• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.27.1-27.1
• /
• 2011

The recent extensive research of one-dimensional (1D) nanostructures such as nanowires (NWs) and nanotubes (NTs) has been the driving force to fabricate new kinds of nanoscale devices in electronics, optics and bioengineering. We attempt to produce silicon oxide nanowires (SiOxNWs) in a simple way without complicate deposition process, gaseous Si containing precursors, or starting material of $SiO_2$. Nickel (Ni) nanoparticles (NPs) were applied on Si wafer and thermally treated in a furnace. The temperature in the furnace was kept in the ranges between 900 and $1,100^{\circ}C$ and a mixture of nitrogen ($N_2$) and hydrogen ($H_2$) flowed through the furnace. The SiOxNWs had widths ranging from 100 to 200 nm with length extending up to ~10 ${\mu}m$ and their structure was amorphous. Ni NPs were acted as catalysts. Since there were no other Si materials introduced into the furnace, the Si wafer was the only Si sources for the growth of SiOxNWs. When the Si wafer with deposition of Ni NPs was heated, the liquid Ni-Si alloy droplets were formed. The droplets as the nucleation sites induce an initiation of the growth of SiOxNWs and absorb oxygen easily. As the droplets became supersaturated, the SiOxNWs were grown, by the reaction between Si and O and continuously dissolving Si and O onto NPs. Photoluminescence (PL) showed that blue emission spectrum was centered at the wavelength of 450 nm (2.76 eV). The details of growth mechanism of SiOxNWs and the effect of Ni NPs on the formation of SiOxNWs will be presented.

• 한국진공학회지
• /
• 제2권4호
• /
• pp.439-454
• /
• 1993

The phase sequence of codeposited Co-Si alloy and Co/si multilayer thin film was investigated by differential scanning calormetry(DSC) and X-ray diffraction (XRD) analysis, The phase sequence in codeposition and codeposited amorphous Co-Si alloy thin film were CoSilongrightarrow Co2Si and those in Co/Si multilayer thin film were CoSilongrightarrowCo2Silongrightarrow and CoSilongrightarrowCo2Si longrightarrowCoSilongrightarrowCoSi2 with the atomic concentration ration of Co to Si layer being 2:1 and 1:2 respectively. The observed phase sequence was analyzed by the effectvie heat of formatin . The phase determining factor (PDF) considering structural facotr in addition to the effectvie heat of formation was used to explain the difference in the first crystalline phase between codeposition, codeposited amorphous Co-Si alloy thin film and Co/Si multilayer thin film. The crystallinity of Co-silicide deposited by multitarget bias cosputter deposition (MBCD) wasinvestigated as a funcion of deposition temperature and substrate bias voltage by transmission electron microscopy (TEM) and epitaxial CoSi2 layer was grown at $200^{\circ}C$ . Parameters, Ear, $\alpha$(As), were calculate dto quantitatively explain the low temperature epitaxial grpwth of CoSi2 layer. The phase sequence and crystallinity had a stronger dependence on the substrate bias voltage than on the deposition temperature due to the collisional daxcade mixing, in-situ cleannin g, and increase in the number of nucleation sites by ion bombardment of growing surface.

• 한국수소및신에너지학회논문집
• /
• 제7권2호
• /
• pp.181-191
• /
• 1996

기계적인 합금화는 planetary mill을 사용하여 이루어졌으며, 시료의 조성은 Mg-10wt.%Ni과 Mg-25wt.%Ni이었다. 수소화물 형성 분해 cycling에 의해 혼합물 내에 $Mg_2Ni$상이 형성되었다. Mg-10wt.%Ni, Mg-25wt.%Ni은 583K, $0{\sim}8barH_2$에서 각각 n=7, n=6정도 후 활성화가 완료되었으며, 583K, $8barH_2$에서 10분 동안에 Mg-10wt.%Ni과 Mg-25wt.%Ni 시료에 의해 흡수된 수소의 중량 퍼센트 Ha(10min)은 각각 4.99, 4.52이었다. Mg-10wt.%Ni과 Mg-25wt.%Ni 혼합물은, 다른 Mg의 합금이나 혼합물에 비해 수소화물 형성 속도는 훨씬 높고, 수소화물 분해 속도와 수소 저장 용량은 비교적 높은 우수한 수소 저장 특성을 가진 수소 저장 재료라 판단된다. 기계적인 합금 처리와 수소 화합물 형성 분해 cycling의 효과는 핵 생성 site를 만들어 주고 입자의 크기를 줄이는 것으로 생각된다.

