• Transactions on Electrical and Electronic Materials
• /
• 제12권6호
• /
• pp.249-252
• /
• 2011

We investigated the low firing of $Li_2CO_3$ added $0.2Pb(Mg_{1/3}Nb_{2/3})O_3$ - 0.3Pb($Fe_{1/2}Nb_{1/2}$) - $0.5Pb(Zr_{0.475}Ti_{0.525})O_3$ (PMN-PFN-PZT) ceramics and multilayer actuators (MLAs) using Ag inner electrodes. It was found that 0.1 wt% $Li_2CO_3$ was quite effective in lowering the sintering temperature of PMN-PFN-PZT ceramics from $1,100^{\circ}C$ down to $900^{\circ}C$ without deteriorating their piezoelectric ceramics ($d_{33}$ = 425 pC/N and $k_p$ = 61.9%). However, excess $Li_2CO_3$ up to 0.3 wt% brings about unwanted problems such as the formation of a $LiPbO_2$ secondary phase and subsequent degradation in the piezoelectric properties. Using 0.1 wt% $Li_2CO_3$ added PMN-PFN-PZT ceramics, MLAs with Ag inner electrodes were successfully fabricated, resulting in a normalized strain of 580 pm/V at an electric field of 1.5 kV/mm.

• 한국세라믹학회지
• /
• 제40권3호
• /
• pp.301-308
• /
• 2003

완전 세라믹 치관 재료로 응용할 수 있는 유리가 침투한 알루미나 복합체를 제조하였다. SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$계 유리에서 $Al_2$O$_3$의 함량을 변화시키며 다양한 조성의 유리를 만들고 이들 유리를 저온 소결한 다공성 알루미나에 침투시켰다. 그리고 이때 A1$_2$O$_3$의 함량변화가 유리의 침투 특성과 얻어진 복합체의 강도에 미치는 영향에 대하여 연구하였다. 유리 조성에서 A1$_2$O$_3$의 양을 증가시킬수록 알루미나 소결체의 부식 현상이 현저히 줄었으며 이에 따라 복합체의 강도가 증가하였다. 알루미나 소견체에는 거대기공이 존재하고 있어 복합체의 강도 저하에 영향을 미쳤는데 알루미나의 소결 온도를 130$0^{\circ}C$까지 증가시켜 이를 감소시켰다. 진공 분위기에서 알루미나 소결체에 유리를 침투시켰을 때 최고 453$\pm$31 MPa의 굽힘 강도 값을 얻을 수 있었다.