Polyurethane resin containing isocyanate is marked by excellent tensile and mechanical strengths and this test aims to gauge its applicability as a medical high polymer. Tris [2-(acryloyloxy)ethyl]isocyanurate and hexamethylenediisocyanate were added to a basic mixing ratio of HEMA (2-hydroxyethyl methacrylate), MMA (methyl methacrylate), NVP (n-vinyl-2-pyrrolidone) and crosslink agent, EGDMA (ethylene glycol dimethacrylate) with increasing proportions and copolymerized respectively. Also, the basic physical properties of the polymerized high polymers including refraction rate, tensile strength, light transmission and water content were measured to confirm that they are appropriate as hydrogelcontact lenses. After measuring the physical properties of high performance polymers produced by adding tris [2-(acryloyloxy) ethyl]isocyanurate, it was found that the average tensile strengths of sample TRIS1 to TRIS10 were between 0.285 and 0.612 kgf, while the average values of refractive index were ranged from 1.441 to 1.449 with water content from 30.00 to 37.35%.The measurement of physical properties of the copolymers generated by adding hexamethylenediisocyanate showed that the average tensile strength of sample HEXA1 to HEXA10 ranged from 0.267 to 1.742 kgf, the refractive index ranged from 1.443 to 1.475 and water contents were in the range of 21.22 to 35.58%. In all combinations the transmission rates satisfied the transmittance of general hydrogel contact lenses. From theresults, it is possible to conclude that the produced copolymers can be used as contact lens materials with excellent tensile strength.

• Polymer(Korea)
• /
• v.29 no.1
• /
• pp.59-63
• /
• 2005

Kinetic study of a reaction between poly(caprolactone diol) and aliphatic isocyanate was investigated by FTIR spectroscopy. The reaction rate was obtained from analyzing the absorbance change of NCO peak (2265 $cm^{-1}$) in series IR spectra. In the results, the overall reaction between PCL and isocyanate conformed to the simple second-order law, and the rate constant increases with increasing reaction temperature. The activation energies obtained from the evaluation of kinetic data were 25.4∼30.9 kJ/mol for hexamethylene diisocyanate and 16.8∼22.1 kJ/mol for cyclohexylmethane diisocyanate, respectively.

• Journal of the Korean Wood Science and Technology
• /
• v.26 no.4
• /
• pp.43-49
• /
• 1998

The availability of large quantities of waste woods provides an impetus for investigating woody biomass potential uses. Polyurethane (PU) foams are prepared with reacting isocyanates and polyols, and are used. in various industry fields. Thus, lignocellulosic waste raw-materials are proposed as replacement for synthetic polyol to PU foam formulation. In this study PU foams were manufactured from liquefied woods, methanediisocyanate(MDI), catalyst, foaming stabilizer, and viscosity aids. The polyol content, isocyanate.hydroxyl group (NCO/OH) ratio, and water content were varied to evaluate their effects on the foaming and water absorption of the PU foams. Less than 400 Molecular weight. of polyethylene glycol(PEG) and 1 to 3 solvent to woody raw-material ratio were desirable for liquefying woody materials. Liquefying rate was increased with more than 3 % addition of inorganic and organic catalysts and raising reaction temperature more than $150^{\circ}C$. Addition of starch enhanced liquefying of woody materials. Fourty percents of starch resulted in about 90% liquefying rates. Foaming rates were increased with increasing moisture contents of liquefied wood. Moisture contents of 0.6% resulted in 5 time-foaming rates, and seven percents of moisture contents more than 30 time-foaming rates. But, an increase in water content may result in a decrease in cross-links between wood polyol and isocyanate, because the NCO/OH ratio is constant. Increasing moisture contents have significantly decreased density of PU foams. The optimum water content should be about 2.5% or less in this adopted condition.

