• Restorative Dentistry and Endodontics
• /
• v.32 no.4
• /
• pp.365-376
• /
• 2007

The purpose of this study was to evaluate the effect of different etching times on microtensile bond strength (${\mu}TBS$) to dentin both initial and after thermocycling with 3 different types of total-etching adhesives. Fifty four teeth were divided into 18 groups by etching times (5, 15, 25 sec), adhesives types (Scotchbond Multipurpose (SM), Single Bond (SB), One-Step (OS)) and number of thermocycling (0, 2,000 cycles). Flat dentin surfaces were prepared on mid-coronal dentin of extracted third molars. After exposed fresh dentin surfaces were polished with 600-grit SiC papers, each specimen was acid-etched with 35% phosphoric acid (5, 15, 25 sec) and bonded with 3 different types of total etching adhesives respectively. Then, hybrid composite Z-250 was built up. Half of them were not thermocycled (control group) and the ethers were subjected to 2,000 thermocycle (experimental group). They were sectioned occluso-gingivally into $1.0\;{\times}\;1.0\;mm^2$ composite-dentin beams and tested with universal testing machine at a crosshead speed of 1.0 mm/min. Within limited data of this study, the results were as follows 1. There was no statistically significant difference in ${\mu}TBS$ between the thermocycled and non-thermocycled groups, except for both SM and SB etched for 25 sec. 2. In thermocycled SM and SB groups, bond strength decreased by extended etching time. In total etching systems, adhesive durability for dentin could be affected by type of solvents in adhesive and etching time. Especially, extended etching time may cause deteriorate effects on bond strength when ethanol-based adhesive was used.

• Restorative Dentistry and Endodontics
• /
• v.47 no.1
• /
• pp.4.1-4.13
• /
• 2022

Objectives: This study evaluated the effects of different smear layer preparations on the dentin permeability and microtensile bond strength (µTBS) of 2 self-etching adhesives (Clearfil SE Bond [CSE] and Clearfil Tri-S Bond Universal [CTS]) under dynamic pulpal pressure. Materials and Methods: Human third molars were cut into crown segments. The dentin surfaces were prepared using 4 armamentaria: 600-grit SiC paper, coarse diamond burs, superfine diamond burs, and carbide burs. The pulp chamber of each crown segment was connected to a dynamic intra-pulpal pressure simulation apparatus, and the permeability test was done under a pressure of 15 cmH₂O. The relative permeability (%P) was evaluated on the smear layer-covered and bonded dentin surfaces. The teeth were bonded to either of the adhesives under pulpal pressure simulation, and cut into sticks after 24 hours water storage for the µTBS test. The resin-dentin interface and nanoleakage observations were performed using a scanning electron microscope. Statistical comparisons were done using analysis of variance and post hoc tests. Results: Only the method of surface preparation had a significant effect on permeability (p < 0.05). The smear layers created by the carbide and superfine diamond burs yielded the lowest permeability. CSE demonstrated a higher µTBS, with these values in the superfine diamond and carbide bur groups being the highest. Microscopic evaluation of the resin-dentin interface revealed nanoleakage in the coarse diamond bur and SiC paper groups for both adhesives. Conclusions: Superfine diamond and carbide burs can be recommended for dentin preparation with the use of 2-step CSE.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.29 no.1
• /
• pp.37-44
• /
• 2013

Sodium hypochlorite and ethylene diamine tetra acetic acid are substances usually used during endodontic treatment. Several studies found that the bonding was negated with certain irrigants and some of the used irrigants have demineralizing and chealating effects, so it was advocated to omit the etching step in etch and rinse adhesive systems. The purpose of this in vitro study was to evaluate the influence of NaOCl & EDTA on the bonding strength of ethanol wet bonding. Thirty human molars were selected and mesiodistally sectioned into halves, thus providing sixty specimens. The specimens were randomly assigned to 4 groups(n=15) according to the irrigant regimen used : (1) irrigated with distilled water for 10min (control); (2) irrigated with 5.25% NaOCl(10min), flushed with 5.25% NaOCl(1min) (3) irrigated with 5.25% NaOCl, flushed with 17% EDTA (4) irrigated with 5.25% NaOCl, flushed with 17% EDTA. Each group was acid-etched with 37% phosphoric acid(except group 4) and had their dentin surfaces dehydrated with ethanol solutions : 50%, 70%, 80%, 95%, 3x100%, 30s for each application. After dehydration, a primer( 50% all bond 3 resin + 50% ethanol) was used, followed by the adhesive(ALL-BOND 3 RESIN) application. Resin composite build-ups were then prepared using an incremental technique. Specimens were sectioned into beams and submitted to a tensile load using a Micro Tensile Tester(Bisco Inc.). The data were statistically analyzed using one-way ANOVA and Tukey HSD at p<0.5 level. There was no significant difference on G1(control) and G2(irrigated with NaOCl only ). (p>0.05). G3(flushed with EDTA) showed significantly high tensile bonding strength compared to the G2 (p<0.05). G4( treated with EDTA but no acid-etching) was significantly lower value than G3. (p<0.05) Although there was no significant difference, 5.25% NaOCl seemed to have an adverse effect on the bonding strength of ethanol wet bonding. The flushing with EDTA after NaOCl irrigation prevents the decrease of bonding strength. The use of 17% EDTA as a final flush can enhance the bonding strength but EDTA flushing can't substitute for a acid-etching.

