\Omega{\cdot}cm$. AZO film shows C-axis oriented structure and its grain size is calculated at about 5.3 nm, which is lower than grain size in conventional sputtering.