• 한국주조공학회지
• /
• 제40권3호
• /
• pp.85-96
• /
• 2020

The effect of an aluminum scrap addition ratio on the tensile and solidification cracking properties of the AC4A aluminum alloy in the as-cast state and heat-treated state were investigated in this study. Generally, the expected problem of using scrap in aluminum casting is an increase of hydrogen and Fe element inside the aluminum melt. Another issue is an oxide film which has a weak interface with the molten aluminum and acts as potent nucleation sites for internal porosity and crack initiation. Solidification cracking is one of the critical defects that must be resolved to produce high quality castings. A conventional evaluation method for solidification cracking is a relative and qualitative analysis method which does not provide quantitative data on the thermal stress in the solidification process. Therefore, a newly designed solidification cracking test apparatus was used in this study, and the device can provide quantitative data. As a result, after conducting experiments with different scrap addition ratios (0%, 20%, 35%, 50%), the tensile strengths and elongations in the as-cast state were 214, 187.7, 182.1 and 170.4MPa and 4.6%, 3.4%, 3.1% and 2.3%, respectively. In the case of the T6 heat-treated state, the tensile strengths and elongations were 314.9, 294.6, 293.1 and 271.1MPa and 5.4%, 4.6%, 3.8% and 3.1%, respectively. The strength of the solidification cracking was 3.1, 2.4, 2.2and 1.6MPa as the scrap addition ratio increases.

• 한국태양에너지학회 논문집
• /
• 제29권5호
• /
• pp.35-44
• /
• 2009

In this study, boiling heat transfer coefficients(HTCs) and critical heat flux(CHF) are measured on a smooth square flat copper heater in a pool of pure water with and without carbon nano tubes(CNTs) dispersed at $60^{\circ}C$. Tested aqueous nanofluids are prepared using multi-walled CNTs whose volume concentrations are 0.0001, 0.001, 0.01, and 0.05%. For dispersion of CNTs, polyvinyl pyrrolidone(PVP) is used in distilled water. Pool boiling HTCs are taken from $10kW/m^2$ to critical heat flux for all nanofluids. Test results show that the pool boiling HTCs of the nanofluids are lower than those of pure water in entire nucleate boiling regime. On the other hand, critical heat flux is enhanced greatly showing up to 200% increase at volume concentration of 0.001% CNTs as compared to that of pure water. This is related to the change of surface characteristics by the deposition of CNTs. This deposition makes a thin CNT layer on the surface and the active nucleation sites of heat transfer surface are decreased due to this layer. The thin layer acts as the thermal resistance and also decreases the bubble generation rate resulting in a decrease in pool boiling HTCs. The same layer, however, maintains the nucleate boiling even at very high heat fluxes and reduces the formation of large vapor canopy at near CHF resulting in a significant increase in CHF.

• 열처리공학회지
• /
• 제18권1호
• /
• pp.3-11
• /
• 2005

Using various thermo-mechanical schedules characterized by varying reheating temperature, deformation temperature and strain, the austenite recrystallization and ferrite refinement of a Nb bearing low carbon steel(0.15C-0.25Si-1.11Mn-0.04Nb) were investigated. For single pass heavy deformations at $800^{\circ}C$, the 40% deformed austenite was not recrystallized while the 80% deformed one was fully recrystallized. Ferrite grains formed in the 80% deformed specimen was not very small compared with those in the 40% deformed specimen, which implied the recrystallized austenite was not more beneficial to ferrite refinement than the non-recrystallized one. In case of deformation in low temperature austenite region, a multi-pass deformation made finer ferrites than a single-pass deformation, as the total reduction was the same, due to more ferrite nucleation sites in the non-recrystallization of austenite for multi-pass deformation. When specimen was deformed at $775^{\circ}C$ that was $10^{\circ}C$ higher than $Ar_3$, the ferrite of about $1{\mu}m$ was formed through deformation induced ferrite transformation(DIFT), and the amount of ferrite was increased with increasing reduction. Dislocation density was very high and no carbides were observed in DIFT ferrites, presumably due to supersaturated carbon solution. By deformation in two phase(50% austenite+50% ferrite) region the very refined ferrite grains of less than $1{\mu}m$ were formed certainly by recovery and recrystallization of deformed ferrites and, a large portion of ferrites were divided by subgrain boundaries with misorientation angles smaller than 10 degrees.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2004년도 제5회 압연심포지엄 신 시장 개척을 위한 압연기술
• /
• pp.63-71
• /
• 2004

Recently, a sheet forming process of Mg alloys is highlighted again due to increasing demand for Mg wrought alloys in the applications of casings of mobile electronics and outer-skins of light-weight transportation. Microstructure control is essential for the enhancement of workability and formability of Mg alloy sheets. In this research, AZ31 Mg alloy sheets were prepared by hot rolling process and the rolling condition dependency of the microstructure and texture evolution was studied by employing a conventional rolling mill as well as an asymmetric rolling mill. When rolled through multiple passes with a small reduction per pass, fine-grained and homogeneous microstructure evolved by repetitive dynamic and static recrystallization. With higher rolling temperature, dynamic recrystallization was initiated in lower reduction. However with increasing reduction per pass, deformation was locallized in band-like regions, which provided favorable nucleation sites f3r dynamic recrystallization. Through post annealing process, the microstructures could be transformed to more equiaxed and homogeneous grain structures. Textures of the rolled sheets were characterized by $\{0002\}$ basal plane textures and retained even after post annealing. On the other hand, asymmetrically rolled and subsequently annealed sheets exhibited unique annealing texture, where $\{0002\}$ orientation was rotated to some extent to the rolling direction and its intensity was reduced.

