• Korean Journal of Materials Research
• /
• v.16 no.12
• /
• pp.739-742
• /
• 2006

The ${\gamma}-Fe_2O_3$ nano particles in the size range of $5{\sim}30$ nm were prepared by a chemical coprecipitation method. The nano particles were coated with 2nd surfactants for obtaining the water-based. The size effect of ${\gamma}-Fe_2O_3$ nano particles for the ultraviolet protection was investigated. The variation of the UV-Vis transmittance spectra as a function of wavelength for a ${\gamma}-Fe_2O_3$ nano particles were showed red-shifted increase with the particle size. The protective effects of UVA onset at near 469, 494, 591 nm for a particle size of 8.7, 9.1 and 12 nm. It is shown that the ${\gamma}-Fe_2O_3$ nano particles was good materials for protect of UV.

• Journal of Powder Materials
• /
• v.9 no.5
• /
• pp.341-345
• /
• 2002

Nanoparticles of $Fe_2O_3$ with a mean particle size of 4-30 nm have been prepared by a pulsed wire evaporation method, and its structural and magnetic properties were studied by SQUID magnetometer and Mossbauer spectroscopy. From the main peak intensity of XRD and absorption rate of Mossbauer spectrum, the amounts of $\gamma-Fe_2O_3$ and $\alpha-Fe_2O_3$ in as-prepared sample are about 70% and 30%, respectively. The coercivity (53 Oe) and the saturation magnetization (14 emu/g) are about 20% of those of the bulk $\gamma-Fe_2O_3$. The low value of coercivity and saturation magnetization indicate that the $\gamma-Fe_2O_3$ phase nearly shows the spin glass-like behavior. Analysis of the set of Mossbauer spectrum indicates a distribution of magnetic hyperfine fields due to the particle size distribution yielding 20 nm of average particle size. The magnetic hyperfine parameters are consistent with values reported of bulk $\gamma-Fe_2O_3$ and $alpha-Fe_2O_3$. A quadrupole line on the center of spectrum represents of superparamagnetic phase of $\gamma-Fe_2O_3$ with a mean particle size of 7 nm or below.

• Journal of Powder Materials
• /
• v.11 no.1
• /
• pp.50-54
• /
• 2004

Nanoparticles of iron oxides have been prepared by the levitational gas condensation (LGC) method, and their structural and magnetic properties were studied by XRD, TEM and Mossbauer spectroscopy. Fe clusters were evaporated from a surface of the levitated liquid Fe droplet and then condensed into nanoparticles of iron oxide with particle size of 14 to 30 nm in a chamber filled with mixtures of Ar and $O_2$ gases. It was found that the phase transition from both $\gamma$-$Fe_2O_3$ and $\alpha$-Fe to $Fe_3O_4$, which was evaluated from the results of Mossbauer spectra, strongly depended on the $O_2$ flow rate. As a result, $\gamma$-$Fe_2O_3$ was synthesized under the $O_2$ flow rate of 0.1$\leq$$Vo_2$(Vmin)$\leq$0.15, whereas $Fe_3O_4$ was synthesized under the $O_2$, flow rate of 0.15$\leq$$Vo_2$(Vmin)$\leq$0.2.

• Journal of Magnetics
• /
• v.9 no.3
• /
• pp.83-85
• /
• 2004

Magnetic nanoparticles have been investigated for use as biomedical purposes for several years. For biomedical applications the use of particles that present superparamagnetic behavior at room temperature is preferred [1-4]. To control the magnetic materials by magnetic field is essential locate particle to the suitable destination on feeding by injection. In order to use them properly, the particles should be nano size. However there are many difficulties in applications, because there is lack of identifications in nano magnetic properties. In our studies, structural and magnetic properties of iron oxide nanoparticles were investigated by XRD, VSM, TEM, and Mossbauer spectroscopy. At 13 K, hyperfine fields of ${\gamma}-Fe_2O_3$ were 516 kOe and 490 kOe, that of $Fe_3O_4$ were 517 kOe and 482 kOe. The saturation magnetizations were 21.42 emu/g and 39.42 emu/g. The particle size of powders is 5～19 nm.

