• Clean Technology
• /
• v.20 no.1
• /
• pp.7-12
• /
• 2014

Hydrogenolysis of glycerol to propylene glycol was performed over binary and ternary metal oxide catalysts. The conversion of glycerol and selectivity to propylene glycol were increased on Cu/Zn and Cu/Cr mixed oxides compared to pure CuO and ZnO oxides. The addition of alumina into Cu/Zn mixed oxide very highly increased the conversion of glycerol and selectivity to propylene glycol. The conversion of glycerol was increased with increasing the reaction temperature but the selectivity to propylene glycol was shown to have maximum value at $200^{\circ}C$ and then decreased at $250^{\circ}C$. The conversion of glycerol and selectivity to propylene glycol were decreased with increasing the glycerol concentration.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.12
• /
• pp.3543-3548
• /
• 2010

A kinetic study on nucleophilic displacement reactions of 2-pyridyl X-substituted benzoates 1a-e with potassium ethoxide (EtOK) in anhydrous ethanol is reported. Plots of pseudo-first-order rate constants ($k_{obsd}$) vs. $[EtOK]_o$ exhibit upward curvature. The $k_{obsd}$ value at a fixed $[EtOK]_o$ decreases steeply upon addition of 18-crown-6-ether (18C6) to the reaction mixture up to [18C6]/$[EtOK]_o$ = 1 and then remains nearly constant thereafter. In contrast, $k_{obsd}$ increases sharply upon addition of LiSCN or KSCN. Dissection of $k_{obsd}$ into $k_{EtO^-}$ and $k_{EtOM}$ has revealed that ion-paired EtOK is more reactive than dissociated $EtO^-$, indicating that $K^+$ ion acts as a Lewis acid catalyst. Hammett plots for the reactions of 1a-e with dissociated $EtO^-$ and ion-paired EtOK result in excellent linear correlation with $\rho$ values of 3.01 and 2.67, respectively. The $k_{EtOK}/k_{EtO^-}$ ratio increases as the substituent X in the benzoyl moiety becomes a stronger electron-donating group. $K^+$ ion has been concluded to catalyze the current reaction by stabilizing the transition state through formation of a 6-membered cyclic complex.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.08a
• /
• pp.252.2-252.2
• /
• 2013

ZnO nanostructures have a lot of interest for decades due to its varied applications such as light-emitting devices, power generators, solar cells, and sensing devices etc. To get the high performance of these devices, the factors of nanostructure geometry, spacing, and alignment are important. So, Patterning of vertically- aligned ZnO nanowires are currently attractive. However, many of ZnO nanowire or nanorod fabrication methods are needs high temperature, such vapor phase transport process, metal-organic chemical vapor deposition (MOCVD), metal-organic vapor phase epitaxy, thermal evaporation, pulse laser deposition and thermal chemical vapor deposition. While hydrothermal process has great advantages-low temperature (less than $100^{\circ}C$), simple steps, short time consuming, without catalyst, and relatively ease to control than as mentioned various methods. In this work, we investigate the dependence of ZnO nanowire alignment and morphology on si substrate using of nanosphere template with various precursor concentration and components via hydrothermal process. The brief experimental scheme is as follow. First synthesized ZnO seed solution was spun coated on to cleaned Si substrate, and then annealed $350^{\circ}C$ for 1h in the furnace. Second, 200nm sized close-packed nanospheres were formed on the seed layer-coated substrate by using of gas-liquid-solid interfacial self-assembly method and drying in vaccum desicator for about a day to enhance the adhesion between seed layer and nanospheres. After that, zinc oxide nanowires were synthesized using a low temperature hydrothermal method based on alkali solution. The specimens were immersed upside down in the autoclave bath to prevent some precipitates which formed and covered on the surface. The hydrothermal conditions such as growth temperature, growth time, solution concentration, and additives are variously performed to optimize the morphologies of nanowire. To characterize the crystal structure of seed layer and nanowires, morphology, and optical properties, X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), Raman spectroscopy, and photoluminescence (PL) studies were investigated.