• Journal of the Korean Wood Science and Technology
• /
• v.48 no.5
• /
• pp.755-764
• /
• 2020

Due to pronounced mechanical performance and being environmental friendly, aqueous polymer isocyanate adhesive (API) has been widely applied in the production of formaldehyde-free wood products. In this study, flame retardant formaldehyde-free plywood was prepared by incorporation of flame retardants into the API adhesive. Partially phosphorylated poly (vinyl alcohol) (PPVA) which was prepared by reacting poly (vinyl alcohol) with phosphoric acid was used to replace PVA in API formula. In addition, Mg-Al layered double hydroxides (LDH) was chosen as additive flame retardant, replacing traditional filler CaCO₃ in API adhesive formula. And then, the flame retardant API adhesive with main agent (PPVA replacing PVA70wt.%, SBR emulsion 30wt.%), curing agent 10wt.% (accounts for of the main agent), and 20wt.% LDHs (accounts of the main agent) was used to prepare flame retardant plywood. The effect of application of PPVA and Mg-Al LDH on bonding strength of plywood was investigated. The flammability characteristics of the plywood were determined by cone calorimeter test (CCT). The results revealed that compared with the plywood prepared with API adhesive, the use of PPVA and LDH enhanced the flame retardancy of plywood without negatively affecting bonding strength. The CCT tests indicated that the heat release and smoke production flame retardant API plywood were lower than those of the ordinary API glued plywood. Promising developments for flame retardant API adhesive were expected in future applications of flame retardant formaldehyde-free plywood.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.11 no.3
• /
• pp.249-253
• /
• 2001

The purpose of this study is the development of the simple and precise sampling and analysis method of methyl isocyanate(MIC) in the work place as their secondary aliphatic amine derivatives by gas chromatography with flame ionization detector. The urea derivatives are quantitatively and simultaneously derived from MIC with secondary aliphatic amines such as dipropylamine(DPA), dibutylamine(DBA), and dipentylamine (DAA) in methylene chloride. The method is based on sampling glass tube in XAD-2 resin which is coated with secondary aliphatic amines. The samples are desorbed by $2m{\ell}$ methylene chloride and analysed using gas chromatography with flame ionization detector(GC/FID). In the results, the detection limit of the overall procedure and reliable quantity are $0.020-0.027{\mu}g$($1.347-1.740{\mu}g/m^3$(0.529-0.684 ppb) based on a 15 L air volume) MIC per sample. The average desorption efficiencies are 97.96 - 101.23 %. The results of versus storage time are high and stable recovery rates.

• Journal of the Korean Wood Science and Technology
• /
• v.31 no.5
• /
• pp.23-34
• /
• 2003

This study was carried out to investigate the mechanical properties of fabric E-glass fiber reinforced laminated timber. Specimens used to Korean red pine(Pinus densiflora) and Japanese larch(Larix kaemferi). Fabric E-glass fiber was inserted in the solid wood with aqueous polymer-isocyanate resin(MPU-500). The results were as follows: 1. Aqueous polymer-isocyanate resin(MPU-500) was good resin to manufacture laminated timber. specially, it was satisfied to property standard of construction laminated timber(KS F 3021) except for two ply glass fiber. 2. Bending and shear strengths of solid wood inserted with fabric glass fibers were not different from control solid wood. But, proportional limit bending stress was increased following the number of fabric glass fibers. Therefore, it was considered that to improve the bending and shear strength of fabric glass fiber reinforced laminated timber, the glass fiber thickness and its mesh should be modified to fitness following working conditions.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.16 no.3
• /
• pp.222-232
• /
• 2006

Objectives: The objective of this study was to propose the total isocyanate analytical method which involves derivation of 2,4-toluene diisocyanate(2,4-TDI), 2,6-toluene diisocyanate(2,6-TDI), 4,4'-methylenediphenyl diisocyanate(4,4'-MDI) and 1,6-hexamethylene diisocyanate(1,6-HDI) using 2-chlorobenzyl alcohol(2-CBA) or 2,4-dichlorobenzyl alcohol(2,4-DCBA), and analyzing of hydrolysate of the synthesized urethane with the gas chromatography(GC)/flame ionization detector(FID), GC/pulsed discharge ionization detector-electron capture detector(PD-ECD) and GC/mass selective detector(MSD). Methods: Urethanes were synthesized by reacting 2,4-TDI, 2,6-TDI, 4,4'-MDI and 1,6-HDI to 2-CBA or 2,4-DCBA. Urethanes was verified by TLC, HPLC/UVD and GC/MSD. For field application, the most suitable condition that 2-CBA coated in glass fiber filter removed completely and urethanes were not removed was searched. 2-CBA generated from hydrolysis of urethanes according to hydrolysis conditions. Diisocyanates were collected on field air and analyzed. Results: Urethanes which were white and solid phase synthesized by reacting 2,4-TDI, 2,6-TDI, 4,4'-MDI, 1,6-HDI and 2-CBA or 2,4-DCBA. And urethanes were verified by TLC, HPLC/UVD and GC/MSD. The most suitable conditions to remove 2-CBA coated in glass fiber filter were $87^{\circ}C$ and 20 mmHg and urethanes were not removed under same condition. Hydrolysis yields of urethanes were 99 % to 111 %. 2-CBA, the hydrolysate of urethanes was analyzed by GC/FID, GC/PD-ECD and GC/MSD. Conclusions: Simultaneous analysis of 2,4-TDI, 2,6-TDI, 4,4'-MDI and 1,6-HDI deriving with 2-CBA and 2,4-DCBA, along with a total isocyanate analysis, was feasible with GC/FID, GC/PD-ECD and GC/MSD. This result will be a guide of further study on total isocyanate analysis.

