Effect of Glass Composition on the Properties of Glass-infiltrated Alumina(I) : Effect of Al2O3

Glass-infiltrated alumina, which can be used as an all-ceramic dental crown, was prepared. The glasses in the system of SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$with various amount of $Al_2$O$_3$infiltrated into a porous sintered alumina. The effect of $Al_2$O$_3$on the infiltration characteristics and its mechanical strength were studied. The corrosion of the sintered alumina by infiltrated glasses was prevented by increasing the amount of $Al_2$O$_3$in the glass batches, this increased the bending strength of the glass infiltrated alumina composite. The crack like voids in the sintered alumina was a cause of the deteriorating the mechanical strength of the composite, and this can be eliminated by sintering the alumina at 130$0^{\circ}C$. Glass infiltration under the vacuum atmosphere enhanced the hording strength of the composite up to 453$\pm$31 MPa.

유리가 침투된 알루미나 복합체의 물성에 미치는 유리조성의 영향(I): Al2O3의 영향

완전 세라믹 치관 재료로 응용할 수 있는 유리가 침투한 알루미나 복합체를 제조하였다. SiO$_2$-B$_2$O$_3$-Al$_2$O$_3$-CaO-La$_2$O$_3$계 유리에서 $Al_2$O$_3$의 함량을 변화시키며 다양한 조성의 유리를 만들고 이들 유리를 저온 소결한 다공성 알루미나에 침투시켰다. 그리고 이때 A1$_2$O$_3$의 함량변화가 유리의 침투 특성과 얻어진 복합체의 강도에 미치는 영향에 대하여 연구하였다. 유리 조성에서 A1$_2$O$_3$의 양을 증가시킬수록 알루미나 소결체의 부식 현상이 현저히 줄었으며 이에 따라 복합체의 강도가 증가하였다. 알루미나 소견체에는 거대기공이 존재하고 있어 복합체의 강도 저하에 영향을 미쳤는데 알루미나의 소결 온도를 130$0^{\circ}C$까지 증가시켜 이를 감소시켰다. 진공 분위기에서 알루미나 소결체에 유리를 침투시켰을 때 최고 453$\pm$31 MPa의 굽힘 강도 값을 얻을 수 있었다.