• Macromolecular Research
• /
• v.16 no.3
• /
• pp.204-211
• /
• 2008

A platinum-catalyzed polyelectrolyte porous membrane was prepared by solid-state compression of electrospun polystyrene (PS) fibers and in-situ metallization of counter-balanced ionic metal sources on the polymer surface. Using this ion-exchange metal-polymer composite system, fiber entangled pores were formed in the interstitial space of the fibers, which were surrounded by sulfonic acid sites ($SO_3^-$) to give a cation-selective polyelectrolyte porous bed with an ion exchange capacity ($I_{EC}$) of 3.0 meq/g and an ionic conductivity of 0.09 S/cm. The Pt loading was estimated to be 16.32 wt% from the $SO_3^-$ ions on the surface of the sulfonated PS fibers, which interact with the cationic platinum complex, $Pt(NH_3)_4^{2+}$, at a ratio of 3:1 based on steric hindrance and the arrangement of interacting ions. This is in good agreement with the Pt loading of 15.82 wt% measured by inductively coupled plasma-optical emission spectroscopy (ICP-OES). The Pt-loaded sulfonated PS media showed an ionic conductivity of 0.32 S/cm. The in-situ metallized platinum provided a nano-sized and strongly-bound catalyst in robust porous media, which highlights its potential use in various electrochemical and catalytic systems.

• Transactions of the Korean hydrogen and new energy society
• /
• v.28 no.1
• /
• pp.9-16
• /
• 2017

Hydrogen forms metal hydrides with some metals and alloys leading to solid-state storage under moderate temperature and pressure that gives them the safety advantage over the gas and liquid storage methods. However, it has disadvantages of slow hydrogen adsorption-desorption time and low thermal conductivity. To improve characteristics of metal hydrides, it is important that activation and thermal conductivity of metal hydrides are improved. In this study, we have been investigated hydrogen storage properties of Hydralloy C among Ti-Mn alloys. Also, the characteristics of activation and thermal conductivity of Hydralloy C were enhanced to improve kinetics of hydrogen adsorption-desorption. As physical activation method, PHEM (planetary high energy mill) was performed in Ar or $H_2$ atmosphere. Hydralloy C was also activated by $TiCl_3$ catalyst. To improve thermal conductivity, various types of ENG (expanded natural graphite) were used. The prepared samples were compacted at pressure of 500 bar. As a result, the activation properties of $H_2$ PHEM treated Hydralloy C was better than the other activation methods. Also, the amounts of hydrogen storage showed up to 1.6 wt%. When flake type ENG was added to Hydralloy C, thermal conductivity and hydrogen storage properties were improved.

• Applied Chemistry for Engineering
• /
• v.29 no.4
• /
• pp.432-439
• /
• 2018

Metal catalysts such as Fe, Co, Mn, and Pd supported on the activated carbon (AC) were prepared to improve functional groups for the chemical adsorption and catalytic ozonation. Following ascending orders of the phenol decomposition rate, dissolved ozone decomposition ratio and TOC (total organic carbon) removal from experimental results of advanced oxidation process (AOP) were observed: Fe-AC < AC < Co-AC < Mn-AC < Pd-AC. BET analysis results showed that the physical properties of the metal impregnated activated carbon had no effect on the catalytic ozonation, and the catalytic effect was dependent on the kind of impregnated metal. The ratio of the formed concentration of OH radical to that of ozone (RCT) was measured by using the decomposition outcome of p-chlorobenzoic acid, a probe compound that reacts rapidly with OH radical but slowly with ozone. The measured values of RCT were $5.48{\times}10^{-9}$ and $1.47{\times}10^{-8}$ for the ozone alone and activated carbon processes, respectively, and $2.13{\times}10^{-9}$, $1.51{\times}10^{-8}$, $4.77{\times}10^{-8}$, and $5.58{\times}10^{-8}$ for Fe-AC, Co-AC, Mn-AC, and Pd-AC processes, respectively.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.28 no.spc
• /
• pp.30-36
• /
• 2022

