• The Journal of Advanced Prosthodontics
• /
• 제15권5호
• /
• pp.248-258
• /
• 2023

PURPOSE. This study aims to evaluate the effects of exposure energy on the lateral resolution and mechanical strength of dental zirconia manufactured using digital light processing (DLP). MATERIALS AND METHODS. A zirconia suspension and a custom top-down DLP printer were used for in-office manufacturing. The viscosity of the suspension and uniformity of the exposed light intensity were controlled. Based on the exposure energy dose delivered to each layer, the specimens were classified into three groups: low-energy (LE), medium-energy (ME), and high-energy (HE). For each energy group, a simplified molar cube was used to measure the widths of the outline (X_o and Y_o) and isthmus (X_i and Y_i), and a bar-shaped specimen of the sintered body was tested. A Kruskal-Wallis test for the lateral resolution and one-way analysis of variance for the mechanical strength were performed (α = .05). RESULTS. The zirconia green bodies of the ME group showed better lateral resolution than those of the LE and HE groups (both P < .001). Regarding the flexural strength of the sintered bodies, the ME group had the highest mean value, whereas the LE group had the lowest mean value (both P < .05). The ME group exhibited fewer agglomerates than the LE group, with no distinctive interlayer pores or surface defects. CONCLUSION. Based on these findings, the lateral resolution of the green body and flexural strength of the sintered body of dental zirconia could be affected by the exposure energy dose during DLP. The exposure energy should be optimized when fabricating DLP-based dental zirconia.

• 기본간호학회지
• /
• 제10권3호
• /
• pp.399-407
• /
• 2003

Purpose: This study was done to identify levels of physical fitness in student nurses and to ascertain the relationship among the different aspects of physical fitness of strength, power, muscle endurance, agility, balance and flexibility. Method: The participants were 266 students selected from one college of nursing. From May 1 to July 31 in 2003, physical constitution, muscle strength (grip strength, back strength), power (standing long jump), muscle endurance (sit-ups), agility (whole body reaction time-light, sound), balance (close-eyes foot-balance), and flexibility (sitting trunk flexion) were measured. Result: The mean(standard deviation) for grip strength was 22.59(3.93) kg., for back strength, 48.52(12.85) kg., for standing long jump, 135.29(20.54) m., for sit-up's, 23.66(9.35) per minute, whole body reaction time (light), 0.43(0.11) sec, whole body reaction time (sound), 0.50(0.16) sec, close-eyes foot-balance, 33.35(38.67) sec, and sitting trunk flexion 34.72(9.37) cm. Conclusion: This study showed that the physical fitness of student nurses is very low compared to the results in a report from the Korea Sports Science Institute. It is necessary to include exercise programs for student nurses in order to improve their physical fitness.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 추계 학술발표회 논문집
• /
• pp.845-848
• /
• 2006

This study sought to investigate the characteristics of cellular concrete, such as porosity, strength and density, according to the cell addition rate. Based on the result, it examined the application to a cellular concrete panel. Porosity was found to increase according to the cell addition rate, measuring continuous porosity of 42% and 47%, and total porosity of 61% and 66%. In terms of cell addition rate, measurements were 7% and 11% respectively. Compressive strength represented 5.0MPa, 3.8MPa and 2.8 MPa in terms of 7%, 9% and 11% respectively, decreasing 1 MPa of strength according to every 2% increase of cell addition rate. Density showed 0.55, 0.44 and 0.36 in terms of 7%, 9% and 11% respectively, decreasing 1.0 MPa according to every 2% increase of cell addition rate proportionally. In addition the sandwich panel of cellular concrete which was fabricated during this research was found to be relatively heavy and non-flammable with an excellent strength of 4.0 MPa. Compared with a light concrete panel, considering the compressive strength that accountsfor 10 MPa, it appeared relatively low in strength. However it would be excellent for application due to the light density of only 0.4 MPa.

• 대한치과교정학회지
• /
• 제28권2호
• /
• pp.277-284
• /
• 1998

본 연구의 목적은 브라켓 간접부착술식에서 레진 베이스의 재료에 따른 전단결합강도와 파절양상을 비교해 봄으로써 광중합형 레진 베이스 사용의 타당성을 평가해보는데 있다. 소의 하악 중절치를 포매하여 만든 시편의 석고 모형에 화학중합형 레진 접착제인 Excel과 광중합형 레진 접착제인 Light-Bond 및 열중합형 레진 접착제 인 Therma-Cure를 이용하여 금속 브라켓을 위치시 킨 후 transfer tray를 사용하여 시편에 옮겨 부착한 다음 만능물성 시험기를 이용하여 전단결합강도를 측정하고, 파절양상을 관찰하여 다음과 같은 결과를 얻었다. 1. 평균 전단결합강도가 화학중합형 레진 베이스를 사용한 군에서 $154.20{\pm}35.53kg/cm^2$, 광중합형 레진 베이스를 사용한 군에서 $148.61{\pm}39.21kg/cm^2$, 열중합형 레진 베이스를 사용한 군에서 $145.69{\pm}36.69kg/cm^2$로 나타났으며, 세군간에 유의한 차이가 없었다 (P>0.05). 2. 접착제 잔류지수를 통하여 파절양상을 비교 관찰한 결과 세 군간에 유의한 차이를 보이지 않았다(P>0.05). 이상의 실험결과는 브라켓 간접부착술식에서 레진 베이스의 재료로 화학중합형, 열중합형 레진과 함께 광중합형 레진도 사용될 수 있음을 시사하였다.

