• Journal of the Korean Ceramic Society
• /
• v.49 no.5
• /
• pp.417-422
• /
• 2012

Copper nano particles have been considered as the materials for conductive ink due to its good thermal, electrical conductivity and low cost. However, copper nanoparticles oxidize easily, decreasing dispersion stability and electrical conductivity. Therefore, it is important to develop a method to minimize oxidation of copper nano particles to improve its dispersion stability property in copper nano ink. In this study, copper nano particles were coated with 1-Octanethiol VSAM(Vaporized Self Assembled Multilayers) to prevent oxidation and coated copper powders were dispersed in conductive ink successfully by studying its relationship of different chain length of solvents to 1-Octanethiol coating layer to fabricate nano ink. Various alcohol solvents, such as 1-Hexanol, 1-Octanol, and 1-Decanol were used. The coating layer was observed using FESEM and TEM. Furthermore, dispersion of copper nano particles in nano inks, was characterized using Turbiscan analyzer, viscometer, and contact angle measurement tool.

• Journal of Powder Materials
• /
• v.17 no.5
• /
• pp.390-398
• /
• 2010

Aqueous gold nanoparticle dispersion was synthesized by chemical reduction method using diethanolamine as reducing agent and polyethyleneimine as dispersion stabilizer. The synthesis conditions for the stable dispersion of the gold nanoparticle suspension were determined by changing the amount of the reducing agent and dispersant during the wet chemical synthesis procedures. The face centered cubic lattice structure of the gold nanoparticles was confirmed by using X-ray diffraction and the morphologies of the nanoparticles were observed by transmission electron microscope. The synthesized gold nanoparticle dispersion was concentrated by evaporating the dispersion medium at room temperature followed by the addition of ethyleneglycol as humectant for the increase of the elastic properties to obtain gold nanoparticle inks for direct ink writing process. The line patterns were obtained with the gold nanoparticle inks during the writing procedures and the morphologies of the fine patterns were observed by scanning electron microscope.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.1466-1468
• /
• 2009

The preparation method of copper nanopowder by dry process for conductive ink was investigated. Inert gas condensation method was used to synthesize copper nanopowder. The produced powders was spherical and sized 10~100nm flowing the conditions. The results showed that input voltage and evaporation rate is critical variables for nano-sized copper powder.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.865-867
• /
• 2009

In this paper, we describe the fabrication of nano-scale ink particles with narrow size distribution to offer high optical density in electrophoretic display applications. Charged white ($TiO_2$ and polyester) and black (carbon black and polyester) nano size ink particles in size range of 200 ~ 700nm were made successively using modified non-aqueous base emulsion process. The EPD showed white reflectance of 58% and saturation voltage of ${\pm}10V$.

• Journal of Powder Materials
• /
• v.20 no.2
• /
• pp.120-124
• /
• 2013

This study is carried out to develop the new process for the fabrication of ultra-fine electrodes on the flexible substrates using superhydrophobic effect. A facile method was developed to form the ultra-fine trenches on the flexible substrates treated by plasma etching and to print the fine metal electrodes using conductive nano-ink. Various plasma etching conditions were investigated for the hydrophobic surface treatment of flexible polyimide (PI) films. The micro-trench on the hydrophobic PI film fabricated under optimized conditions was obtained by mechanical scratching, which gave the hydrophilic property only to the trench area. Finally, the patterning by selective deposition of ink materials was performed using the conductive silver nano-ink. The interface between the conductive nanoparticles and the flexible substrates were characterized by scanning electron microscope. The increase of the sintering temperature and metal concentration of ink caused the reduction of electrical resistance. The sintering temperature lower than $200^{\circ}C$ resulted in good interfacial bonding between Ag electrode and PI film substrate.

