• Journal of Adhesion and Interface
• /
• v.8 no.2
• /
• pp.9-14
• /
• 2007

Poly(ethylene glycol) (PEG), isophoron diisocyanate (IPDI), and 1,1,1-tris(hydroxymethyl)propane (THMP) were used to synthesize polyurethane microgel. The formulation to form a microgel was determined, and the shape and the properties of the microgel were characterized with SEM and particle size analyzer. The microgel was only formed when PEG was used more than THMP exceedingly. Therefore, it is believed that PEG plays an important role in the synthesis of the microgel. During the formation of the microgel, the viscosity of the microgel solution was decreased. Molecular weights of the PEGs which were used in this research were 2,000, 6,000, and 10,000. The microgel synthesized with PEG 6000 showed the best property in comparison with others. The size of the microgel measured by particle size analyzer were about 130~230 nm.

• Applied Chemistry for Engineering
• /
• v.9 no.4
• /
• pp.591-594
• /
• 1998

Biodegradable microsphere containing bovine serum albumine (BSA) as a model drug were prepared with the microgel based on poly(caprolactone diol) by a modified solvent evaporation method. The influence of the stirring speed, the concentration of microgel and the mixing rate but increased with increasing the concentration of microgel in methylene chloride. The biodegradability of microsphere in 100 unit/mL of lipase solution was investigated. A lot of small pores appeared on the surface of microsphere after 3 hours of incubation time and the pores and cracks were developed with increasing the incubation time and microsphere lost their own shape after 36 hours of incubation time.

• Applied Chemistry for Engineering
• /
• v.7 no.2
• /
• pp.350-355
• /
• 1996

Poly(AA-co-EGDMA) microgels were prepared by precipitation polymerization in highly swollen polystyrene gel solution. The polymerization was carried out in selective solvent such as cyclohexane/acetone at $60^{\circ}C$. Poly(AA-co-EGDMA) microgels with various site of $0.18{\sim}0.55{\mu}m$ were obtained from different concentration of polystyrene(PS), concentration of crosslinking agent(EGDMA), ratio of Ps/monomer and volume ratio of solvents. The particle size of poly(AA-co-EGDMA) microgels decreased with increasing the concentration of PS and increased with that of EGDMA.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.8
• /
• pp.1396-1400
• /
• 2007

In this study, poly(iso-butyl methacrylate-co-ethylene glycol dimethacrylate) [poly(iso-BMA-co-EGDMA)] microgel was prepared and used as a face powder additive. The spreading, adhesiveness, and skin reactivity of poly(iso-BMA-co-EGDMA) microgel-containing face powder II were investigated and compared with the same properties of commercially available Silica bead 700-containing face powder I. In the results, the particle size of the poly(iso-BMA-co-EGDMA) microgel was significantly swelled as a result of sebum absorption. Face powder II showed a lower primary irritation index and a higher adhesiveness than did face powder I. Face powder I showed a low sebum absorption ratio and a relatively high rate of sebum absorption, whereas face powder II, contrastingly, exhibited a high sebum absorption ratio and a low rate of sebum absorption, which properties would reduce the phenomena of facial strain and sliminess. These results indicate that poly(iso- BMA-co-EGDMA) microgel has outstanding sebum absorption characteristic and adhesiveness, and thus that it is a good candidate for use as a face powder additive.

• Proceedings of the Polymer Society of Korea Conference
• /
• 2006.10a
• /
• pp.318-318
• /
• 2006

4-Vinylbenzyl maltohexaoside peracetate, 1, was copolymerized with divinylbenzene using the initiator for nitroxide-mediated living radical polymerization, 2, to afford the polystyrene microgel with acetyl maltohexaose, 3. The deacetylation of 3 was achieved by treatment with sodium methoxide in dry 1,4-dioxane to produce the polystyrene microgel with maltohexaose, 4. A good coating property of the polystyrene microgel was combined with an excellent hydrophilic property derived from maltohexaose. In addition, 4 showed the ability to solubilize fullerene in aqueous solution. Therefore, 4 has a potential application as a special coating using functional but incompatible compounds such as fullerene on the surface of various hydrophilic materials.