A sensor is needed to continuously and automatically measure the change in HNS concentration in industrial facilities that directly discharge to the sea after water treatment. The basic function of the sensor is to be able to detect ppb levels even at room temperature. Therefore, a method for increasing the sensitivity of the existing sensor is proposed. First, a method for increasing the conductivity of a film using a conductive carbon-based additive in a nanoparticle thin film and a method for increasing ion adsorption on the surface using a catalyst metal were studied.. To improve conductivity, carbon black was selected as an additive in the film using ITO nanoparticles, and the performance change of the sensor according to the content of the additive was observed. As a result, the change in resistance and response time due to the increase in conductivity at a CB content of 5 wt% could be observed, and notably, the lower limit of detection was lowered to about 250 ppb in an experiment with organic solvents. In addition, to increase the degree of ion adsorption in the liquid, an experiment was conducted using a sample in which a surface catalyst layer was formed by sputtering Au. Notably, the response of the sensor increased by more than 20% and the average lower limit of detection was lowered to 61 ppm. This result confirmed that the chemical resistance sensor using metal oxide nanoparticles could detect HNS of several tens of ppb even at room temperature.

• Macromolecular Research
• /
• v.9 no.4
• /
• pp.220-227
• /
• 2001

The polymerization of 1,6-heptadiyne was carried out by molybdenum and tungsten-based transition metal catalysts. This polymerization by MoCl$\_$5/ alone proceeded well to give a quantitative yield of polymer. The effect of monomer to catalyst mole ratio (M/C), initial monomer concentration ([M]$\_$0/), and the polymerization temperature for the cyclopolymerization of 1,6-heptadiyne was studied and discussed. The polymerization solution exhibited red color even after 30 min of polymerization time. The resulting polymers were mostly brown powders and mostly insoluble in any organic solvents although the polymerization proceeded in homogeneous manner in some cases. The polymer structure was characterized by various instrumental methods to have the conjugated polymer backbone structure carrying cyclic recurring unit. The thermal and morphological properties of the resulting poly(1,6-heptadiyne) were also discussed.

• Journal of the Korean Chemical Society
• /
• v.54 no.1
• /
• pp.23-26
• /
• 2010

A Schiff base ligand (Z)-N-((Z)-2-(sec-butylimino)-1,2-diphenylethylidene)butan-2-amine was synthesized by condensation of benzil with sec-butyl amine. Complexation of the ligand was carried out with first row transition elements, manganese(II) and nickel(II). Ligand and complexes were characterized by FTIR, elemental analysis and thermogravimetric analysis in solid state and by NMR ($^1H,\;^{13}C$) in solution form. Both the complexes demonstrate good catalytic activity for butadiene oligomerization under mild conditions with methylaluminoxane (MAO) as co-catalyst.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.169-169
• /
• 2012

The high-temperature superconductor YBa2Cu3O7-x (YBCO) have attached attentions because of a high superconducting transition temperature, low surface resistance, high superconducting critical current density (Jc), and superior superconducting capability under magnetic field. Moreover, the Jc of YBCO superconductors can be enhanced by adding impurities to the YBCO films for vortex-pinning. Understanding and controlling pinning centers are key factors to realize high Jc superconductors. We synthesized vertically-aligned ZnO nanorods on SrTiO3 (STO) substrates by catalyst-free metal-organic chemical vapor deposition (MOCVD), and subsequently, deposited YBCO films on the ZnO nanorods/STO templates using pulsed laser deposition (PLD). The various techniques were used to analyze the structural and interfacial properties of the YBCO/ZnO nanorods/STO hybrid structures. SEM, TEM, and XRD measurements demonstrated that YBCO films on ZnO nanorods/STO were well crystallized with the (001) orientation. EXAFS measurements from YBCO/ZnO nanorods/STO at Cu K edge demonstrated that the local structural properties around Cu atoms in YBCO were quite similar to those of YBCO/STO.