• 생물환경조절학회지
• /
• 제5권1호
• /
• pp.34-42
• /
• 1996

시설하우스에 이용되고 있는 보온커튼의 기초자료를 얻고, 시공기준을 설정하기 위하여 종류별, 두께별로 물리적, 광학적 특성을 시험 분석하였다. 시설하우스용 보온재는 광투과성, 차광성 및 인장응력을 비교시험 하였으며, 시험결과를 요약하면 다음과 같다. 1) 보온 커튼재의 인장응력 시험결과를 보면 인장하중은 3.4-13.4kg 범위이고 인장응력은 0.32-l.82kg/$\textrm{mm}^2$ 범위에서 커튼이 두꺼워짐에 따라 인장하중은 증가하나 인장응력은 큰 차이가 나타나지 않았으며 폴리프로필렌계가 신장율이 크고, 폴리에스터계는 인장 하중과 응력이 큰 경향을 보였다. 2) 광투과성은 390-1100nm 파장대 범위에서 평균 50.3-81.7% 범위로 보온커튼재가 두꺼울수록 광투과율이 낮고 상대적으로 차광율이 높아지며, 비슷한 두께에서 폴리프로필렌계가 폴리에스터계보다 광투과율이 20-30% 더 높은 것으로 나타났다. 3) 보온율은 18.2-41.1% 범위에서 보온재가 두꺼워질수록 증가하였으며, 폴리프로필렌계가 폴리에스터보다 보온율이 다소 높은 경향을 보였다. 4) 보온 커튼재는 폴리프로필렌계가 신장율, 보온성, 광투성 측면에서 우수하고 폴리에스테계가 인장응력이나 차광성 측면에서 우수하기 때문에 농가가 시설하우스 형태나 재배하는 작물의 특성에 따라 신중히 선택하여야 할 것으로 판단된다.

• 한국펄프종이공학회:학술대회논문집
• /
• 한국펄프종이공학회 1999년도 Pre-symposium of the 10th ISWPC Recent Advances in Paper Science and Technology
• /
• pp.386-389
• /
• 1999

Amphoteric polymers have brought to papermakers' attention gradually. In this paper, a series of amphoteric starches with different cationic and anionic degree of substitution (DS) are prepared. Better product has been selected and used under different condition. As retention and drainage aids, amphoteric starches were used in shorter fiber length, weak strength and poor drainage bleached AQ-Soda wheat straw pulp. In neutral and alkaline papermaking system, when amphoteric starches contain 0.024-0.026 anionic degree of substitution (DS), it is shown that the higher the cationic degree of substitution (DS) in amphoteric starches, the better the filler retention. The filler retention is improved 12.5%, 30.3%, and 35.1% and 32.5% respectively by adding 1% amphoteric starch LS-L2 -1 (0.034), LS-L2-2 (0.040), LS-L2-3 (0.047) and LS-L2-4 (0.052). But the strength of handsheets if affected a little. By adding 2% Al2 (SO4)3 and 1.5% LS-L2-3 at pH 7.5, filler retention can be improved from 38% to 80%, and breaking length of sheet only decreases 3.2%. As dry strengthening aids, amphoteric starches were used in eucalyptus APMP. Amphoteric starches are used in eucalyptus APMP. The amphoteric starch LS-L2-2 is better dry strength aid. Adding 1% LS-L2-2 can improve breaking length 24.5%, burst index 42.9%, tear index 38.8%, folding endurance and density of the handsheets.