• 한국재료학회지
• /
• 제4권2호
• /
• pp.241-249
• /
• 1994

항공기용 고력 AI합금인 7075 AI합금의 물성개선을 위한 가공열처리 방안으로서 과시효처리후 온간 및 냉간 압연에 의한 소성가공이 재결정조직과 강도에 미치는 영향에 대하여 연구하였다. 소송가공후 재결정처리에 의해 결정립을 미세화하는 공정에서 소성가공 전 과시효를 함으로써 재결정립의 미세화 정도는 더욱 현저하였다. 이는 과시효에 의한 조대한 석출물이 재결정처리시 핵생성 site로서 작용하였음을 의미한다. 본 연구에서 항복강도와 재결정립의 크기와는 Hall-petch식을 만족하지 않았으며 이는 등축이 아닌 연신된 결정조직에 기인된 결과로 보이며, 항복강도가 재결정립의 종횡비에 직선적으로 비례하였다. 또한 결정립 미세화를 통한 강도, 인성향상을 목적으로 하는 TMT(Thermo mechanical Treatment)공정에서는 심한 냉간가공에 의해서보다는 온간에서의 소성가공이 바람직함을 알 수 있었다.

• 한국표면공학회지
• /
• 제44권4호
• /
• pp.131-136
• /
• 2011

A kinetic study has been made for the growth of nanocrystalline diamond (NCD) particles to a continuous thin film on silicon substrate in a microwave plasma chemical vapor deposition reactor. Parameters of deposition have been microwave power of 1.2 kW, the chamber pressure of 110 Torr, and the Ar/$CH_4$ ratio of 200/2 sccm. The deposition has been carried out at temperatures in the range of $400\sim700^{\circ}C$ for the times of 0.5~16 h. It has been revealed that a continuous diamond film evolves from the growth and coalescence of diamond crystallites (or particles), which have been heterogeneously nucleated at the previously scratched sites. The diamond particles grow following an $h^2$ = k't relationship, where h is the height of particles, k' is the particle growth rate constant, and t is the deposition time. The k' values at the different deposition temperatures satisfy an Arrhenius equation with the apparent activation energy of 4.37 kcal/mol or 0.19 eV/ atom. The rate limiting step should be the diffusion of carbon species over the Si substrate surface. The growth of diamond film thickness (H) shows an H = kt relationship with deposition time, t. The film growth rate constant, k, values at the different deposition temperatures show another Arrhenius-type expression with the apparent activation energy of 3.89 kcal/mol or 0.17 eV/atom. In this case, the rate limiting step might be the incorporation reaction of carbon species from the plasma on the film surface.

• 한국주조공학회지
• /
• 제13권4호
• /
• pp.369-381
• /
• 1993

Aluminum alloy(AC8A) matrix composites reinforced with SiC particles(10% in vol.) were fabricated by Centrifugal Spray Deposition(CSD) process. The microstructures were investigated in order to evaluate both the mixing mode between aluminum matrix and SiC particles, and the effect of SiC particles on the cooling behaviours of droplets during flight and preforms deposited. A non-continuum mathematical calculation was performed to explain and to quantify the evolution of microstructures in the droplets and preforms deposited. Conclusions obtained are as follows; 1. The powders produced by CSD process showed, in general, ligament type, and more than 60% of the powders produced were about 300 to 850 um in size. 2. AC8A droplets solidified during flight showed fine dendritic structure, but AC8A droplets mixed with SiC particles showed fine equiaxed grain structure, and eutectic silicon were formed to crystallize granularly between fine aluminum grains. 3. SiC particles seem to act as a nucleation sites for pro-eutectic silicon during solidification of AC8A alloy. 4. The microstructure of composite powders formed by CSD process showed particle embedded type, and resulted in dispersed type microstructure in preforms deposited. 5. The pro-eutectic silicon crystallized granularly between fine aluminum grains seem to prohibit grains from growth during spray deposition process. 6. The interfacial reactions between aluminum matrix and SiC particles were not observed from the deposit performs and the solidified droplets. 7. The continuum model seem to be useful in connecting the processing parameters with the resultant microstructures. From these results, it was concluded that the fabrication of aluminum matrix composites reinforced homogeneously with SiC particles was possible.