• The Journal of Korean Academy of Prosthodontics
• /
• v.57 no.2
• /
• pp.95-101
• /
• 2019

Purpose: The aim of this study is to evaluate the effects of various primers on the microtensile bond strength (${\mu}TBS$) of resin cements to cobalt-chromium (Co-Cr) dental casting alloy. Materials and methods: Four adhesive primers (Universal primer, Metal primer II, Alloy primer, and Metal/Zirconia primer) and two resin cements (Panavia F2.0, G-CEM LinkAce) were tested. One hundred fifty Co-Cr beams were prepared from Co-Cr ingots via casting ($6mm\;ength{\times}1mm\;width{\times}1mm\;thick$). The metal beams were randomly divided into ten groups according to the adhesive primers and resin cements used; the no-primer groups served as the control (n = 15). After sandblasting with aluminum oxide ($125{\mu}m$ grain), the metal and resin cements were bonded together using a silicone mold. Prior to testing, all metal-resin beams were examined under stereomicroscope, and subjected to the ${\mu}TBS$ test. The mean value of each group was analyzed via one-way ANOVA with Tukey's test as post hoc (${\alpha}=.05$) using SPSS software. Results: The mean ${\mu}TBS$ of all groups was ranged from 20 to 28 MPa. There is no statistically significant difference between groups (P > .05). Mixed failure, which is the combination of adhesive and cohesive failures, is the most prevalent failure mode in both the Panavia F2.0 and G-Cem LinkAce groups. Conclusion: The ${\mu}TBS$ of all tested groups are relatively high; however, the primers used in this study result in no favorable effect in the ${\mu}TBS$ of Panavia F2.0 and G-Cem LinkAce resin cement to Co-Cr alloy.

• Restorative Dentistry and Endodontics
• /
• v.43 no.2
• /
• pp.14.1-14.16
• /
• 2018

Objectives: The aim of this systematic review was to critically analyze previously published studies of the effects of dentin surface pretreatment with deproteinizing agents on the bonding of self-etch (SE) adhesives to dentin. Additionally, a meta-analysis was conducted to quantify the effects of the above-mentioned surface pretreatment methods on the bonding of SE adhesives to dentin. Materials and Methods: An electronic search was performed using the following databases: Scopus, PubMed and ScienceDirect. The online search was performed using the following keywords: 'dentin' or 'hypochlorous acid' or 'sodium hypochlorite' and 'self-etch adhesive.' The following categories were excluded during the assessment process: non-English articles, randomized clinical trials, case reports, animal studies, and review articles. The reviewed studies were subjected to meta-analysis to quantify the effect of the application time and concentration of sodium hypochlorite (NaOCl) and hypochlorous acid (HOCl) deproteinizing agents on bonding to dentin. Results: Only 9 laboratory studies fit the inclusion criteria of this systematic review. The results of the meta-analysis revealed that the pooled average microtensile bond strength values to dentin pre-treated with deproteinizing agents (15.71 MPa) was significantly lower than those of the non-treated control group (20.94 MPa). Conclusions: In light of the currently available scientific evidence, dentin surface pretreatment with deproteinizing agents does not enhance the bonding of SE adhesives to dentin. The HOCl deproteinizing agent exhibited minimal adverse effects on bonding to dentin in comparison with NaOCl solutions.

