• Journal of the Korean Ceramic Society
• /
• v.29 no.11
• /
• pp.863-869
• /
• 1992

A SOG(spin glass) solution with excellent wetting to Si wafers was prepared by acid-hydrolysis of Si(OEt)4 and Me2Si(OEt)2. The solution was spin coated on Si wafers, and effects of heat treatment of the film were characterized by TG/DTA, FTIR and Ellipsometry. Silica film was obtained by heat treatment at $600^{\circ}C$ within one hour, but heat treatment at 80$0^{\circ}C$ caused interfacial oxidation of the silicon substrate. Unexpectedly silica films with much better adhesion were obtained by curing at $600^{\circ}C$ for over 30 min. than those obtained by thermal oxidation.

• Proceedings of the KAIS Fall Conference
• /
• 2010.11a
• /
• pp.478-481
• /
• 2010

Antimony doped tin oxide (ATO) nanoparticles were added as nanofillers to UV-curable polyester-acrylate (PEA) resin for coating to improve thermal, mechanical, and electrical properties. In this study, ATO nanoparticles were grafted by 3-glycidyloxypropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane respectively to improve dispersion and interfacial adhesion. The physical properties and surface scratch hardness of the UV-curable nanocomposite coating were improved considerably by introducing the modified ATO nanoparticles.

• Korean Journal of Materials Research
• /
• v.30 no.3
• /
• pp.105-110
• /
• 2020

Cu/PET composite films are widely used in a variety of wearable electronics. Lifetime of the electronics is determined by adhesion between the Cu film and the PET substrate. The formation of an anisotropic nanostructure on the PET surface by surface modification can enhance Cu/PET interfacial adhesion. The shape and size of the anisotropic nanostructures of the PET surface can be controlled by varying the surface modification conditions. In this work, the effect of Cu/PET interface nanostructures on the failure mechanism of a Cu/PET flexible composite film is studied. From observation of the morphologies of the anisotropic nanostructures on plasma-treated PET surfaces, and cross-sections and surfaces of the fractured specimens, the Cu/PET interface area and nanostructure width are analyzed and the failure mechanism of the Cu/PET film is investigated. It is found that the failure mechanism of the Cu/PET flexible composite film depends on the shape and size of the plasmatreated PET surface nanostructures. Cu/PET interface nanostructures with maximal peel strength exhibit multiple craze-crack propagation behavior, while smaller or larger interface nanostructures exhibit single-path craze-crack propagation behavior.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.252-259
• /
• 2016

In order to form an aluminum-doped zinc oxide (AZO) transparent electrode film on a polyethylene terephthalate (PET) substrate used for a flexible display substrate, the AZO transparent electrode was produced at low temperature without substrate heating. Even though the produced electrode showed characteristic optical transmittance of 90 % (at 550 nm) and sheet resistance within $100{\Omega}/sq$, cracks occurred 10 minutes after loading applied 2 mm radius of curvature, and the sheet resistance increased linearly. An insertion layer of ZrCu was formed between the AZO film and the PET substrate to suppress the generation of cracks on the AZO film. It was verified that the crack was not generated 30 minutes after the loading of 2 mm radius of curvature, and no increase in sheet resistance was recorded. There was also not cracks in the dynamic bending test of 4 mm radius, but surface resistance was slightly increased. As a result, the ZrCu insertion film improved the interfacial adhesion between the substrate and AZO film layer without increasing sheet resistance and decreasing transmittance.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.351-355
• /
• 1999

BN films with a high content of cubic phase has been deposited by a variety of techniques. It is well known that c-BN films grow with a unique microstructure consisting of $sp^2$ and $sp^{3-}$ bonded layers. Because of existence of the initially grown $sp^{2-}$ /bonded layer, BN films are not adhesive to the substrates. In this study, post-N$^{+ }$ / implantation was applied to improve the adhesion of the films. A Monte Carlo program TAMIX was used to simulate this modification process. The simulation showed nitrogen concentration profile at $1200\AA$ in depth in case of 50keV -implantation energy. FTIR spectra of the $N^{+}$ implanted specimens demonstrated a strong change of absorption band at 1380 cm$^{ -1 }$The films were also investigated by HRTEM. From these results, it is concluded that the post ion implantation could be an effective technique which improves the adhesion between BN film and substrate.