• Bulletin of the Korean Chemical Society
• /
• v.28 no.9
• /
• pp.1493-1498
• /
• 2007

In this work, alkyl methacrylate-based microgels were synthesized by an experimental design method, and their sebum absorption characteristics were investigated. The results of fractional factorial experimentation indicated that the cross-linking agent content, solvent content, and stirring speed were the main parameters in the synthesis of the microgels. The suitable synthesis conditions were determined by the response surface design method. Through a study of the monomer and solvent effects, it was confirmed that the microgel shows the highest sebum absorption ratio when t-butyl methacrylate is used as a monomer or when acetone is used as a solvent. The optimal microgel synthesis conditions for cosmetic application were determined, and the resulting microgel had a mean particle size of 4.7 μm and a sebum absorption ratio of 435%.

• Textile Coloration and Finishing
• /
• v.28 no.4
• /
• pp.280-289
• /
• 2016

Silica microgel was prepared by sol-gel process and then functional groups, epoxy group and ethoxy group, were introduced on the particle by coupling treatment with 3-glysidoxypropyltrimethoxysilane. The functional silica microgel(functional SiGel) formation was identified using FT-IR spectrometry. Phase stability for DMF solution of functional SiGel, PU resin and pigment was evaluated by Turbiscan Lab. And physical properties of artificial suede including hand values, morphology and dyeing fastness were investigated. The mean particle size and the specific surface area of the functional SiGel were $0.77{\mu}m$ and $380m^2/g$. Mixture containing the functional SiGel, PU resin and pigment was more stable than the functional SiGel-free mixed solution. Artificial suede prepared by the functional SiGel had appearance and feeling close to natural suede. The migration fastness, the solvent wicking fastness and rubbing fastness of the artificial suede were enhanced to 4~5 grades, 4~5 grades and 3~4 grades, respectively.

• Applied Chemistry for Engineering
• /
• v.16 no.3
• /
• pp.397-402
• /
• 2005

Core-shell Poly(styrene-co-N-isopropylacrylamide) (poly(St-co-NIPAm) was prepared by soap-free emulsion polymerization of styrene (St) and N-isopropylacrylamide (NIPAm) in aqueous solution with potassium persulfate (KPS) as an initiator. The effects of St/NIPAm ratio, concentrations of monomer and crosslinker were studied. Also, Thermo sensitivity of microgels prepared was investigated. Particle size of microgels increased with increasing mol ratio of NIPAm to styrene. Transmittance of the microgel dispersion decreased rapidly when heated above a low critical solution temperature (near $32{\sim}34^{\circ}C$, cloud point). Swelling ratio of the microgel increased with increasing of the concentration of monomer (NIPAm) and decreased proportional to the concentration of crosslinker.

• Elastomers and Composites
• /
• v.35 no.4
• /
• pp.281-287
• /
• 2000

Waterborne polyurethane(PU) microgel dispersions were synthesized with different mole ratio of polytetramethylene glycol(PTMG) to dimethylol propionic acid(DMPA). Particle size distribution, thermal and mechanical properties of the PU microgels were investigated. Particle size of the microgels was distributed in the range of $98{\sim}$680{\mu}m$ and decreased with increasing the mole ratio of DMPA and 1,2,6-hexanetriol. Glass transition temperature and melting temperature of the microgels were in the range of $-79.7 {\sim}-78.1^{\circ}C$, $22{\sim}24^{\circ}C$ respectively. Tensile strength and elongation of the PU microgel films were maximum in the case of 60/40 mole ratio of PTMG/DMPA.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.2
• /
• pp.645-655
• /
• 2019

In this study, colloidal microgel with viscoelasticity were prepared by using dispersion containing physical crosslinking agents and microgels with various strengths depending on the degree of cross-links.As the chemical crosslinking agent PEGDA400 content increased, hydrogels have various physical properties the swelling ratio decreased from $2.0{\times}10^4%$ to $6.0{\times}10^3%$ and increased viscosity by about 60%. The colloidal microgel was prepared with micro hydrogel grinded to $100{\mu}m$ size and the rheological behavior was confirmed with physical cross linking agent. A colloidal microgel having various viscosities was prepared by controlling starch and alginate based on micro-hydrogel containing 0.75% (w/v) of PEGDA400. In conclusion, these results would be highly useful for applying as a product that can give various physical properties to the colloidal suspensions, cosmetics, paint, and food industry.