• Journal of the Korean Magnetics Society
• /
• v.20 no.5
• /
• pp.196-200
• /
• 2010

$\gamma-Fe_2O_3$ nanoparticles have been prepared by a sol-gel method. The structural and magnetic properties have been investigated by XRD, VSM and Mossbauer spectroscopy. $\gamma-Fe_2O_3$ powder annealed at $150^{\circ}C$ has a spinel structure and superparamagnetical behavior. The estimated size of superparammagnetic $\gamma-Fe_2O_3$ nanoparticle is around 7 nm. The hyperfine fields at $-261^{\circ}C$ for the A and B patterns were found to be 503 and 485 kOe, respectively. The blocking temperature ($T_B$) of superparammagnetic $\gamma-Fe_2O_3$ nanoparticle is about $-183^{\circ}C$. The magnetic anisotropy constant of $\gamma-Fe_2O_3$ nanoparticle was calculated to be $1.6{\times}10^6ergs/cm^3$. $\gamma-Fe_2O_3$ nanoparticle annealed at $150^{\circ}C$ can be a candidate for biomedicine applications as magnetic carriers.

• Corrosion Science and Technology
• /
• v.7 no.2
• /
• pp.119-124
• /
• 2008

Steel is generally not corrosion resistant to water with formation of non protective rusts on its surface. Rusts are composed of iron oxides such as $Fe_3O_4$, $\alpha-$, $\beta-$, $\gamma-$and ${\delta}-FeOOH$. However, steel, particularly weathering steel containing small amounts of Cu, Ni and Cr etc., shows good corrosion resistance against rural, industrial or marine environment. Its corrosion rate is exceedingly small as compared with that of carbon steel. According to the exposure test results undertaken in outdoor environments, the atmospheric corrosion rate for weathering steel is only 1 mm for a century. Atmospheric corrosion for steels proceeds under alternate dry and wet conditions. Dry condition is encountered on steel surface on fine or cloudy days, and wet condition is on rainy or snowy days. The reason why weathering steel shows superior atmospheric corrosion resistance is due to formation of corrosion protective rusts on its surface under very thin water layer. The protective rusts are usually composed of two layer rusts; the upper layer is ${\gamma}-FeOOH$ termed as lepidocrocite, and inner layer is nano-particle ${\alpha}-FeOOH$ termed as goethite. This paper is aimed at elucidating the atmospheric corrosion mechanism for steel in comparison with corrosion in bulky water environment by use of empirical data.The summary is as follows: 1. No corrosion protective rusts are formed on steel in bulky water. 2. Atmospheric corrosion for steel is the corrosion under wetting and drying conditions. Corrosion and passivation occur alternately on steel surface. Steel, particularly weathering steel with small amounts of alloying elements such as Cu, Ni and Cr etc. enhances forming corrosion protective rusts by passivation.

• Korean Journal of Materials Research
• /
• v.20 no.3
• /
• pp.132-136
• /
• 2010

This study examined the biostability and drug delivery efficiency of g-$Fe_2O_3$ magnetic nanoparticles (GMNs) by cytotoxicity tests using various tumor cell lines and normal cell lines. The GMNs, approximately 20 nm in diameter, were prepared using a chemical coprecipitation technique, and coated with two surfactants to obtain a water-based product. The particle size of the GMNs loaded on hangamdan drugs (HGMNs) measured 20-50 nm in diameter. The characteristics of the particles were examined by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-TEM) and Raman spectrometer. The Raman spectrum of the GMNs showed three broad bands at 274, 612 and $771\;cm^1$. A 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide (MTT) assay showed that the GMNs were non-toxic against human brain cancer cells (SH-SY5Y, T98), human cervical cancer cells (Hela, Siha), human liver cancer cells (HepG2), breast cancer cells (MCF-7), colon cancer cells (CaCO2), human neural stem cells (F3), adult mencenchymal stem cells (B10), human kidney stem cells (HEK293 cell), human prostate cancer (Du 145, PC3) and normal human fibroblasts (HS 68) tested. However, HGMNs were cytotoxic at 69.99% against the DU145 prostate cancer cell, and at 34.37% in the Hela cell. These results indicate that the GMNs were biostable and the HGMNs served as effective drug delivery vehicles.