• Restorative Dentistry and Endodontics
• /
• v.28 no.1
• /
• pp.89-99
• /
• 2003

The purpose of this study was to investigate the bonding of resin- based root canal sealer, AH26 when the sealer was applied as a thin layer between dentine and gutta-percha surface. In this study forty non-caries extracted human molars and resin-based root canal sealer(AH 26, DeTrey/Dentsply, Germany) were used. Disks of gutta-percha, 6mm in diameter.6mm thick (Diadent/Dentsply, Korea) for thermoplastic obturation were used and dentin surfaces were treated with 2% NaOCl(Group 1) or 2%NaOCl+17% EDTA(Group 3). Disks of gutta-Percha, 6mm in diameter.6mm thick (Diadent/Dentsply, Korea) for conventional obturation were used and dentin surface were treated with 2% NaOCl(Group 2) or 2%NaOCl+17% EDTA(Group 4). Enamel was removed by a horizontal section 1mm below the deepest portion of the central occlusal groove by using a watercooled low speed diamond saw. A second horizontal section was done around cementoenamel junction. Exposed dentin surface was cut to approximately $8{\times}8{\;}mm$ rectangular shape and was ground against 320, 400, 600 grade silicon carbide abrasive paper serially. After grinding, the dentine surface were soaked in a solution of 2% NaOCl for 30 minutes and twenty of specimens were treated with 17% EDTA solution for 1 minute. The treated specimens were washed and dried, Root canal sealer, AH26 was prepared according to the manufacture's instructions The Gutta-percha and dentin surface were coated with a thin layer of the freshly mixed seal or. The specimens were left overnight at room temperature. After their initial set, they were transferred to an incubator at $37$^{\circ}C$ for 72 h. After 72 hours, resin blocks were made. The resin block was serially sectioned vertically into stick of $1{\cdot}1mm$. Twenty sticks were prepared from each group. After that, tensile bond strength f3r each stick was measured with Microtensile Tester Failure patterns of the specimens at the interface between gutta-percha and dentin were observed under the SEM(x1000) and Stereomicroscope (LEICA M42O, Meyer Inst., TX U.S.A) at 1.25 x25 magnification. The results were statistically analysed by using a One-way ANOVA and Tukey's test. The results were as follows; 1. Tensile bond strengths($mean{\pm}SD$) were expressed with ascending order as follows: Group 1, $3.09{\pm}$ 1.05Mpa : Group 2, $6.23{\pm}1.16MPa$ : Group 3, $7.12{\pm}1.07MPa$ : Group 4, $10.32{\pm}2.06MPa$. 2. Tensile bond strengths of the group 2 and 4 used disks of gutta-percha for conventional obturation were significantly higher than that of the group 1 and 3 used fir thermoplastic obturation. (p < 0.05). 3. Tensile bond strengths of the group 3 and 4 treated with 2% NaOC1+17% EDTA were significantly higher than that of the group 1 and 2 treated with 2% NaOCl. (p < 0.05). 4. In analysis of failure patterns at the interface between sealer and gutta-percha, there were observed 49 (61%)cases of adhesive failure patterns and 31 (39%) cases of mixed failures patterns.

• Journal of Dental Rehabilitation and Applied Science
• /
• v.27 no.2
• /
• pp.161-174
• /
• 2011

The purpose of this study was to evaluate the effect of ethanol addition on efficacy of two-step total-etch adhesive under over-wet condition by measurement of remaining volatile part (RVP), microtensile bond strength (${\mu}TBS$), and degree of conversion (DC). Two-step total-etch adhesive, Optibond Solo Plus (Kerr, Orange, USA), was used. Experimental groups were divided into 8 groups: Group 1 (only 10 ${\mu}l$ adhesive), Group 2 (mixture of 3 ${\mu}l$ distilled water and 10 ${\mu}l$ adhesive), From Group 3 to Group 8 (mixture of 3 ${\mu}l$ distilled water, 10 ${\mu}l$ adhesive, and ethanol added in 1 ${\mu}l$ increment from 1 ${\mu}l$ to 6 ${\mu}l$). The mixtures were placed on slide glass and evaporated for 10 s, 30 s, and 60 s by air-drying. The weight of RVP was measured by precision weight. Same procedures were performed for ${\mu}TBS$ test and measurement of DC. The condition of mixed solution was observed under light microscope. For RVP weight, the weights of experimental groups except for group 1 decreased with the increase of air-drying time (p<0.05). The DC increased with the increase of air-drying time in only group 5 and 6 (p<0.05). The ${\mu}TBS$ increased with the increase of air-drying time in group only 5, 6, and 7 (p<0.05). The phase separation was examined and water blisters were diminished with the increase of air-drying time in group 5, 6, 7, and 8. Within the limits of this study, ethanol additionally applied to adhesive decreased RVP and increased DC and ${\mu}TBS$ under over-wet condition. It was shown that the addition of ethanol to two-step total-etch adhesive under over-wet condition would remove water and increase the efficacy of adhesive.