• 대한소아치과학회지
• /
• 제28권1호
• /
• pp.45-53
• /
• 2001

레진 수복에서 초기에 저광도로 중합하여 레진의 유동성을 허용함으로써 중합시 내부응력을 상쇄하며, 다시 고광도로 중합하여 레진의 물성도 유지할 수 있는 방법이 시도되고 있어 초기 저광도 중합이 상아질과의 결합 강도와 레진의 미세경도에 미치는 영향을 알아보고자 하였다. 소의 건전한 하악 전치 20개를 3개의 절편으로 절단하여 각 군에 배분하고 상아질면에 레진을 충전한 후, I군은 $450mW/cm^2$의 광도도 40초간, II군은 $300mW/cm^2$와 $600mW/cm^2$의 광도로 각각 20초씩 III군은 $250mW/cm^2$와 $450mW/cm^2$에서 각각 20초씩 광중합하여 전단 결합 강도를 측정하였고, 직경 5.0mm깊이 2.0mm레진 시편을 제작하여 상, 하면 중앙에서 Vickers 미세 경도를 측정하였다. 전단결합 강도는 초기 저광도 중합군의 평균이 다소 높았으나 각 군간 통계학적 유의한 차이는 없었으며, 미세 경도는 상하면 모두에서 각 군간 통계학적으로 유의한 차이는 보이지 않았다.

• 대한치과기공학회지
• /
• 제32권3호
• /
• pp.195-207
• /
• 2010

Purpose: The purpose of this study was to observe the microstructural changes of surface in the specimens, performing the shear bond strength testing. The currently most used non-precious alloys are nickel-chromium based alloys with or without beryllium. However, their biocompatibility has been questioned concerning possible damages to the health of the patient and professionals involved in the fabrication of prosthesis caused by long exposure to Ni and Be. An option to nickel-chromium alloys is the cobalt-chromium alloy, an alternative that does not sacrifice the physical properties of the metal porcelain systems. Studies in the animals substantially show that the cobalt-chromium alloys are relatively well tolerated, being therefore more biocompatible than the nickel-chromium alloys. Methods: Non-addition Be to nickel-chromium based alloy(Bellabond plus) and cobalt-chromium alloy which has been widely used(Wirobond C) fused with ZEO light porcelain classified control group and cobalt-chromium alloy which is developing alloy of Alphadent company in Korea(Alphadent alloy) fused with ZEO light porcelain classified experimental group. The specimens of $4mm{\times}4mm{\times}0.5mm$ were prepared as-cast and as-opaque to cast body to analyze the mechanical characteristic change, the microstructure of alloy surface. The phase change was used to observe through XRD analysis and OM/SEM was used to observe the surface of specimens as-cast and as-opaque to cast body. Chemical formation of their elements was measured with EDS. Then hardness was measured with Micro Vicker's hardness tester. Shear bond strength test thirty specimens of $10mm{\times}10mm{\times}2mm$ was prepared, veneered, 3mm high and 3mm in diameter, over the alloy specimens. The shear bond strength test was performed in a universal testing machine(UTM) with a cross head speed of 0.5mm/min. Ultimate shear bond strength data were analyzed with one-way ANOVA and the Scheffe's test (P<0.05). Within the limits of this study, the following conclusions were drawn: The X-ray diffraction analysis results for the as-cast and as-opaque specimens showed that the major relative intensity of Bellabond plus alloy were changed smaller than Wirobond C and Alphadent Co-Cr based alloys. Results: Microstructural analysis results for the opaque specimens showed all the alloys increased carbides and precipitation(PPT). Alphadent Co-Cr based alloy showed the carbides of lamellar type. The Vickers hardness results for the opaque specimens showed Wirobond C and Alphadent Co-Cr based alloys were increaser than before ascast, but Bellabond plus alloy relatively decreased. The mean shear bond strengths (MPa) were: 33.11 for Wirobond C/ZEO light; 25.00 for Alphadent Co-Cr alloy/ZEO light; 18.02 for Bellabond plus/ZEO light. Conclusion: The mean shear bond strengths for Co-Cr and Ni-Cr based alloy were significantly different. But the all groups showed metal-metal oxide modes in shear bond strengths test at the interface.

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2001년도 춘계학술대회 논문집
• /
• pp.193-199
• /
• 2001

In this study, the carbody design of the rubber tired AGT(Automated Guide-way Transit System) under development by KRRI was numerically analysed to evaluate its structural strength according to the standard specifications for Korean LRT (Light Rail Transit). The numerical results showed that the detail design of the carbody was strong enough to satisfy the specifications with respect to the axial compression strength, the vertical strength and the vertical stiffness(natural frequency). However, the carbody design had some problems on the fatigue strength by twist loadings. So, it was recommended that the carbody design should be modified to improve the twisting strength by reinforcing the front end structures.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표대회 논문집(III)
• /
• pp.803-808
• /
• 1998

As carbon fiber is a light-weight materials, high tensile strength and durability compared with rebar, the retrofitting method for RC structures using carbon fiber sheet (CFS) must be use widely. In this paper, the tensile strength test for carbon fiber sheet variable of CF's weight and elastic modulus to evaluate the design tensile strength of carbon fiber sheet which is needed for the strengthening design of CFS and the calculation of strengthening effect. As a result, the design tensile strength of CFS can be calculate using the effect coefficient of strengthening(α) of CFS, the average tensile strength of CFS and the standard deviation of CFS(equation 5)