• Analytical Science and Technology
• /
• v.29 no.1
• /
• pp.35-42
• /
• 2016

A new nano-composite carbon ink for the development of disposable dopamine (DA) biosensors based on screen-printed carbon electrodes (SPCEs) is introduced. The method developed uses SPCEs coupled with a tyrosinase modified nano-composite carbon ink. The ink was prepared by an “in-house” procedure with reduced graphene oxide (rGO), Pt nanoparticles (PtNP), and carbon materials such as carbon black and graphite. The rGO-PtNP carbon composite ink was used to print the working electrodes of the SPCEs and the reference counter electrodes were printed by using a commercial Ag/AgCl ink. After the construction of nano-composite SPCEs, tyrosinase was immobilized onto the working electrodes by using a biocompatible matrix, chitosan. The composite of nano-materials was characterized by X-ray photoelectron spectroscopy (XPS) and the performance characteristics of the sensors were evaluated by using voltammetric and amperometric techniques. The cyclic voltammetry results indicated that the sensors prepared with the rGO-PtNP-carbon composite ink revealed a significant improvement in electro-catalytic activity to DA compared with the results obtained from bare or only PtNP embedded carbon inks. Optimum experimental parameters such as pH and operating potential were evaluated and calibration curves for dopamine were constructed with the results obtained from a series of amperometric detections at −0.1 V vs. Ag/AgCl. The limit of detection was found to be 14 nM in a linear range of 10 nM to 100 µM of DA, and the sensor’s sensitivity was calculated to be 0.4 µAµM⁻¹cm⁻².

• 한국정보디스플레이학회:학술대회논문집
• /
• 2006.08a
• /
• pp.1382-1385
• /
• 2006

We have studied ink-jet printing method for patterning of conductive line on flexible plastic substrates. Synthesized copper nano-particles of ${\sim}40\;nm$ were used for the conductive ink and the printed patterns exhibit a smooth line whose line width is about $100\;{\mu}m$.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1491-1494
• /
• 2005

We have studied ink-jet printing method for patterning conductive line on flexible plastic substrates. Synthesized silver nano-particles of ${\sim}$20nm were used for the conductive ink and the printed patterns exhibit a smooth line whose linewidth is below 100 ${\mu}m$. This ink-jet printing technique can be applied to flexible displays and electronics.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.788-791
• /
• 2004

We have studied the fabrication of silver micro lines using the silver nano sol on ITO substrate by an ink-jet method. The average particles size of $10wt\%$ silver nano sol synthesized with polyelectrolytes was smaller than 10 nm. The pattern formation of silver nano sol on the substrate closely related with the contact angle of the silver nano sol. The dot shaped of silver nano sol on bare ITO substrate was formed due to the high contact angle of silver nano sol. When ITO substrates was treated with 100 ppm polyethylenimine for silver nano sol patterning, fine silver micro lines of $60{\sim}100{\mu}m$ width was fabricated by ink-jet method.

• Korean Journal of Materials Research
• /
• v.24 no.2
• /
• pp.73-80
• /
• 2014

Ink-jet printing technology has been widely attractive due to its facility for direct and fine printing on various substrates. Recent studies have focused on expanding the application of ink-jet printing technology from general consumer use and design companies to the prototype production of precision parts and parts manufacturing. The use of ink-jet printing technology in decorated tableware, tiles, and other ceramic products also has many advantages. The printing process is fast and can be adaptable to various kinds of objects because there is no direct contact point between the printer and the substrates to be printed. For application to ceramic product decoration, inks containing highly dispersed inorganic nano-pigments are required. Here we report the synthesis and characterization of blue $CoAl_2O_4$ nanopigment for ink-jet printing. Blue ceramic ink based on the obtained $CoAl_2O_4$ pigment was prepared by dissolving $CoAl_2O_4$ pigment in a mixed solution of ethylene glycol and ethanol with volume ratios of 7:3 and 8:2, respectively, to obtain the appropriate viscosity for ink-jet printing. The ink solution contained 15 wt% of $CoAl_2O_4$ pigment and Cetyltrimethyl ammonium bromide(CTAB) and Sodium dodecyl sulfate(SDS) as dispersive agents. The prepared blue ceramic ink was stably jetted and formed a sphere-shaped droplet from an ink-jet printer.