• Journal of the Korean Society of Radiology
• /
• v.16 no.2
• /
• pp.103-113
• /
• 2022

In this paper, a combined ¹⁸F-FDG(fluorodeoxyglucose) and MNP(magnetic nanoparticles) contrast agent was synthesized using N-(p-maleimidophenyl) isocyanate as the crosslinker for use in simultaneous PET-MRI scans. PET-MRI images were acquired and evaluated before and after injection of the combined contrast imaging agent (¹⁸F-FDG labeled MNP) from a glioma stem cell mouse model. After setting the region of interest (ROI) on each acquired image, the area of the lesion was calculated by segmentation. As a result, the PET image was larger than the MRI. In particular, the simultaneous PET-MRI images showed accurate lesions along with the surrounding soft tissue. The mean and standard deviation values were higher in the MRI images alone than in the PET images or the simultaneous PET-MRI images, regardless of whether the contrast agent was injected. In addition, the simultaneous PET-MRI image values were higher than for the PET images. For PSNR experiments, the original image was PET Image using 18F-FDG, MRI using MNPs, and MRI without contrast medium, and the target image was simultaneous PET-MRI image using 18F-FDG labeled MNPs contrast medium. As a result, all of them appeared significantly, suggesting that the 18F-FDG labeled MNPs contrast medium is useful. Future research is needed to develop an agent that can simultaneously diagnose and treat through SPECT-MRI imaging research that can use various nuclides.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.2
• /
• pp.143-148
• /
• 2018

The aim of this research was to determine the physical and mechanical properties of glued laminated lumber (glulam) made from jabon (Anthocephalus cadamba) and pine (Pinus merkusii). Three layers of lamina from each wood species were bonded using isocyanate adhesive with a glue spread of $280g{\cdot}m^{-2}$ and then pressed using cold press with a specific pressure of 1.47 MPa. Samples had dimensions of $3cm{\times}6cm{\times}100cm$ (thickness, width, and length, respectively). Glulam properties were tested based on Japanese Agricultural Standard (JAS) 234-2003. The results showed that the density of glulam was $0.36g{\cdot}m^{-3}$ for jabon and $0.73g{\cdot}m^{-3}$ for pine. The moisture content of all glulams fulfilled the JAS standard. The mechanical properties of pine glulam fulfilled the JAS standard in all tests, whereas jabon glulam fulfilled the standard in the modulus of rupture and shear tests.

• Journal of the Korean Applied Science and Technology
• /
• v.23 no.3
• /
• pp.264-271
• /
• 2006

PU type flame-retardant coatings (TBAO/L-75, TBAOL ; TBAO/N-100, TBAON) were prepared by blending bromine-containing modified polyester (TBAO) which was synthesized in our earlier work. with two kinds of isocyanate curing agents, Desmodur L-75 and Desmodur N-100. Physical properties of the prepared flame-retardant coatings were tested. TBAOL shows better hardness than TBAON, while TBAON shows better viscosity, accelerated weathering resistance, yellowness index and lightness index difference than TBAOL. There were no remarkable differences in fineness of grind, $60^{\circ}$ specular gloss, cross-hatch adhesion, and abrasion resistance of TBAOL and TBAON. There was no discernable difference in flame-retardancy between the two flame-retardant coatings, TBAOL and TBAON. When the content of tribromo acetic acid, which is flame-retarding component, was 30wt% the LOI value was in a range of $29{\sim}30%$, which indicates that the two coatings are good flame-retardant coatings.