• Journal of Adhesion and Interface
• /
• v.19 no.1
• /
• pp.13-18
• /
• 2018

At ruthenium (Ru) catalyst was exposed from the atmosphere, the degree of catalyst activation decreased. The change of catalyst activity with the number of days of exposure to air for the Ru catalyst was confirmed using the surface tension method quantitatively. Mechanical properties and surfactant change after polymerization by DCPD using Ru catalyst for each air exposure day was evaluated. The Ru catalyst mixed with a dilution agent was exposed in the air and color was monitored for each day. Surface tension was measured using Wilhelmy and PTFE and associated with different catalyst activities. Heat was measured in real time during polymerizing DCPD with Ru catalyst. After polymerization, tensile strength was measured for p-DCPD and the change of material property was measured. Interfacial properties were also evaluated via microdroplet pull-out tests between glass fiber and p-DCPD. The surface tension was stable until the 4 days (33 dyne/cm) whereas the surface energy increased at the 10 days (34 dyne/cm), which could be correlated with oxidation of the catalyst. Tensile property and interfacial shear strength (IFSS) was also stable until the 4 days (tensile strength: 38 MPa and IFSS: 26 MPa) whereas the mechanical property decrease at 10 days (tensile strength: 15 MPa and IFSS: 3 MPa) dramatically.

• Journal of the Microelectronics and Packaging Society
• /
• v.29 no.3
• /
• pp.37-42
• /
• 2022

Recently, the semiconductor package structures are becoming thinner and more complex. As the thickness decrease, interfacial delamination due to material mismatch can be further maximized, so the reliability of interface is a critical issue in industry field. Especially, the polymers, which are widely used in semiconductor packaging, are significantly affected by the temperature and moisture. Therefore, in this study, the delamination prediction at the interface of package structure was performed through finite element analysis considering the moisture absorption and desorption under the various temperature conditions. The material properties such as diffusivity and saturated moisture content were obtained from moisture absorption test. The hygro-swelling coefficients of each material were analyzed through TMA and TGA after the moisture absorption. The micro-shear test was conducted to evaluate the adhesion strength of each interface at various temperatures considering the moisture effect. The finite element analysis of interfacial delamination was performed that considers both deformation due to temperature and moisture absorption. Consequently, the interfacial delamination was successfully predicted in consideration of the in-situ moisture desorption and temperature behavior during the reflow process.

• Elastomers and Composites
• /
• v.39 no.1
• /
• pp.3-11
• /
• 2004

Plasma treatment is frequently used to increase surface functionality and surface activity. It enables to improve various surface properties such as catalytic selectivity, printability, and interfacial adhesion between various materials. Surface or the ethylene-vinyl acetate (EVA) is exposed under an atmospheric pressure plasma torch (APPT), generated by dielectric barrier discharge (DBD), and the treated surfaces are systemically investigated. Argon, air, and oxygen are used as a processing gas. Properties of the treated EVA surfaces are investigated by the zeta-potential measurements and surface free energies. It is shown that the plasma treatment leads to a drastic increase of surface functional groups of EVA, as the increase of its adhesion energy ($G_{IC}$). Therefore, it is concluded that the APPT process is an effective means to improve adhesion of EVA and polyurethane (PU).

• Tribology and Lubricants
• /
• v.39 no.5
• /
• pp.190-196
• /
• 2023

Anti-adhesion coatings are very important in the processing of adhesive materials such as optical clear adhesive (OCA) films. Choosing the appropriate release coating material for dies and tools can be quite challenging. Hydrophobic surface treatment is usually performed, and its performance is often estimated by the static water contact angle (CA). However, the relationship between the release performance and the CA is not well understood. In this study, the water CAs of surfaces coated with anti-adhesion materials and the peel strengths of the acrylic-based adhesive films are evaluated. STC5 and SUS304 are selected as the base materials. Base materials with different surface roughnesses are produced by hairline finishing, mirror-polishing, and end milling. Four fluoropolymer compounds, including a self-assembled monolayer, are selected to make the base surface hydrophobic. Static, advancing, and receding CAs are mostly increased due to the coating, but the CA hysteresis is found to increase or decrease depending on the coating material. The peel strengths all decreased after coating and are largely dependent on the coating material, with significantly lower values observed for fluorosilane and perfluoropolyether silane coatings. The peel strength is observed to correlate better with the static CA and advancing CA than with the receding CA or hysteresis. However, it is not possible to accurately predict the anti-adhesion performance based on water CA alone, as the peel strengths are not fully proportional to the CAs.

• Composites Research
• /
• v.16 no.4
• /
• pp.74-79
• /
• 2003

Comparison of interfacial properties and microfailure mechanisms of oxygen-plasma treated poly(p-phenylene-2,6-benzobisoxazole(PBO. Zylon) and poly(p-phenylene terephthalamide)(PPTA, Kevlar) fibers/ epoxy composites were investigated using micromechanical technique and nondestructive acoustic emission(AE). Interfacial shear strength(IFSS) and work of adhesion, Wa of PBO or Kevlar fibers/epoxy composites increased by oxygen-plasma treatment. Plasma-treated Kevlar fiber shooed the maximum critical surface tension and polar term, whereas the untreated PBO fiber showed the minimum value. Microfibril fracture pattern of plasma-treated Kevlar fiber appeared obviously. Based on the propagation of microfibril failure toward core region. the number of AE events for plasma-treated PBO and Kevlar fibers increased significantly. The results oi nondestructive AE were consistent well with microfailure modes by optical observation in microdroplet and two-fiber composites tests.